Compressive Failure Mechanics and Acoustic Emission Characteristics of Fiber Reinforced Concrete afterHigh Temperature

Abstract

Abstract: In order to explore the effects of temperature and fiber type on uniaxial compression performance of concrete after high temperature, uniaxial compression tests were carried out on normal concrete, polypropylene imitation steel fiber and polypropylene imitation steel fiber-steel fiber reinforced concrete blocks at different temperatures (20, 200, 400 and 600 ℃), and the acoustic emission monitoring system was used to monitor the compression failure process of concrete. According to the test data obtained from acoustic emission and uniaxial compression test, the damage behavior of concrete after high temperature was analyzed. The results show that the compression failure process of concrete is divided into compaction stage, crack propagation stage and instability cracking stage, and the corresponding acoustic emission process is divided into contact stage, slow increase stage and sharp increase stage. The compressive strength loss rate of each sample at different temperatures ranges from 9% to 49%. Through quantitative analysis of acoustic emission signals, it is known that the incorporation of polypropylene imitation steel fiber and polypropylene imitation steel fiber-steel fiber can reduce the initial damage of concrete at 200, 400 and 600 ℃.

Key words: fiber reinforced concrete, polypropylene imitation steel fiber, high temperature environment, acoustic emission, proportion of stage cumulative amount

CLC Number:

TU528

WANG Qiang, WANG Jiacheng, WANG Nan, ZHANG Wei, XU Dongyu. Compressive Failure Mechanics and Acoustic Emission Characteristics of Fiber Reinforced Concrete afterHigh Temperature[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2025, 44(3): 915-923.

References

[1] KODUR V K R. High-temperature performance of concrete in compression[J].Materials and Structures, 2020, 53(4): 1-14.
[2] 何倍, 张红恩, 朱新平, 等. 高温环境下超高性能混凝土力学性能及劣化机制研究进展[J].硅酸盐学报, 2024, 52(11): 3470-3481.
HE B, ZHANG H E, ZHU X P, et al. Review on mechanical properties and degradation mechanism of ultra-high performance concrete in elevated environment[J].Journal of the Chinese Ceramic Society, 2024, 52(11): 3470-3481 (in Chinese).
[3] 冷玲倻, 张鹏飞, 梁文文. 高温下玄武岩纤维增强地质聚合物混凝土的动态压缩力学行为[J].硅酸盐通报, 2024, 43(3): 914-921.
LENG L Y, ZHANG P F, LIANG W W. Dynamic compressive mechanical behavior of basalt fiber reinforced geopolymer concrete under high temperature[J].Bulletin of the Chinese Ceramic Society, 2024, 43(3): 914-921 (in Chinese).
[4] 王晓磊, 许登钰, 李彦苍, 等. 玄武岩纤维再生混凝土高温水冷损伤试验研究[J].水电能源科学, 2024, 42(3): 83-87.
WANG X L, XU D Y, LI Y C, et al. Experimental study on high-temperature water cooling damage of basalt fiber reinforced recycled concrete[J].Water Resources and Power, 2024, 42(3): 83-87 (in Chinese).
[5] 朱明, 宫能平, 穆朝民, 等. 高温后钢纤维自密实混凝土动、静态力学性能研究[J].硅酸盐通报, 2023, 42(11): 3895-3905.
ZHU M, GONG N P, MU C M, et al. Dynamic and static mechanical properties of steel fiber reinforced self-compacting concrete after exposed to high temperature[J].Bulletin of the Chinese Ceramic Society, 2023, 42(11): 3895-3905 (in Chinese).
[6] 张劲竹, 刘华新, 王家贺, 等. 混杂纤维混凝土高温后性能劣化分析与强度预测[J].硅酸盐通报, 2023, 42(4): 1260-1269.
ZHANG J Z, LIU H X, WANG J H, et al. Performance degradation analysis and strength prediction of hybrid fiber reinforced concrete after high temperature[J].Bulletin of the Chinese Ceramic Society, 2023, 42(4): 1260-1269 (in Chinese).
[7] 朱德, 韩阳, 沈雷, 等. 高温后钢纤维混凝土热学性能试验研究[J].消防科学与技术, 2020, 39(11): 1477-1481.
ZHU D, HAN Y, SHEN L, et al. Experimental study on thermal properties of steel fiber reinforced concrete after elevated temperature[J].Fire Science and Technology, 2020, 39(11): 1477-1481 (in Chinese).
[8] LEI L, DONG L, AN H, et al. Experimental study of the thermal and dynamic behaviors of polypropylene fiber-reinforced concrete[J].Applied Sciences, 2021, 11(22): 10757.
[9] 庞建勇, 郑瑞琪, 胡秀月, 等. 高温后冷却方式对玄武岩纤维混凝土力学性能的影响[J].硅酸盐通报, 2024, 43(1): 92-101.
PANG J Y, ZHENG R Q, HU X Y, et al. Effect of cooling method after high temperature on mechanical properties of basalt fiber reinforced concrete[J].Bulletin of the Chinese Ceramic Society, 2024, 43(1): 92-101 (in Chinese).
[10] 姚秀鹏, 韩阳, 沈雷, 等. 高温后聚丙烯纤维混凝土抗压强度与气渗系数试验研究[J].混凝土, 2022(2): 85-89.
YAO X P, HAN Y, SHEN L, et al. Experimental study on compressive strength and air permeability of polypropylene fiber reinforced concrete after elevated temperature[J].Concrete, 2022(2): 85-89 (in Chinese).
[11] 许成祥, 赵晓悦, 许奇琦, 等. 钢-PVA混杂纤维高性能混凝土高温后残余力学性能试验研究[J].科学技术与工程, 2024, 24(5): 2015-2025.
XU C X, ZHAO X Y, XU Q Q, et al. Experimental study on the residual mechanical properties of steel-PVA hybrid fiber high performance concrete after high temperature[J].Science Technology and Engineering, 2024, 24(5): 2015-2025 (in Chinese).
[12] ARASH B, HWA K C, TOMOKI S. Advanced structural health monitoring of concrete structures with the aid of acoustic emission[J].Construction and Building Materials, 2014, 65: 282-302.
[13] 刘鑫, 杨鼎宜, 刘廉, 等. 热-力耦合作用下PVA纤维混凝土力学性能及其声发射响应[J].材料导报, 2018, 32(18): 3135-3141.
LIU X, YANG D Y, LIU L, et al. Mechanical properties and acoustic emission response of PVA fiber reinforced concrete under thermo-mechanical coupling[J].Materials Review, 2018, 32(18): 3135-3141 (in Chinese).
[14] 刘鑫, 侯新宇, 林军, 等. 实时高温下钢纤维混凝土的力学特性及其声发射响应[J].硅酸盐通报, 2021, 40(2): 447-454.
LIU X, HOU X Y, LIN J, et al. Mechanical properties and acoustic emission response of steel fiber reinforced concrete under real time high temperature[J].Bulletin of the Chinese Ceramic Society, 2021, 40(2): 447-454 (in Chinese).
[15] 黄加圣, 杨鼎宜, 朱振东, 等. 高温后聚乙烯醇纤维混凝土受压破坏声发射特性研究[J].混凝土, 2019(1): 47-51+56.
HUANG J S, YANG D Y, ZHU Z D, et al. Study on acoustic emission characteristics of polyvinyl alcohol fiber concrete compression damage after high temperature[J].Concrete, 2019(1): 47-51+56 (in Chinese).
[16] 崔正龙, 孙万吉, 费海超, 等.碳化高温后再生混凝土受压声发射特性与损伤演化[J].土木与环境工程学报, 2024, 46(4): 175-185.
CUI Z L, SUN W J, FEI H C, et al. Acoustic emission characteristics and damage evolution of recycled concrete after carbonization at high temperature under axial compression[J].Journal of Civil and Environmental Engineering, 2024, 46(4): 175-185 (in Chinese).
[17] 宿辉, 栾亚伟, 胡宝文, 等. 基于声发射的混凝土热力耦合损伤特性研究[J].水电能源科学, 2023, 41(10): 158-162.
SU H, LUAN Y W, HU B W, et al. Analysis of damage characteristics of concrete thermodynamic coupling based on acoustic emission[J].Water Resources and Power, 2023, 41(10): 158-162 (in Chinese).
[18] LI X, CHEN X D, JIVKOV A P, et al. Assessment of damage in hydraulic concrete by gray wolf optimization-support vector machine model and hierarchical clustering analysis of acoustic emission[J].Structural Control and Health Monitoring, 2022, 29(4): 1-22.
[19] 赵海溪, 丁梦磊, 刘雪艳, 等.岩石声发射b值及其计算方法研究[J].河南科技, 2023, 42(8): 69-72.
ZHAO H X, DING M L, LIU X Y, et al. Study on rock acoustic emission b-value and Its calculation method[J].Henan Science Technology, 2023, 42(8): 69-72 (in Chinese).
[20] CARPINTERI A, LACIDOGNA G, PUZZI S. From criticality to final collapse: evolution of the “b-value” from 1.5 to 1.0[J].Chaos, Solitons & Fractals, 2009, 41(2): 843-853.
[21] 中华人民共和国住房和城乡建设部. 混凝土物理力学性能试验方法标准: GB/T 50081—2019[S].北京: 中国建筑工业出版社, 2019.
Ministry of Housing and Urban-Rural Development of the People's Republic of China, State Administration of Market Supervision and Administration. Standard for test methods of physical and mechanical properties of concrete: GB/T 50081—2019[S].Beijing: China Construction Industry Press, 2019 (in Chinese).
[22] 中国建筑科学研究院. 纤维混凝土应用技术规程: JGJ/T 221—2010[S].北京: 中国建筑工业出版社, 2010.
China Academy of Building Research. Technical specification for application of fiber reinforced concrete: JGJ/T 221—2010[S].Beijing: China Construction Industry Press, 2010 (in Chinese).
[23] 门进杰. 混凝土构件的声发射性能: 试验、理论和方法[M].北京: 科学出版社, 2020.
MEN J J. Acoustic emission properties of concrete members: tests, theories and methods[M].Beijing: Science Press, 2020 (in Chinese).
[24] 杨康, 李冬雪, 何兆益, 等. 基于声发射的混凝土全时域损伤试验研究[J].重庆交通大学学报(自然科学版), 2021, 40(12): 110-116.
YANG K, LI D X, HE Z Y, et al. Experimental study on full time domain damage of concrete based on acoustic emission[J].Journal of Chongqing Jiaotong University(Natural Science), 2021, 40(12): 110-116 (in Chinese).