高放废液煅烧物与基础玻璃高温反应物相与结构转变研究

硅酸盐通报 ›› 2022, Vol. 41 ›› Issue (11): 4075-4080.

所属专题：玻璃

• 新型功能玻璃与玻璃新技术、新结构 • 上一篇下一篇

高放废液煅烧物与基础玻璃高温反应物相与结构转变研究

方广¹, 徐冬青¹, 谭盛恒², 张华², 贾瑞东¹, 徐凯¹

1.武汉理工大学硅酸盐建筑材料国家重点实验室,武汉 430070;
2.中国原子能科学研究院放射化学研究所,北京 102413

收稿日期:2022-08-23 修订日期:2022-09-08 出版日期:2022-11-15 发布日期:2022-12-12
通信作者: 徐凯,博士,研究员。E-mail:kaixu@whut.edu.cn
作者简介:方广(1995—),男,博士研究生。主要从事放射性废物玻璃固化方面的研究。E-mail:735308159@qq.com
基金资助:
国家自然科学基金(21876138)

Phase and Structure Transitions of High-Level Liquid Waste Calcine and Glass at Elevated Temperature

FANG Guang¹, XU Dongqing¹, TAN Shengheng², ZHANG Hua², JIA Ruidong¹, XU Kai¹

1. State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology, Wuhan 430070, China;
2. Department of Radiochemistry, China Institute of Atomic Energy, Beijing 102413, China

Received:2022-08-23 Revised:2022-09-08 Online:2022-11-15 Published:2022-12-12

摘要/Abstract

摘要： 高放废液玻璃固化是我国亟待突破的关键环节之一,而高放废液玻璃固化过程中高放废液与基础玻璃反应发生的物相转变与结构变化一直是关注的重点。本文以模拟高放废液煅烧物和基础玻璃的混合物为研究对象,利用DSC、原位XRD、NMR、Raman等表征方法开展玻璃固化过程中高温反应物相与结构变化研究。研究结果表明:模拟高放废液煅烧物在~700 ℃开始溶解于基础玻璃中,并在800~900 ℃生成系列硅(铝)酸盐中间物相;煅烧物与基础玻璃高温反应过程中,高放废液中的大量玻璃网络改变体溶入基础玻璃中,导致玻璃网络聚合度下降。

关键词: 高放废液, 玻璃固化, 物相转变, 玻璃结构, 高温反应, 硅酸盐玻璃

Abstract: The vitrification of high-level liquid waste (HLLW) is one of the challenges in the reprocessing of spent nuclear fuel in China. The feed-to-glass conversion comprising quite complex chemical reactions and structure transitions has been of great concern. In this paper, the phase and structure transitions of the heat-treated feed (mixture of simulated HLLW calcine and glass frit) during vitrification were analyzed with DSC, in-situ XRD, NMR and Raman. The results show that the simulated HLLW calcine begins to dissolve in the glass frit at ~700 ℃, and the intermediate phases of aluminosilicates appeare at 800~900 ℃. During the reactions of HLLW calcine and glass frit at elevated temperatures, most of network modifiers from HLLW enter into the glass network of glass frit, resulting in a decrease of the network polymerization.

Key words: high-level liquid waste, vitrification, phase transition, glass structure, elevated temperature reaction, silicate glass

中图分类号:

TQ171

方广, 徐冬青, 谭盛恒, 张华, 贾瑞东, 徐凯. 高放废液煅烧物与基础玻璃高温反应物相与结构转变研究[J]. 硅酸盐通报, 2022, 41(11): 4075-4080.

FANG Guang, XU Dongqing, TAN Shengheng, ZHANG Hua, JIA Ruidong, XU Kai. Phase and Structure Transitions of High-Level Liquid Waste Calcine and Glass at Elevated Temperature[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(11): 4075-4080.

参考文献

[1] OJOVAN M I, LEE W E. An introduction to nuclear waste immobilisation[M]. 2nd ed. Amsterdam: Elsevier, 2005.
[2] GIN S, ABDELOUAS A, CRISCENTI L J, et al. An international initiative on long-term behavior of high-level nuclear waste glass[J]. Materials Today, 2013, 16(6): 243-248.
[3] 徐凯.核废料玻璃固化国际研究进展[J].中国材料进展,2016,35(7):481-488+517.
XU K. Review of international research progress on nuclear waste vitrification[J]. Materials China, 2016, 35(7): 481-488+517 (in Chinese).
[4] GOEL A, MCCLOY J S, POKORNY R, et al. Challenges with vitrification of Hanford high-level waste (HLW) to borosilicate glass-an overview[J]. Journal of Non-Crystalline Solids: X, 2019, 4: 100033.
[5] VERNAZ É, BRUEZIÈRE J. History of nuclear waste glass in France[J]. Procedia Materials Science, 2014, 7: 3-9.
[6] MARCIAL J, CHUN J, HRMA P, et al. Effect of bubbles and silica dissolution on melter feed rheology during conversion to glass[J]. Environmental Science & Technology, 2014, 48(20): 12173-12180.
[7] GUILLEN D P, LEE S, HRMA P, et al. Evolution of chromium, manganese and iron oxidation state during conversion of nuclear waste melter feed to molten glass[J]. Journal of Non-Crystalline Solids, 2020, 531: 119860.
[8] MARCIAL J, KLOUŽEK J, VERNEROVÁ M, et al. Effect of Al and Fe sources on conversion of high-level nuclear waste feed to glass[J]. Journal of Nuclear Materials, 2022, 559: 153423.
[9] MONTEIRO A, SCHULLER S, TOPLIS M J, et al. Chemical and mineralogical modifications of simplified radioactive waste calcine during heat treatment[J]. Journal of Nuclear Materials, 2014, 448(1/2/3): 8-19.
[10] XU K, HRMA P, RICE J, et al. Melter feed reactions at T≤700 ℃ for nuclear waste vitrification[J]. Journal of the American Ceramic Society, 2015, 98(10): 3105-3111.
[11] XU K, HRMA P, RICE J A, et al. Conversion of nuclear waste to molten glass: cold-cap reactions in crucible tests[J]. Journal of the American Ceramic Society, 2016, 99(9): 2964-2970.
[12] WORRALL A. Core and fuel technologies in integral pressurized water reactors (iPWRs)[M]//CARELLI M D, INGERSOLL D T. Handbook of small modular nuclear reactors (second edition). Cambridge: Woodhead Publishing, 2021: 69-93.
[13] 李争,李泉鑫,张华,等.蔗糖脱硝对模拟动力堆高放废液煅烧产物性能及结构的影响[J].原子能科学技术,2022,56(3):434-442.
LI Z, LI Q X, ZHANG H, et al. Effect of denitration with sucrose on property and structure of calcinate of simulated PWR high-level liquid waste[J]. Atomic Energy Science and Technology, 2022, 56(3): 434-442 (in Chinese).
[14] LI H, CHARPENTIER T, DU J C, et al. Composite reinforcement: recent development of continuous glass fibers[J]. International Journal of Applied Glass Science, 2017, 8(1): 23-36.
[15] ZHU H Z, WANG F, LIAO Q L, et al. Structure features, crystallization kinetics and water resistance of borosilicate glasses doped with CeO₂[J]. Journal of Non-Crystalline Solids, 2019, 518: 57-65.
[16] KIM M, HA M G, UM W, et al. Relationship between leaching behavior and glass structure of calcium-aluminoborate waste glasses with various La₂O₃ contents[J]. Journal of Nuclear Materials, 2020, 539: 152331.
[17] BAEK J Y, SHIN S H, KIM S H, et al. Thermal history driven molecular structure transitions in alumino-borosilicate glass[J]. Journal of the American Ceramic Society, 2018, 101(8): 3271-3275.
[18] EL-DAMRAWI G, EL-EGILI K. Characterization of novel CeO₂-B₂O₃ glasses, structure and properties[J]. Physica B: Condensed Matter, 2001, 299(1/2): 180-186.
[19] 谭盛恒,HAND R J.钼酸盐在硼硅酸盐玻璃体系中的溶解[J].中国材料进展,2016,35(7):496-503+517.
TAN S H, HAND R J. Dissolution of molybdate anions in borosilicate glasses for nuclear waste vitrification use[J]. Materials China, 2016, 35(7): 496-503+517 (in Chinese).
[20] BREHAULT A, PATIL D, KAMAT H, et al. Compositional dependence of solubility/retention of molybdenum oxides in aluminoborosilicate-based model nuclear waste glasses[J]. The Journal of Physical Chemistry B, 2018, 122(5): 1714-1729.

高放废液煅烧物与基础玻璃高温反应物相与结构转变研究

Phase and Structure Transitions of High-Level Liquid Waste Calcine and Glass at Elevated Temperature

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	李秋, 朱翔, 耿海宁, 李宗刚, 马浩森, 陈伟. 地聚合物基多相陶瓷高放废液固化体固化机理与浸出性能[J]. 硅酸盐通报, 2023, 42(4): 1437-1447.
[2]	杨静泊, 罗欣, 陈远扬, 安红娜, 徐立国, 吴浪. 磷钼杂多酸盐含量对硼硅酸盐玻璃固化体结构和抗浸出性能的影响[J]. 硅酸盐通报, 2023, 42(4): 1448-1457.
[3]	姚颖, 张壮森, 王宾, 连启会, 李会东, 吴浪. 硫酸铅在硼硅酸盐玻璃熔体中的溶解特性[J]. 硅酸盐通报, 2022, 41(3): 1044-1052.
[4]	黄欣, 王兵兵, 顾少轩, 乔昂, 陶海征. 锌镁替换铝硅酸盐玻璃的玻璃转变和晶化行为探索[J]. 硅酸盐通报, 2022, 41(11): 3806-3812.
[5]	傅茂洋, 廖其龙, 王辅, 胥有利, 何泽旭, 竹含真. CaO含量对镧硼硅酸盐玻璃陶瓷晶相和化学稳定性的影响[J]. 硅酸盐通报, 2022, 41(11): 3861-3869.
[6]	刘红刚, 平文亮, 李升, 康庆伟, 陈健濠, 肖子凡, 董国平. 碱金属和碱土金属铝硅酸盐微晶盖板玻璃的研究现状和发展趋势[J]. 硅酸盐通报, 2022, 41(11): 3925-3936.
[7]	田昊东, 徐驰, 吴志远, 周绍骏, 祖成奎. Na⁺浓度对化学增强钠铝硅酸盐玻璃性能的影响[J]. 硅酸盐通报, 2022, 41(11): 3945-3951.
[8]	徐美姿, 王兵兵, 顾少轩, 黄欣, 陶海征. ZnO·Al₂O₃·nSiO₂玻璃抗裂纹萌生能力反常演化的结构起源探索[J]. 硅酸盐通报, 2022, 41(11): 4067-4074.
[9]	孟保健, 朱永昌, 杨德博, 崔竹, 焦云杰, 刘昊, 戴长友. 碱土金属氧化物含量对模拟高放废液玻璃固化体析晶行为的影响[J]. 硅酸盐通报, 2022, 41(11): 4081-4088.
[10]	王明忠, 刘红刚, 钟波, 许银生, 李继忠, 陆平. Na₂O-Al₂O₃-SiO₂-P₂O₅玻璃的结构和析晶性能研究[J]. 硅酸盐通报, 2022, 41(1): 295-301.
[11]	张晓阳, 卯江江, 陈丽婷, 茆亚南, 王天天, 孙梦利, 彭海波, 王铁山. 硼硅酸盐玻璃浸出前后结构变化的研究[J]. 硅酸盐通报, 2021, 40(6): 2075-2082.
[12]	孟保健, 朱永昌, 焦云杰, 赵崇, 万伟, 韩勖, 崔竹, 杨德博. 模拟高放废液玻璃固化体析晶性能研究[J]. 硅酸盐通报, 2021, 40(10): 3516-3522.
[13]	何光;郭富强;陈筱丽;龚财云;粟勇. 小型玻璃电熔窑的数值模拟[J]. 硅酸盐通报, 2020, 39(4): 1302-1307.
[14]	王照猛;朱雪梅;陈淑勇;李从云;马立云. 分子动力学模拟研究混合碱土金属对无碱硼铝硅酸盐玻璃结构和性能的影响[J]. 硅酸盐通报, 2020, 39(10): 3340-3346.
[15]	昝昱廷;陆平;牛韵雅. P2O5对Na2O-Al2O3-SiO2系统玻璃结构和分相的影响[J]. 硅酸盐通报, 2019, 38(8): 2492-249.