沸石粉对硫铝酸盐水泥水化行为的影响机理研究

硅酸盐通报 ›› 2021, Vol. 40 ›› Issue (7): 2138-2144.

沸石粉对硫铝酸盐水泥水化行为的影响机理研究

桂若铭, 廖宜顺, 黄浩然

武汉科技大学城市建设学院,武汉 430065

收稿日期:2021-02-10 修回日期:2021-03-26 出版日期:2021-07-15 发布日期:2021-08-04
通讯作者: 廖宜顺,博士,副教授。E-mail:liaoyishun@wust.edu.cn
作者简介:桂若铭(1993—),男,硕士研究生。主要从事新型水泥基材料的研究。E-mail:1007559772@qq.com
基金资助:
长江科学院开放研究基金(CKWV2019756/KY);省部共建耐火材料与冶金国家重点实验室主任基金(ZR201901);国家自然科学基金(51608402)

Effect of Zeolite Powder on Hydration Behavior of Calcium Sulfoaluminate Cement

GUI Ruoming, LIAO Yishun, HUANG Haoran

School of Urban Construction, Wuhan University of Science and Technology, Wuhan 430065, China

Received:2021-02-10 Revised:2021-03-26 Online:2021-07-15 Published:2021-08-04

摘要/Abstract

摘要： 研究了沸石粉对硫铝酸盐水泥浆体流动度、凝结时间和抗压强度的影响规律,并通过自收缩、电阻率和XRD测试分析了沸石粉在硫铝酸盐水泥水化行为中的作用机理。结果表明,掺入沸石粉后水泥浆体的流动度明显降低,凝结时间显著延长,且延长时间随掺量的增大呈先增大后减小的趋势。当沸石粉掺量为5%~15%(质量分数)时,硬化水泥浆体的1 d、3 d、7 d抗压强度均有显著提高;沸石粉掺量为10%时,水泥浆体3 d、7 d、28 d的强度增长幅度最大,和空白组相比,分别增长了21.6%、13.9%和5.4%。掺入沸石粉后水泥浆体的24 h电阻率显著增大,硬化浆体的7 d自收缩减小,且在相同龄期时,硬化浆体的自收缩随沸石粉掺量的增大而减小。XRD分析显示沸石粉的掺入能有效促进硫铝酸盐水泥的水化,有利于1 d、3 d和28 d龄期内钙矾石的形成。

关键词: 沸石粉, 硫铝酸盐水泥, 水化, 抗压强度, 电阻率, 钙矾石

Abstract: The effects of zeolite powder on fluidity, setting time and compressive strength of calcium sulfoaluminate cement pastes were studied, and the mechanism of zeolite powder in the hydration behavior of calcium sulfoaluminate cement was analyzed by autogenous shrinkage, electrical resistivity and XRD. The results show that the fluidity of the cement paste decreases obviously with the addition of zeolite powder, and the setting time increases significantly, and then increases slowly with the increase of zeolite powder. When the zeolite powder mass content is from 5% to 15%, the compressive strength of hardened cement paste at 1 d, 3 d and 7 d increases significantly. When the zeolite powder mass content is 10%, the compressive strength of cement paste at 3 d, 7 d and 28 d increases by 21.6%, 13.9% and 5.4%, respectively, compared with the control group. After adding zeolite powder, the electrical resistivity of cement paste at 24 h increases significantly, and the autogenous shrinkage of hardened cement paste decreases at 7 d. At the same age, the autogenous shrinkage of hardened cement paste decreases with the increase of zeolite powder. XRD analysis shows that the addition of zeolite powder effectively promotes the hydration of calcium sulfoaluminate cement, and is beneficial to the formation of ettringite at 1 d, 3 d and 28 d ages.

Key words: zeolite powder, calcium sulfoaluminate cement, hydration, compressive strength, electrical resistivity, ettringite

中图分类号:

TU528

桂若铭, 廖宜顺, 黄浩然. 沸石粉对硫铝酸盐水泥水化行为的影响机理研究[J]. 硅酸盐通报, 2021, 40(7): 2138-2144.

GUI Ruoming, LIAO Yishun, HUANG Haoran. Effect of Zeolite Powder on Hydration Behavior of Calcium Sulfoaluminate Cement[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(7): 2138-2144.

参考文献

[1] ELAIOPOULOS K, PERRAKI T, GRIGOROPOULOU E. Monitoring the effect of hydrothermal treatments on the structure of a natural zeolite through a combined XRD, FTIR, XRF, SEM and N₂-porosimetry analysis[J]. Microporous and Mesoporous Materials, 2010, 134(1/2/3): 29-43.
[2] 武铁明,林怀立.利用沸石粉配制高性能混凝土的应用研究[J].混凝土,2001(10):17-20+58.
WU T M, LIN H L. The research of high perfomace concrete incorporated with zeolite powder[J]. Concrete, 2001(10): 17-20+58 (in Chinese).
[3] ORTEGA E A, CHEESEMAN C, KNIGHT J, et al. Properties of alkali-activated clinoptilolite[J]. Cement and Concrete Research, 2000, 30(10): 1641-1646.
[4] PERRAKI T, KAKALI G, KONTORI E. Characterization and pozzolanic activity of thermally treated zeolite[J]. Journal of Thermal Analysis and Calorimetry, 2005, 82(1): 109-113.
[5] CAPUTO D, LIGUORI B, COLELLA C. Some advances in understanding the pozzolanic activity of zeolites: the effect of zeolite structure[J]. Cement and Concrete Composites, 2008, 30(5): 455-462.
[6] SNELLINGS R, MERTENS G, ELSEN J. Supplementary cementitious materials[J]. Reviews in Mineralogy and Geochemistry, 2012, 74(1): 211-278.
[7] TRAN Y T, LEE J, KUMAR P, et al. Natural zeolite and its application in concrete composite production[J]. Composites Part B: Engineering, 2019, 165: 354-364.
[8] SERAJ S, FERRON R D, JUENGER M C G. Calcining natural zeolites to improve their effect on cementitious mixture workability[J]. Cement and Concrete Research, 2016, 85: 102-110.
[9] 孙恩禹,陈啸洋.天然沸石粉对氯氧镁水泥耐水性影响研究[J].硅酸盐通报,2021,40(1):41-47.
SUN E Y, CHEN X Y. Effect of natural zeolite powder on water resistance of magnesium oxychloride cement[J]. Bulletin of the Chinese Ceramic Society, 2021, 40(1): 41-47 (in Chinese).
[10] LV Y, YE G, DE SCHUTTER G. Investigation on the potential utilization of zeolite as an internal curing agent for autogenous shrinkage mitigation and the effect of modification[J]. Construction and Building Materials, 2019, 198: 669-676.
[11] 王燕谋,苏慕珍,路永华.中国特种水泥[M].北京:中国建材工业出版社,2012:173.
WANG Y M, SU M Z, LU Y H. China special cement[M]. Beijing: China Building Materials Industry Press, 2012:173 (in Chinese).
[12] BURRIS L E, KURTIS K E. Influence of set retarding admixtures on calcium sulfoaluminate cement hydration and property development[J]. Cement and Concrete Research, 2018, 104: 105-113.
[13] 罗孙一鸣.硫铝酸盐水泥混凝土早期收缩及调控研究[D].北京:清华大学,2015:10-18.
LUO S Y M. Studies and controls on shrinkage of sulfoaluminate cement concrete[D]. Beijing: Tsinghua University, 2015: 10-18 (in Chinese).
[14] 胡红梅,马保国.混凝土矿物掺合料[M].北京:中国电力出版社,2016:3-6.
HU H M, MA B G. Concrete mineral admixtures[M]. Beijing: China Electric Power Press, 2016:3-6 (in Chinese).
[15] 张云飞,张德成,张鸣,等.掺合料对硫铝酸盐水泥性能的影响[J].济南大学学报(自然科学版),2006,20(4):292-295.
ZHANG Y F, ZHANG D C, ZHANG M, et al. Hydration performance of sulphoaluminate cement mixed with blending material[J]. Journal of Jinan University (Science and Technology), 2006, 20(4): 292-295 (in Chinese).
[16] WANG S B, PENG Y L. Natural zeolites as effective adsorbents in water and wastewater treatment[J]. Chemical Engineering Journal, 2010, 156(1): 11-24.
[17] AHMADI B, SHEKARCHI M. Use of natural zeolite as a supplementary cementitious material[J]. Cement and Concrete Composites, 2010, 32(2): 134-141.
[18] CHUN L, DENG C, ZHI Q C. Effect of zeolite powder on the hydration and microstructure evolution of hardened cement paste at low water-binder ratio[J]. Romanian Journal of Materials, 2020, 50(3): 331-336.
[19] RAMEZANIANPOUR A A, MOUSAVI R, KALHORI M, et al. Micro and macro level properties of natural zeolite contained concretes[J]. Construction and Building Materials, 2015, 101: 347-358.
[20] HE Z, YANG H M, LIU M Y. Hydration mechanism of sulphoaluminate cement[J]. Journal of Wuhan University of Technology-Mater Sci Ed, 2014, 29(1): 70-74.
[21] 魏小胜.用电阻率表征水泥混凝土结构形成动力学及性能[M].武汉:武汉理工大学出版社,2016.
WEI X S. The resistivity is used to characterize the formation kinetics and properties of cement concrete structures[M]. Wuhan: Wuhan University of Technology Press, 2016 (in Chinese).
[22] ZHANG J, HAN Y D, GAO Y, et al. Integrative study on the effect of internal curing on autogenous and drying shrinkage of high-strength concrete[J]. Drying Technology, 2013, 31(5): 565-575.