Effect of Filtrate Circulation on Preparation of Desulfurization Gypsum Whiskers in H2SO4-NaCl-H2O System

Abstract

Abstract: The pretreated desulfurization gypsum was used as raw material,the sulfuric acid was used to adjust the pH value of the reaction solution, and the desulfurization gypsum whiskers were prepared by hydrothermal method to realize green production. Through the recycling of filtrate with or without reagent compensation, the effect of cycle number of filtrate on the quality of whiskers, pH value of solution and concentration of Na⁺ was studied. The results show that, with the increase of cycle number of filtrate, the pH value of filtrate gradually increases, but the concentration of Na⁺ decreases and its loss is from 27.3% to 34.6% in the condition of no reagent compensation. When H₂SO₄ and NaCl are used to compensate the reaction solution, the effect of cycle number of filtrate on the concentration of Ca²⁺ is slight before and after reaction. However, the cycle number of filtrate has an obviously effect on the crystal morphology, aspect ratio and quality of whiskers. When the cycle number of filtrate is less than 5, the quality of prepared whiskers is relatively good.

Key words: desulfurization gypsum, whisker, filtrate circulation, reagent compensation, hydrothermal method, green production

CLC Number:

TQ132.32

LIU Qiang, WANG Xiao, JIN Biao, LIN Xingtong, ZHANG Jianwu, WANG Yubin. Effect of Filtrate Circulation on Preparation of Desulfurization Gypsum Whiskers in H₂SO₄-NaCl-H₂O System[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(9): 3202-3207.

References

[1] 史培阳,邓志银,袁义义,等.利用脱硫石膏水热合成硫酸钙晶须[J].东北大学学报(自然科学版),2010,31(1):76-79.
SHI P Y, DENG Z Y, YUAN Y Y, et al. Preparation of calcium sulfate whiskers from desulphurized gypsum by hydrothermal synthesis[J]. Journal of Northeastern University (Natural Science), 2010, 31(1): 76-79 (in Chinese).
[2] 吴晓琴,裘建军.常压盐溶液法从烟气脱硫石膏制备硫酸钙晶须研究[J].武汉科技大学学报,2011,34(2):104-110.
WU X Q, QIU J J. Preparation of calcium sulfate whiskers from flue gas desulfurization gypsum in salt solution at atmospheric pressure[J]. Journal of Wuhan University of Science and Technology, 2011, 34(2): 104-110 (in Chinese).
[3] LUO K B, LI C M, XIANG L, et al. Influence of temperature and solution composition on the formation of calcium sulfates[J]. Particuology, 2010, 8(3): 240-244.
[4] 王宇斌.硫酸钙晶须晶型稳定化研究[D].沈阳:东北大学,2008.
WANG Y B. Study on the stabilization of crystalline phase of calcium sulfate whiskers[D]. Shenyang: Northeastern University, 2008 (in Chinese).
[5] 何花,董发勤,何平.混合助晶剂促进大长径比硫酸钙晶须的调控研究[J].人工晶体学报,2012,41(6):1679-1685.
HE H, DONG F Q, HE P. Regulation preparation of large aspect ratio calcium sulfate whisker in the presence of mixed crystallization promoting agents[J]. Journal of Synthetic Crystals, 2012, 41(6): 1679-1685 (in Chinese).
[6] HAMDONA S K, AL HADAD O A. Influence of additives on the precipitation of gypsum in sodium chloride solutions[J]. Desalination, 2008, 228(1/2/3): 277-286.
[7] HAMDONA S K, AL HADAD U A. Crystallization of calcium sulfate dihydrate in the presence of some metal ions[J]. Journal of Crystal Growth, 2007, 299(1): 146-151.
[8] SARGUT S T, SAYAN P, KIRAN B. Gypsum crystallization in the presence of Cr³⁺ and citric acid[J]. Chemical Engineering & Technology, 2010, 33(5): 804-811.
[9] GUAN B H, YANG L C, WU Z B. Effect of Mg²⁺ ions on the nucleation kinetics of calcium sulfate in concentrated calcium chloride solutions[J]. Industrial & Engineering Chemistry Research, 2010, 49(12): 5569-5574.
[10] WANG X, YANG L S, ZHU X F, et al. Preparation of calcium sulfate whiskers from FGD gypsum via hydrothermal crystallization in the H₂SO₄-NaCl-H₂O system[J]. Particuology, 2014, 17: 42-48.
[11] 汪潇,金彪,王宇斌,等.阴离子在脱硫石膏晶须水热结晶中的作用机理[J].高等学校化学学报,2020,41(3):473-480.
WANG X, JIN B, WANG Y B, et al. Interaction mechanism of anions in hydrothermal crystallization of desulfurization gypsum whiskers[J]. Chemical Journal of Chinese Universities, 2020, 41(3): 473-480 (in Chinese).
[12] 彭家惠,张建新,瞿金东,等.有机酸对α半水脱硫石膏晶体生长习性的影响与调晶机理[J].硅酸盐学报,2011,39(10):1711-1718.
PENG J H, ZHANG J X, QU J D, et al. Effect of organic acid on crystalline habit of α-hemihydrate desulfurization gypsum and its crystal modification mechanism[J]. Journal of the Chinese Ceramic Society, 2011, 39(10): 1711-1718 (in Chinese).
[13] 彭家惠,瞿金东,张建新,等.EDTA吸附特性及其对α半水脱硫石膏晶形的影响[J].材料研究学报,2011,25(6):566-572.
PENG J H, QU J D, ZHANG J X, et al. Adsorption characteristics of EDTA on α-hemihydrate desulfurization gypsum surface and its influence on crystal morphology[J]. Chinese Journal of Materials Research, 2011, 25(6): 566-572 (in Chinese).
[14] CHAROLA A E, PÜHRINGER J, STEIGER M. Gypsum: a review of its role in the deterioration of building materials[J]. Environmental Geology, 2007, 52(2): 339-352.
[15] 汪潇,杨留栓,朱新峰,等.湿法脱硫石膏颗粒特性与杂质赋存状况分析[J].环境科学与技术,2013,36(9):135-138.
WANG X, YANG L S, ZHU X F, et al. Analysis of particle characteristics and existing formation of the impurities in wet FGD gypsum[J]. Environmental Science & Technology, 2013, 36(9): 135-138 (in Chinese).
[16] 汪潇,杨留栓,王宇斌,等.脱硫石膏的提纯工艺及其提纯出的石膏原料:CN102616825A[P].2012-08-01.
WANG X, YANG L S, WANG Y B, et al. Purification process of desulfurized gypsum and its purified gypsum raw materials: CN102616825A[P]. 2012-08-01 (in Chinese).
[17] YANG L S, WANG X, ZHU X F, et al. Preparation of calcium sulfate whisker by hydrothermal method from flue gas desulfurization (FGD) gypsum[J]. Applied Mechanics and Materials, 2012, 268/269/270: 823-826.
[18] 汪潇.脱硫石膏制备硫酸钙晶须媒晶剂的筛选及作用机理研究[D].武汉:华中科技大学,2014.
WANG X. Selection of the crystal modifier in the preparation of calcium sulfate whisker from the FGD gypsum and its mechanism[D]. Wuhan: Huazhong University of Science and Technology, 2014 (in Chinese).
[19] HOU S C, WANG J, WANG X X, et al. Effect of Mg²⁺ on hydrothermal formation of α-CaSO₄·0.5H₂O whiskers with high aspect ratios[J]. Langmuir: the ACS Journal of Surfaces and Colloids, 2014, 30(32): 9804-9810.
[20] 汪潇,金彪,张小婷,等.氯盐体系下阳离子对脱硫石膏晶须水热结晶的影响及其机理[J].化工进展,2022,41(7):3957-3965.
WANG X, JIN B, ZHANG X T, et al. Effect of cation on hydrothermal crystallization of desulfurized gypsum whiskers in chloride system and its mechanism[J]. Chemical Industry and Engineering Progress, 2022, 41(7): 3957-3965 (in Chinese).

Effect of Filtrate Circulation on Preparation of Desulfurization Gypsum Whiskers in H₂SO₄-NaCl-H₂O System

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	HUANG Jia, JIN Yingrong, YANG Hualin, CHEN Wei, LI Yuling, WANG Zhijie. Whiskers Growth and Mechanism Analysis by Titanium Gypsum under Alkaline Conditions [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(8): 2828-2835.
[2]	ZHANG Yubin, BAO Shihui, ZHANG Cong. Flexural Properties of Hybrid Fiber-Reinforced Ultra-High Performance Pervious Concrete [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(6): 1955-1962.
[3]	CAO Yongdan, ZHAO Tianyue, CAO Zhao, ZHANG Jinshan, DONG Hongjuan. Preparation of Calcium Sulfate Whiskers from Desulfurized Gypsum [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(5): 1765-1773.
[4]	ZHU Siyu, LI Li, LIU Ze, ZHANG Tong, HAN Fenglan, MA Zhenfei, LIU Jiayu. Hydrothermal Synthesis and Characterization of Zeolite NaA Based on Combination of Silico-Manganese Slag and Fly Ash [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(2): 634-639.
[5]	WANG Bo, DUAN Xiaobo, DENG Lirong, WANG Jiabo, LU Shuhe, WANG Xiaogang. Subcritical Hydrothermal Removal of Common Metal Impurity in β-SiC Powder [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(8): 2713-2718.
[6]	HU Qiguo, LIU Ying, SHAO Qing, LI Ji. Properties of Mullite Whisker Precursor In-Situ Reinforced Urchin-Like Mullite Materials [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(5): 1679-1684.
[7]	LU Pengfei, XU Guangwen, CUI Yanbin, WU Rongcheng. Preparation of Silicon Carbide Whiskers from Tire Semicoke [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(3): 951-956.
[8]	WANG Bo, DUAN Xiaobo, DENG Lirong, LU Shuhe, WANG Xiaogang, BAI Xiao. Subcritical Hydrothermal Removal of Si Impurity in β-SiC Powder [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(2): 591-596.
[9]	CHEN Haijun, XU Enxia, LI Miao, GAO Jinxing, GE Tiezhu. Effect of Heat Treatment Temperature on Properties of ZrO₂ Fiber Composite ZrO₂-C Material [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(10): 3219-3225.
[10]	SHANG Jiaqi, LIU Hao, WANG Zhoufu, YANG Zhiqian, CHEN Senna, MA Yan, WANG Xitang. Preparation and Properties of Aluminum Borate-Potassium Hexatitanate Whisker Composite Thermal Insulation Materials [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(10): 3273-3278.
[11]	WANG Wenkai, TAN Juan, WANG Shihan, QIU Xin. Synthesis and Catalytic Cracking Performance of Small-Sized NaY Zeolite/Kaolin Composites with High Framework SiO₂/Al₂O₃ Ratio [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(10): 3479-3489.
[12]	YAN Kechong, LI Zipeng, LI Yangmin, WANG Pingzhi. Adsorption of Mercury in Aqueous Solution by Zeolite Prepared from Coal Fly Ash Using Alkali Fusion-Hydrothermal Method [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2020, 39(12): 3939-3944.
[13]	GAO Lin-xiao;GUO Meng;ZHEN De-shuai;LI Chang-an. Progress on Preparation of Calcium Carbonate using Phosphogypsum [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2018, 37(5): 1643-1648.
[14]	XIA Dong-lin;YAN Xin-zheng;QIN Ke;LI Yun-feng. Hydrothermal Growth and Characterization of ZnO Nanorods [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2018, 37(4): 1132-1138.
[15]	XU Wen;WU Xiao-lei. Influence Research of the Calcium Silicon Ratio on the Synthetizing Hydrated Calcium Silicate [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2018, 37(4): 1294-1298.