粉煤灰基地聚物的性能影响因素及其凝胶产物研究进展

摘要/Abstract

摘要： 粉煤灰基地聚物材料因绿色、低碳等优点受到建材行业关注。本文基于地聚物的形成及优势,分析了粉煤灰作为硅铝基材的优点,着重阐述了激发剂离子、养护方式和钙组分对粉煤灰基地聚物材料性能的影响,综述了粉煤灰基地聚物材料的凝胶产物变化及其反应机理研究进展。目前含钙固废作为添加物逐渐应用于改性粉煤灰基地聚物中,因此明确凝胶产物组成和反应机理将为粉煤灰基地聚物材料性能优化提供理论指导。

关键词: 粉煤灰, 地聚物, 钙组分, 养护条件, 凝胶产物, 反应机理

Abstract: Fly ash-based geopolymer materials are favored in the building material industry owing to the advantages of green and low-carbon. Silica-aluminum precursors, alkali-activators and water are the basic components for geopolymeric reaction. However, the gel products in fly ash-based geopolymer material are changing with additional calcium content in system. In this paper, based on the formation and advantage of geopolymer, the advantage of fly ash was analyzed as silica-aluminum precursor. Also, the influences of activator ions, curing conditions and calcium-components were emphasized on the performances of modified fly ash-based geopolymer material. Furthermore, the research developments of gel products and reaction mechanisms were reviewed for fly ash-based geopolymer materials. Currently, the calcium-containing solid wastes tend to be utilized as the inorganic additives to improve the performances of modified fly ash-based geopolymer materials. Therefore, clarifying gel products and reaction mechanisms will provide the theoretical guidance for the performance optimization of fly ash-based geopolymer materials.

Key words: fly ash, geopolymer, calcium-component, curing condition, gel product, reaction mechanism

中图分类号:

TU526

赵献辉, 王浩宇, 周博宇, 高涵. 粉煤灰基地聚物的性能影响因素及其凝胶产物研究进展[J]. 硅酸盐通报, 2021, 40(3): 867-876.

ZHAO Xianhui, WANG Haoyu, ZHOU Boyu, GAO Han. Research Development on Influencing Factors of Performances and Gel Products in Fly Ash-Based Geopolymer Material[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(3): 867-876.

参考文献

[1] PALOMO A, GRUTZECK M W, BLANCO M T. Alkali-activated fly ashes: a cement for the future[J]. Cement and Concrete Research, 1999, 29(8): 1323-1329.
[2] 施惠生,夏明,郭晓潞.粉煤灰基地聚合物反应机理及各组分作用的研究进展[J].硅酸盐学报,2013,41(7):972-980.
SHI H S, XIA M, GUO X L. Research development on mechanism of fly ash-based geopolymer and effect of each component[J]. Journal of the Chinese Ceramic Society, 2013, 41(7): 972-980 (in Chinese).
[3] YIP C K, LUKEY G C, PROVIS J L, et al. Effect of calcium silicate sources on geopolymerisation[J]. Cement and Concrete Research, 2008, 38(4): 554-564.
[4] TEMUUJIN J, VAN RIESSEN A, WILLIAMS R. Influence of calcium compounds on the mechanical properties of fly ash geopolymer pastes[J]. Journal of Hazardous Materials, 2009, 167(1/2/3): 82-88.
[5] KHALE D, CHAUDHARY R. Mechanism of geopolymerization and factors influencing its development: a review[J]. Journal of Materials Science, 2007, 42(3): 729-746.
[6] ALLALI F, JOUSSEIN E, KANDRI N I, et al. The influence of calcium content on the performance of metakaolin-based geomaterials applied in mortars restoration[J]. Materials & Design, 2016, 103: 1-9.
[7] MEHTA A, SIDDIQUE R. Properties of low-calcium fly ash based geopolymer concrete incorporating OPC as partial replacement of fly ash[J]. Construction and Building Materials, 2017, 150: 792-807.
[8] YIP C K, PROVIS J L, LUKEY G C, et al. Carbonate mineral addition to metakaolin-based geopolymers[J]. Cement and Concrete Composites, 2008, 30(10): 979-985.
[9] PANGDAENG S, PHOO-NGERNKHAM T, SATA V, et al. Influence of curing conditions on properties of high calcium fly ash geopolymer containing Portland cement as additive[J]. Materials & Design, 2014, 53: 269-274.
[10] GARCIA-LODEIRO I, APARICIO-REBOLLO E, FERNÁNDEZ-JIMENEZ A, et al. Effect of calcium on the alkaline activation of aluminosilicate glass[J]. Ceramics International, 2016, 42(6): 7697-7707.
[11] BERNAL S A, DE GUTIERREZ R M, PROVIS J L, et al. Effect of silicate modulus and metakaolin incorporation on the carbonation of alkali silicate-activated slags[J]. Cement and Concrete Research, 2010, 40(6): 898-907.
[12] PASUPATHY K, BERNDT M, SANJAYAN J, et al. Durability of low-calcium fly ash based geopolymer concrete culvert in a saline environment[J]. Cement and Concrete Research, 2017, 100: 297-310.
[13] SAHA S M, RAJASEKARAN C. Enhancement of the properties of fly ash based geopolymer paste by incorporating ground granulated blast furnace slag[J]. Construction and Building Materials, 2017, 146: 615-620.
[14] SARKER P K, MCBEATH S. Fire endurance of steel reinforced fly ash geopolymer concrete elements[J]. Construction and Building Materials, 2015, 90: 91-98.
[15] MEHTA A, SIDDIQUE R. An overview of geopolymers derived from industrial by-products[J]. Construction and Building Materials, 2016, 127: 183-198.
[16] FAHIM HUSEIEN G, MIRZA J, ISMAIL M, et al. Geopolymer mortars as sustainable repair material: a comprehensive review[J]. Renewable and Sustainable Energy Reviews, 2017, 80: 54-74.
[17] GLUKHOVSKY V D. Soil silicates. Their properties, technology and manufacturing and fields of application[D]. Kiev: Civil Engineering Institute, 1965.
[18] MEHTA A, SIDDIQUE R. Sulfuric acid resistance of fly ash based geopolymer concrete[J]. Construction and Building Materials, 2017, 146: 136-143.
[19] GÖRHAN G, KÜRKLÜ G. The influence of the NaOH solution on the properties of the fly ash-based geopolymer mortar cured at different temperatures[J]. Composites Part B: Engineering, 2014, 58: 371-377.
[20] BAKHAREV T. Geopolymeric materials prepared using class F fly ash and elevated temperature curing[J]. Cement and Concrete Research, 2005, 35(6): 1224-1232.
[21] 郭晓潞,施惠生.钙对粉煤灰基土聚水泥性能的影响研究[J].水泥,2011(4):11-13.
GUO X L, SHI H S. Effects of calcium on performance of fly ash based geopolymeric cement[J]. Cement, 2011(4): 11-13 (in Chinese).
[22] RATTANASAK U, CHINDAPRASIRT P. Influence of NaOH solution on the synthesis of fly ash geopolymer[J]. Minerals Engineering, 2009, 22(12): 1073-1078.
[23] FENG D, TAN H, VAN DEVENTER J S J. Ultrasound enhanced geopolymerisation[J]. Journal of Materials Science, 2004, 39(2): 571-580.
[24] PROVIS J L, LUKEY G C, VAN DEVENTER J S J. Do geopolymers actually contain nanocrystalline zeolites? A reexamination of existing results[J]. Chemistry of Materials, 2005, 17(12): 3075-3085.
[25] PROVIS J L, VAN DEVENTER J S J. Geopolymerisation kinetics. 2. Reaction kinetic modelling[J]. Chemical Engineering Science, 2007, 62(9): 2318-2329.
[26] 侯云芬,王栋民,李俏,等.水玻璃性能对粉煤灰基矿物聚合物的影响[J].硅酸盐学报,2008,36(1):61-64+68.
HOU Y F, WANG D M, LI Q, et al. Effect of water glass performance on fly ash-based geopolymers[J]. Journal of the Chinese Ceramic Society, 2008, 36(1): 61-64+68 (in Chinese).
[27] 王亚超.碱激发粉煤灰基地质聚合物强化增韧及耐久性能研究[D].西安:西安建筑科技大学,2014:90-95.
WANG Y C. Investigations on reinforcing, toughening and durability of alkali-activated fly ash-based geopolymer[D]. Xi’an: Xi’an University of Architecture and Technology, 2014: 90-95 (in Chinese).
[28] CHEN C, GONG W L, LUTZE W, et al. Kinetics of fly ash leaching in strongly alkaline solutions[J]. Journal of Materials Science, 2011, 46(3): 590-597.
[29] WANG Y C, ZHANG Y J, XU D L, et al. Influence of different curing temperatures on mechanical properties of alkali activated silica fume and fly ash based geopolymer[J]. Materials Research Innovations, 2013, 17(s1): 21-25.
[30] GRAYTEE A, SANJAYAN J G, NAZARI A. Development of a high strength fly ash-based geopolymer in short time by using microwave curing[J]. Ceramics International, 2018, 44(7): 8216-8222.
[31] HADI M N S, AL-AZZAWI M, YU T. Effects of fly ash characteristics and alkaline activator components on compressive strength of fly ash-based geopolymer mortar[J]. Construction and Building Materials, 2018, 175: 41-54.
[32] ROVNANÍK P. Effect of curing temperature on the development of hard structure of metakaolin-based geopolymer[J]. Construction and Building Materials, 2010, 24(7): 1176-1183.
[33] 陈晨,程婷,贡伟亮,等.粉煤灰地聚物反应体系下的反应影响因素分析[J].材料导报,2016,30(24):118-123.
CHEN C, CHENG T, GONG W L, et al. Analysis of reaction factors under fly ash based geopolymer system[J]. Materials Review, 2016, 30(24): 118-123 (in Chinese).
[34] ZHUANG X Y, CHEN L, KOMARNENI S, et al. Fly ash-based geopolymer: clean production, properties and applications[J]. Journal of Cleaner Production, 2016, 125: 253-267.
[35] HELMY A I I. Intermittent curing of fly ash geopolymer mortar[J]. Construction and Building Materials, 2016, 110: 54-64.
[36] SOMNA K, JATURAPITAKKUL C, KAJITVICHYANUKUL P, et al. NaOH-activated ground fly ash geopolymer cured at ambient temperature[J]. Fuel, 2011, 90(6): 2118-2124.
[37] ZHANG M, ZHAO M X, ZHANG G P, et al. Calcium-free geopolymer as a stabilizer for sulfate-rich soils[J]. Applied Clay Science, 2015, 108: 199-207.
[38] GARCIA-LODEIRO I, PALOMO A, FERNÁNDEZ-JIMÉNEZ A, et al. Compatibility studies between N-A-S-H and C-A-S-H gels. Study in the ternary diagram Na₂O-CaO-Al₂O₃-SiO₂-H₂O[J]. Cement and Concrete Research, 2011, 41(9): 923-931.
[39] XU H, VAN DEVENTER J S J. Geopolymerisation of multiple minerals[J]. Minerals Engineering, 2002, 15(12): 1131-1139.
[40] LEE W K W, VAN DEVENTER J S J. Structural reorganisation of class F fly ash in alkaline silicate solutions[J]. Colloids and Surfaces A: Physicochemical and Engineering Aspects, 2002, 211(1): 49-66.
[41] YIP C K, LUKEY G C, VAN DEVENTER J S J. The coexistence of geopolymeric gel and calcium silicate hydrate at the early stage of alkaline activation[J]. Cement and Concrete Research, 2005, 35(9): 1688-1697.
[42] BUCHWALD A, HILBIG H, KAPS C. Alkali-activated metakaolin-slag blends—performance and structure in dependence of their composition[J]. Journal of Materials Science, 2007, 42(9): 3024-3032.
[43] PROVIS J L, ROSE V, BERNAL S A, et al. High-resolution nanoprobe X-ray fluorescence characterization of heterogeneous calcium and heavy metal distributions in alkali-activated fly ash[J]. Langmuir, 2009, 25(19): 11897-11904.
[44] DIAZ E I, ALLOUCHE E N, EKLUND S. Factors affecting the suitability of fly ash as source material for geopolymers[J]. Fuel, 2010, 89(5): 992-996.
[45] OH J E, MONTEIRO P J M, JUN S S, et al. The evolution of strength and crystalline phases for alkali-activated ground blast furnace slag and fly ash-based geopolymers[J]. Cement and Concrete Research, 2010, 40(2): 189-196.
[46] HUSEIEN G F, MIRZA J, ISMAIL M, et al. Influence of different curing temperatures and alkali activators on properties of GBFS geopolymer mortars containing fly ash and palm-oil fuel ash[J]. Construction and Building Materials, 2016, 125: 1229-1240.
[47] DUAN P, YAN C J, ZHOU W. A novel water permeable geopolymer with high strength and high permeability coefficient derived from fly ash, slag and metakaolin[J]. Advanced Powder Technology, 2017, 28(5): 1430-1434.
[48] RAFEET A, VINAI R, SOUTSOS M, et al. Effects of slag substitution on physical and mechanical properties of fly ash-based alkali activated binders (AABs)[J]. Cement and Concrete Research, 2019, 122: 118-135.
[49] ZHAO X H, LIU C Y, ZUO L M, et al. Investigation into the effect of calcium on the existence form of geopolymerized gel product of fly ash based geopolymers[J]. Cement and Concrete Composites, 2019, 103: 279-292.
[50] ZHAO X H, LIU C Y, WANG L, et al. Physical and mechanical properties and micro characteristics of fly ash-based geopolymers incorporating soda residue[J]. Cement and Concrete Composites, 2019, 98: 125-136.
[51] ZHAO X H, LIU C Y, ZUO L M, et al. Synthesis and characterization of fly ash geopolymer paste for goaf backfill: reuse of soda residue[J]. Journal of Cleaner Production, 2020, 260: 121045.
[52] ZHAO X H, LIU C Y, ZUO L M, et al. Preparation and characterization of press-formed fly ash cement incorporating soda residue[J]. Materials Letters, 2020, 259: 126852.
[53] DAVIDOVITS J. Geopolymers and geopolymeric materials[J]. Journal of Thermal Analysis, 1989, 35(2): 429-441.
[54] XU H, VAN DEVENTER J S J. The geopolymerization of alumino-silicate minerals[J]. International Journal of Mineral Processing, 2000, 59: 247-266.
[55] FANG Y, KAYALI O. The fate of water in fly ash-based geopolymers[J]. Construction and Building Materials, 2013, 39: 89-94.
[56] 马鸿文,杨静,任玉峰,等.矿物聚合材料:研究现状与发展前景[J].地学前缘,2002,9(4):397-407.
MA H W, YANG J, REN Y F, et al. Mineral polymer: current developments and prospects[J]. Earth Science Frontiers, 2002, 9(4): 397-407 (in Chinese).
[57] 赵献辉,刘春原,刘宇飞,等.碱渣-粉煤灰基新型注浆材料固化机理试验研究[J].硅酸盐通报,2017,36(4):1417-1423.
ZHAO X H, LIU C Y, LIU Y F, et al. Experimental research on solidified mechanism of new soda residue-fly ash-based grouting materials[J]. Bulletin of the Chinese Ceramic Society, 2017, 36(4): 1417-1423 (in Chinese).
[58] 赵献辉,刘春原,左丽明,等.采空区充填新型浆液固化机理与影响因素研究[J].长江科学院院报,2018,35(8):72-77.
ZHAO X H, LIU C Y, ZUO L M, et al. New grouting slurry for filling goaf: solidification mechanism and influential factors[J]. Journal of Yangtze River Scientific Research Institute, 2018, 35(8): 72-77 (in Chinese).
[59] 张晓晓.碱渣土路用性能研究与微观结构分析[D].天津:河北工业大学,2015:38-54.
ZHANG X X. Research of soda residue performance in haighway and microstructure characteristics[D]. Tianjin: Hebei University of Technology, 2015: 38-54 (in Chinese).
[60] 赵献辉,刘春原,王文静,等.路堤填垫用碱渣拌合土物理力学性能试验研究[J].硅酸盐通报,2017,36(4):1406-1411+1423.
ZHAO X H, LIU C Y, WANG W J, et al. Experimental research on physical and mechanical properties of soda residue mixing soils used for filling embankment[J]. Bulletin of the Chinese Ceramic Society, 2017, 36(4): 1406-1411+1423 (in Chinese).
[61] FERNÁNDEZ-JIMÉNEZ A, PALOMO A, CRIADO M. Microstructure development of alkali-activated fly ash cement: a descriptive model[J]. Cement and Concrete Research, 2005, 35(6): 1204-1209.