乳酸钠对超硫酸盐水泥强度的影响及作用机理

摘要/Abstract

摘要： 超硫酸盐水泥是一种资源节约和环境友好型胶凝材料,但由于存在早期强度低等缺陷,限制了其推广应用。为提高超硫酸盐水泥早期强度,研究了乳酸钠掺量对超硫酸盐水泥强度的影响,通过ICP-OES、MIP、XRD、SEM等测试,分析了离子浓度、水化产物及微结构,并对相关机制进行了探讨。结果表明,超硫酸盐水泥中掺入少量乳酸钠能提高水泥强度,尤其是早期强度,但是掺量过高时其作用效果降低,甚至对强度不利。综合考虑早期强度和后期强度提高效果,乳酸钠掺量以0.25%(质量分数)左右为宜。乳酸钠提高超硫酸盐水泥强度的主要原因在于其能促进矿渣溶解,加快钙矾石和C-S-H等水化产物生成,从而改善水泥石微结构。

关键词: 超硫酸盐水泥, 乳酸钠, 强度, 离子浓度, 钙矾石, 微结构

Abstract: Supersulfate cement is a kind of resource saving and environmentally friendly cementitious material, but its application is limited because of its low strength in early stage. In order to improve its early strength, the effect of sodium lactate content on the strength of supersulfate cement was studied, the ion concentration, hydration products and microstructure were analyzed by ICP-OES, MIP, XRD and SEM, and the related mechanism was discussed. The results show that the strength of supersulfate cement, especially the early strength, is improved by adding a small amount of sodium lactate, but it is detrimental to the strength when adding too much. Considering the increasing effect of early strength and late strength, the suitable content of sodium lactate is about 0.25% (mass fraction). The main reasonwhy sodium lactate improves the strength of supersulfate cement is that sodium lactate can promote the dissolution of slag, accelerate the formation of ettringite and C-S-H, and thus improve the microstructure of cement.

Key words: supersulfate cement, sodium lactate, strength, ion concentration, ettringite, microstructure

中图分类号:

TQ172

武双磊, 季军荣, 周威杰, 陈宇, 周润铎, 周洲, 陈胡星. 乳酸钠对超硫酸盐水泥强度的影响及作用机理[J]. 硅酸盐通报, 2022, 41(9): 3008-3015.

WU Shuanglei, JI Junrong, ZHOU Weijie, CHEN Yu, ZHOU Runduo, ZHOU Zhou, CHEN Huxing. Effect and Mechanism of Sodium Lactate on Strength of Supersulfate Cement[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(9): 3008-3015.

参考文献

[1] 赵青林,周明凯,FISCHER H,等.超硫酸盐水泥在德国的研究与应用[J].新世纪水泥导报,2008,14(6):5-10+25.
ZHAO Q L, ZHOU M K, FISCHER H, et al. Research and application of supersuiphated cement in Germany[J]. Cement Guide for New Epoch, 2008, 14(6): 5-10+25 (in Chinese).
[2] CABRERA-LUNA K, MALDONADO-BANDALA E E, NIEVES-MENDOZA D, et al. Novel low emissions supersulfated cements of pumice in concrete: mechanical and electrochemical characterization[J]. Journal of Cleaner Production, 2020, 272: 122520.
[3] 陆建鑫,水中和,田素芳,等.超硫酸盐水泥与波特兰水泥混凝土显微结构与性能的比较研究[J].武汉理工大学学报,2013,35(5):1-7.
LU J X, SHUI Z H, TIAN S F, et al. Investigation of the microstructure and property for supersulphated cement concrete and the Portland cement concrete[J]. Journal of Wuhan University of Technology, 2013, 35(5): 1-7 (in Chinese).
[4] DING S, SHUI Z H, CHEN W, et al. Properties of supersulphated phosphogysumslag cement (SSC) concrete[J]. Journal of Wuhan University of Technology-Mater Sci Ed, 2014, 29(1): 109-113.
[5] 陈宇,季军荣,周洲,等.超硫酸盐水泥早期强度影响因素及提高途径[J].硅酸盐通报,2021,40(5):1413-1419.
CHEN Y, JI J R, ZHOU Z, et al. Influencing factors and enhancement methods of early strength of supersulfated cement[J]. Bulletin of the Chinese Ceramic Society, 2021, 40(5): 1413-1419 (in Chinese).
[6] CABRERA-LUNA K, MALDONADO-BANDALA E E, NIEVES-MENDOZA D, et al. Supersulfated binders based on volcanic raw material: optimization, microstructure and reaction products[J]. Construction and Building Materials, 2018, 176: 145-155.
[7] MATSCHEI T, BELLMANN F, STARK J. Hydration behaviour of sulphate-activated slag cements[J]. Advances in Cement Research, 2005, 17(4): 167-178.
[8] GRUSKOVNJAK A, LOTHENBACH B, HOLZER L, et al. Hydration of alkali-activated slag: comparison with ordinary Portland cement[J]. Advances in Cement Research, 2006, 18(3): 119-128.
[9] GRUSKOVNJAK A, LOTHENBACH B, WINNEFELD F, et al. Hydration mechanisms of super sulphated slag cement[J]. Cement and Concrete Research, 2008, 38(7): 983-992.
[10] 高育欣,王军,向佳瑜,等.基于粉料粒径变化的超硫酸盐水泥力学性能研究[J].混凝土与水泥制品,2014(3):14-18.
GAO Y X, WANG J, XIANG J Y, et al. Mechanical properties study on super sulphate cement(SSC) based on powder particle diameter change[J]. China Concrete and Cement Products, 2014(3): 14-18 (in Chinese).
[11] 成希弼,缪纪生.硫铝酸钙的形成过程对石膏矿渣水泥性能的影响[J].硅酸盐学报,1965(1):11-21.
CHENG X B, MIAO J S. Effect of calcium sulphoaluminate formation process on properties of gypsum slag cement[J]. Journal of the Chinese Ceramic Society, 1965(1): 11-21 (in Chinese).
[12] 楼宗汉,周志朝,徐先宇,等.硫铝酸钙的形成和水泥硬化过程碱性条件问题的研究[J].浙江大学学报,1964(1):85-104.
LOU Z H, ZHOU Z Z, XU X Y, et al. Research on the formation of calcium sulphoaluminate and the alkaline conditions in the hardening process of cement [J]. Journal of Zhejiang University, 1964(1): 85-104 (in Chinese).
[13] 崔崇,谢运波,朱守东.少熟料水泥中大掺量矿渣激发条件的研究[J].水泥,2000(2):13-16.
CUI C, XIE Y B, ZHU S D. Research on the activation of minor clinker cement with large addition of slag[J]. Cement, 2000(2): 13-16 (in Chinese).
[14] 孙正宁,周健,慕儒,等.新型超硫酸盐水泥水化硬化机理[J].硅酸盐通报,2019,38(8):2362-2368.
SUN Z N, ZHOU J, MU R, et al. Hydration and hardening mechanisms of newly developed supersulfated cement[J]. Bulletin of the Chinese Ceramic Society, 2019, 38(8): 2362-2368 (in Chinese).
[15] 向佳瑜,余保英,李红傲.硅灰掺量对超硫酸盐水泥水化进程的影响[J].施工技术,2015,44(3):89-92.
XIANG J Y, YU B Y, LI H A. The influence of silica fume content for super sulfate cement hydration process[J]. Construction Technology, 2015, 44(3): 89-92 (in Chinese).
[16] 余保英,向佳瑜,李红傲.微珠不同掺量下超硫酸盐水泥的水化行为[J].硅酸盐通报,2014,33(6):1394-1397.
YU B Y, XIANG J Y, LI H A. Hydration behavior of super sulphated cement with different dosage of microbead[J]. Bulletin of the Chinese Ceramic Society, 2014, 33(6): 1394-1397 (in Chinese).
[17] NGUYEN H A, CHANG T P, SHIH J Y, et al. Influence of low calcium fly ash on compressive strength and hydration product of low energy super sulfated cement paste[J]. Cement and Concrete Composites, 2019, 99: 40-48.
[18] MASOUDI R, HOOTON R D. Examining the hydration mechanism of supersulfated cements made with high and low-alumina slags[J]. Cement and Concrete Composites, 2019, 103: 193-203.
[19] BELLMANN F, STARK J. Activation of blast furnace slag by a new method[J]. Cement and Concrete Research, 2009, 39(8): 644-650.
[20] MASOUDI R, HOOTON R D. Influence of alkali lactates on hydration of supersulfated cement[J]. Construction and Building Materials, 2020, 239: 117844.
[21] 迟琳.高贝利特硫铝酸盐水泥活化和水化机理研究[D].哈尔滨:哈尔滨工业大学,2019.
CHI L. Study on the activation and hydration mechanism of belite calcium sulfoaluminate cement[D]. Harbin: Harbin Institute of Technology, 2019 (in Chinese).
[22] 张金山.钙矾石形貌调控及其机理研究[D].北京:中国建筑材料科学研究总院,2017.
ZHANG J S. Study on the regulation of ettringite morphology and its mechanism[D]. Beijing: China Building Materlals Academy, 2017 (in Chinese).