石粉含量对C45凝灰岩机制砂混凝土性能的影响

硅酸盐通报 ›› 2021, Vol. 40 ›› Issue (3): 775-783.

石粉含量对C45凝灰岩机制砂混凝土性能的影响

王旭昊^1,2, 甘珑¹, 余海洋¹, 李程^1,2, 高新民³, 张亚刚², 李联伟³, 边庆华³

1.长安大学公路学院,西安 710064;
2.甘肃路桥建设集团有限公司,公路建设与养护技术、材料及装备交通运输行业研发中心,兰州 730030;
3.甘肃路桥第三公路工程有限责任公司,兰州 730050

收稿日期:2020-10-10 修回日期:2020-11-17 出版日期:2021-03-15 发布日期:2021-04-13
通讯作者: 甘珑,硕士研究生。E-mail:ganlong16@163.com
作者简介:王旭昊(1987—),男,博士,副教授。主要从事高性能混凝土、绿色新型材料的研究。E-mail:wangxh@chd.edu.cn
基金资助:
公路建设与养护技术、材料及装备交通运输行业研发中心(甘肃路桥建设集团有限公司)开放基金课题(GLKF201804,GLKF201807);甘肃省交通运输厅科技项目(2019-16,2019-17)

Effect of Stone Powder Content on Properties of C45 Tuff Manufactured Sand Concrete

WANG Xuhao^1,2, GAN Long¹, YU Haiyang¹, LI Cheng^1,2, GAO Xinmin³, ZHANG Yagang², LI Lianwei³, BIAN Qinghua³

1. School of Highway, Chang’an University, Xi’an 710064, China;
2. Research and Development Center of Transport Industry of Technologies, Materials and Equipments of Highway Construction and Maintenance, Gansu Road and Bridge Construction Group Co., Ltd., Lanzhou 730030, China;
3. Gansu Road and Bridge Third Highway Engineering Co., Ltd., Lanzhou 730050, China

Received:2020-10-10 Revised:2020-11-17 Online:2021-03-15 Published:2021-04-13

摘要/Abstract

摘要： 采用坍落度、振动凯氏球体试验,以及抗压强度、静压弹性模量、劈裂抗拉、混凝土表观电阻率试验,分析了石粉含量对C45凝灰岩机制砂混凝土(MSC)工作性、力学性能、抗氯离子渗透性能的影响;通过二次项式拟合分析,结合MSC与天然砂混凝土(NSC)的对比研究,给出了C45凝灰岩MSC的推荐石粉含量。结果表明:随着石粉含量的提高,C45凝灰岩MSC的坍落度、振动凯氏系数、抗压强度、静压弹性模量、劈裂抗拉强度、抗氯离子渗透性能均先增大后减小,存在最佳石粉含量;当对混凝土的要求为坍落度>100 mm、静压弹性模量>44 GPa时,C45凝灰岩MSC的推荐石粉含量为2%~5%(质量分数,下同);当对混凝土的要求为坍落度<100 mm、静压弹性模量<44 GPa时,推荐石粉含量为可放宽为5%~8%;合理控制机制砂石粉含量可以使C45凝灰岩MSC的综合性能优于C45 NSC。

关键词: 凝灰岩机制砂混凝土, 石粉含量, 工作性, 力学性能, 抗氯离子渗透性能

Abstract: The effect of stone powder content on the workability, mechanical properties and chloride ion penetration resistance of C45 tuff manufactured sand concrete (MSC) were assessed by applying the slump test,Vkelly test, compressive strength, elastic modulus, splitting tensile strength and surface resistivity tests. In accordance with the fitting analysis of quadratic formula and the comparative study of MSC and natural sand concrete (NSC), the suggested stone powder content of C45 tuff MSC was established. The results indicate that the slump, Vkelly index compressive strength, elastic modulus, splitting tensile strength andchloride ion penetration resistance of C45 tuff MSC increase first and then start to decrease with the increase of stone powder content in a certain range. In engineering applications, if the specific required slump is greater than 100 mm and elastic modulus is higher than 44 GPa, the suggested stone powder content of C45 tuff MSC is between 2% (mass fraction, the same below) and 5%. Otherwise, the suggested stone powder content between 5% and 8% is accepted. Reasonable control of the stone powder content of manufactured sand can yield a better engineering performance of C45 tuff MSC compared with C45 NSC.

Key words: tuff manufactured sand concrete, stone powder content, workability, mechanical property, chloride ion penetration resistance

中图分类号:

TU528

王旭昊, 甘珑, 余海洋, 李程, 高新民, 张亚刚, 李联伟, 边庆华. 石粉含量对C45凝灰岩机制砂混凝土性能的影响[J]. 硅酸盐通报, 2021, 40(3): 775-783.

WANG Xuhao, GAN Long, YU Haiyang, LI Cheng, GAO Xinmin, ZHANG Yagang, LI Lianwei, BIAN Qinghua. Effect of Stone Powder Content on Properties of C45 Tuff Manufactured Sand Concrete[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(3): 775-783.

参考文献

[1] 颜从进.机制砂特性对混凝土性能的影响研究[D].重庆:重庆大学,2014.
YAN C J. Research of effects of mechanism sand characteristics on concrete[D]. Chongqing: Chongqing University, 2014 (in Chinese).
[2] 王稷良.机制砂特性对混凝土性能的影响及机理研究[D].武汉:武汉理工大学,2008.
WANG J L. Research of effects and mechanism of manufactured sand characteristics on Portland cement concrete[D]. Wuhan: Wuhan University of Technology, 2008 (in Chinese).
[3] 刘战鳌,周明凯,李北星.石粉对机制砂混凝土性能影响的研究进展[J].材料导报,2014,28(19):100-103.
LIU Z A, ZHOU M K, LI B X. Research progress on influence of microfines on manufactured sand concrete’s performance[J]. Materials Review, 2014, 28(19): 100-103 (in Chinese).
[4] 谢开仲,王红伟,肖杰,等.石粉含量对机制砂混凝土力学性能影响试验[J].建筑科学与工程学报,2019,36(5):31-38.
XIE K Z, WANG H W, XIAO J, et al. Experiment on influence of stone powder content on mechanical properties of manufactured sand concrete[J]. Journal of Architecture and Civil Engineering, 2019, 36(5): 31-38 (in Chinese).
[5] DIAB A M, ABD ELMOATY A E M, ALY A A. Long term study of mechanical properties, durability and environmental impact of limestone cement concrete[J]. Alexandria Engineering Journal, 2016, 55(2): 1465-1482.
[6] RAMEZANIANPOUR A A, GHIASVAND E, NICKSERESHT I, et al. Influence of various amounts of limestone powder on performance of Portland limestone cement concretes[J]. Cement and Concrete Composites, 2009, 31(10): 715-720.
[7] 刘牧天,黎梦圆,王强.等强度条件下石灰石粉对混凝土收缩和耐久性的影响[J].硅酸盐通报,2014,33(8):1967-1972+1977.
LIU M T, LI M Y, WANG Q. Influence of limestone powder on the shrinkage and durability of concrete at the given strength levels[J]. Bulletin of the Chinese Ceramic Society, 2014, 33(8): 1967-1972+1977 (in Chinese).
[8] 唐凯靖,刘来宝,周应.岩性对机制砂特性及其混凝土性能的影响[J].混凝土,2011(12):62-63+66.
TANG K J, LIU L B, ZHOU Y. Effects of lithology on properties of manufactured sand and the performance of the concrete with manufactured sand[J]. Concrete, 2011(12): 62-63+66 (in Chinese).
[9] RIZWAN S A, BIER T A. Blends of limestone powder and fly-ash enhance the response of self-compacting mortars[J]. Construction and Building Materials, 2012, 27(1): 398-403.
[10] 王振,李化建,黄法礼,等.不同岩性石粉-水泥胶砂流动性和力学性能研究[J].硅酸盐通报,2019,38(5):1585-1590.
WANG Z, LI H J, HUANG F L, et al. Fluidity and mechanical properties of cement mortar with different lithological powders[J]. Bulletin of the Chinese Ceramic Society, 2019, 38(5): 1585-1590 (in Chinese).
[11] 周玉娟,陈三安,占文,等.用于箱梁的凝灰岩机制砂混凝土力学及耐久性能研究[J].施工技术,2015,44(18):16-18.
ZHOU Y J, CHEN S A, ZHAN W, et al. Research on the mechanical and durability performance of tuff manufactured sand concrete used for box girder[J]. Construction Technology, 2015, 44(18): 16-18 (in Chinese).
[12] HOWARD E L, LEAVITT G. Kelly ball vs slump cone-comparative tests of samples taken at travis air base[J]. Journal of the American Concrete Institute, 1951, 48(4): 353-356.
[13] WANG X H. A novel test to determine the workability of slipform concrete mixtures[J]. Magazine of Concrete Research, 2017, 69(6): 292-305.
[14] WANG Y L, JIN Z Q, LIU S X, et al. Physical filling effect of aggregate micro fines in cement concrete[J]. Construction and Building Materials, 2013, 41: 812-814.
[15] 宋军伟,王露,刘数华,等.石灰石粉在超高性能水泥基材料中的作用机理[J].硅酸盐通报,2016,35(12):4104-4109.
SONG J W, WANG L, LIU S H, et al. Functionary mechanism of limestone powder in ultra high performance cement-based materials[J]. Bulletin of the Chinese Ceramic Society, 2016, 35(12): 4104-4109 (in Chinese).
[16] 史才军,王德辉,贾煌飞,等.石灰石粉在水泥基材料中的作用及对其耐久性的影响[J].硅酸盐学报,2017,45(11):1582-1593.
SHI C J, WANG D H, JIA H F, et al. Role of limestone powder and its effect on durability of cement-based materials[J]. Journal of the Chinese Ceramic Society, 2017, 45(11): 1582-1593 (in Chinese).
[17] 刘战鳌,周明凯,姚楚康.机制砂中细粉的危害性及评价研究[J].建筑材料学报,2015,18(1):150-155.
LIU Z A, ZHOU M K, YAO C K. Research on harmfulness and evaluation of various microfines in manufactured sand[J]. Journal of Building Materials, 2015, 18(1): 150-155 (in Chinese).
[18] 张礼华,刘来宝,周永生,等.石粉含量对机制砂混凝土力学性能与微观结构的影响[J].混凝土与水泥制品,2011(12):22-26.
ZHANG L H, LIU L B, ZHOU Y S, et al. Influences of content of stone powder on mechanical properties and microstructure of manufactured sand concrete[J]. China Concrete and Cement Products, 2011(12): 22-26 (in Chinese).
[19] RUPNOW T D, ICENOGLE P J. Surface resistivity measurements evaluated as alternative to rapid chloride permeability test for quality assurance and acceptance[J]. Transportation Research Record: Journal of the Transportation Research Board, 2012, 2290(1): 30-37.
[20] American Association of State Highway and Transportation Officials. Standard method of test for surface resistivity of concrete’s ability to resist chloride ion penetration: AASHTO TP 95[S]. Washington, 2011.