Effect of LDHs-NO2 on Properties of Cement Mortar and Corrosion of Steel Bar

doi:10.16552/j.cnki.issn1001-1625.2024.1003

Abstract

Abstract: In this paper, NO^-₂ was intercalated into the interlayer of Zn-Al-LDHs (layered double hydroxides, LDHs) by hydrothermal method to prepare modified hydrotalcite (LDHs-NO₂), and LDHs-NO₂ was characterized. The effect of different LDHs-NO₂ content on the fluidity, mechanical properties, chloride ion diffusion coefficient, pore structure, chloride ion adsorption of cement mortar and corrosion resistance of steel bar was investigated. The test results show that the compressive strength and flexural strength of cement mortar are improved, and the chloride ion diffusion coefficient and porosity are decreased by adding different content of LDHs-NO₂ into cement mortar. Compared with the reference group, the performance of cement mortar with 2% (mass fraction) LDHs-NO₂ is the most significant. Then, with the continuous increase of LDHs-NO₂ content (4%, 6%), the fluidity and mechanical properties of mortar decrease, but still higher than the reference group. The porosity of cement mortar has increased, but it is still lower than the reference group. LDHs-NO₂ achieves the adsorption of Cl^- through interlayer ion exchange, which is accompanied by the release of interlayer NO^-₂ during the adsorption of Cl^-. LDHs-NO₂ can effectively delay the corrosion of steel bars in cement mortar, and the more LDHs-NO₂ content in a certain range, the better the corrosion resistance of steel bars.

Key words: cement mortar, modified hydrotalcite, chloride ion adsorption, corrosion of steel bar, rust inhibition mechanism

CLC Number:

TU528

ZHANG Yi, ZHANG Biao, DENG Xiangwen, HE Hongjie. Effect of LDHs-NO₂ on Properties of Cement Mortar and Corrosion of Steel Bar[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2025, 44(1): 1-10.

References

[1] 郭群, 李晓珍, 宋屹林, 等. 钢筋阻锈剂在碳化钢筋混凝土中的阻锈作用[J]. 建筑材料学报, 2023, 26(1): 21-28.
GUO Q, LI X Z, SONG Y L, et al. Effect of steel bar corrosion inhibitors in carbonated reinforced concrete[J]. Journal of Building Materials, 2023, 26(1): 21-28 (in Chinese).
[2] LI C Z, JIANG L H, LI S S. Effect of limestone powder addition on threshold chloride concentration for steel corrosion in reinforced concrete[J]. Cement and Concrete Research, 2020, 131: 106018.
[3] ZUO J D, WU B, DONG B Q, et al. Effects of nitrite ion intercalated CaAl and MgAl layered double hydroxides on the properties of concrete mortar[J]. Cement and Concrete Composites, 2024, 145: 105306.
[4] ZHANG Y G, SUN C T, ZHANG P, et al. Chloride binding of monosulfate hydrate (AFm) and its effect on steel corrosion in simulated concrete pore solution[J]. Journal of Building Engineering, 2023, 67: 105945.
[5] 梁文杰, 谭洪波, 吕周岭. 混凝土内源氯离子固化的研究进展[J]. 硅酸盐通报, 2023, 42(8): 2667-2682.
LIANG W J, TAN H B, LYU Z L. Research progress on endogenous chloride ion binding of concrete[J]. Bulletin of the Chinese Ceramic Society, 2023, 42(8): 2667-2682 (in Chinese).
[6] HU X, POON C S. Chloride-related steel corrosion initiation in cement paste prepared with the incorporation of blast-furnace slag[J]. Cement and Concrete Composites, 2022, 126: 104349.
[7] 冯跃, 耿健, 李东. 焙烧水滑石对砂浆中氯离子渗透的影响[J]. 硅酸盐通报, 2018, 37(4): 1195-1199.
FENG Y, GENG J, LI D. Influence of calcined hydrotalcite on chloride penetration in mortar[J]. Bulletin of the Chinese Ceramic Society, 2018, 37(4): 1195-1199 (in Chinese).
[8] 李珂珂, 薛江伟, 王露威, 等. 镁铝水滑石对高铁低钙硅酸盐水泥性能的影响[J]. 无机盐工业, 2024, 56(4): 57-63.
LI K K, XUE J W, WANG L W, et al. Effect of MgAl-layered double hydroxides on properties of high-iron low-calcium Portland cement[J]. Inorganic Chemicals Industry, 2024, 56(4): 57-63 (in Chinese).
[9] CHEN Y X, SHUI Z H, CHEN W, et al. Chloride binding of synthetic Ca-Al-NO₃ LDHs in hardened cement paste[J]. Construction and Building Materials, 2015, 93: 1051-1058.
[10] YANG Z X, FISCHER H, POLDER R. Synthesis and characterization of modified hydrotalcites and their ion exchange characteristics in chloride-rich simulated concrete pore solution[J]. Cement and Concrete Composites, 2014, 47: 87-93.
[11] CAO Y H, ZHENG D J, LUO J S, et al. Insight into the fabrication of ZnAl layered double hydroxides intercalated with organic anions and their corrosion protection of steel reinforced concrete[J]. Journal of the Electrochemical Society, 2019, 166(16): 617-623.
[12] TIAN Y W, DONG C F, WANG G, et al. Zn-Al-NO₂ layered double hydroxide as a controlled-release corrosion inhibitor for steel reinforcements[J]. Materials Letters, 2019, 236: 517-520.
[13] CHEN M Z, WU F, YU L W, et al. Chloride binding capacity of LDHs with various divalent cations and divalent to trivalent cation ratios in different solutions[J]. CrystEngComm, 2019, 21(44): 6790-6800.
[14] SU Y, QIU S H, YANG D P, et al. Active anti-corrosion of epoxy coating by nitrite ions intercalated MgAl LDH[J]. Journal of Hazardous Materials, 2020, 391: 122215.
[15] WANG Y, ZHANG D. Synthesis, characterization, and controlled release anticorrosion behavior of benzoate intercalated Zn-Al layered double hydroxides[J]. Materials Research Bulletin, 2011, 46(11): 1963-1968.
[16] ALIBAKHSHI E, GHASEMI E, MAHDAVIAN M, et al. Corrosion inhibitor release from Zn-Al-[PO^3-₄]-[CO^2-₃] layered double hydroxide nanoparticles[J]. Progress in Color, Colorants and Coatings, 2016, 9: 233-248.
[17] HE Q Q, ZHOU M J, HU J M. Electrodeposited Zn-Al layered double hydroxide films for corrosion protection of aluminum alloys[J]. Electrochimica Acta, 2020, 355: 136796.
[18] SUBASRI R, SOMA RAJU K R C, REDDY D S, et al. Environmentally friendly Zn-Al layered double hydroxide (LDH)-based sol-gel corrosion protection coatings on AA 2024-T3[J]. Journal of Coatings Technology and Research, 2019, 16(5): 1447-1463.
[19] CHEN M Z, WEI Y N, ZHENG H B, et al. Ca-LDH-modified cementitious coating to enhance corrosion resistance of steel bars[J]. Journal of Building Engineering, 2022, 51: 104301.
[20] 张曼, 赵云良, 吴飞达. 焙烧态Ca-Mg-Al类水滑石的制备及其吸附As(Ⅴ)的研究[J]. 硅酸盐通报, 2018, 37(4): 1344-1349+1354.
ZHANG M, ZHAO Y L, WU F D. Preparing calcined Ca-Mg-Al hydrotalcite-like compound for adsorption of As(Ⅴ) in water[J]. Bulletin of the Chinese Ceramic Society, 2018, 37(4): 1344-1349+1354 (in Chinese).
[21] TANG Y M, ZHANG F, HU S X, et al. Novel benzimidazole derivatives as corrosion inhibitors of mild steel in the acidic media. part I: gravimetric, electrochemical, SEM and XPS studies[J]. Corrosion Science, 2013, 74: 271-282.
[22] POZNYAK S K, TEDIM J, RODRIGUES L M, et al. Novel inorganic host layered double hydroxides intercalated with guest organic inhibitors for anticorrosion applications[J]. ACS Applied Materials & Interfaces, 2009, 1(10): 2353-2362.
[23] CAO Y H, DONG S G, ZHENG D J, et al. Multifunctional inhibition based on layered double hydroxides to comprehensively control corrosion of carbon steel in concrete[J]. Corrosion Science, 2017, 126: 166-179.
[24] YANG Z X, FISCHER H, POLDER R. Laboratory investigation of the influence of two types of modified hydrotalcites on chloride ingress into cement mortar[J]. Cement and Concrete Composites, 2015, 58: 105-113.
[25] SHARMILA P, DHINAKARAN G. Compressive strength, porosity and sorptivity of ultra fine slag based high strength concrete[J]. Construction and Building Materials, 2016, 120: 48-53.
[26] DUAN P, CHEN W, MA J T, et al. Influence of layered double hydroxides on microstructure and carbonation resistance of sulphoaluminate cement concrete[J]. Construction and Building Materials, 2013, 48: 601-609.
[27] SHI J J, MING J, SUN W. Electrochemical behaviour of a novel alloy steel in alkali-activated slag mortars[J]. Cement and Concrete Composites, 2018, 92: 110-124.
[28] CUI L, HANG M Y, HUANG H H, et al. Experimental study on multi-component corrosion inhibitor for steel bar in chloride environment[J]. Construction and Building Materials, 2021, 313: 125533.
[29] BELLAL Y, BENGHANEM F, KERAGHEL S. A new corrosion inhibitor for steel rebar in concrete: synthesis, electrochemical and theoretical studies[J]. Journal of Molecular Structure, 2021, 1225: 129257.

Effect of LDHs-NO₂ on Properties of Cement Mortar and Corrosion of Steel Bar

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	SHEN Fei, QIAO Min, SHAN Guangcheng, WU Qingyong. Preparation of SiO₂ Composite Materials Loaded with Different Air-Entraining Agents and Their Application in Cement-Based Materials [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2024, 43(9): 3157-3163.
[2]	CUI Yingying, HE Jianhui, LYU Minwang, YANG Lu, LIU Yunpeng. Performance of Belite Cement Clinker from Completely Recyclable Cement Mortars [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2024, 43(9): 3348-3358.
[3]	HUANG Huanghuang, CHEN Tiefeng, GAO Xiaojian. Effect of CO₂-Mineralized High-Calcium Fly Ash on Mechanical Properties and Micro-Structure of Cement Mortar [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2024, 43(5): 1889-1896.
[4]	ZHANG Luman, HOU Feng. Thermal Performance Test and Numerical Simulation of Phase Change Thermostatic Wall Board [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2024, 43(3): 866-877.
[5]	ZHANG Yizhou, SU Junru, ZHENG Cheng, WANG Yinghao, PU Yundong, ZHANG Huiyi, YUAN Xiaoya. Effect of Co-Addition of Graphene and Hydroxyl Graphene on Properties of Cement Mortar [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2024, 43(11): 3968-3975.
[6]	ZHANG Na, SUN Qian, ZHANG Pengyu, WANG Dongmei, WANG Qin. Effects of Polymers on Waterproofing and Mechanical Properties of Mortar after Heat Treatment [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2023, 42(8): 2703-2711.
[7]	HE Yalan, NING Lin, LI Yang, ZHONG Xiujie. Study on Pore Structure and Water Migration Characteristics of Cement Mortar after High Temperature Based on NMR Technology [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2023, 42(7): 2336-2343.
[8]	ZHOU Lina, CAI Ying, MA Cailong, LUO Ling. Research Progress on Adsorption Capacity of Hydrotalcite for Chloride Ions in Cement-Based Materials [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2023, 42(4): 1137-1147.
[9]	CHEN Wenyao, ZHANG Zhuoxiang, MENG Ercong, LI Qiang. Impermeability and Crack Resistance of Bentonite and Basalt Fiber Modified Cement Mortar [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2023, 42(2): 439-447.
[10]	LI Xian, NING Lin, CHEN Liangliang, LI Yang, DENG Xiaojiang. Study on Effect of Aggregate Particle Size on Microstructure of Cement Mortar Based on Nuclear Magnetic Resonance Technology [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2023, 42(12): 4216-4223.
[11]	LI Shuai, MEI Junpeng, LI Hainan, DAI Junjie, XIE Anhe. Mechanical Properties of Polyformaldehyde-Basalt Hybrid Fiber Reinforced Mortar [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2023, 42(10): 3454-3461.
[12]	XU Ning, YANG Heng, XIONG Chuansheng, ZHANG Dong, JIANG Peng, LIU Can, LIU Xinxin, CHENG Xingliao. Research Progress of Anti-Corrosion Additives in Reinforced Concrete [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2023, 42(1): 1-21.
[13]	WANG Chuanlin, ZHANG Siyi, HUANG Junxuan, JIANG Tao, LIANG Ping, ZHOU Zhibing, WANG Yihong. Effect of Flocculant on Properties of Portland Cement Mortar [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(9): 3028-3035.
[14]	ZHANG Jie, LIU Yongjia, HOU Jingwen, LI Yan. Determination Method of EVA by Thermal Gravimetric Analysis Coupled with Mass Spectrometry [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(9): 3115-3120.
[15]	LI Shentong, YANG Yong, ZHOU Dongliang, HU Cong, LIU Jinzhi, ZHANG Zhiyong. Synthesis of Polycarboxylate Superplasticizer Based on Hydrophobic-Modified Polyoxyethylene Ether and Its Viscosity-Reducing Performance [J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(7): 2251-2257.