硅酸盐通报 ›› 2021, Vol. 40 ›› Issue (7): 2145-2151.

养护条件对EVA乳液改性水泥浆体水化行为和孔结构的影响

丁少沛^1,2, 王健涛^1,2, 刘云鹏¹, 何永佳¹

1.武汉理工大学硅酸盐建筑材料国家重点实验室,武汉 430070;
2.武汉理工大学材料科学与工程学院,武汉 430070

收稿日期:2021-02-05 修回日期:2021-03-24 出版日期:2021-07-15 发布日期:2021-08-04
通讯作者: 刘云鹏,副研究员。E-mail:liuyunpeng@whut.edu.cn
作者简介:丁少沛(2000—),女。主要从事水泥混凝土的研究。E-mail:875780202@qq.com
基金资助:
国家重点研发计划(2017YFB0310000);国家自然科学基金(51972250)

Effects of Curing Conditions on Hydration Behavior and Pore Structure of EVA Emulsion Modified Cement Paste

DING Shaopei^1,2, WANG Jiantao^1,2, LIU Yunpeng¹, HE Yongjia¹

1. State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology, Wuhan 430070, China;
2. School of Materials Science and Engineering, Wuhan University of Technology, Wuhan 430070, China

Received:2021-02-05 Revised:2021-03-24 Online:2021-07-15 Published:2021-08-04

摘要/Abstract

摘要： 本文制备了不同乙烯-醋酸乙烯酯(EVA)乳液含量的聚合物改性硅酸盐水泥浆体,对比了其在相同水灰比,不同养护制度(标准养护、蒸汽养护)条件的水化性能与孔结构。通过X射线衍射分析、水化热分析、压汞分析、氮吸附测试,以及立方体抗压强度测试评价了EVA乳液在不同养护状态下对水泥水化产物、水化特性、孔结构以及抗压强度的影响。结果表明,与标准养护相比,蒸汽养护下EVA乳液没有改变水泥水化产物,在EVA乳液较高掺量下,降低了其延缓水泥水化的程度,降低了试样的孔隙率,并且增加了试样中小孔的含量,而蒸汽养护削弱了EVA乳液对水泥净浆强度的负面影响。

关键词: EVA乳液, 蒸汽养护, 压汞分析, 水化行为, 孔结构

Abstract: In this paper, the polymer modified Portland cement paste with different EVA emulsion content was prepared. The hydration properties and pore structure of the modified Portland cement paste under the same water cement ratio and different curing systems (standard curing and steam curing) were compared. The effects of EVA emulsion on the hydration products, hydration characteristics, pore structure and compressive strength of the cement under different curing conditions were evaluated by X ray diffraction analysis, hydration heat analysis, mercury intrusion analysis, nitrogen adsorption test and cube compressive strength test. The results show that compared with the standard curing, EVA emulsion does not change the hydration products of cement under the steam curing. When the amount of EVA emulsion is higher, it decreases the degree of cement hydration, reduces the porosity of samples, increases the pore size of samples, and the steam curing decreases the negative effect of EVA emulsion on the strength of the cement paste.

Key words: EVA emulsion, steam curing, mercury intrusion analysis, hydration behavior, pore structure

中图分类号:

TQ172

丁少沛, 王健涛, 刘云鹏, 何永佳. 养护条件对EVA乳液改性水泥浆体水化行为和孔结构的影响[J]. 硅酸盐通报, 2021, 40(7): 2145-2151.

DING Shaopei, WANG Jiantao, LIU Yunpeng, HE Yongjia. Effects of Curing Conditions on Hydration Behavior and Pore Structure of EVA Emulsion Modified Cement Paste[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(7): 2145-2151.

参考文献

[1] 彭波,丁庆军,王红喜,等.水泥与混凝土制品的蒸汽养护生产关键技术进展[J].国外建材科技,2007,28(3):21-24.
PENG B, DING Q J, WANG H X, et al. Advances in key technology of steam-cured cement and concrete products[J]. Science and Technology of Overseas Building Materials, 2007, 28(3): 21-24 (in Chinese).
[2] ESCALANTE-GARCÍA J I, SHARP J H. The microstructure and mechanical properties of blended cements hydrated at various temperatures[J]. Cement and Concrete Research, 2001, 31(5): 695-702.
[3] NIE S, ZHANG W Q, HU S G, et al. Improving the fluid transport properties of heat-cured concrete by internal curing[J]. Construction and Building Materials, 2018, 168: 522-531.
[4] 耿健,彭波,孙家瑛.蒸汽养护制度对水泥石孔结构的影响[J].建筑材料学报,2011,14(1):116-118+123.
GENG J, PENG B, SUN J Y. Effect of steam curing system on pore structure of cement paste[J]. Journal of Building Materials, 2011, 14(1): 116-118+123 (in Chinese).
[5] MUHAMMAD N Z, KEYVANFAR A, ABD MAJID M Z, et al. Waterproof performance of concrete: a critical review on implemented approaches[J]. Construction and Building Materials, 2015, 101: 80-90.
[6] YANG Z X, SHI X M, CREIGHTON A T, et al. Effect of styrene-butadiene rubber latex on the chloride permeability and microstructure of Portland cement mortar[J]. Construction and Building Materials, 2009, 23(6): 2283-2290.
[7] WANG R, MA D X, WANG P M, et al. Study on waterproof mechanism of polymer-modified cement mortar [J]. Magazine of Concrete Research, 2015, 67(18): 1-8.
[8] RAMLI M, TABASSI A A, HOE K W. Porosity, pore structure and water absorption of polymer-modified mortars: an experimental study under different curing conditions[J]. Composites Part B: Engineering, 2013, 55: 221-233.
[9] ZHANG C Y, KONG X M, LU Z C, et al. Pore structure of hardened cement paste containing colloidal polymers with varied glass transition temperature and surface charges[J]. Cement and Concrete Composites, 2019, 95: 154-168.
[10] YUAN B, YANG Y G, WANG Y Q, et al. Self-healing efficiency of EVA-modified cement for hydraulic fracturing wells[J]. Construction and Building Materials, 2017, 146: 563-570.
[11] SILVA D A, JOHN V M, RIBEIRO J L D, et al. Pore size distribution of hydrated cement pastes modified with polymers[J]. Cement and Concrete Research, 2001, 31(8): 1177-1184.
[12] REINHARDT H W, STEGMAIER M. Influence of heat curing on the pore structure and compressive strength of self-compacting concrete (SCC)[J]. Cement and Concrete Research, 2006, 36(5): 879-885.

[1]	陈梦竹, 余林文, 袁慧慧, 郑海兵, 吴芳, 蔡渝新, 李伟华. 木质素磺酸钠改性Ca-LDH对水泥基材料性能的影响[J]. 硅酸盐通报, 2021, 40(7): 2152-2158.
[2]	张超, 邓智聪, 汪智斌, 侯泽宇, 贾子健, 王香港, 贾鲁涛, 陈春, 孙正明, 张亚梅, 潘金龙. 纤维对3D打印混凝土打印性能与力学性能的影响[J]. 硅酸盐通报, 2021, 40(6): 1870-1878.
[3]	王冬丽, 杨策, 潘慧敏, 李通, 迟亚奥, 徐泽华. 水泥基材料孔结构与吸水性能关系研究进展[J]. 硅酸盐通报, 2021, 40(5): 1420-1428.
[4]	陈志武. 饱和面干再生细骨料对超高性能混凝土流动度及强度的影响[J]. 硅酸盐通报, 2021, 40(5): 1503-1509.
[5]	陈逸明, 林培桐, 李云龙, 刘锦红, 汪峻峰, 鲁刘磊. 高抗蚀胶凝材料的制备及其抗硫酸盐侵蚀性能研究[J]. 硅酸盐通报, 2021, 40(4): 1116-1127.
[6]	林培桐, 曾宇, 赵永钢, 刘锦红, 汪峻峰, 鲁刘磊. 纳米二氧化硅改性大掺量矿粉-水泥胶凝体系性能与微结构研究[J]. 硅酸盐通报, 2021, 40(2): 384-391.
[7]	高育欣, 李坤杰, 马建峰, 高达, 杨文, 毕耀, 罗遥凌. 城市污泥掺量对煤气化渣陶粒性能影响[J]. 硅酸盐通报, 2021, 40(2): 579-586.
[8]	谭洪波, 吕周岭, 马保国, 吉晓莉, 刘晓海, 蹇守卫. 黄姜废渣发泡陶瓷的制备及其性能研究[J]. 硅酸盐通报, 2021, 40(2): 597-604.
[9]	高帅;陈逸明;林培桐;许亮;汪峻峰;鲁刘磊. 高温对碱激发超高性能混凝土力学性能的影响[J]. 硅酸盐通报, 2020, 39(9): 2815-2820.
[10]	万惠文;符昱;杨正波;李泾娴;刘俊岩;胡章胤;肖家冬. 利用超声分散提高矿粉激发时效的研究[J]. 硅酸盐通报, 2020, 39(9): 2870-2876.
[11]	王立宁;陈振;张增志. 发泡剂对矿渣基地质聚合物气孔结构及吸水性的影响[J]. 硅酸盐通报, 2020, 39(7): 2085-2091.
[12]	杨文武;杜蓬娟;范伟;李想. 海工磨细矿渣混凝土的冻渗性与孔结构研究[J]. 硅酸盐通报, 2020, 39(7): 2134-2138.
[13]	张楠楠;李云龙;刘锦红;苏峰平;许亮;康明;汪峻峰;鲁刘磊. 玄武岩粉对海工胶凝材料性能及水化的影响[J]. 硅酸盐通报, 2020, 39(7): 2204-2210.
[14]	史璐玉;孙诗兵;马存喜;陈艳晓;李群艳;吕锋. SiO2-Al2O3-R2O-Fe2O3系统发泡陶瓷及其孔结构研究[J]. 硅酸盐通报, 2020, 39(6): 1916-1922.
[15]	尚吉祥;赵文杰. 丁苯水泥改性剂改性水泥基材料的机理研究进展[J]. 硅酸盐通报, 2020, 39(5): 1384-1389.