Effects of Ultrafine and Highly Active Mineral Admixtures on Hydration and Shrinkage Properties of UHPC

Abstract

Abstract: Ultra-high performance concrete (UHPC) was prepared by ultrafine and highly active mineral admixtures (ultrafine admixtures) and silica fume in single or compound admixture. The effects of ultrafine admixtures with different dosage on the workability, mechanical properties, hydration heat and shrinkage properties of UHPC were analyzed. The results show that the fluidity of UHPC increases with the increase of the ultrafine admixtures, and the highest fluidity of jumping table is 275 mm. When UHPC is prepared by mixing the ultrafine admixtures with 10% (mass fraction) silica fume, the flexural strength increases first and then decreases with the increase of ultrafine admixture, while the compressive strength increases first and then keeps steady. The maximum flexural strength and compressive strength are 25.9 MPa and 150.0 MPa, repectively. The hydration heat of UHPC cementitious material prepared by compounding ultrafine admixture and10% (mass fraction) silica fume increases at first and then decreases with the increase of ultrafine admixture. The early shrinkage of UHPC prepared by compounding the ultrafine admixture and silica fume with a mass fraction of 10%, is the smallest, which is 50.92% lower than that of UHPC prepared by silica fume with a mass fraction of 20% alone.

Key words: ultrafine admixture, UHPC, hydration heat, shrinkage, fluidity, mechanical property

CLC Number:

TU528

WEI Yu, CHEN Ping, MING Yang, LUO Junhui, ZHANG Gefen, WU Yong. Effects of Ultrafine and Highly Active Mineral Admixtures on Hydration and Shrinkage Properties of UHPC[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(2): 461-468.

References

[1] 龚建清,罗鸿魁,张阳,等.减缩剂和HCSA膨胀剂对UHPC力学性能和收缩性能的影响[J].材料导报,2021,35(8):8042-8048+8063.
GONG J Q, LUO H K, ZHANG Y, et al. Effect of shrinkage reducing agent and HCSA expansion agent on mechanical properties and shrinkage properties of UHPC[J]. Materials Reports, 2021, 35(8): 8042-8048+8063 (in Chinese).
[2] 祖庆贺,臧军,沈晓冬.粗粒度区间钢渣微粉在UHPC中的应用研究[J].混凝土与水泥制品,2019(8):1-4.
ZU Q H, ZANG J, SHEN X D. Application study of steel slag fine powders with coarse particle sizes rang in ultra high performance concrete(UHPC)[J]. China Concrete and Cement Products, 2019(8): 1-4 (in Chinese).
[3] LARRARD F D, SEDRAN T. Optimization of ultra-high-performance concrete by the use of a packing model[J]. Cement and Concrete Research, 1994, 24(6): 997-1009.
[4] 冀伟.水泥水化热试验研究分析[J].公路交通技术,2016,32(1):13-16.
JI W. Experimental research and analysis of hydration heat of cement[J]. Technology of Highway and Transport, 2016, 32(1): 13-16 (in Chinese).
[5] 陈炜一,周予启,李嵩,等.水化热抑制剂对水泥-粉煤灰胶凝材料水化和混凝土性能的影响[J].硅酸盐学报,2021,49(8):1609-1618.
CHEN W Y, ZHOU Y Q, LI S, et al. Impact of temperature rising inhibitor on hydration of cement-fly ash cementitious materials and performance of concrete[J]. Journal of the Chinese Ceramic Society, 2021, 49(8): 1609-1618 (in Chinese).
[6] 刘子科,胡建伟,翁智财,等.蒸汽养护对水泥基材料性能影响的研究进展[J].混凝土,2020(4):9-13.
LIU Z K, HU J W, WENG Z C, et al. Research progress on the effect of steam curing on the performance of cementitious materials[J]. Concrete, 2020(4): 9-13 (in Chinese).
[7] 段思宇.钢渣-粉煤灰-脱硫石膏复合胶凝体系的反应机制及应用研究[D].太原:山西大学,2020.
DUAN S Y. Reaction mechanisms and application study of steel slag-fly ash-desulfurized gypsum composite cementitious system[D]. Taiyuan: Shanxi University, 2020 (in Chinese).
[8] 杨霆,何曦.高炉矿渣资源化利用的研究现状及展望[J].中国环保产业,2020(3):65-68.
YANG T, HE X. Research status and prospect of blast furnace slag resource recycling[J]. China Environmental Protection Industry, 2020(3): 65-68 (in Chinese).
[9] 刘天成,杨华明.超细钢渣及高性能混凝土掺合料的最新进展[J].金属矿山,2006(9):8-13.
LIU T C, YANG H M. Ultrafine steel slag and latest advance in blending materials of high performance concrete[J]. Metal Mine, 2006(9): 8-13 (in Chinese).
[10] 段思宇,李溪,马卓慧,等.粉磨方式对钢渣微粉特性的影响[J].粉末冶金材料科学与工程,2020,25(1):51-57.
DUAN S Y, LI X, MA Z H, et al. Effect of grinding method on properties of steel slag powder[J]. Materials Science and Engineering of Powder Metallurgy, 2020, 25(1): 51-57 (in Chinese).
[11] 王会刚,彭犇,岳昌盛,等.钢渣改性研究进展及展望[J].环境工程,2020,38(5):133-137+106.
WANG H G, PENG B, YUE C S, et al. Research progress and prospect of steel slag modification[J]. Environmental Engineering, 2020, 38(5): 133-137+106 (in Chinese).
[12] 王喆,王强,杨建伟,等.钢渣-磨细粉煤灰复合矿物掺合料对混凝土性能的影响[J].混凝土,2015(5):79-82.
WANG Z, WANG Q, YANG J W, et al. Influence of steel slag-superfine fly ash composite mineral admixture on the properties of concrete[J]. Concrete, 2015(5): 79-82 (in Chinese).
[13] 尹韶宁,吴小缓,袁鹏,等.粉煤灰-矿粉复合超细粉制备及其在水泥中的应用试验研究[J].水泥,2020(6):1-4.
YIN S N, WU X H,YUAN P, et al. Study on preparation of fly ash-slag powder composite ultrafine powder and its application in cement[J]. Cement, 2020(6): 1-4 (in Chinese).
[14] 佘亮,温煦,汤畅,等.钢渣-矿粉复合掺和料制备及其对混凝土的性能影响[J].绿色环保建材,2019(6):7-8+12.
SHE L, WEN X, TANG C, et al. Preparation of steel slag-ore powder composite admixture and its effect on concrete performance [J]. Green Environmental Protection Building Materials, 2019(6): 7-8+12 (in Chinese).
[15] 廖伟华,陈金义.西北大跨连续刚构施工期腹板开裂成因分析[J].公路,2020,65(11):183-188.
LIAO W H, CHEN J Y. Cause analysis of web cracking of northwest long-span continuous rigid frame during construction [J]. Highway, 2020, 65(11): 183-188 (in Chinese).
[16] 杨如东,权娟娟,陈健.水泥水化热与混凝土绝热温升研究综述[J].科学技术创新,2020(4):100-101.
YANG R D, QUAN J J, CHEN J. Research review on heat of cement hydration and adiabatic temperature rise of concrete [J]. Scientific and Technological Innovation, 2020(4): 100-101 (in Chinese).
[17] 任旭,张秀贞,刘志超,等.多元胶凝材料水化热动力学研究[J].混凝土与水泥制品,2021(6):13-18.
REN X, ZHANG X Z, LIU Z C, et al. Study on hydration thermodynamics and kinetics of multiple cementitious materials[J]. China Concrete and Cement Products, 2021(6): 13-18 (in Chinese).
[18] 李瑶,刘润清,齐雯涵,等.硅灰粒径分布对混凝土微观结构及其低温抗压强度的影响[J].中国粉体技术,2019,25(6):75-80.
LI Y, LIU R Q, QI W H, et al. Effects of particle size distribution of silica fume on pore structure and compressive strength of concrete at low temperature[J]. China Powder Science and Technology, 2019, 25(6): 75-80 (in Chinese).
[19] 陈新星,韩明珍,吴昊,等.掺钢渣-矿渣-粉煤灰复合微粉混凝土高温后抗压强度数学分析[J].硅酸盐通报,2015,34(8):2254-2259.
CHEN X X, HAN M Z, WU H, et al. Mathematical analysis on the compressive strength of high temperature micro powder concrete added with stell slag, slag and fly ash[J]. Bulletin of the Chinese Ceramic Society, 2015, 34(8): 2254-2259 (in Chinese).
[20] 王琼,严捍东.建筑垃圾再生骨料透水性混凝土试验研究[J].合肥工业大学学报(自然科学版),2004,27(6):682-686.
WANG Q, YAN H D. Experiment on the water-permeable concrete with construction waste as recycled aggregate[J]. Journal of Hefei University of Technology (Natural Science), 2004, 27(6): 682-686 (in Chinese).