涂层对速凝3D打印水泥砂浆力学性能的影响

硅酸盐通报 ›› 2022, Vol. 41 ›› Issue (5): 1547-1553.

涂层对速凝3D打印水泥砂浆力学性能的影响

向忆寒¹, 陈旭浩¹, 邓永杰¹, 包亦望², 李维红¹

1.大连大学建筑工程学院,大连 116000;
2.中国建筑材料科学研究总院,北京 100024

收稿日期:2021-12-25 修回日期:2022-03-10 出版日期:2022-05-15 发布日期:2022-06-01
通讯作者: 李维红,博士,教授。E-mail:liweihong714@163.com
作者简介:向忆寒(1996—),女,硕士研究生。主要从事土木工程材料及结构特性研究。E-mail:352427909@qq.com
基金资助:
国家自然科学基金重点项目(52032011);国家重点研发计划(2018YFF0214500);辽宁省教育厅科学研究经费项目(LJKZ1177);大学生创新创业训练计划项目(D202103091415093197)

Effect of Coating on Mechanical Properties of Rapid Setting 3D Printing Cement Mortar

XIANG Yihan¹, CHEN Xuhao¹, DENG Yongjie¹, BAO Yiwang², LI Weihong¹

1. College of Architectural Engineering, Dalian University, Dalian 116000, China;
2. China Building Materials Academy, Beijing 100024, China

Received:2021-12-25 Revised:2022-03-10 Online:2022-05-15 Published:2022-06-01

摘要/Abstract

摘要： 3D打印砂浆普遍存在层间界面粘结较弱、抗折强度较低的问题,而膨胀水泥浆涂层涂覆于砂浆表面可产生表层压应力,进而提升其抗折强度,作为界面剂涂覆于层间可同时增强其界面粘结强度。本文通过将硫铝酸盐水泥与膨胀剂混合而成的涂层涂覆于速凝3D打印砂浆的表面与层间,研究了该涂层对不掺纤维及掺0.5%(体积分数)玄武岩纤维3D打印砂浆试件力学性能的影响规律。结果表明,涂覆层间涂层对无纤维与掺纤维速凝3D打印砂浆的层间界面粘结强度提升率分别为21.4%、12.2%,同时对其抗压强度也有一定提升作用。仅涂覆表面涂层与仅涂覆层间涂层对3D打印砂浆的抗折强度提升效果相当;同时涂覆表面及层间涂层对3D打印砂浆的抗折强度提升效果最显著,与无纤维、掺纤维的无涂层试件相比,提升率最高分别可达44.2%、23.2%。涂层对于无纤维3D打印试件层间粘结强度及抗折强度的提升效果优于掺纤维试件。

关键词: 3D打印水泥砂浆, 涂层, 表层压应力, 界面粘结强度, 抗折强度, 抗压强度

Abstract: 3D printing mortar generally has the problems of weak interlayer interface bonding and low flexural strength. The expansion cement slurry coated on the surface of mortar can produce surface compressive stress and then improve its flexural strength. As an interface agent, coating between layers can simultaneously enhance the interfacial bond strength. In this paper, the coating composed of sulphoaluminate cement and expansive agent was coated on the surface and interlayer of the 3D printing mortar, and the effect of the coating on the mechanical properties of the 3D printing mortar specimens without fiber and with 0.5% (volume fraction) basalt fiber was studied. The experimental results show that the interlayer coating improves the interlayer interfacial bond strength of fiber-free and fiber-doped rapid setting 3D printing mortar by 21.4% and 12.2%, respectively. At the same time, it also improves the compressive strength. The effect of coating only surface on the flexural strength of the 3D printing mortar is similar to that of coating only between layers. At the same time, surface coating and interlayer coating have the most obvious improvement effect on the flexural strength of the 3D printing mortar. Compared with the fiber-free and fiber-doped non-coating specimens, the highest improvement rates are 44.2% and 23.2%, respectively. The effect of coating on the interlayer interfacial bond strength and flexural strength of fiber-free 3D printing specimens is better than that of fiber-doped specimens.

Key words: 3D printing cement mortar, coating, surface compressive stress, interfacial bond strength, flexural strength, compressive strength

中图分类号:

TU528

向忆寒, 陈旭浩, 邓永杰, 包亦望, 李维红. 涂层对速凝3D打印水泥砂浆力学性能的影响[J]. 硅酸盐通报, 2022, 41(5): 1547-1553.

XIANG Yihan, CHEN Xuhao, DENG Yongjie, BAO Yiwang, LI Weihong. Effect of Coating on Mechanical Properties of Rapid Setting 3D Printing Cement Mortar[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(5): 1547-1553.

参考文献

[1] 叶俊宏,郑怡,余江滔,等.3D打印纤维增强混凝土材料研究进展[J].硅酸盐学报,2021,49(11):2538-2548.
YE J H, ZHENG Y, YU J T, et al. Research progress on 3D printable fiber reinforced concrete[J]. Journal of the Chinese Ceramic Society, 2021, 49(11): 2538-2548 (in Chinese).
[2] 刘天浩,王里,李之建,等.混凝土3D打印加筋增韧方法研究进展[J].工业建筑,2021,51(6):9-15.
LIU T H, WANG L, LI Z J, et al. A review of incorporating reinforcement method in 3D concrete printing[J]. Industrial Construction, 2021, 51(6): 9-15 (in Chinese).
[3] ZHANG J C, WANG J L, DONG S F, et al. A review of the current progress and application of 3D printed concrete[J]. Composites Part A: Applied Science and Manufacturing, 2019, 125: 105533.
[4] MA G W, WANG L. A critical review of preparation design and workability measurement of concrete material for largescale 3D printing[J]. Frontiers of Structural and Civil Engineering, 2018, 12(3): 382-400.
[5] 孙晓燕,叶柏兴,王海龙,等.3D打印混凝土材料与结构增强技术研究进展[J].硅酸盐学报,2021,49(5):878-886.
SUN X Y, YE B X, WANG H L, et al. Recent development on reinforcing technology of 3D printing concrete materials and structure[J]. Journal of the Chinese Ceramic Society, 2021, 49(5): 878-886 (in Chinese).
[6] PANDA B, CHANDRA PAUL S, JEN TAN M. Anisotropic mechanical performance of 3D printed fiber reinforced sustainable construction material[J]. Materials Letters, 2017, 209: 146-149.
[7] MA G W, LI Z J, WANG L, et al. Mechanical anisotropy of aligned fiber reinforced composite for extrusion-based 3D printing[J]. Construction and Building Materials, 2019, 202: 770-783.
[8] 张超,邓智聪,汪智斌,等.纤维对3D打印混凝土打印性能与力学性能的影响[J].硅酸盐通报,2021,40(6):1870-1878+1888.
ZHANG C, DENG Z C, WANG Z B, et al. Effects of fibers on printing performance and mechanical properties of 3D printing concrete[J]. Bulletin of the Chinese Ceramic Society, 2021, 40(6): 1870-1878+1888 (in Chinese).
[9] MARCHMENT T, SANJAYAN J. Mesh reinforcing method for 3D concrete printing[J]. Automation in Construction, 2020, 109: 102992.
[10] PERROT A, JACQUET Y, RANGEARD D, et al. Nailing of layers: a promising way to reinforce concrete 3D printing structures[J]. Materials, 2020, 13(7): 1518.
[11] BOS F P, AHMED Z Y, JUTINOV E R, et al. Experimental exploration of metal cable as reinforcement in 3D printed concrete[J]. Materials (Basel, Switzerland), 2017, 10(11): 1314.
[12] WANG L, TIAN Z H, MA G W, et al. Interlayer bonding improvement of 3D printed concrete with polymer modified mortar: experiments and molecular dynamics studies[J]. Cement and Concrete Composites, 2020, 110: 103571.
[13] BAO Y W, KUANG F H, SUN Y, et al. A simple way to make pre-stressed ceramics with high strength[J]. Journal of Materiomics, 2019, 5(4): 657-662.
[14] 包亦望,孙熠,旷峰华,等.高强度预应力陶瓷的发展与探索[J].无机材料学报,2020,35(4):399-406.
BAO Y W, SUN Y, KUANG F H, et al. Development and prospects of high strength pre-stressed ceramics[J]. Journal of Inorganic Materials, 2020, 35(4): 399-406 (in Chinese).
[15] ARUNOTHAYAN A R, NEMATOLLAHI B, RANADE R, et al. Development of 3D-printable ultra-high performance fiber-reinforced concrete for digital construction[J]. Construction and Building Materials, 2020, 257: 119546.
[16] ZAREIYAN B, KHOSHNEVIS B. Effects of mixture ingredients on interlayer adhesion of concrete in contour crafting[J]. Rapid Prototyping Journal, 2018, 24(3): 584-592.
[17] 黄璐,卓卫东,谷音,等.界面剂对新旧混凝土界面粘结性能影响的试验研究[J].福州大学学报(自然科学版),2018,46(3):396-402.
HUANG L, ZHUO W D, GU Y, et al. Effect test of interface agent on bonding of old and new concrete[J]. Journal of Fuzhou University (Natural Science Edition), 2018, 46(3): 396-402 (in Chinese).