渗锡量的定性检测及降低玻璃表面渗锡量的措施研究

硅酸盐通报 ›› 2017, Vol. 36 ›› Issue (3): 1035-1039.

渗锡量的定性检测及降低玻璃表面渗锡量的措施研究

王宙

河北建材职业技术学院,秦皇岛,066004

出版日期:2017-03-15 发布日期:2021-01-18

Measures for Reducing Amount of Tin Infiltration and Its Qualitative Detection

WANG Zhou

Online:2017-03-15 Published:2021-01-18

摘要/Abstract

摘要： 浮法工艺生产平板玻璃,由于玻璃在锡槽内成形,玻璃下表面必然会引入一定的渗锡量,当渗锡量达到一定程度时,如果玻璃进行钢化加工,就会出现钢化彩虹,从而影响到玻璃的外观质量.分析了浮法玻璃钢化彩虹的形成与渗锡量的关系,提出了浮法玻璃生产中渗锡量的定性快速检测方法,可以避免玻璃在后续加工中造成损失;论述了降低玻璃渗锡量的措施,可用于指导浮法玻璃生产.

关键词: 玻璃;钢化彩虹;表面渗锡量;检测

Abstract: In float process, glass formed in tin bath, which caused of tin penetration.Tempering bloom would appear when glass that had tin infiltration over a certain amount was tempered, thus affecting the appearance quality of glass.In this paper, the relationship between the formation of tempering bloom and the amount of tin infiltration was analyzed.The rapid qualitative detection methods were recommended to avoid waste in subsequent processing.The measures to reduce the amount of tin infiltration were discussed to guide the glass production.

Key words: glass;tempering bloom;amount of tin infiltration;detection

中图分类号:

TQ171.6

王宙. 渗锡量的定性检测及降低玻璃表面渗锡量的措施研究[J]. 硅酸盐通报, 2017, 36(3): 1035-1039.

WANG Zhou. Measures for Reducing Amount of Tin Infiltration and Its Qualitative Detection[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2017, 36(3): 1035-1039.

[1]	杜秀红;李茂刚. 光伏压延玻璃中锑酸盐结石的形成机理研究[J]. 硅酸盐通报, 2020, 39(2): 601-604.
[2]	郑伟宏;王玲玲;张谋;侯延升;刘欣悦;周颖;郭振强. 温度对柔性玻璃狭缝下拉成形过程的影响[J]. 硅酸盐通报, 2018, 37(9): 2935-2940.
[3]	韩韬;刘宗明;李贤松;赵蔚琳;张铁柱. 单元玻璃窑炉富氧燃烧空间的数值模拟研究[J]. 硅酸盐通报, 2010, 29(1): 77-82.