Experimental Study on Sound Barrier Performance of Fly Ash Ceramsite Lightweight Concrete

Abstract

Abstract: Concrete is a widely used building material that can be prepared using a variety of solid waste. In this study, fly ash ceramsite was used as lightweight aggregate, and cement-fly ash-silica fume-coal metakaolin was used as composite cementitious material to prepare fly ash ceramsite lightweight concrete for sound barrier. The mechanical properties, sound absorption performance and carbonation resistance of fly ash ceramsite lightweight concrete were studied. The results show that when the total content of fly ash-silica fume-coal metakaolin is 10% of total mass of cementitious materials, the mechanical properties and carbonation resistance of samples are improved, and the sound absorption performance is reduced. With the further increase of fly ash-silica fume-coal metakaolin content, the mechanical properties and carbonation resistance of samples decrease, and sound absorption performance increases. The sound absorption coefficient changes little at 1 500 Hz and below, and the sound absorption effect is the best at 2 000 Hz. The average sound absorption coefficient of sample is 0.44~0.58, and the noise reduction coefficient is 0.74~0.89.

Key words: fly ash ceramsite, lightweight concrete, mechanical property, sound absorption coefficient, noise reduction coefficient, carbonation resistance

CLC Number:

TU55⁺2

GENG Limin, DU Hongxiu, NIE Xiaoqing, ZHOU Xingyu, YAN Changhao, LEI Yibin. Experimental Study on Sound Barrier Performance of Fly Ash Ceramsite Lightweight Concrete[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2024, 43(5): 1897-1905.

References

[1] 陈兴, 张毅超, 陈迎庆, 等. 我国高速铁路声屏障气动效应研究与探索[J]. 中国铁道科学, 2023, 44(4): 84-91.
CHEN X, ZHANG Y C, CHEN Y Q, et al. Research and exploration of aerodynamic effect of high-speed railway sound barrier in China[J]. China Railway Science, 2023, 44(4): 84-91 (in Chinese).
[2] 薛正, 茹旭, 李绍富, 等. 既有铁路桥梁增设声屏障方法研究[J]. 铁路工程技术与经济, 2023, 38(3): 9-13+36.
XUE Z, RU X, LI S F, et al. Study on adding noise barrier to existing railway bridges[J]. Railway Engineering Technology and Economy, 2023, 38(3): 9-13+36 (in Chinese).
[3] 郝龙, 林倩, 宋迎前, 等. 高速公路声屏障降噪有限元仿真研究[J]. 现代交通与冶金材料, 2023, 3(1): 89-93.
HAO L, LIN Q, SONG Y Q, et al. Study on noise reduction of sound barrier of expressway based on finite element simulation[J]. Modern Transportation and Metallurgical Materials, 2023, 3(1): 89-93 (in Chinese).
[4] 王艳雯. 声屏障技术在交通噪声治理中的应用[J]. 上海船舶运输科学研究所学报, 2022, 45(4): 75-78.
WANG Y W. Application of noise barrier technology in traffic noise control[J]. Journal of Shanghai Ship and Shipping Research Institute, 2022, 45(4): 75-78 (in Chinese).
[5] 晏方, 陈宇良, 陈宗平, 等. 粉煤灰陶粒轻骨料混凝土循环受压力学性能试验研究[J]. 硅酸盐通报, 2020, 39(8): 2615-2621.
YAN F, CHEN Y L, CHEN Z P, et al. Cyclic compressive mechanical performance of fly ash ceramsite lightweight aggregate concrete[J]. Bulletin of the Chinese Ceramic Society, 2020, 39(8): 2615-2621 (in Chinese).
[6] 刘柳. 粉煤灰陶粒混凝土早龄期基本力学性能研究[J]. 四川水泥, 2016(5): 302+285.
LIU L. Study on basic mechanical properties of fly ash aggregate concrete in early age[J]. Sichuan Cement, 2016(5): 302+285 (in Chinese).
[7] 李瑞. 粉煤灰陶粒轻骨料混凝土性能试验研究[D]. 银川: 宁夏大学, 2015.
LI R. Experimental study on properties of fly ash ceramsite lightweight aggregate concrete[D]. Yinchuan: Ningxia University, 2015 (in Chinese).
[8] 史永建, 白会人, 李金奎. 粉煤灰陶粒混凝土抗冻性能研究[J]. 混凝土, 2016(11): 86-89.
SHI Y J, BAI H R, LI J K. Lytag concrete antifreeze performance study[J]. Concrete, 2016(11): 86-89 (in Chinese).
[9] 柴春镜, 宋慧平, 冯政君, 等. 粉煤灰陶粒的研究进展[J]. 洁净煤技术, 2020, 26(6): 11-22.
CHAI C J, SONG H P, FENG Z J, et al. Research progress on the fly ash ceramsite[J]. Clean Coal Technology, 2020, 26(6): 11-22 (in Chinese).
[10] 武京. 纳米SiO₂改性粉煤灰陶粒混凝土力学性能和耐久性能的研究[D]. 长春: 吉林大学, 2019.
WU J. Study on mechanical properties and durability of nano-SiO₂ modified fly ash ceramsite concrete[D]. Changchun: Jilin University, 2019 (in Chinese).
[11] 陈新. 掺粉煤灰陶粒混凝土路面耐久性研究[D]. 重庆: 重庆交通大学, 2017.
CHEN X. Study on durability of ceramsite concrete pavement mixed with fly ash[D].Chongqing: Chongqing Jiaotong University, 2017 (in Chinese).
[12] DUAN C Y, CUI G, XU X B, et al. Sound absorption characteristics of a high-temperature sintering porous ceramic material[J]. Applied Acoustics, 2012, 73(9): 865-871.
[13] 汪洋, 朱万旭, 邵炼, 等. 城市地铁轨道吸声板性能分析[J]. 施工技术, 2014, 43(10): 102-105.
WANG Y, ZHU W X, SHAO L, et al. Performance analysis of city subway rail acoustic panels[J]. Construction Technology, 2014, 43(10): 102-105 (in Chinese).
[14] 淳野杨. 粉煤灰免烧结多孔陶粒的制备和吸声性能研究[D]. 柳州: 广西科技大学, 2018.
CHUN Y Y. Sintering-free preparation of porous ceramsite of fly ash using temperature decomposing pore former and its sound-absorbing performance[D]. Liuzhou: Guangxi University of Science and Technology, 2018 (in Chinese).
[15] 于萍, 赵晶. 粉煤灰陶粒混凝土的耐久性分析[J]. 低温建筑技术, 2009, 31(8): 1-3.
YU P, ZHAO J. Durability analysis of sintered fly ash concrete[J]. Low Temperature Architecture Technology, 2009, 31(8): 1-3 (in Chinese).
[16] 张冰. 粉煤灰陶粒混凝土基本性能及相关耐久性能研究[D]. 包头: 内蒙古科技大学, 2012.
ZHANG B. Study on basic properties and related durability of fly ash ceramsite concrete[D]. Baotou: Inner Mongolia University of Science & Technology, 2012 (in Chinese).