Cr2O3微粉加入量对Al2O3-Cr2O3质耐火材料性能的影响

硅酸盐通报 ›› 2021, Vol. 40 ›› Issue (10): 3285-3291.

Cr₂O₃微粉加入量对Al₂O₃-Cr₂O₃质耐火材料性能的影响

康鑫¹, 张利新², 邓俊杰², 刘萍², 徐恩霞¹, 李素平¹

1.郑州大学材料科学与工程学院,河南省高温功能材料重点实验室,郑州 450052;
2.中钢洛耐科技股份有限公司,洛阳 471039

收稿日期:2021-08-15 修回日期:2021-09-02 出版日期:2021-10-15 发布日期:2021-11-11
通讯作者: 李素平,博士,副教授。E-mail:lisuping@zzu.edu.cn
作者简介:康鑫(1996—),男,硕士研究生。主要从事耐火材料的研究。E-mail:kang960421@163.com

Effect of Addition of Cr₂O₃ Micropowder on Properties of Al₂O₃-Cr₂O₃ Refractory

KANG Xin¹, ZHANG Lixin², DENG Junjie², LIU Ping², XU Enxia¹, LI Suping¹

1. Henan Key Laboratory of High Temperature Functional Ceramics, School of Material Science and Engineering, Zhengzhou University,Zhengzhou 450052, China;
2. Sinosteel Luonai Materials Technology Corporation, Luoyang 471039, China

Received:2021-08-15 Revised:2021-09-02 Online:2021-10-15 Published:2021-11-11

摘要/Abstract

摘要： 以电熔铬刚玉和白刚玉为主要原料,用Cr₂O₃微粉部分替代电熔铬刚玉细粉,研究了Cr₂O₃微粉加入量对Al₂O₃-Cr₂O₃质耐火材料常温和高温性能、物相组成和显微结构的影响。结果表明,随着Cr₂O₃微粉加入量的增加,原位形成了(Al_1-xCr_x)₂O₃固溶体,促进了烧结,材料的显气孔率先降低后升高,且(Al_1-xCr_x)₂O₃固溶体的晶格常数呈线性增加,符合Vegard定律。材料的常温抗折强度和常温耐压强度随Cr₂O₃微粉加入量的增加先升高后降低,在Cr₂O₃微粉加入量为15%(质量分数)时强度达到最大值。而当Cr₂O₃微粉加入量为20%(质量分数)时,由于有挥发现象,材料显气孔率上升,强度下降。材料高温抗折强度随Cr₂O₃微粉加入量的增加而增加,材料的残余强度保持率呈先降低后升高的趋势。

关键词: Al₂O₃-Cr₂O₃质耐火材料, Cr₂O₃微粉, (Al_1-xCr_x)₂O₃固溶体, 晶格常数, Vegard定律, 高温性能

Abstract: The effect of the addition of Cr₂O₃ micropowder on the normal temperature and high temperature performances, phase composition and microstructure of Al₂O₃-Cr₂O₃ refractories was studied by using fused chromium corundum and white corundum as the main raw materials, and using Cr₂O₃ micropowder to partially replace the fused chromium corundum fine powder. The results show that with the increase of the addition of Cr₂O₃ micropowder, (Al_1-xCr_x)₂O₃ solid solution is in-situ formed, which promotes sintering. And the apparent porosity of the material decreases first and then increases. The lattice constant of (Al_1-xCr_x)₂O₃ solid solution increases linearly with the increase of the addition of Cr₂O₃ micropowder, which conforms to Vegard’s law. The cold modulus of rupture and cold compressive strength increase first and then decrease with the increase of the addition of Cr₂O₃ micropowder. When the addition of Cr₂O₃ micropowder is 15% (mass fraction), the strength of the material reaches the maximum value. When the addition of Cr₂O₃ micropowder is 20% (mass fraction), the apparent porosity of the material increases and the strength decreases due to volatilization. The hot modulus of rupture of the material increases, and the residual strength rate of the material decreases first and then increases with the increase of the addition of Cr₂O₃ micropowder.

Key words: Al₂O₃-Cr₂O₃ refractory, Cr₂O₃ micropowder, (Al_1-xCr_x)₂O₃ solid solution, lattice constant, Vegard’s law, high temperature performance

中图分类号:

TQ175.71

康鑫, 张利新, 邓俊杰, 刘萍, 徐恩霞, 李素平. Cr₂O₃微粉加入量对Al₂O₃-Cr₂O₃质耐火材料性能的影响[J]. 硅酸盐通报, 2021, 40(10): 3285-3291.

KANG Xin, ZHANG Lixin, DENG Junjie, LIU Ping, XU Enxia, LI Suping. Effect of Addition of Cr₂O₃ Micropowder on Properties of Al₂O₃-Cr₂O₃ Refractory[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(10): 3285-3291.

参考文献

[1] CHEN L G, MALFLIET A, VLEUGELS J, et al. Degradation mechanisms of alumina-chromia refractories for secondary copper smelter linings[J]. Corrosion Science, 2018, 136: 409-417.
[2] GEHRE P, ANEZIRIS C G, BEREK H, et al. Corrosion of magnesium aluminate spinel-rich refractories by sulphur-containing slag[J]. Journal of the European Ceramic Society, 2015, 35(5): 1613-1620.
[3] HIRATA T, MORIMOTO T, OHTA S, et al. Improvement of the corrosion resistance of alumina-chromia ceramic materials in molten slag[J]. Journal of the European Ceramic Society, 2003, 23(12): 2089-2096.
[4] CHEN J F, XIAO J L, ZHANG Y, et al. Corrosion mechanism of Cr₂O₃-Al₂O₃-ZrO₂ refractories in a coal-water slurry gasifier: a post-mortem analysis[J]. Corrosion Science, 2020, 163: 108250.
[5] CHEN D, HUANG A, GU H Z, et al. Corrosion of Al₂O₃-Cr₂O₃ refractory lining for high-temperature solid waste incinerator[J]. Ceramics International, 2015, 41(10): 14748-14753.
[6] 杨秀丽,李冰,刘会林,等.Al₂O₃-Cr₂O₃-ZrO₂砖在医疗垃圾焚烧炉上的应用[J].耐火材料,2014,48(2):143-144.
YANG X L, LI B, LIU H L, et al. Application of Al₂O₃-Cr₂O₃-ZrO₂ brick in medical waste incinerator[J]. Refractories, 2014, 48(2): 143-144 (in Chinese).
[7] 徐腾腾,李亚伟,徐义彪,等.危废焚烧炉用Al₂O₃-Cr₂O₃-ZrO₂砖抗渣侵蚀性及六价铬形成研究[J].硅酸盐通报,2019,38(10):3273-3277+3286.
XU T T, LI Y W, XU Y B, et al. Slag corrosion resistance of Al₂O₃-Cr₂O₃-ZrO₂ bricks for hazardous waste incinerators and concurrent formation of hexavalent chromium[J]. Bulletin of the Chinese Ceramic Society, 2019, 38(10): 3273-3277+3286 (in Chinese).
[8] WANG X H, ZHAO P D, CHEN J W, et al. Corrosion resistance of Al-Cr-slag containing chromium-corundum refractories to slags with different basicity[J]. Ceramics International, 2018, 44(11): 12162-12168.
[9] NATH M, GHOSH A, TRIPATHI H S. Hot corrosion behavior of Al₂O₃-Cr₂O₃ refractory by molten glass at 1 200 ℃ under static condition[J]. Corrosion Science, 2016, 102: 153-160.
[10] ZHAO P D, ZHAO H Z, YU J, et al. Crystal structure and properties of Al₂O₃-Cr₂O₃ solid solutions with different Cr₂O₃ contents[J]. Ceramics International, 2018, 44(2): 1356-1361.
[11] KAFKASLIOLU YILDIZ B, YILMAZ H, TÜR Y K. Evaluation of mechanical properties of Al₂O₃-Cr₂O₃ ceramic system prepared in different Cr₂O₃ ratios for ceramic armour components[J]. Ceramics International, 2019, 45(16): 20575-20582.
[12] NATH M, KUMAR P, MALDHURE A V, et al. Anomalous densification behavior of Al₂O₃-Cr₂O₃ system[J]. Materials Characterization, 2016, 111: 8-13.
[13] HIRATA T, AKIYAMA K, YAMAMOTO H. Sintering behavior of Cr₂O₃-Al₂O₃ ceramics[J]. Journal of the European Ceramic Society, 2000, 20(2): 195-199.
[14] NATH M, SEN S, BANERJEE K, et al. Densification behavior and properties of alumina-chrome ceramics: effect of TiO₂[J]. Ceramics International, 2013, 39(1): 227-232.
[15] 王义龙,王子军,马伟平,等.硅微粉对ρ-Al₂O₃结合莫来石浇注料的影响[J].硅酸盐通报,2014,33(11):3046-3049.
WANG Y L, WANG Z J, MA W P, et al. Effect of silica powder on ρ-Al₂O₃ bonded mullite castables[J]. Bulletin of the Chinese Ceramic Society, 2014, 33(11): 3046-3049 (in Chinese).
[16] CUI K K, ZHANG Y Y, FU T, et al. Effects of Cr₂O₃ content on microstructure and mechanical properties of Al₂O₃ matrix composites[J]. Coatings, 2021, 11(2): 234.
[17] SABRI K, RAIS A, TAIBI K, et al. Structural Rietveld refinement and vibrational study of MgCr_xFe_2-xO₄ spinel ferrites[J]. Physica B: Condensed Matter, 2016, 501: 38-44.
[18] EL BACHRAOUI F, CHCHIYAI Z, TAMRAOUI Y, et al. Effect of the composition and structure on the optical properties of Ba_1-xLa_xTi_1-xFe_xO₃ (0≤x≤1) solid solution: correlation study using Rietveld refinement[J]. Materials Characterization, 2021, 175: 111058.

Cr₂O₃微粉加入量对Al₂O₃-Cr₂O₃质耐火材料性能的影响

Effect of Addition of Cr₂O₃ Micropowder on Properties of Al₂O₃-Cr₂O₃ Refractory

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	王岚, 郭志祥, 张宝鑫, 宋长振, 何立琦. 盐冻融循环下温/热拌胶粉改性沥青混合料高低温性能研究[J]. 硅酸盐通报, 2021, 40(4): 1395-1404.
[2]	韩晓源, 石凯, 夏熠, 洪思阳, 刘洋, 商剑钊. 不同铝基原料对MgO-Al-C材料性能和显微结构的影响[J]. 硅酸盐通报, 2021, 40(10): 3232-3240.
[3]	吴金荣;李飞;宋风宁;崔善成. 粉煤灰/聚酯纤维沥青混合料马歇尔试验研究[J]. 硅酸盐通报, 2020, 39(4): 1343-1350.
[4]	李宁;申爱琴;周彬;马俊. 回收橡胶树脂改性沥青混合料高温性能及微观分析[J]. 硅酸盐通报, 2019, 38(9): 2910-291.
[5]	谷昱杰;邵寒蕊;涂慧镧;王长安;彭景;赵惠忠. 粉煤灰于耐火材料应用领域的常规性能研究[J]. 硅酸盐通报, 2019, 38(6): 1908-191.
[6]	肖庆一;赵鹏;林永会;张萌骐. 热老化作用下废机油改性沥青高温流变性能研究[J]. 硅酸盐通报, 2019, 38(11): 3597-360.
[7]	宋乐春;李志军;陈保莲;宁爱民;范思远;张静;程国香. 高模量沥青混凝土添加剂研究[J]. 硅酸盐通报, 2018, 37(4): 1221-1224.
[8]	曹集舒. 硅酸盐水泥耐高温性能研究[J]. 硅酸盐通报, 2017, 36(4): 1452-1456.
[9]	张向冈;邝肖梅;牛海成;杨健辉. 废橡胶改性再生混凝土材料性能研究进展[J]. 硅酸盐通报, 2017, 36(12): 4050-4059.
[10]	庞超明;吕梦媛;孙友康. 核壳结构免烧轻骨料的制备与性能研究[J]. 硅酸盐通报, 2016, 35(7): 2121-2127.
[11]	李丹;何锐;王帅;王锴;盛燕萍. PVA纤维增强水泥基复合材料高温性能研究[J]. 硅酸盐通报, 2015, 34(6): 1604-1610.
[12]	刘新;曲殿利;姚瑶. 矾土熟料与均质矾土熟料性能及应用的对比研究[J]. 硅酸盐通报, 2014, 33(7): 1667-1671.
[13]	李早元;伍鹏;程小伟;王岩;郭小阳. 矿渣对铝酸盐水泥石性能影响的研究[J]. 硅酸盐通报, 2014, 33(12): 3338-3342.
[14]	雷牧云;李法荟;闻芳;汪志华;李祯;宋庆海. 透明尖晶石陶瓷的高温性能和应用研究[J]. 硅酸盐通报, 2009, 28(z1): 190-193.
[15]	张向华;肖思国;丁庆磊;夏艳琴;刘政威. 不同冷却方式对Er3+/Yb3+共掺BaF2粉末上转换发光效率的影响[J]. 硅酸盐通报, 2006, 25(6): 67-71.