Preparation of Cordierite Based Porous Ceramics byImpregnation Method

Abstract

Abstract: Cordierite porous ceramics were prepared by organic foam impregnation method using kaolin from Panxi region as main raw material and adding a small amount of alumina and magnesium oxide, to study the effects of organic foam pretreatment time and slurry solid content on the microstructure and physical properties of cordierite porous ceramics. The results show that when m(kaolin) ∶m(Al₂O₃) ∶m(MgO)=66 ∶21 ∶13, the sintering temperature is 1 250 ℃ and the holding time is 0.5 h, the pore size of cordierite porous ceramics is 1.0~1.2 mm, the apparent porosity is 75.42%~96.27%, the compressive strength is 0.23~1.78 MPa, and the permeability coefficient is 18.58~25.86 cm·s^-1. When the mass fraction of slurry solid content is 40%, the water permeability and apparent porosity of cordierite porous ceramics produced by pretreatment of organic foam (NaOH solution soaking) for 6 h, and heat preservation at 1 250 ℃ for 0.5 h are 20.45 cm·s^-1 and 90.73%, respectively.

Key words: cordierite, porous ceramics, impregnation method, water permeability coefficient, compressive strength

CLC Number:

TQ175

CHEN Dongli. Preparation of Cordierite Based Porous Ceramics byImpregnation Method[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2024, 43(3): 1070-1077.

References

[1] 邓先功. 发泡-注凝成型法制备莫来石柱晶自增强多孔陶瓷及其高温力学和热学性能[D]. 武汉: 武汉科技大学, 2016.
DENG X G. Preparation of mullite columnar self-reinforced porous ceramics by foaming-injection molding method and its high temperature mechanical and thermal properties[D]. Wuhan: Wuhan University of Science and Technology, 2016 (in Chinese).
[2] 秦梦黎. 堇青石合成及晶须原位增强堇青石质隔热材料的研究[D]. 武汉: 武汉科技大学, 2018.
QIN M L. Study on synthesis of cordierite and in-situ reinforcement of cordierite thermal insulation materials by whiskers[D]. Wuhan: Wuhan University of Science and Technology, 2018 (in Chinese).
[3] WANG S X, WANG H, CHEN Z W, et al. Fabrication and characterization of porous cordierite ceramics prepared from fly ash and natural minerals[J]. Ceramics International, 2019, 45(15): 18306-18314.
[4] LI F K, SHEN B X, TIAN L H, et al. Enhancement of SCR activity and mechanical stability on cordierite supported V₂O₅-WO₃/TiO₂ catalyst by substrate acid pretreatment and addition of silica[J]. Powder Technology, 2016, 297: 384-391.
[5] 李昊, 李翠伟, 汪长安. 轻质高强堇青石多孔陶瓷的制备与表征[J]. 陶瓷学报, 2021, 42(4): 632-638.
LI H, LI C W, WANG C A. Preparation and characterization of lightweight and high-strength cordierite porous ceramics[J]. Journal of Ceramics, 2021, 42(4): 632-638 (in Chinese).
[6] 徐卫, 侯蕾, 杜霞茹, 等. 蜂窝陶瓷负载Pd基整体式催化剂制备及催化燃烧性能[J]. 工业催化, 2019, 27(11): 54-56.
XU W, HOU L, DU X R, et al. Preparation and properties of honeycomb ceramic supported Pd based monolithic catalyst for catalytic combustion[J]. Industrial Catalysis, 2019, 27(11): 54-56 (in Chinese).
[7] OBRADOVIĆ N, RUSMIROVIĆ J, FILIPOVIĆ S, et al. Porous cordierite-supported polyethyleneimine composites for nickel(II) and cadmium(II) ions removal[J]. Desalination and Water Treatment, 2020, 192: 283-296.
[8] 王露露, 马北越. 堇青石多孔陶瓷制备及其性能优化研究进展[J]. 耐火材料, 2022, 56(1): 82-87.
WANG L L, MA B Y. Progress in the preparation of cordierite porous ceramics and optimization of its properties[J]. Refractory Materials, 2022, 56(1): 82-87 (in Chinese).
[9] 金宏, 张伟, 邓湘云, 等. 不同铝源对SiC/堇青石复相多孔陶瓷的制备及性能影响[J]. 硅酸盐通报, 2018, 37(2): 403-410.
JIN H, ZHANG W, DENG X Y, et al. Effect of different aluminum sources on the preparation and properties of SiC/cordierite composite porous ceramics[J]. Bulletin of the Chinese Ceramic Society, 2018, 37(2): 403-410 (in Chinese).
[10] FUJI M, SHIROKI Y, MENCHAVEZ R L, et al. Fabrication of cordierite filter by in situ solidification for high temperature dust collection[J]. Powder Technology, 2007, 172(1): 57-62.
[11] 袁磊, 和珍宝, 于景坤. 超塑性高温发泡制备闭孔多孔Al₂O₃基陶瓷[J]. 东北大学学报(自然科学版), 2013, 34(7): 939-943.
YUAN L, HE Z B, YU J K. Fabrication of Al₂O₃-based porous ceramic with closed pores by superplastic high-temperature foaming method[J]. Journal of Northeastern University (Natural Science), 2013, 34(7): 939-943 (in Chinese).
[12] 马北越, 魏新崇, 尹国学. 煅烧温度对粉煤灰制备莫来石闭孔陶瓷性能的影响[J]. 耐火材料, 2020, 54(4): 334-337.
MA B Y, WEI X C, YIN G X. Effects of calcination temperature on properties of closed pore mullite ceramics prepared from coal ash[J]. Refractories, 2020, 54(4): 334-337 (in Chinese).
[13] 丁昌库. 凝胶注模法制备堇青石多孔陶瓷的研究[D]. 济南: 山东大学, 2016.
DING C K. Study on preparation of cordierite porous ceramics by gel injection molding[D]. Jinan: Shandong University, 2016 (in Chinese).
[14] LI H, LI C W, WU L H. Porous cordierite ceramics prepared by foam-gelcasting technique: phase evolution and properties[J]. Journal of Alloys and Compounds, 2019, 791: 690-699.
[15] ROMERO A, ELSAYED H, BERNARDO E. Highly porous cordierite ceramics from engineered basic activation of metakaolin/talc aqueous suspensions[J]. Journal of the European Ceramic Society, 2020, 40: 6254-6258.
[16] 耿鹏. 煤系高岭土冷冻干燥法制备多孔堇青石的研究[D]. 徐州: 中国矿业大学, 2018.
GENG P. Study on preparation of porous cordierite by freeze-drying of coal-series kaolin[D]. Xuzhou: China University of Mining and Technology, 2018 (in Chinese).
[17] PAN Y H, ZHU P F, WANG R, et al. Direct ink writing of porous cordierite honeycomb ceramic[J]. Ceramics International, 2019, 45(12): 15230-15236.
[18] 康永, 张庆. 有机泡沫浸渍法氧化铝多孔陶瓷制备研究[J]. 佛山陶瓷, 2016, 26(11): 45-49.
KANG Y, ZHANG Q. Study on preparation of alumina porous ceramics by organic foam impregnation method[J]. Foshan Ceramics, 2016, 26(11): 45-49 (in Chinese).
[19] 陈若愚, 黑大千, 汪瑜凡, 等. 有机泡沫浸渍法制备多孔结构陶瓷研究现状[J]. 耐火材料, 2018, 52(6): 475-480.
CHEN R Y, HEI D Q, WANG Y F, et al. Progress in preparation of porous structure ceramics by organic foam impregnation method[J]. Refractories, 2018, 52(6): 475-480 (in Chinese).
[20] 岳瑞, 魏耀武, 孙华云, 等. 浆料固含量对有机泡沫浸渍法制备CaO基泡沫陶瓷显微结构的影响[J]. 耐火材料, 2019, 53(5): 342-347.
YUE R, WEI Y W, SUN H Y, et al. Effect of slurry solid content on microstructure of CaO based porous ceramics prepared by polymeric foam impregnation[J]. Refractories, 2019, 53(5): 342-347 (in Chinese).
[21] 周显芝. 有机泡沫浸渍法制备多孔莫来石—刚玉陶瓷及其性能研究[D]. 合肥: 安徽建筑大学, 2022.
ZHOU X Z. Preparation and properties of porous mullite-corundum ceramics by organic foam impregnation[D]. Hefei: Anhui Jianzhu University, 2022 (in Chinese).
[22] 何秀兰, 杨亦天, 杨悦, 等. 有机泡沫浸渍法制备Al₂O₃多孔陶瓷及其性能研究[J]. 中国陶瓷, 2014, 50(7): 54-57.
HE X L, YANG Y T, YANG Y, et al. Study on the preparation and properties of porous Al₂O₃ ceramics prepared by the organic foam impregnation method[J]. China Ceramics, 2014, 50(7): 54-57 (in Chinese).
[23] 张学斌, 任祥军, 王松林, 等. 堇青石多孔陶瓷的制备与性能表征[J]. 硅酸盐学报, 2006, 34(2): 247-250.
ZHANG X B, REN X J, WANG S L, et al. Preparation and characterization of porous cordierite ceramics from fly ash[J]. Journal of the Chinese Ceramic Society, 2006, 34(2): 247-250 (in Chinese).
[24] 姚秀敏, 谭寿洪, 黄政仁. 聚氨酯海绵的预处理对网眼多孔陶瓷性能的影响[J]. 硅酸盐学报, 2005, 33(10): 1215-1219.
YAO X M, TAN S H, HUANG Z R. Influence of polymeric sponge pre-treatment on properties of reticulated porous ceramics[J]. Journal of the Chinese Ceramic Society, 2005, 33(10): 1215-1219 (in Chinese).