Preparation and Properties of Gradient Porous Ag LoadedHydroxyapatite Ceramics

Abstract

Abstract: Gradient porous Ag loaded hydroxyapatite (Ag-HA) ceramic was prepared by adding pore-forming agent method.The effects of pore-forming agent distribution,sintering temperature on the porosity were studied.The phase composition and microstructure of the sintered products were analyzed,the compression and antibacterial properties of sintered gradient porous (Ag-HA) ceramics were measured.The experimental results show that the porosity of gradient porous Ag-HA ceramics increases with the increase of the contents of interlayer pore-forming agent,but the compressive strength decreases.With the increase of sintering temperature,the porosity of gradient porous Ag-HA ceramics decreases,but the compressive strength increases.When the distribution of pore-forming agent of is 20%-10%-20% (mass fraction),the pressing pressure is 100 MPa,the sintering temperature is 1 150 ℃ and Ag content is 2% (mole fraction),the porosity and compressive strength of the sintered gradient porous 2.0Ag-HA ceramics are 24.7% and 12.6 MPa,respectively.XRD analysis shows that the sintered products are HA phase doped with Ag ions.SEM observation shows that the pores of sintered samples present gradient distribution.The antibacterial experiments of gradient porous Ag-HA ceramics show that with the increase of Ag loading and porosity,the antibacterial ring diameter of gradient porous Ag-HA ceramics against escherichia coli and staphylococcus aureus increases.The gradient porous Ag-HA has good antibacterial properties,while pure HA ceramic shows no antibacterial properties.

Key words: Ag loaded hydroxyapatite ceramics, gradient porous, porosity, compressive strength, bacteriostatic zone, sterilization rate

CLC Number:

TB34

CHEN Chen, YU Jingyuan, LI Qiang. Preparation and Properties of Gradient Porous Ag LoadedHydroxyapatite Ceramics[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(1): 241-251.

References

[1] 李淼.微量元素掺杂羟基磷灰石的制备及生物学效应研究[D].上海:上海师范大学,2019.
LI M.Preparation and biological effect of trace element doped hydroxyapatite[D].Shanghai:Shanghai Normal University,2019 (in Chinese).
[2] 王丽萍.微量氟、锌、锶掺杂羟基磷灰石晶体结构及生物学效应研究[D].北京:中国科学院大学,2018.
WANG L P.Crystal structure and biological effects of hydroxyapatite doped with trace fluorine,zinc,and strontium[D].Beijing:University of Chinese Academy of Sciences,2018 (in Chinese).
[3] 吴金结,李艳,魏仁初,等.微振动应力环境影响羟基磷灰石陶瓷生物活性及力学稳定性的体外评价[J].无机材料学报,2019,34(4):417-424.
WU J J,LI Y,WEI R C,et al.Bioactivity and mechanical stability of hydroxyapatite ceramics under micro-vibration environment[J].Journal of Inorganic Materials,2019,34(4):417-424 (in Chinese).
[4] 张永霞,严亮,卢晓龙.PPC/纳米羟基磷灰石复合材料的制备及其性能研究[J].塑料科技,2019,47(8):7-11.
ZHANG Y X,YAN L,LU X L.Preparation and properties of PPC/nano-hydroxyapatite composites[J].Plastics Science and Technology,2019,47(8):7-11 (in Chinese).
[5] Zhou H J,LEE J.Nanoscale hydroxyapatite particles for bone tissue engineering[J].Acta Biomaterialia,2011,7(7):2769-2781.
[6] 张峻峰,蒋明慧,张顺锋,等.多孔羟基磷灰石生物陶瓷的制备及研究进展[J].中国陶瓷,2017,53(3):6-12.
ZHANG J F,JIANG M H,ZHANG S F,et al.Progress of preparation and research on porous hydroxyapatite bioceramics[J].China Ceramics,2017,53(3):6-12 (in Chinese).
[7] Li R J,Chen K X,Li G,et al.Structure design and fabrication of porous hydroxyapatite microspheres for cell delivery[J].Journal of Molecular Structure,2016,1120:34-41.
[8] Kurashina K,Kurita H,Wu Q,et al.Ectopic osteogenesis with biphasic ceramics of hydroxyapatite and tricalcium phosphate in rabbits[J].Biomaterials,2002,23(2):407-412.
[9] Guo Y J,Wang Y Y,Chen T,et al.Hollow carbonated hydroxyapatite microspheres with mesoporous structure:hydrothermal fabrication and drug delivery property[J].Materials Science and Engineering:C,2013,33(6):3166-3172.
[10] Salerno A,Guarnieri D,Iannone M,et al.Effect of micro- and macroporosity of bone tissue three-dimensional-poly(epsilon-caprolactone) scaffold on human mesenchymal stem cells invasion,proliferation,and differentiation in vitro[J].Tissue Engineering.Part A,2010,16(8):2661-2673.
[11] 王慎海.多孔羟基磷灰石材料的制备及表征[D].济南:齐鲁工业大学,2012.
WANG S H.Preparation and characterization of porous hydroxyapatite materials[D].Jinan:Qilu University of Technology,2012 (in Chinese).
[12] 徐伏秋,陈华军,丁梧秀.载银羟基磷灰石抗菌粉体和陶瓷的制备及抗菌性能[J].无机化学学报,2013,29(12):2582-2586.
XU F Q,CHEN H J,DING W X.Preparation and antibacterial property of Ag-doped hydroxyapatite antibacterial powders and antibacterial ceramic[J].Chinese Journal of Inorganic Chemistry,2013,29(12):2582-2586 (in Chinese).

[1]	WEI Da, ZHU Pinghua, WANG Xinjie, LIU Hui, LIU Shaofeng, JIA Xuejun. Effect of Attached Mortar Content of Recycled Coarse Aggregate on Frost Resistance Durability of Recycled Aggregate Concrete [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(3): 765-774.
[2]	XUE Wen, WANG Teng, CHENG Wenjie, SHEN Hongru, LI Yi, CHEN Jiangying, ZHU Yaohong. Influence of Low Temperature Freeze-Thaw Cycle on Dynamic Mechanical Properties of Ceramsite Concrete [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(3): 821-828.
[3]	LIU Guangying, GUO Xiangyu, DAI Shibing, DAI Shibao, MAN Xiaolei. Effect of Calcination Temperature on Physical and Mechanical Properties of Natural Hydraulic Lime [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(3): 883-888.
[4]	LIU Qian, GUO Yusen, ZHONG Tao, HUANG Qingyun. Effect of Adding Amount of Calcined Coal Gangue with High Pozzolanic Reactivity on Cement Compressive Strength [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(3): 936-942.
[5]	SHEN Yan, ZHU Hangyu, WANG Peifang, ZHANG Wei. Effect of Lithium Salt on Function of Borax in Sulphoaluminate Cement [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(2): 377-383.
[6]	LIN Peitong, ZENG Yu, ZHAO Yonggang, LIU Jinhong, WANG Junfeng, LU Liulei. Property and Pore Structure of Nano-SiO₂ Modified High Volume Slag Powder-Cement Cementitious System [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(2): 384-391.
[7]	XU Donghang, ZHU Pinghua, CHEN Chunhong, LIU Hui, LIU Shaofeng. Effects of Curing Regimes on Tunnel Fire Resistance of Self-Compacting Concrete Coated with Aerogel Cement Paste [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(2): 423-430.
[8]	LUO Yaoling, YANG Wen, XIE Yuhao, YAN Xinyi, BI Yao. Effect of Curing Temperature on Hydration and Mechanical Properties of UHPC [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(2): 431-438.
[9]	XIE Guoliang, SHEN Xiangdong, LIU Jinyun, ZHANG Bin. Deterioration Law of Recycled Concrete under the Coupling of Chloride and Freeze-Thaw [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(2): 473-479.
[10]	HU Xing, CHEN Dongping, YU Linwen, WANG Wenwen, WU Wenjie. Mix Design and Performance Research of Environment-Friendly Sleeve Grouting Material [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(2): 557-564.
[11]	ZHU Dianzhi, LIU Zuoyu, DONG Changhong, LIU Qingfeng, NIU Mengdie, LI Guoxin. Study on Corrosion Resistance of Nano SiO₂-CSA-OPCRepair Mortar in Saline Soil [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(1): 83-89.
[12]	NIU Zhigang, ZHU Pinghua, CHEN Chunhong, WANG Xinjie, LIU Hui. Design Method of Novel Recycled Pervious Concrete forResisting Rainstorm and Waterlogging [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(1): 106-112.
[13]	LIU Shulong, LI Gongcheng, LIU Guolei, WANG Fagang, WANG Jie, QI Zhaojun, YANG Jiguang. Ratio Optimization of Slag-Based Solid Waste Cementitious MaterialBased on Response Surface Method [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(1): 187-193.
[14]	YANG Zhenying, ZHOU Changshun. Effect of Glass Powder on Mechanical Properties of Recycled Concrete [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2020, 39(12): 3874-3880.
[15]	WEI Wei, GAO Yanbin, CHEN Zhongqing, ZHU Wentao, ZHU Zewei. Experimental Study on Proportion of Room Temperature Alkali-Activated Low-Calcium Fly Ash Geopolymer [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2020, 39(12): 3889-3896.