Ni2+-Fe3+-CO2-3-LDHs亲油改性及其除油性能研究

硅酸盐通报 ›› 2017, Vol. 36 ›› Issue (8): 2792-2798.

Ni2+-Fe3+-CO2-3-LDHs亲油改性及其除油性能研究

党睿;马向荣;刘洁莹;白艳霞;张智芳;张宇鑫;钱肃进

榆林学院化学与化工学院,榆林,719000

出版日期:2017-08-15 发布日期:2021-01-18
基金资助:
国家自然科学基金项目(51601167)%陕西省科技厅项目(2015SF262)%陕西省教育厅协同创新、服务地方计划项目(15JF035)%榆林学院专项科研计划项目(14YK22)

Lipophilic Modification of Ni2+-Fe3+-CO2-3-LDHs Materials andStudy of Its Oil Absorption Properties

DANG Rui;MA Xiang-rong;LIU Jie-ying;BAI Yan-xia;ZHANG Zhi-fang;ZHANG Yu-xin;QIAN Su-jin

Online:2017-08-15 Published:2021-01-18

摘要/Abstract

摘要： 尿素作为沉淀剂,采用均相沉淀技术制备了Ni2+-Fe3+-CO2-3-LDHs层状材料.以Ni2+-Fe3+-CO2-3-LDHs作为前驱体,分别与NaCl、十二烷基磺酸钠(CH3(CH2)11SO3Na)进行离子交换反应得到Ni2+-Fe3+-CH3(CH2)11SO-3-LDHs新型吸附剂材料,成功实现了将CH3(CH2)11SO-3负载到Ni2+-Fe3+-LDHs层状材料,对Ni2+-Fe3+-CO2-3-LDHs进行亲油改性,研究表明该改性后的材料为介孔材料,其比表面积为196.2m2/g,平均孔径为18.3nm.利用Ni2+-Fe3+-CH3(CH2)11SO-3-LDHs复合材料对含油污水进行处理,实验表明十二烷基磺酸根离子插层Ni2+-Fe3+-LDHs后的产物增强了LDHs的亲油吸附性能,其饱和吸附量为6.57μL/g.

关键词: CH3(CH2)11SO-3;Ni2+-Fe3+-CO2-3-LDHs;插层组装

Abstract: Ni2+-Fe3+-CO2-3-LDHs was prepared by homogeneous precipitation method.Ni2+-Fe3+-CH3(CH2)11SO-3-LDHs was successfully synthetized through ion exchange reach with NaCl and dodecyl sulfonic acid (CH3(CH2)11SO-3) respectively using Ni2+-Fe3+-CH3(CH2)11SO-3-LDHs as precursor, which made the CH3(CH2)11SO-3 load to layer spacing of Ni2+-Fe3+-CO2-3-LDHs.The experimental results show that the Ni2+-Fe3+-CH3(CH2)11SO-3-LDHs is belonging to mesoporous materials.The BET surface area and average pore of the obtained materials are 196.2 m2/g and 18.3 nm respectively.Ni2+-Fe3+-CH3(CH2)11SO-3-LDHs is used as an adsorbent for the treatment of waste containing wastewater.The experiment results indicate that the dodecyl sulfonic acid (CH3(CH2)11SO-3) ion insertion product of layer Ni2+-Fe3+-CO2-3-LDHs enhanced oil adsorption properties and its saturated adsorption capacity is 6.57 μL/g.

Key words: CH3(CH2)11SO-3;Ni2+-Fe3+-CO2-3-LDHs;intercalation

中图分类号:

党睿;马向荣;刘洁莹;白艳霞;张智芳;张宇鑫;钱肃进. Ni2+-Fe3+-CO2-3-LDHs亲油改性及其除油性能研究[J]. 硅酸盐通报, 2017, 36(8): 2792-2798.

DANG Rui;MA Xiang-rong;LIU Jie-ying;BAI Yan-xia;ZHANG Zhi-fang;ZHANG Yu-xin;QIAN Su-jin. Lipophilic Modification of Ni2+-Fe3+-CO2-3-LDHs Materials andStudy of Its Oil Absorption Properties[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2017, 36(8): 2792-2798.

[1]	刘洁莹;党睿;李梅;马向荣;刘丹;李小红;冯荣利. Ni2+-Al3+-MoO2-4-LDHs防腐缓蚀剂的制备及其表征[J]. 硅酸盐通报, 2017, 36(1): 380-384.
[2]	赫文秀;张永强;蒋文全;傅钟臻;于丽敏;张文广. 球形覆Co氢氧化镍的合成及性能研究[J]. 硅酸盐通报, 2008, 27(2): 276-280.
[3]	高立国;刘四霞;宋小利;高雄雄;李婉璐;马向荣. La3+-Zn2+-Al3+-CO2-3-LDHs的制备及其对含Cr(Ⅵ)废水的吸附研究[J]. 硅酸盐通报, 2018, 37(7): 2184-2190.