钙铝质矿相对碱激发矿渣氯离子固化能力的影响研究

硅酸盐通报 ›› 2022, Vol. 41 ›› Issue (3): 878-883.

钙铝质矿相对碱激发矿渣氯离子固化能力的影响研究

杨婷丽, 高旭, 谷倩, 范小春, 朱兆坤

武汉理工大学土木工程与建筑学院,武汉 430070

收稿日期:2021-11-22 修回日期:2021-12-30 出版日期:2022-03-15 发布日期:2022-04-08
通讯作者: 高旭,博士,教授。E-mail:x.gao@whut.edu.cn
作者简介:杨婷丽(1998—),女,硕士研究生。主要从事碱激发材料方面的研究。E-mail:yang265503@163.com
基金资助:
国家自然科学基金青年项目(52108244);武汉理工大学三亚科教创新园开放基金(2020KF0008)

Influences of Calcium and Aluminum Mineral Phases on Chloride Binding Capacity of Alkali-Activated Slag

YANG Tingli, GAO Xu, GU Qian, FAN Xiaochun, ZHU Zhaokun

School of Civil Engineering and Architecture, Wuhan University of Technology, Wuhan 430070, China

Received:2021-11-22 Revised:2021-12-30 Online:2022-03-15 Published:2022-04-08

摘要/Abstract

摘要： 本文提出了一类改性碱激发矿渣胶凝材料,通过在原材料中掺入额外的钙、铝质矿相(Ca(OH)₂和γ-Al₂O₃),促进材料基体中的Friedel's盐(F盐)在氯离子存在条件下的形成,进而提升胶凝材料的氯离子固化能力。本研究探讨了钙、铝质矿物含量对碱矿渣反应产物组成、氯离子固化量以及力学性能的影响。结果表明,钙、铝质矿相的额外补充可显著提高胶凝材料的氯离子固化能力,同时体系的m(Ca)/m(Al)与该能力的相关性较高。物相分析结果表明,钙质矿相的补充使得反应产物中拥有富余的Ca(OH)₂,在氯盐侵蚀作用下,富余的Ca(OH)₂全部转化为F盐或其他物相,证实了体系氯离子固化能力的增强得益于F盐的形成,即得益于化学固氯能力的提升。抗压强度测试结果,表明钙质矿物的掺入对力学性能存在一定负面影响,而铝质矿相的掺入则能够在一定程度上弥补强度损失。

关键词: 碱激发胶凝材料, 矿渣, 钙铝质矿相, 水化产物, 氯离子固化

Abstract: In this paper, a modified alkali-activated slag cementitious material was proposed by applying calcium and alumina mineral phases (Ca(OH)₂ and γ-Al₂O₃) as partial replacement of slag, aiming at promoting the formation of Friedel's salt (F salt) in the matrix when in the presence of chloride, and improving the chloride binding capacity. The effects of calcium and aluminum mineral phase content on reaction products, chloride binding capacity and mechanical properties were discussed. The results show that the addition of calcium and aluminum mineral phases improves the chloride binding capacity of alkali-activated slag, and the mass ratio of Ca(OH)₂ to γ-Al₂O₃ is highly related to this capacity. XRD analyses show that there exists unreacted Ca(OH)₂ within the reaction products, and all those Ca(OH)₂ transform into F salt or other phases after chloride attack. It is demonstrated that the enhancement of chloride binding capacity is attributed to the formation of F salt. The compressive strength results indicate that the addition of Ca(OH)₂ exhibits a negative impact, while the γ-Al₂O₃ can compensate for the strength loss due to the Ca(OH)₂ addition.

Key words: alkali-activated cementitious material, slag, calcium and aluminum mineral phase, hydration product, chloride binding capacity

中图分类号:

TU528.01

杨婷丽, 高旭, 谷倩, 范小春, 朱兆坤. 钙铝质矿相对碱激发矿渣氯离子固化能力的影响研究[J]. 硅酸盐通报, 2022, 41(3): 878-883.

YANG Tingli, GAO Xu, GU Qian, FAN Xiaochun, ZHU Zhaokun. Influences of Calcium and Aluminum Mineral Phases on Chloride Binding Capacity of Alkali-Activated Slag[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(3): 878-883.

参考文献

[1] 史才军,何富强,FERNANDEZ-JIMIENEZ A,等.碱激发水泥的类型与特点(英文)[J].硅酸盐学报,2012,40(1):69-75.
SHI C J, HE F Q, FERNANDEZ-JIMIENEZ A, et al. Classification and characteristics of alkali-activated cements[J]. Journal of the Chinese Ceramic Society, 2012, 40(1): 69-75.
[2] 万小梅,韩笑,于琦,等.碱激发矿渣净浆对氯离子的固化作用[J].建筑材料学报,2021,24(5):952-960.
WAN X M, HAN X, YU Q, et al. Solidification of chloride ions in alkali-activated slag paste[J]. Journal of Building Materials, 2021, 24(5): 952-960 (in Chinese).
[3] 勾密峰,管学茂,孙倩.水化硅酸钙对氯离子的吸附[J].建筑材料学报,2015,18(3):363-368.
GOU M F, GUAN X M, SUN Q. Adsorption of chloride ion by calcium silicate hydrate[J]. Journal of Building Materials, 2015, 18(3): 363-368 (in Chinese).
[4] 罗睿,蔡跃波,王昌义.磨细矿渣净浆和砂浆结合外渗氯离子的性能[J].建筑材料学报,2001,4(2):148-153.
LUO R, CAI Y B, WANG C Y. Binding capability of chloride ions in mortar and paste with ground granulated blast furnace slag[J]. Journal of Building Materials, 2001, 4(2): 148-153 (in Chinese).
[5] KE X Y, BERNAL S A, PROVIS J L. Uptake of chloride and carbonate by Mg-Al and Ca-Al layered double hydroxides in simulated pore solutions of alkali-activated slag cement[J]. Cement and Concrete Research, 2017, 100: 1-13.
[6] ZHANG J, SHI C J, ZHANG Z H. Chloride binding of alkali-activated slag/fly ash cements[J]. Construction and Building Materials, 2019, 226: 21-31.
[7] 杨长辉,朱效宏,郑雨佳,等.内掺Ca(OH)₂对碱矿渣混凝土水化进程的影响[J].建筑材料学报,2017,20(2):161-167.
YANG C H, ZHU X H, ZHENG Y J, et al. Effect of calcium hydroxide on hydration process of alkali-activated slag concrete[J]. Journal of Building Materials, 2017, 20(2): 161-167 (in Chinese).
[8] FLOREA M V A, BROUWERS H J H. Chloride binding related to hydration products: part I: ordinary Portland cement[J]. Cement and Concrete Research, 2012, 42(2): 282-290.
[9] MANGAT P S, OJEDOKUN O O. Free and bound chloride relationships affecting reinforcement cover in alkali activated concrete[J]. Cement and Concrete Composites, 2020, 112: 103692.
[10] TANG L P, NILSSON L O. Chloride binding capacity and binding isotherms of OPC pastes and mortars[J]. Cement and Concrete Research, 1993, 23(2): 247-253.
[11] SHI Z G, GEIKER M R, LOTHENBACH B, et al. Friedel's salt profiles from thermogravimetric analysis and thermodynamic modelling of Portland cement-based mortars exposed to sodium chloride solution[J]. Cement and Concrete Composites, 2017, 78: 73-83.
[12] 勾密峰,黄飞,管学茂.矿渣对氯离子的固化作用[J].材料导报,2014,28(10):120-122+144.
GOU M F, HUANG F, GUAN X M. The binding effect of slag on the chloride ions[J]. Materials Review, 2014, 28(10): 120-122+144 (in Chinese).
[13] ZIBARA H, HOOTON R D, THOMAS M D A, et al. Influence of the C/S and C/A ratios of hydration products on the chloride ion binding capacity of lime-SF and lime-MK mixtures[J]. Cement and Concrete Research, 2008, 38(3): 422-426.
[14] 朱效宏,郑雨佳,张帆,等.内掺Ca(OH)₂对碱矿渣混凝土强度发展的影响[J].功能材料,2016,47(8):8079-8083.
ZHU X H, ZHENG Y J, ZHANG F, et al. Strength development of alkali-activated slag concrete (AASC) by the addition of calcium hydroxide[J]. Journal of Functional Materials, 2016, 47(8): 8079-8083 (in Chinese).

[1]	周明凯, 林方亮, 陈立顺, 王怀德, 陈潇. SiO₂含量对钛矿渣微晶玻璃晶化行为的影响[J]. 硅酸盐通报, 2022, 41(4): 1133-1140.
[2]	黄伟, 周佳敏, 衷从浩, 麻秀星, 方云辉, 柯余良, 韦建刚. 早强型聚羧酸系减水剂对基准水泥早期水化的影响研究[J]. 硅酸盐通报, 2022, 41(4): 1211-1221.
[3]	韦琦, 刘艳, 耿海宁, 马浩森, 陈伟, 王东文, 潘社奇, 李秋. 聚合硫酸铝改性低碱度水泥性能研究[J]. 硅酸盐通报, 2022, 41(4): 1237-1244.
[4]	刘泽平, 王传林, 张宇轩, 张腾腾. 海水和矿物掺合料对硫铝酸盐水泥砂浆性能的影响[J]. 硅酸盐通报, 2022, 41(4): 1245-1255.
[5]	王思纯, 廖宜顺, 万世辉. 不同温度下矿渣对铝酸盐水泥早期水化行为的影响[J]. 硅酸盐通报, 2022, 41(4): 1343-1351.
[6]	吴亚男, 王璜琪, 王栋民, 孙睿, 吕南. 矿渣种类对新型石膏矿渣硫铝酸盐水泥水化硬化的影响[J]. 硅酸盐通报, 2022, 41(4): 1352-1361.
[7]	安强, 潘慧敏, 王帅, 赵庆新. 粉煤灰和矿渣粒度分布对混凝土微观结构和抗氯离子渗透性的影响[J]. 硅酸盐通报, 2022, 41(3): 884-893.
[8]	贾新松, 陈德平, 于晓伟, 郭林芳, 郝月涵, 薛三梅. 海水浸泡下全固废胶凝材料的试验研究[J]. 硅酸盐通报, 2022, 41(3): 913-921.
[9]	贾行伟, 罗中秋, 周新涛, 宋向荣. 矿渣基草酸钙化学键合材料的制备及其固化重金属的研究[J]. 硅酸盐通报, 2022, 41(3): 953-958.
[10]	丁正东, 孙家瑛. 矿渣微粉与珍珠岩尾矿复合对免烧陶粒性能的影响[J]. 硅酸盐通报, 2022, 41(2): 513-519.
[11]	张文艳, 林华夏, 王帅, 薛孟芬, 冉俊生, 朱建平. 减缩剂对碱激发煤矸石-矿渣胶凝材料性能的影响[J]. 硅酸盐通报, 2022, 41(2): 526-535.
[12]	李云云, 梁文特, 倪文, 牟欣丽, 李玥, 樊康. 钢渣尾泥-矿渣-脱硫石膏三元体系水化硬化特性[J]. 硅酸盐通报, 2022, 41(2): 536-544.
[13]	张涛, 陈铁军, 陈永亮, 潘料庭, 黄学忠, 陈兴. 机械活化和不锈钢渣掺量对矿渣胶凝材料性能的影响[J]. 硅酸盐通报, 2022, 41(2): 553-561.
[14]	杨振甲, 何猛, 吴杨, 史钰鹏, 孙亮, 潘竹, 张默. 矿渣-粉煤灰地聚物固化淤泥力学性能和路用性能研究[J]. 硅酸盐通报, 2022, 41(2): 693-703.
[15]	王旭影, 乔京生, 赵建业, 蔡田明, 梁晨达. 电石渣激发钢渣-矿渣固化淤泥质土的试验研究[J]. 硅酸盐通报, 2022, 41(2): 733-739.