再生粗骨料附着砂浆含量对再生混凝土抗冻耐久性的影响

摘要/Abstract

摘要： 选取五种不同附着砂浆含量的商用再生粗骨料在全取代天然粗骨料条件下制备C40再生混凝土,探讨了30%极限拉应力水平下,再生粗骨料附着砂浆含量对再生混凝土抗冻耐久性的影响规律,通过数学拟合确定了基于相对动弹性模量和抗冻耐久性指数要求的砂浆界限含量。结果表明:冻融循环后,再生混凝土抗压强度损失率与附着砂浆含量存在较强线性关系;再生混凝土质量损失率、相对动弹性模量、抗冻耐久性指数均与再生粗骨料附着砂浆含量呈二次函数关系;以冻融循环300次后再生混凝土相对动弹性模量降至60%为限值,获得对应的砂浆界限含量为49.52%(质量分数);以不同设计使用年限及不同冻融工况所规定的抗冻耐久性指数作为界定条件,得到了再生混凝土在拉应力条件下满足相应抗冻耐久性指数的砂浆界限含量。最后,通过搜集文献数据验证了本研究结果的合理性。

关键词: 再生混凝土, 再生粗骨料, 附着砂浆, 界限含量, 抗压强度损失率, 质量损失率, 相对动弹性模量, 抗冻耐久性指数

Abstract: Five kinds of commercial recycled coarse aggregate (RCA) with different attached mortar content were selected to prepare C40 recycled aggregate concrete under the condition of full substitution for natural coarse aggregate. The effect of attached mortar content of RCA on the frost resistance durability of recycled aggregate concrete under 30% of ultimate tensile stress level was discussed, and the mortar limit content based on relative dynamic elastic modulus and frost resistance durability factor was determined by mathematical fitting. The results show that there is a strong linear relationship between the loss rate of compressive strength of recycled aggregate concrete and the attached mortar content after freeze-thaw cycles. The mass loss rate, relative dynamic elastic modulus and frost resistance durability factor of recycled aggregate concrete have a quadratic function relation with the attached mortar content of recycled coarse aggregate. The relative dynamic elastic modulus of recycled aggregate concrete after 300 freeze-thaw cycles is reduced to 60% as the limit value, and the corresponding mortar limit content is obtained to be 49.52% (mass fraction). Taking the durability factor specified by different design service life and freeze-thaw working conditions as the defining conditions, the mortar limit content satisfying the corresponding durability factor under tensile stress is obtained. Finally, the rationality of the research results is verified by collecting literature data.

Key words: recycled aggregate concrete, recycled coarse aggregate, attached mortar, limit content, loss rate of compressive strength, mass loss rate, relative dynamic elastic modulus, frost resistance durability factor

中图分类号:

TU528.79

魏达, 朱平华, 王新杰, 刘惠, 刘少峰, 贾学军. 再生粗骨料附着砂浆含量对再生混凝土抗冻耐久性的影响[J]. 硅酸盐通报, 2021, 40(3): 765-774.

WEI Da, ZHU Pinghua, WANG Xinjie, LIU Hui, LIU Shaofeng, JIA Xuejun. Effect of Attached Mortar Content of Recycled Coarse Aggregate on Frost Resistance Durability of Recycled Aggregate Concrete[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(3): 765-774.

参考文献

[1] XIAO J Z, LI W G, FAN Y H, et al. An overview of study on recycled aggregate concrete in China (1996—2011)[J]. Construction and Building Materials, 2012, 31: 364-383.
[2] 李佳彬,肖建庄,孙振平.再生粗骨料特性及其对再生混凝土性能的影响[J].建筑材料学报,2004,7(4):390-395.
LI J B, XIAO J Z, SUN Z P. Properties of recycled coarse aggregate and its influence on recycled concrete[J]. Journal of Building Materials, 2004, 7(4): 390-395 (in Chinese).
[3] GOKCE A, NAGATAKI S, SAEKI T, et al. Identification of frost-susceptible recycled concrete aggregates for durability of concrete[J]. Construction and Building Materials, 2011, 25(5): 2426-2431.
[4] GUO H, SHI C J, GUAN X M, et al. Durability of recycled aggregate concrete: a review[J]. Cement and Concrete Composites, 2018, 89: 251-259.
[5] DUAN Z H, POON C S. Properties of recycled aggregate concrete made with recycled aggregates with different amounts of old adhered mortars[J]. Materials & Design, 2014, 58: 19-29.
[6] DE JUAN M S, GUTIÉRREZ P A. Study on the influence of attached mortar content on the properties of recycled concrete aggregate[J]. Construction and Building Materials, 2009, 23(2): 872-877.
[7] QUAN H Z. Study on strength and durability of concrete containing recycled coarse aggregate manufactured with various method[J]. Advanced Materials Research, 2011, 287/288/289/290: 1015-1018.
[8] ŠEPS K, FLÁDR J, BROUKALOVÁ I. Resistance of recycled aggregate concrete to freeze-thaw and deicing salts[J]. Procedia Engineering, 2016, 151: 329-336.
[9] ZHU P H, HAO Y L, LIU H, et al. Durability evaluation of three generations of 100% repeatedly recycled coarse aggregate concrete[J]. Construction and Building Materials, 2019, 210: 442-450.
[10] GOKCE A, NAGATAKI S, SAEKI T, et al. Freezing and thawing resistance of air-entrained concrete incorporating recycled coarse aggregate: the role of air content in demolished concrete[J]. Cement and Concrete Research, 2004, 34(5): 799-806.
[11] 谢静静,朱平华.基于抗冻性的混凝土再生粗骨料最优取代率试验研究[J].建筑结构,2016,46(2):35-38.
XIE J J, ZHU P H. Experimental research on the optimal replacement ratio of recycled coarse aggregate based on the frost resistance[J]. Building Structure, 2016, 46(2): 35-38 (in Chinese).
[12] 张剑波,吴勇生,孙可伟,等.再生骨料混凝土孔隙结构的试验研究[J].硅酸盐通报,2011,30(1):239-244.
ZHANG J B, WU Y S, SUN K W, et al. Experiment and study on pore structure of recycled aggregate concrete[J]. Bulletin of the Chinese Ceramic Society, 2011, 30(1): 239-244 (in Chinese).
[13] 中华人民共和国国家质量监督检验检疫总局,中国国家标准化管理委员会.混凝土用再生粗骨料:GB/T 25177—2010[S].北京:中国标准出版社,2011.
General Administration of Quality Supervision, Inspection and Quarantine of the People’s Republic of China, Standardization Administration. Recycled coarse aggregate for concrete: GB/T 25177—2010[S]. Beijing: Standards Press of China, 2011 (in Chinese).
[14] TAM V W Y, TAM C M, WANG Y. Optimization on proportion for recycled aggregate in concrete using two-stage mixing approach[J]. Construction and Building Materials, 2007, 21(10): 1928-1939.
[15] 中华人民共和国国家质量监督检验检疫总局,中国国家标准化管理委员会.建设用卵石、碎石:GB/T 14685—2011[S].北京:中国标准出版社,2012.
General Administration of Quality Supervision, Inspection and Quarantine of the People’s Republic of China, Standardization Administration. Pebble and crushed stone for construction: GB/T 14685—2011[S]. Beijing: Standards Press of China, 2012 (in Chinese).
[16] PEPE M, TOLEDO FILHO R D, KOENDERS E A B, et al. Alternative processing procedures for recycled aggregates in structural concrete[J]. Construction and Building Materials, 2014, 69: 124-132.
[17] 中华人民共和国住房和城乡建设部,国家市场监督管理总局.混凝土物理力学性能试验方法标准:GB/T 50081—2019[S].北京:中国建筑工业出版社,2019.
Ministry of Housing and Urban-Rural Development of the People’s Republic of China, State Administration for Market Regulation. Standard test methods for physical and mechanical properties of concrete: GB/T 50081—2019[S]. Beijing: China Architecture & Building Press, 2019 (in Chinese).
[18] 中华人民共和国住房和城乡建设部.普通混凝土长期性能和耐久性能试验方法标准:GB/T 50082—2009[S].北京:中国建筑工业出版社,2009.
Ministry of Housing and Urban-Rural Development of the People’s Republic of China. Standard test method for long-term performance and durability of ordinary concrete: GB/T 50082—2009[S]. Beijing: China Architecture & Building Press, 2009 (in Chinese).
[19] 中华人民共和国住房和城乡建设部.混凝土结构耐久性设计规范:GB/T 50476—2019[S].北京:中国建筑工业出版社,2019.
Ministry of Housing and Urban-Rural Development of the People’s Republic of China. Code for designing durability of concrete structures: GB/T 50476—2019[S]. Beijing: China Architecture & Building Press, 2019 (in Chinese).
[20] LIU K H, YAN J C, HU Q, et al. Effects of parent concrete and mixing method on the resistance to freezing and thawing of air-entrained recycled aggregate concrete[J]. Construction and Building Materials, 2016, 106: 264-273.
[21] LI Z H, DENG Z H, YANG H F, et al. Bond behavior between recycled aggregate concrete and deformed rebar after freeze-thaw damage[J]. Construction and Building Materials, 2020, 250: 118805.
[22] WU B, LI Z. Mechanical properties of compound concrete containing demolished concrete lumps after freeze-thaw cycles[J]. Construction and Building Materials, 2017, 155: 187-199.
[23] LOVATO P S, POSSAN E, MOLIN D C C D, et al. Modeling of mechanical properties and durability of recycled aggregate concretes[J]. Construction and Building Materials, 2012, 26(1): 437-447.
[24] 武海荣,金伟良,张锋剑,等.关注环境作用的混凝土冻融损伤特性研究进展[J].土木工程学报,2018,51(8):37-46.
WU H R, JIN W L, ZHANG F J, et al. A state-of-the-art review on freeze-thaw damage characteristics of concrete under environmental actions[J]. China Civil Engineering Journal, 2018, 51(8): 37-46 (in Chinese).
[25] XIAO Q H, CAO Z Y, GUAN X, et al. Damage to recycled concrete with different aggregate substitution rates from the coupled action of freeze-thaw cycles and sulfate attack[J]. Construction and Building Materials, 2019, 221: 74-83.
[26] 罗晓辉,卫军,罗昕.混凝土劣化与有害孔洞的物理关系[J].华中科技大学学报(自然科学版),2006,34(3):94-96.
LUO X H, WEI J, LUO X. Physics relation between concrete deterioration and harmful pore[J]. Journal of Huazhong University of Science and Technology (Nature Science Edition), 2006, 34(3): 94-96 (in Chinese).
[27] 赵霄龙,卫军,黄玉盈.混凝土冻融耐久性劣化与孔结构变化的关系[J].武汉理工大学学报,2002,24(12):14-17.
ZHAO X L, WEI J, HUANG Y Y. Relationship between pore structure change of concrete and its frost durability degradation[J]. Journal of Wuhan University of Technology, 2002, 24(12): 14-17 (in Chinese).
[28] KIM Y, HANIF A, USMAN M, et al. Influence of bonded mortar of recycled concrete aggregates on interfacial characteristics-porosity assessment based on pore segmentation from backscattered electron image analysis[J]. Construction and Building Materials, 2019, 212: 149-163.
[29] ABBAS A, FATHIFAZL G, ISGOR O B, et al. Durability of recycled aggregate concrete designed with equivalent mortar volume method[J]. Cement and Concrete Composites, 2009, 31(8): 555-563.
[30] ZAHARIEVA R, BUYLE-BODIN F, WIRQUIN E. Frost resistance of recycled aggregate concrete[J]. Cement and Concrete Research, 2004, 34(10): 1927-1932.
[31] 肖前慧,曹志远,关虓,等.冻融与硫酸盐侵蚀耦合作用下再生混凝土劣化规律[J].硅酸盐通报,2020,39(2):352-358.
XIAO Q H, CAO Z Y, GUAN X, et al. Degradation law of recycled concrete under the coupling of freeze-thaw and sulfate erosion[J]. Bulletin of the Chinese Ceramic Society, 2020, 39(2): 352-358 (in Chinese).
[32] 何晓莹,王瑞骏,陶喆,等.低掺量粉煤灰再生混凝土抗冻耐久性试验研究[J].硅酸盐通报,2018,37(11):3522-3527.
HE X Y, WANG R J, TAO Z, et al. Experimental study on frost-resistant durability of recycled concrete with low content of fly ash[J]. Bulletin of the Chinese Ceramic Society, 2018, 37(11): 3522-3527 (in Chinese).
[33] LEI B, LI W G, TANG Z, et al. Durability of recycled aggregate concrete under coupling mechanical loading and freeze-thaw cycle in salt-solution[J]. Construction and Building Materials, 2018, 163: 840-849.
[34] 朱平华,张苏承.弯曲荷载作用下循环再生混凝土抗冻性研究[J].混凝土,2016(1):84-87.
ZHU P H, ZHANG S C. Frost resistance of circular recycled aggregate concrete under bending load[J]. Concrete, 2016(1): 84-87 (in Chinese).