山核桃蒲壳生物炭砂浆基本性能及机理研究

摘要/Abstract

摘要： 将生物炭用于水泥基材料可改善其基本性能,实现固碳的同时丰富了生物质固废资源化利用的途径。为研究山核桃蒲壳生物炭作为细骨料对水泥砂浆性能的影响规律及作用机理,将其以不同体积分数替代细骨料制备砂浆,对水泥砂浆拌合物的流动性、硬化砂浆的微观结构、基本力学性能及保温性能展开试验研究。结果表明:1)拌和时添加25%(占生物炭质量分数)的水作为附加用水,拌合物的工作性最稳定。2)生物炭25%(体积分数)替代砂时,骨料周围可形成良好的浆体握裹及界面过渡区,使砂浆试件抗折强度和抗压强度最高;随着砂替代率的增加,砂浆试件的强度均逐级减小。3)随着生物炭用量的增加,水泥砂浆导热系数呈显著的逐级下降趋势,生物炭的原生孔隙延长了热传导路径,并发挥了慢导热作用,添加生物炭可显著提高水泥砂浆的保温隔热性能。

关键词: 山核桃蒲壳生物炭, 砂浆, 细骨料, 工作性能, 强度, 保温性能

Abstract: The use of biochar in cement-based materials can improve their basic properties and achieve carbon sequestration while enriching the ways of resource utilization of biomass solid waste. To study the effect of carya cathayensis peels biochar on mortar's performance, including fluidity, microstructure, basic mechanical properties and thermal insulation, mortar samples whose fine aggregates were partially or completely replaced by carya cathayensis peels biochar were prepared. The experiment results suggest that: 1) the best workability of the mix is found with extra water addition at the rate of 25% of biochar by mass. 2) The highest flexural and compressive strength are found in mortar with 25% biochar-sand-replacement by volume fraction, which has a better interfacial transition zone and paste-wrapping around the aggregates particles, beyond this addition. With the increase of sand substitution rate, the strength of mortar specimens decreases step by step. 3) The thermal conductivity of cement mortar presents a significant decreasing trend with the increase of biochar addition. The native pores of biochar prolong the heat transporting path and exhibit the effect of slowing down thermal conduction which significantly improve the thermal insulation and heat preservation performance of cement mortar.

Key words: carya cathayensis peels biochar, mortar, fine aggregate, working property, strength, thermal insulation property

中图分类号:

TU528.59

周文建, 薛文, 许丹, 李颖. 山核桃蒲壳生物炭砂浆基本性能及机理研究[J]. 硅酸盐通报, 2023, 42(9): 3186-3195.

ZHOU Wenjian, XUE Wen, XU Dan, LI Ying. Research on Basic Properties and Mechanism of Carya Cathayensis Peels Biochar Mortar[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2023, 42(9): 3186-3195.

参考文献

[1] ZHANG D, GHOULEH Z, SHAO Y X. Review on carbonation curing of cement-based materials[J]. Journal of CO₂ Utilization, 2017, 21: 119-131.
[2] 姜志翔, 郑浩, 李锋民, 等. 生物炭碳封存技术研究进展[J]. 环境科学, 2013, 34(8): 3327-3333.
JIANG Z X, ZHENG H, LI F M, et al. Research progress on biochar carbon sequestration technology[J]. Environmental Science, 2013, 34(8): 3327-3333 (in Chinese).
[3] JANG J G, KIM G M, KIM H J, et al. Review on recent advances in CO₂ utilization and sequestration technologies in cement-based materials[J]. Construction and Building Materials, 2016, 127: 762-773.
[4] LENG L J, HUANG H J, LI H, et al. Biochar stability assessment methods: a review[J]. Science of the Total Environment, 2019, 647: 210-222.
[5] DAI Y J, ZHANG N X, XING C M, et al. The adsorption, regeneration and engineering applications of biochar for removal organic pollutants: a review[J]. Chemosphere, 2019, 223: 12-27.
[6] LEHMANN J, RILLIG M C, THIES J, et al. Biochar effects on soil biota: a review[J]. Soil Biology and Biochemistry, 2011, 43(9): 1812-1836.
[7] YOU S M, OK Y S, CHEN S S, et al. A critical review on sustainable biochar system through gasification: energy and environmental applications[J]. Bioresource Technology, 2017, 246: 242-253.
[8] MENSAH R, SHANMUGAM V, NARAYANAN S, et al. Biochar-added cementitious materials: a review on mechanical, thermal, and environmental properties[J]. Sustainability, 2021, 13(16): 9336.
[9] AHMAD S, KHUSHNOOD R A, JAGDALE P, et al. High performance self-consolidating cementitious composites by using micro carbonized bamboo particles[J]. Materials & Design, 2015, 76: 223-229.
[10] GUPTA S, KUA H W, KOH H J. Application of biochar from food and wood waste as green admixture for cement mortar[J]. Science of the Total Environment, 2018, 619/620: 419-435.
[11] GUPTA S, KUA H W. Carbonaceous micro-filler for cement: effect of particle size and dosage of biochar on fresh and hardened properties of cement mortar[J]. Science of the Total Environment, 2019, 662: 952-962.
[12] AKHTAR A, SARMAH A K. Novel biochar-concrete composites: manufacturing, characterization and evaluation of the mechanical properties[J]. Science of the Total Environment, 2018, 616/617: 408-416.
[13] 李赫. 污泥生物炭混凝土性能及效益研究[D]. 西安: 长安大学, 2020.
LI H. Performances and effects of the sludge biochar concrete[D]. Xi'an: Changan University, 2020 (in Chinese).
[14] CUTHBERTSON D, BERARDI U, BRIENS C, et al. Biochar from residual biomass as a concrete filler for improved thermal and acoustic properties[J]. Biomass and Bioenergy, 2019, 120: 77-83.
[15] 姜晓雨. 生物炭水泥基复合材料性能影响研究[D]. 邯郸: 河北工程大学, 2020.
JIANG X Y. Research on the influence of biochar cement-based composite materials[D]. Handan: Hebei University of Engineering, 2020 (in Chinese).
[16] TAN K H, PANG X J, QIN Y H, et al. Properties of cement mortar containing pulverized biochar pyrolyzed at different temperatures[J]. Construction and Building Materials, 2020, 263: 120616.
[17] WU F, YU Q L, LIU C W. Durability of thermal insulating bio-based lightweight concrete: understanding of heat treatment on bio-aggregates[J]. Construction and Building Materials, 2021, 269: 121800.
[18] 施麟芸, 匡敬忠, 刘松柏, 等. 铜尾矿建材化应用研究现状及矿物组成影响作用规律[J]. 硅酸盐通报, 2022, 41(10): 3511-3524.
SHI L Y, KUANG J Z, LIU S B, et al. Research status of building material application of copper tailings and influencing rules of mineral composition[J]. Bulletin of the Chinese Ceramic Society, 2022, 41(10): 3511-3524 (in Chinese).
[19] 张学兵. 再生混凝土改性及配合比设计研究[D]. 长沙: 湖南大学, 2015.
ZHANG X B. Modification and mix proportion design of recycled concrete[D]. Changsha: Hunan University, 2015 (in Chinese).
[20] 黄开林, 李书进, 臧旭航. 不同类型再生细骨料对保温混凝土力学性能的影响[J]. 硅酸盐通报, 2021, 40(7): 2341-2347+2379.
HUANG K L, LI S J, ZANG X H. Effects of different types of recycled fine aggregate on mechanical properties of thermal insulation concrete[J]. Bulletin of the Chinese Ceramic Society, 2021, 40(7): 2341-2347+2379 (in Chinese).
[21] 董帅锋. 高温损伤水泥砂浆微结构演化及水分传输与力学性能的试验研究[D]. 青岛: 青岛理工大学, 2019.
DONG S F. Experimental study on microstructure evolution, water transport and mechanical properties of high temperature damaged cement mortar[D]. Qingdao: Qingdao Tehcnology University, 2019 (in Chinese).
[22] 申嘉荣, 徐千军. 高温对混凝土孔隙结构改变和抗压强度降低作用的规律研究[J]. 材料导报, 2020, 34(2): 2046-2051.
SHEN J R, XU Q J. Characteristics of pore structure change and compressive strength reduction of concrete under elevated temperatures[J]. Materials Reports, 2020, 34(2): 2046-2051 (in Chinese).
[23] 陈猛, 颜鑫, 陈建淞, 等. 回收轮胎聚合物纤维混凝土高温损伤超声特性研究[J]. 材料导报, 2022, 36(11): 120-125.
CHEN M, YAN X, CHEN J S, et al. Study on ultrasonic characteristics of high temperature damage of recycled tyre polymer fiber reinforced concrete[J]. Materials Reports, 2022, 36(11): 120-125 (in Chinese).
[24] 彭小芹. 土木工程材料[M]. 4版. 重庆: 重庆大学出版社, 2021: 56-79.
PENG X Q. Civil engineering materials [M]. 4th ed. Chongqing: Chongqing University Press, 202: 56-79 (in Chinese).