环境作用下粗骨料对混凝土性能影响的时变研究

doi:10.16552/j.cnki.issn1001-1625.2024.0053

硅酸盐通报 ›› 2025, Vol. 44 ›› Issue (1): 133-141.DOI: 10.16552/j.cnki.issn1001-1625.2024.0053

环境作用下粗骨料对混凝土性能影响的时变研究

张文静^1,2, 张戎令³, 张岩^1,2, 王玉林⁴, 张富奎⁵, 王先龙⁵, 安康乐³

1.甘肃省交通科学研究院集团有限公司,兰州 730000;
2.甘肃省道路材料工程实验室,兰州 730000;
3.兰州交通大学道桥工程灾害防治技术国家地方联合工程实验室,兰州 730070;
4.甘肃省公交建集团有限公司,兰州 730030;
5.甘肃省交通规划勘察设计院股份有限公司,兰州 730030

收稿日期:2024-01-11 修订日期:2024-03-23 出版日期:2025-01-15 发布日期:2025-01-23
通信作者: 张戎令,博士,教授。E-mail:mogzrlggg@163.com
作者简介:张文静(1992—),女。主要从事混凝土耐久性与寿命预测的研究。E-mail:wjzhang22@qq.com
基金资助:
交通运输行业重点科技项目(2021-ZD2-073);兰州市科技计划项目(2022-5-47);甘肃省科技重点研发计划(21YF11GA011);甘肃省科技厅中小企业创新基金项目(22CX3GA073)

Time-Varying Study on Effect of Coarse Aggregate on Concrete Performance under Environmental Action

ZHANG Wenjing^1,2, ZHANG Rongling³, ZHANG Yan^1,2, WANG Yulin⁴, ZHANG Fukui⁵, WANG Xianlong⁵, AN Kangle³

1. Gansu Provincial Transportation Research Institute Group Co., Ltd., Lanzhou 730000, China;
2. Gansu Provincial Road Materials Engineering Laboratory, Lanzhou 730000, China;
3. National and Local Joint Engineering Laboratory of Road & Bridge Engineering Disaster Prevention Technology Engineering, Lanzhou Jiaotong University, Lanzhou 730070, China;
4. Gansu Province Highway Construction Group Co., Ltd., Lanzhou 730030, China;
5. Gansu Province Planning Survey＆Design Institute Co., Ltd., Lanzhou 730030, China

Received:2024-01-11 Revised:2024-03-23 Published:2025-01-15 Online:2025-01-23

摘要/Abstract

摘要： 为探究冻融循环-硫酸盐腐蚀环境下辉长岩(SMK)、花岗岩(LBH)、辉绿岩(HYS)、片麻岩(LFS)、硅化英安岩(SSH)对混凝土性能的影响,通过抗压强度、孔结构等混凝土宏-微观试验,研究了5种粗骨料所制备混凝土在Na₂SO₄溶液半浸泡下经历不同冻融循环次数的时变规律。结果表明:随着冻融循次数的增加,HYS混凝土和LFS混凝土表观损失较为严重,内部部分粗骨料疏松,强度降低且骨料与水泥砂浆的界面黏结强度降低;在冻融循环初期,5组混凝土试件内孔隙快速扩展且有较多新的孔隙萌生,小孔数量增加,大孔数量减小,抗压强度也随之增大;在冻融循环后期,试样内部大孔径孔隙增多,LFS混凝土内部部分粗骨料疏松膨胀,混凝土开裂加剧;LFS混凝土孔隙扩展最大,HYS混凝土孔隙扩展次之;在冻融循环后期,5组混凝土试件的孔径变化趋势基本一致,混凝土强度降低,且与孔隙变化呈正相关,但强度降低幅度与粗骨料自身性质相关。该研究可为冻融循环-硫酸盐腐蚀环境下粗骨料质量控制及混凝土可持续利用提供借鉴。

关键词: 混凝土, 粗骨料劣化, 冻融循环, 硫酸盐腐蚀, 抗蚀系数, 孔结构分析

Abstract: In order to explore the effects of gabbro (SMK), granite (LBH), diabase (HYS), gneiss (LFS), silicified dacite (SSH) on the properties of concrete under freeze-thaw and sulfate corrosion environment, the macro-micro tests of concrete such as compressive strength and pore structure were carried out to study the time-varying law of concrete prepared by five kinds of coarse aggregates undergoing different freeze-thaw cycle times under semi-immersion of Na₂SO₄ solution. The results show that with the increase of freeze-thaw cycle times, the apparent loss of HYS concrete and LFS concrete is more serious, the internal part of coarse aggregate is loose, the strength is reduced, and the interfacial bonding strength between aggregate and cement mortar is reduced. At the beginning of freeze-thaw cycle test, the pores in the five groups of concrete specimens expand rapidly and many new pores generate. The number of small pores increases, the number of large pores decreases, and the compressive strength also increases. In the later stage of freeze-thaw cycle, the large pore size in specimen increases, the coarse aggregate in LFS concrete is loose and expanded, and the concrete cracking is aggravated. LFS concrete has the largest pore expansion, followed by the HYS concrete pore expansion. The pore size variation trend of the five groups of concrete specimens is basically the same. The strength of concrete decreases and is positively correlated with the pore change, but the strength reduction is related to the performance of coarse aggregate itself. This study can be crude in freeze-thaw and sulfate corrosion environment. The research results can provide reference for quality control of coarse aggregate and sustainable utilization of concrete under freeze-thaw sulfate corrosion environment.

Key words: concrete, coarse aggregate deterioration, freeze-thaw cycle, sulfate corrosion, corrosion resistance coefficient, pore structure analysis

中图分类号:

TU528

张文静, 张戎令, 张岩, 王玉林, 张富奎, 王先龙, 安康乐. 环境作用下粗骨料对混凝土性能影响的时变研究[J]. 硅酸盐通报, 2025, 44(1): 133-141.

ZHANG Wenjing, ZHANG Rongling, ZHANG Yan, WANG Yulin, ZHANG Fukui, WANG Xianlong, AN Kangle. Time-Varying Study on Effect of Coarse Aggregate on Concrete Performance under Environmental Action[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2025, 44(1): 133-141.

参考文献

[1] YANG D Q, YAN C W, LIU S G, et al. Stress-strain constitutive model of concrete corroded by saline soil under uniaxial compression[J]. Construction and Building Materials, 2019, 213: 665-674.
[2] WANG B X, PAN J J, FANG R C, et al. Damage model of concrete subjected to coupling chemical attacks and freeze-thaw cycles in saline soil area[J]. Construction and Building Materials, 2020, 242: 118205.
[3] PASUPATHY K, SINGH CHEEMA D, SANJAYAN J. Durability performance of fly ash-based geopolymer concrete buried in saline environment for 10 years[J]. Construction and Building Materials, 2021, 281: 122596.
[4] ZHANG R L, MA L N, LIU P, et al. Influence mechanisms under different immersion methods and different strengths of concrete in corrosive environments, and verification via long-term field test[J]. Structural Concrete, 2020, 21(5): 1853-1864.
[5] 汪振双. 架构混凝土基础理论研究[D]. 大连: 大连理工大学, 2012.
WANG Z S. Study on basic theory of frame concrete[D]. Dalian: Dalian University of Technology, 2012 (in Chinese).
[6] MEHTA P K,MONTEIRO P J M. Concrete: microstructure, properties, and materials[M]. New York: McGraw-Hill Professional, 2014.
[7] 楚英杰, 王爱国, 孙道胜, 等. 骨料特性影响混凝土体积稳定性的研究进展[J]. 材料导报, 2022, 36(5): 112-121.
CHU Y J, WANG A G, SUN D S, et al. Research progress on the influence of aggregate characteristics on the volume stability of concrete[J]. Materials Reports, 2022, 36(5): 112-121 (in Chinese).
[8] BEUSHAUSEN H, DITTMER T. The influence of aggregate type on the strength and elastic modulus of high strength concrete[J]. Construction and Building Materials, 2015, 74: 132-139.
[9] LIU H Q, BAI G L, GU Y, et al. The influence of coal gangue coarse aggregate on the mechanical properties of concrete columns[J]. Case Studies in Construction Materials, 2022, 17: e01315.
[10] OLAWUYI O A, KAREEM M, ISHOLA K, et al. Mechanical properties of concrete incorporating waste glass as replacement for fine and coarse aggregate[J]. International Journal of Engineering Research in Africa, 2022, 59: 19-28.
[11] ZHOU X, XIE Y J, LONG G C, et al. Effect of surface characteristics of aggregates on the compressive damage of high-strength concrete based on 3D discrete element method[J]. Construction and Building Materials, 2021, 301: 124101.
[12] 王云枫. 粗骨料与水泥砂浆协同作用影响混凝土性能试验研究[D]. 大连: 大连交通大学, 2020.
WANG Y F. The synergistic effect of coarse aggregate and cement mortar on concrete performance was studied[D]. Dalian: Dalian Jiaotong University, 2020 (in Chinese).
[13] 卢京宇. 不同岩性粗骨料对大流态混凝土性能的影响及机理分析[D]. 北京: 北京建筑大学, 2021.
LU J Y. Influence and mechanism analysis of different lithological coarse aggregate on performance of high-fluidity concrete[D]. Beijing: Beijing University of Civil Engineering and Architecture, 2021 (in Chinese).
[14] 许鸽龙. 骨料嵌锁型混凝土特性及其形成机理研究[D]. 武汉: 武汉理工大学, 2020.
XU G L. Properties of aggregate interlocking concrete and its formation mechanism[D]. Wuhan: Wuhan University of Technology, 2020 (in Chinese).
[15] XU L H, WU F H, CHI Y, et al. Effects of coarse aggregate and steel fibre contents on mechanical properties of high performance concrete[J]. Construction and Building Materials, 2019, 206: 97-110.
[16] 赵明, 张雄, 张晓乐, 等. 颗粒整形后粗骨料特征及其对混凝土性能的影响[J]. 同济大学学报(自然科学版), 2016, 44(3): 395-401.
ZHAO M, ZHANG X, ZHANG X L, et al. Research on the characteristic of coarse aggregate after particle shaping and the influence on the concrete performance[J]. Journal of Tongji University (Natural Science), 2016, 44(3): 395-401 (in Chinese).
[17] 王东来. 后掺骨料混凝土力学性能和抗冻性能试验研究[D]. 大连: 大连理工大学, 2017.
WANG D L. Experimental study on mechanical properties and frost resistance of high performance pumping concrete with after-mixing coarse aggregate[D]. Dalian: Dalian University of Technology, 2017 (in Chinese).
[18] 张文静, 李波, 张戎令, 等. 基于NMR技术的自然腐蚀环境下混凝土强度劣化分析[J]. 混凝土与水泥制品, 2023(12): 17-22.
ZHANG W J, LI B, ZHANG R L, et al. Analysis of concrete strength deterioration in freeze-thaw corrosion environment based on NMR technology[J]. China Concrete and Cement Products, 2023(12): 17-22 (in Chinese).
[19] 肖鹏震, 张戎令, 胡锐鹏, 等. 混凝土抗硫酸盐侵蚀性能及其离子扩散影响因素研究[J]. 中国材料进展, 2021, 40(5): 359-365.
XIAO P Z, ZHANG R L, HU R P, et al. Study on the sulfate resistance of concrete and the influencing factors of ion diffusion[J]. Materials China, 2021, 40(5): 359-365 (in Chinese).
[20] 吴中伟, 廉慧珍. 高性能混凝土[M]. 北京: 中国铁道出版社, 1999.
WU Z W, LIAN H Z. High performance concrete[M]. Beijing: China Railway Publishing House, 1999 (in Chinese).
[21] 蒋科, 郭辉, 李洋, 等. 氯盐环境下混凝土冻融循环及孔结构演化研究[J]. 人民长江, 2021, 52(12): 162-167.
JIANG K, GUO H, LI Y, et al. Research on concrete damage and pore structure evolution under freeze-thaw cycles in chloride solution[J]. Yangtze River, 2021, 52(12): 162-167 (in Chinese).
[22] 张雪勤, 徐锋. 基于灰色系统理论的矿渣混凝土氯离子扩散性能与孔结构研究[J]. 科技创新导报, 2020, 17(20): 61-64.
ZHANG X Q, XU F. Study on chloride diffusion performance and pore structure of slag concrete based on grey system theory[J]. Science and Technology Innovation Herald, 2020, 17(20): 61-64 (in Chinese).
[23] 田威, 李小山, 王峰. 冻融循环与硫酸盐溶液耦合作用下混凝土劣化机理试验研究[J]. 硅酸盐通报, 2019, 38(3): 702-710.
TIAN W, LI X S, WANG F. Experimental study on deterioration mechanism of concrete under freeze-thaw cycles coupled with sulfate solution[J]. Bulletin of the Chinese Ceramic Society, 2019, 38(3): 702-710 (in Chinese).
[24] 张瑞稳, 王起才, 张戎令, 等. -3 ℃养护下引气混凝土孔结构与抗渗性研究[J]. 铁道科学与工程学报, 2018, 15(5): 1147-1154.
ZHANG R W, WANG Q C, ZHANG R L, et al. Research of air-entraining concrete for pore structure characteristics and permeability under -3 ℃ curing condition[J]. Journal of Railway Science and Engineering, 2018, 15(5): 1147-1154 (in Chinese).
[25] ZHANG B, LI Q B, MA R, et al. An experimental investigation on the impermeability and durability of concrete with a novel and multifunctional hydrophobic admixture addition[J]. Structural Concrete, 2022, 23(2): 836-848.
[26] 李鹤斌. 基于核磁共振的负温混凝土早期水化及含冰率研究[D]. 哈尔滨: 哈尔滨工业大学, 2020.
LI H B. Study on early hydration and ice content of negative temperature concrete based on nuclear magnetic resonance technology[D]. Harbin: Harbin Institute of Technology, 2020 (in Chinese).

环境作用下粗骨料对混凝土性能影响的时变研究

Time-Varying Study on Effect of Coarse Aggregate on Concrete Performance under Environmental Action

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	冉秋硕, 徐泽辉, 齐文超, 刘磊. 高温后钢-玄武岩混杂纤维混凝土动态力学性能研究[J]. 硅酸盐通报, 2025, 44(1): 69-80.
[2]	陆俊辉, 吕海, 李钧源, 杨海峰, 曹化一. 方铝合金管-海水海砂地聚物混凝土的界面黏结滑移性能[J]. 硅酸盐通报, 2025, 44(1): 90-100.
[3]	赵燕茹, 李环, 李玉萍, 贾宗明, 石磊. 高温后钢筋与纳米TiO₂混凝土粘结性能演化规律研究[J]. 硅酸盐通报, 2025, 44(1): 101-111.
[4]	代薇, 杨淘, 孙彦梅, 张芮瑜, 秦小枫, 蔡君怡, 李阳. 不同气压环境下水工混凝土含气量发展规律研究[J]. 硅酸盐通报, 2025, 44(1): 112-123.
[5]	耿春雷, 郭宏达, 董阳, 张栋, 巩思宇, 李俏. 陶粒泡沫混凝土成型方式及性能研究[J]. 硅酸盐通报, 2025, 44(1): 124-132.
[6]	马金良, 胡娟, 汪伟, 鞠志成, 杨海成, 范志宏. 辐照-干湿-氯盐耦合作用下硅烷浸渍混凝土性能演变规律[J]. 硅酸盐通报, 2025, 44(1): 142-150.
[7]	李汉军, 苏浩然, 于昊男, 赵京, 张久鹏, 胡哲. 橡胶混凝土耐久性能研究进展[J]. 硅酸盐通报, 2025, 44(1): 180-194.
[8]	纪璐鑫, 马红瑞, 马哲洋, 王胜, 崔嘉铭, 巴明芳. 二次铝灰烧结渣料对高强混凝土力学性能和收缩性能的影响[J]. 硅酸盐通报, 2025, 44(1): 212-222.
[9]	罗国仪, 徐桂弘, 任旭, 邓文波, 陈孜伟, 刘次啟. 磷石膏对玄武岩纤维混凝土碳化及抗渗性能的影响[J]. 硅酸盐通报, 2025, 44(1): 231-242.
[10]	余芳, 李林柏, 姚大立. 钢纤维自密实再生混凝土的力学性能[J]. 硅酸盐通报, 2025, 44(1): 264-273.
[11]	朱元浪, 张明亮, 魏京华, 张恒武, 刘子盼, 高嵩. 实海暴露环境再生混凝土三维逾渗特性研究[J]. 硅酸盐通报, 2025, 44(1): 274-288.
[12]	吴晓刚, 杨健辉, 袁冬冬, 田道坡, 李志超, 王庭辉. 骨料种类对超高性能混凝土性能影响机理研究[J]. 硅酸盐通报, 2024, 43(9): 3164-3172.
[13]	赵燕茹, 龙思睿, 白建文, 刘明. 高温后风积沙混凝土力学性能与微观结构试验研究[J]. 硅酸盐通报, 2024, 43(9): 3182-3191.
[14]	张震洋, 张璐, 伊海赫, 郑润, 马克顺, 张琳, 任梦琪, 王春光. 基于响应面法的地聚物混凝土力学性能试验研究[J]. 硅酸盐通报, 2024, 43(9): 3192-3202.
[15]	王萧萧, 董培森, 杨鑫瑞, 张菊, 闫长旺, 董宇飞. 低温作用下钢纤维地聚合物混凝土力学性能研究[J]. 硅酸盐通报, 2024, 43(9): 3203-3213.