硅酸盐通报 ›› 2021, Vol. 40 ›› Issue (10): 3279-3284.

• 专题研究论文 • 上一篇    下一篇

CaCO3微粉对刚玉质弥散型透气砖性能的影响

邱鑫, 李方圆, 张仕鸣, 刘新红, 贾全利   

  1. 郑州大学材料科学与工程学院,河南省高温功能材料重点实验室,郑州 450052
  • 收稿日期:2021-07-25 修回日期:2021-09-02 出版日期:2021-10-15 发布日期:2021-11-11
  • 通讯作者: 贾全利,博士,教授。E-mail:jiaquanli@zzu.edu.cn
  • 作者简介:邱 鑫(1997—),男,硕士研究生。主要从事高温功能材料的研究。E-mail:244877189@qq.com
  • 基金资助:
    国家自然科学基金(52172029);河南省自然科学基金(202300410473)

Effect of CaCO3 Micropowder on Properties of Corundum Based Porous Purging Plug

QIU Xin, LI Fangyuan, ZHANG Shiming, LIU Xinhong, JIA Quanli   

  1. Henan Key Laboratory of High Temperature Functional Ceramics, School of Material Science and Engineering,Zhengzhou University, Zhengzhou 450052, China
  • Received:2021-07-25 Revised:2021-09-02 Online:2021-10-15 Published:2021-11-11

摘要: 弥散型透气砖因具有供气可靠性好、安全性高和精炼效果好等优点得到较多应用,然而其自身多孔结构导致的强度低和使用寿命短等缺陷限制了它的应用。为优化刚玉质弥散型透气砖的使用性能,本文以电熔白刚玉颗粒及细粉、α-Al2O3微粉、Cr2O3微粉等为主要原料,固定颗粒与细粉的质量比为85∶15,分别用质量分数为0%、1%、2%、3%的CaCO3等量替代电熔白刚玉细粉,探索CaCO3微粉的引入对弥散砖性能的影响。结果表明:随CaCO3微粉加入量增加(0%~2%),弥散砖材料常温强度和高温强度增加,由于CaCO3分解生成的CaO与基质中的Al2O3反应生成六铝酸钙,其相互穿插连接增加了基质间的结合程度,从而提高了材料的强度。

关键词: 弥散型透气砖, 刚玉质, 电熔白刚玉, CaCO3微粉, 六铝酸钙, 透气度

Abstract: Porous purging plugs have been widely used due to the advantages of good air supply reliability, high safety and good refining effect. However, its application is limited by the defect such as low strength and short service life caused by its own porous structure. In order to further improve the properties of corundum based porous purging plugs, fused white corundum particles and fine powder, α-Al2O3 micropowder and Cr2O3 micropowder were used as raw materials, the mass ratio of aggregate to matrix was fixed at 85∶15, and 0%, 1%, 2% and 3% (mass fraction) CaCO3 were used to replace fused white corundum fine powder, respectively. The effect of the introduction of CaCO3 micropowder on the properties of porous purging plugs was explored. The results show that the strength at room temperature and high temperature all increase with the amount of CaCO3 powder (from 0% to 2%). The main reason is that the CaO formed by the decomposition of CaCO3 reacts with Al2O3 in the matrix to form calcium hexaaluminate, which intersperses and connects with each other to increase the bonding degree between the matrix, thus improving the strength of the samples.

Key words: porous purging plug, corundum based, fused white corundum, CaCO3 micropowder, calcium hexaaluminate, permeability

中图分类号: