Coherent Silica Fiber Bundles with Ultra-High Resolution

XU Yantao, GUO Haitao, HOU Chaoqi, CUI Xiaoxia, GAO Song, ZHANG Yan, SHE Shengfei

Research Laboratory of Photonic Functional Materials and Devices, Xi'an Institute of Optics and Precision Mechanics, Chinese Academy of Sciences, Xi'an 710119, China

Received:2022-08-15 Revised:2022-09-21 Online:2022-11-15 Published:2022-12-12

摘要/Abstract

摘要： 石英光纤传像束在医疗诊断、工业设备探伤、电力设施监测、大视场成像等领域具有重要应用。本文利用溶胶-凝胶法在像元单丝间隙中引入吸收剂,解决了传像束光串扰难题。采用一次复丝工艺,制备出外径为600 μm、像元为15 000的石英光纤传像束,像元单丝直径约4.4 μm,分辨率约为113 lp/mm。结果表明,传像束无暗丝、断丝,成像清晰,无畸变,达到了商品化使用需求。

关键词: 光纤传像束, 石英光纤, 高分辨率, 复丝法, 溶胶-凝胶法, 吸收剂

Abstract: Coherent silica fiber bundles have important applications in medical diagnosis, industrial equipment defects detection, high-voltage transformer winding monitoring, and large field optical systems. The sol-gel method is used to introduce absorbent into pixel monofilament gap, which successfully solves the problem of crosstalk in bundles. Silica fiber bundles with 600 μm outer diameter, 15 000 pixels, 4.4 μm pixel diameter, and resolution of 113 lp/mm were prepared by one-step multiple-fiber process. The results show that there are no dark or broken pixels, no distortion in bundles and the image is clear, which means the coherent silica fiber bundles meet the commercial use requirements.

Key words: coherent fiber bundle, silica fiber, high resolution, multiple-fiber method, sol-gel method, absorbent

中图分类号:

TB34

许彦涛, 郭海涛, 侯超奇, 崔晓霞, 高菘, 张岩, 折胜飞. 超高分辨率石英光纤传像束[J]. 硅酸盐通报, 2022, 41(11): 3777-3780.

XU Yantao, GUO Haitao, HOU Chaoqi, CUI Xiaoxia, GAO Song, ZHANG Yan, SHE Shengfei. Coherent Silica Fiber Bundles with Ultra-High Resolution[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(11): 3777-3780.

参考文献

[1] QI S S, ZHANG B, ZHAI C C, et al. High-resolution chalcogenide fiber bundles for longwave infrared imaging[J]. Optics Express, 2017, 25(21): 26160-26165.
[2] 孙宏宇,谢欣,卢鑫.基于光纤传输的柔性红外光学成像系统设计[J].光电技术应用,2021,36(3):11-14.
SUN H Y, XIE X, LU X. Design of flexible infrared optical imaging system based on optical fiber transmission[J]. Electro-Optic Technology Application, 2021, 36(3): 11-14 (in Chinese).
[3] HEYVAERT S, OTTEVAERE H, KUJAWA I, et al. Numerical characterization of an ultra-high NA coherent fiber bundle part I: modal analysis[J]. Optics Express, 2013, 21(19): 21991-22011.
[4] ZHOU D C, YU F X, TAN F, et al. Preparation and optical performance detection of acid-leaching optical fiber image bundle[C]//Proc SPIE 7282, 4th International Symposium on Advanced Optical Manufacturing and Testing Technologies: Advanced Optical Manufacturing Technologies. Chengdu: SPIE, 2009.
[5] 扈性纯.酸溶法光纤传像束暗丝分析[J].应用光学,1998,19(1):26-31.
HU X C. Analysis of dark fiber in image transmitting fiber bundle using acid solution method[J]. Journal of Applied Optics, 1998, 19(1): 26-31 (in Chinese).
[6] 王中俭,夏冬,胡一晨,等.酸溶法柔性光纤传像束的玻璃组成及性能[J].材料科学与工程学报,2009,27(6):809-812+836.
WANG Z J, XIA D, HU Y C, et al. Glass compositions and properties for the fabrication of flexible image bundle by using acid leaching process[J]. Journal of Materials Science and Engineering, 2009, 27(6): 809-812+836 (in Chinese).
[7] MATSUDA Y, HATTORI Y, CHIGUSA Y. Low-loss high-resolution silica image fiber fabricated by the new multiple-fiber method[C]//Optical Fiber Communication. Washington: OSA, 1984.
[8] WOOD H A C, HARRINGTON K, BIRKS T A, et al. High-resolution air-clad imaging fibers[J]. Optics Letters, 2018, 43(21): 5311-5314.
[9] 张振远,徐明泉,李莉,等.一种高分辨率大信息量光纤传像束的制造工艺试验[J].玻璃纤维,2010(2):28-31.
ZHANG Z Y, XU M Q, LI L, et al. Experiment of manufacturing a type of image guide with high resolution and large information content[J]. Fiber Glass, 2010(2): 28-31 (in Chinese).

[1]	关彤, 靳钊, 邵华锋, 孙金芮. 单分散大粒径介孔二氧化硅微球的制备及表征[J]. 硅酸盐通报, 2022, 41(9): 3288-3295.
[2]	段宁, 李崇瑞, 陆成龙, 张银凤, 张湘泰, 熊江敏. TiO₂-Al₂O₃复合粉体的制备及光催化性能[J]. 硅酸盐通报, 2022, 41(12): 4477-4486.
[3]	段宁, 张湘泰, 陆成龙, 张银凤, 李崇瑞. 硝酸对溶胶-凝胶法制备AlOOH胶粒粒度的影响[J]. 硅酸盐通报, 2021, 40(9): 3105-3113.
[4]	吴洪, 陈前林, 李翠芹. 多孔竹炭负载SnO₂的制备及其电化学性能研究[J]. 硅酸盐通报, 2021, 40(11): 3740-3749.
[5]	田清泉, 李沛莹, 曹攀婷, 余强霞. 铋及钴掺杂TiO₂陶瓷负载膜的制备及光催化性能[J]. 硅酸盐通报, 2021, 40(11): 3750-3755.
[6]	邵凌波;田长安;梁升;王亚君;陈捷;阳杰. 固体氧化物燃料电池电解质材料 Ce0.8Sm0.2-xCuxO1.9-δ的制备与性能研究[J]. 硅酸盐通报, 2020, 39(5): 1608-1613.
[7]	陈七;何峰;张树岩;张博文;张鸣奇;刘锡宇;施江. 不同ATO掺量对SiO2/ATO-SiO2疏水型抗静电增透膜性能的影响[J]. 硅酸盐通报, 2019, 38(8): 2391-239.
[8]	张小婷;汪潇;杨浩远;李东林;赵建礼. pH值对纤维增强SiO2气凝胶隔热材料性能的影响[J]. 硅酸盐通报, 2019, 38(8): 2668-267.
[9]	焦静涛;姜芸;杨松;张敬敏;邓朝勇;王旭. 锆钛酸钡钙的结构与铁电光学性能研究[J]. 硅酸盐通报, 2019, 38(11): 3524-352.
[10]	陆文涛;赵青南;王晓宏;常潇;董玉红;赵杰. 可见光照射下Fe3+掺杂量对玻璃基TiO2薄膜亲水性能的影响[J]. 硅酸盐通报, 2019, 38(10): 3293-330.
[11]	刘展晴. 钛酸铜镧粉末及陶瓷的制备、结构及介电性能研究[J]. 硅酸盐通报, 2018, 37(4): 1332-1337.
[12]	刘展晴. 溶胶-凝胶法制备Na1/2La1/2Cu3Ti4O12粉体及陶瓷的结构与巨介电性研究[J]. 硅酸盐通报, 2017, 36(3): 816-821.
[13]	赵思琪;马丽萍;杨杰;崔晓婧. CO2捕集的研究现状及钙基吸收剂的应用[J]. 硅酸盐通报, 2017, 36(11): 3683-3690.
[14]	林茵茵;谢襄漓;李存军;王昕;张兵;王林江. LDO负载纳米二氧化钛复合物的制备及其光催化性能研究[J]. 硅酸盐通报, 2017, 36(11): 3829-3834.
[15]	邢宏伟;谷少鹏;刘志刚;杨立荣. 高炉渣纤维负载TiO2光催化材料的制备及其光催化性能[J]. 硅酸盐通报, 2016, 35(8): 2329-2334.

超高分辨率石英光纤传像束

Coherent Silica Fiber Bundles with Ultra-High Resolution

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价