Performance of Desulfurization Building Gypsum Modified by Inorganic Cementitious Materials

Abstract

Abstract: Circulating fluidized bed (CFB) ash has good volcanic ash properties, desulfurization building gypsum was used as the main cementitious material, carbide slag was used as an alkali activator, CFB ash and fly ash were used as mineral additives to study the effect of CFB ash on the fluidity, setting time, compressive strength and expansion rate of desulfurization building gypsum. The hydration products and microstructure were analyzed by using X-ray diffraction (XRD), scanning electron microscopy (SEM), and other methods. The results show that adding CFB ash can effectively improve the mechanical property and water resistance of desulfurization building gypsum, but it has a negative impact on its workability and expansiveness. After composite modification with 20% (mass fraction) CFB fly ash and 5% (mass fraction) carbide slag, the absolute dry compressive strength of desulfurization building gypsum at 1 and 28 d is 20.53 and 22.37 MPa, which increases by 28.6% and 35.9% compared to desulfurization building gypsum based samples, respectively. The calcium silicate hydrate (C-S-H) gel and ettringite (AFt) generated from the hydration of CFB ash are wrapped and filled in the crystal surface and voids of dihydrate gypsum, making the internal structure of the hardened body more compact, thus improving the mechanical property and water resistance of desulfurization building gypsum.

Key words: desulfurization building gysum, CFB fly ash, CFB slag, mechanical property, expansiveness, microstructure

CLC Number:

TQ177

SHAN Junhong, ZHANG Ze, GAO Peng, WANG Kui. Performance of Desulfurization Building Gypsum Modified by Inorganic Cementitious Materials[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2024, 43(1): 268-275.

References

[1] KORALEGEDARA N H, PINTO P X, DIONYSIOU D D, et al. Recent advances in flue gas desulfurization gypsum processes and applications: a review[J]. Journal of Environmental Management, 2019, 251: 109572.
[2] 李逸晨. 石膏行业的发展现状及趋势[J]. 硫酸工业, 2019(11): 1-7+13.
LI Y C. Development status and trend of gypsum industry[J]. Sulphuric Acid Industry, 2019(11): 1-7+13 (in Chinese).
[3] 再协. 2020年全国大、中城市固体废物污染环境防治年报[J]. 中国资源综合利用, 2021, 39(1): 4.
ZAI X. Annual report on prevention and control of environmental pollution by solid waste in large and medium-sized cities in China in 2020[J]. China Resources Comprehensive Utilization, 2021, 39(1): 4 (in Chinese).
[4] 水中和. 胶凝材料学[M]. 武汉: 武汉理工大学出版社, 2018.
SHUI Z H. Cementitious materials science[M]. Wuhan: Wuhan University of Technology Press, 2018 (in Chinese).
[5] 余海燕, 王武祥, 杨久俊. 水泥基多孔材料孔结构与吸声性能关系研究[J]. 混凝土与水泥制品, 2015(5): 93-98.
YU H Y, WANG W X, YANG J J. Study on relationship between pore structure and sound absorption performance of cement-based porous materials[J]. China Concrete and Cement Products, 2015(5): 93-98 (in Chinese).
[6] 耿飞, 桂敬能, 曹欣欣, 等. 脱硫石膏基复合胶凝材料的物理力学性能试验[J]. 南京航空航天大学学报, 2019, 51(1): 124-130.
GENG F, GUI J N, CAO X X, et al. Study on physical and mechanical properties of FGD gypsum-based cementitious materials[J]. Journal of Nanjing University of Aeronautics & Astronautics, 2019, 51(1): 124-130 (in Chinese).
[7] CAMARINI G, DE MILITO J A. Gypsum hemihydrate-cement blends to improve renderings durability[J]. Construction and Building Materials, 2011, 25(11): 4121-4125.
[8] BUTAKOVA M D, GORBUNOV S P. Study of the influence of complex additives on properties of the gypsum-cement-puzzolan binder and concretes on its basis[J]. Procedia Engineering, 2016, 150: 1461-1467.
[9] 郭爽, 邢冬娴, 郭校, 等. 磷石膏基建筑石膏的制备及改性研究[J/OL]. 无机盐工业: 1-15 [2023-08-14]. https://doi.org/10.19964/j.issn.1006-4990.2023-0138.
GUO S, XING D X, GUO X, et al. Preparation and modification of phosphogypsum based building gypsum[J/OL]. Inorganic Salt Industry: 1-15 [2023-08-14]. https://doi.org/10.19964/j.issn.1006-4990.2023-0138 (in Chinese).
[10] 伍勇华, 祝婷, 姚源, 等. 外加剂对脱硫石膏-粉煤灰胶凝体系性能的影响[J]. 非金属矿, 2020, 43(5): 103-106.
WU Y H, ZHU T, YAO Y, et al. Influence of admixture on the properties of desulfurization gypsum-fly ash cementitious system[J]. Non-Metallic Mines, 2020, 43(5): 103-106 (in Chinese).
[11] 万子恒, 金子豪, 苏英, 等. 缓凝剂对磷石膏-硫铝酸盐水泥复合胶凝体系性能影响[J]. 硅酸盐通报, 2023, 42(6): 2131-2139.
WAN Z H, JIN Z H, SU Y, et al. Effects of retarders on properties of phosphogypsum-sulfoaluminate cement composite cementitious system[J]. Bulletin of the Chinese Ceramic Society, 2023, 42(6): 2131-2139 (in Chinese).
[12] 刘虎林, 王昭, 伍媛婷, 等. 固硫灰渣的基本特性及其作水泥混合材的关键问题研究进展[J]. 硅酸盐通报, 2021, 40(6): 2052-2061+2069.
LIU H L, WANG Z, WU Y T, et al. Review on characteristics of fluidized bed combustion ashes and key issues in their application as cement admixtures[J]. Bulletin of the Chinese Ceramic Society, 2021, 40(6): 2052-2061+2069 (in Chinese).
[13] 罗双, 付汝宾, 孔德文, 等. 掺合料对磷石膏基复合胶凝材料耐水性及强度的影响综述[J]. 无机盐工业, 2020, 52(11): 6-11.
LUO S, FU R B, KONG D W, et al. Summary on effects of admixtures on water resistance and strength of phosphogypsum-based composite cementitious materials[J]. Inorganic Chemicals Industry, 2020, 52(11): 6-11 (in Chinese).
[14] 周明凯, 叶青, 陈潇, 等. CFB灰渣抹灰砂浆的组成设计与性能研究[J]. 硅酸盐通报, 2022, 41(2): 425-432+449.
ZHOU M K, YE Q, CHEN X, et al. Composition design and performance of CFB fly ash and CFB slag plastering mortar[J]. Bulletin of the Chinese Ceramic Society, 2022, 41(2): 425-432+449 (in Chinese).
[15] 刘品德, 全峰, 陆洁, 等. 煤粉炉粉煤灰和循环流化床锅炉粉煤灰的特性及其对蒸压加气混凝土性能的影响[J]. 混凝土与水泥制品, 2019(7): 67-70.
LIU P D, QUAN F, LU J, et al. Characteristic of Pu lverized coal ash and circulating fluidized bed ash and the influence of the ashes on performance of autoclaved aer ated concrete[J]. China Concrete and Cement Products, 2019(7): 67-70 (in Chinese).
[16] 纪宪坤. 流化床燃煤固硫灰渣几种特性利用研究[D]. 重庆: 重庆大学, 2007.
JI X K. Study on utilization of several characteristics of sulfur-fixing ash from fluidized bed coal combustion[D]. Chongqing: Chongqing University, 2007 (in Chinese).
[17] 宋远明, 徐惠忠, 王美娥. 流化床燃煤固硫灰渣膨胀控制因素研究[J]. 粉煤灰综合利用, 2010, 23(1): 3-5.
SONG Y M, XU H Z, WANG M E. Study on controlling factors of expansion of FBC ashes[J]. Fly Ash Comprehensive Utilization, 2010, 23(1): 3-5 (in Chinese).[18] 李龙, 李北星, 杨洋. 无机胶凝材料复合改性磷建筑石膏的研究[J]. 非金属矿, 2022, 45(1): 102-106.
LI L, LI B X, YANG Y. Study on inorganic cementitious material composite modified phosphorus building gypsum[J]. Non-Metallic Mines, 2022, 45(1): 102-106 (in Chinese).
[19] 郭会师, 王庆佩, 张果, 等. 普通硅酸盐水泥改性脱硫建筑石膏耐水性能[J]. 硅酸盐通报, 2021, 40(7): 2288-2295.
GUO H S, WANG Q P, ZHANG G, et al. Water resistance of flue gas desulfurization building gypsum modified by ordinary Portland cement[J]. Bulletin of the Chinese Ceramic Society, 2021, 40(7): 2288-2295 (in Chinese).