矿渣微粉与珍珠岩尾矿复合对免烧陶粒性能的影响

硅酸盐通报 ›› 2022, Vol. 41 ›› Issue (2): 513-519.

矿渣微粉与珍珠岩尾矿复合对免烧陶粒性能的影响

丁正东¹, 孙家瑛^1,2

1.上海大学力学与工程科学学院,上海 200444;
2.浙大宁波理工学院土木建筑工程学院,宁波 315000

收稿日期:2021-10-14 修回日期:2022-01-07 出版日期:2022-02-15 发布日期:2022-03-01
通讯作者: 孙家瑛,博士,教授。E-mail:jakys@163.com
作者简介:丁正东(1994—),男,硕士研究生。主要从事绿色建筑材料的研究。E-mail:1574087979@qq.com
基金资助:
“十二五”国家科技支撑计划(2015BAL02B03);面向共同富裕的乡村振兴综合集成技术研发与典型示范(20211ZDYF020199)

Influence of Combination of Fine Slag Powder and Perlite Tailings on Performance of Non-Sintered Ceramsite

DING Zhengdong¹, SUN Jiaying^1,2

1. School of Mechanics and Engineering Science, Shanghai University, Shanghai 200444, China;
2. School of Civil Engineering & Architecture, Ningbotech University, Ningbo 315000, China

Received:2021-10-14 Revised:2022-01-07 Online:2022-02-15 Published:2022-03-01

摘要/Abstract

摘要： 以珍珠岩尾矿、粒化高炉矿渣微粉、水玻璃为原材料研制无熟料免烧陶粒。以水玻璃作为激发剂,探究其模数和掺量对矿渣微粉强度的影响,研究矿渣微粉与珍珠岩尾矿粉复合对陶粒筒压强度和堆积密度的影响。结果表明:当矿渣微粉、水玻璃质量比为90∶10,水玻璃最佳模数为1.06,矿渣微粉、珍珠岩尾矿质量比为90∶10时,可以使陶粒标养28 d达到筒压强度为7.50 MPa,密度等级为900 kg/m³,孔隙率为31.84%,软化系数为0.92,含泥量为2.25%,煮沸质量损失为2.84%;对陶粒表面进行防水处理后,吸水率由11.68%降到4.88%。采用陶粒配制LC30轻集料混凝土进行道路窨井周围道路基层应用,其28 d抗压强度为35.5 MPa,密度等级为1 700 kg/m³,压缩系数为0.001,应用效果良好,防止了城市道路窨井沉陷。

关键词: 免烧陶粒, 矿渣微粉, 珍珠岩尾矿, 吸水率, 轻集料混凝土

Abstract: This paper revolves around the research and production of non-clinker and non-sintered ceramsite with perlite tailings, granulated blast furnace fine slag powder, and water glass as raw materials. The combined influence of the modulus and content of water glass on the intensity of fine slag powderwith sodium silicate as activator, and the effect of the combination of fine slag powder and perlite tailings powder on the compressive strength and bulk density of ceramsite cylinders were explored. The results show that when the mass ratio of slag powder to water glass is 90∶10, the best modulus of water glass is 1.06, and the mass ratio of slag powder to perlite tailings is 90∶10, the ceramsite can reach a technical performance on a 28 d standard maintenance that compressive strength of cylinder is 7.50 MPa, the density grade is 900 kg/m³, the porosity is 31.84%, the softening coefficient is 0.92, the mud content is 2.25%, and the boiling mass loss is 2.84%. Besides, after water proof treatment on the surface of the ceramsite, reducing the water absorption rate decreases from 11.68% to 4.88%. The ceramsite is used to prepare LC30 lightweight aggregate concrete for the application of the road base around manholes. The 28 d compressive strength is 35.5 MPa, the density grade is 1 700 kg/m³, and the compression coefficient is 0.001. The application presents a satisfying result, preventing the sinking of the urban road manholes.

Key words: non-sintered ceramsite, fine slag powder, perlite tailing, water absorption, lightweight aggregate concrete

中图分类号:

TU528

丁正东, 孙家瑛. 矿渣微粉与珍珠岩尾矿复合对免烧陶粒性能的影响[J]. 硅酸盐通报, 2022, 41(2): 513-519.

DING Zhengdong, SUN Jiaying. Influence of Combination of Fine Slag Powder and Perlite Tailings on Performance of Non-Sintered Ceramsite[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(2): 513-519.

参考文献

[1] 邵靖邦.国外免烧粉煤灰陶粒生产技术[J].粉煤灰综合利用,1996,9(4):52-55.
SHAO J B. The technology of producing for the unifired fly ash haydite at abroad[J]. Fly Ash Comprehensive Utilization, 1996, 9(4): 52-55 (in Chinese).
[2] 徐晶,严义云,严群,等.用离子型稀土尾矿制备多孔免烧陶粒[J].金属矿山,2014(12):129-133.
XU J, YAN Y Y, YAN Q, et al. Preparation of porous non-sintered ceramsite with ion-absorbing type rare earth tailings[J]. Metal Mine, 2014(12): 129-133 (in Chinese).
[3] 周颜,贾瑞,周兰,等.疏浚底泥免烧陶粒的制备及其净水效果[J].环境工程学报,2017,11(5):2804-2811.
ZHOU Y, JIA R, ZHOU L, et al. Preparation of dredged sediment unburned ceramsite and its water purification effect[J]. Chinese Journal of Environmental Engineering, 2017, 11(5): 2804-2811 (in Chinese).
[4] 朱万旭,酆磊,周红梅,等.新型免烧粉煤灰陶粒的研制及应用浅析[J].混凝土,2017(5):59-62.
ZHU W X, FENG L, ZHOU H M, et al. Analysis on the development and application of a new type of ash haydite[J]. Concrete, 2017(5): 59-62 (in Chinese).
[5] 高鹏,徐悦清,曹云,等.淤泥基免烧陶粒的制备及性能影响因素[J].硅酸盐通报,2021,40(3):889-899.
GAO P, XU Y Q, CAO Y, et al. Preparation and performance influencing factors of silt-based non-sintered ceramsite[J]. Bulletin of the Chinese Ceramic Society, 2021, 40(3): 889-899 (in Chinese).
[6] 刘丹妮,戴友芝,许友泽,等.给水厂残泥免烧陶粒的制备与性能表征[J].非金属矿,2019,42(1):100-103.
LIU D N, DAI Y Z, XU Y Z, et al. Preparation and characterization of unburned ceramsite from water treatment residuals[J]. Non-Metallic Mines, 2019, 42(1): 100-103 (in Chinese).
[7] 张凯,刘舒豪,张日新,等.免烧法煤气化粗渣制备陶粒工艺及其性能研究[J].煤炭科学技术,2018,46(10):222-227.
ZHANG K, LIU S H, ZHANG R X, et al. Research on preparation of non-sintered ceramsite from gasification cinder and its performance[J]. Coal Science and Technology, 2018, 46(10): 222-227 (in Chinese).
[8] WANG Y L, HU X B, YAO Y H, et al. Research progress of slag structure and hydration activity[J]. Materials Science Forum, 2021, 1035: 972-979.
[9] 齐兆军,刘树龙,刘国磊,等.利用矿渣替代水泥开发矿山新型胶凝材料试验研究[J].矿业研究与开发,2021,41(1):48-52.
QI Z J, LIU S L, LIU G L, et al. Experimental research on development of new cementitious material by using slag to replace cement[J]. Mining Research and Development, 2021, 41(1): 48-52 (in Chinese).
[10] 李颖,吴保华,倪文,等.矿渣-钢渣-石膏体系早期水化反应中的协同作用[J].东北大学学报(自然科学版),2020,41(4):581-586.
LI Y, WU B H, NI W, et al. Synergies in early hydration reaction of slag-steel slag-gypsum system[J]. Journal of Northeastern University (Natural Science), 2020, 41(4): 581-586 (in Chinese).
[11] 于霖.碱激发矿渣胶凝材料的制备及其性能研究[D].郑州:郑州大学,2010.
YU L. A study on the preparation and properties of alkali-activated slag cementitious material[D]. Zhengzhou: Zhengzhou University, 2010 (in Chinese).
[12] FANG S, LAM E S S, LI B, et al. Effect of alkali contents, moduli and curing time on engineering properties of alkali activated slag[J]. Construction and Building Materials, 2020, 249: 118799.
[13] SHI C J, LI Y Y. Investigation on some factors affecting the characteristics of alkali-phosphorus slag cement[J]. Cement and Concrete Research, 1989, 19(4): 527-533.

[1]	段旭晨, 孟凡涛, 魏春城, 李占冲, 穆清林, 刘哲坤, 王玉良. 细粒黄金尾矿制备烧结砖的试验研究[J]. 硅酸盐通报, 2021, 40(8): 2653-2658.
[2]	刘芳, 熊锐, 钟勇强. 表面涂层对混凝土吸水性能的影响[J]. 硅酸盐通报, 2021, 40(7): 2209-2214.
[3]	乔京生, 王旭影, 王冠泓, 赵建业. 粒化高炉矿渣微粉固化淤泥质土的动力特性及微观机理[J]. 硅酸盐通报, 2021, 40(7): 2306-2312.
[4]	迟凤霞, 韩博, 程沁灵, 周文静. 激发剂内部参数对碱激发注浆材料性能的影响[J]. 硅酸盐通报, 2021, 40(5): 1751-1759.
[5]	缪汉良, 赵斌, 纪荣健, 杨建明. 早龄期磷酸钾镁水泥砂浆的抗冻性评价[J]. 硅酸盐通报, 2021, 40(4): 1128-1136.
[6]	高鹏, 徐悦清, 曹云, 韩燕, 刘荣. 淤泥基免烧陶粒的制备及性能影响因素[J]. 硅酸盐通报, 2021, 40(3): 889-899.
[7]	陈伟;金胜;袁波. 脱硫脱硝灰为基体制备早强型粉体矿渣助磨剂性能研究[J]. 硅酸盐通报, 2020, 39(7): 2190-2195.
[8]	张波. 矿渣微粉-糊精灰浆复合胶凝材料的试验研究[J]. 硅酸盐通报, 2020, 39(4): 1208-1213.
[9]	钱达友;杨建明. 水冻融和硫酸盐溶液冻融环境下MKPC砂浆的耐久性评价[J]. 硅酸盐通报, 2020, 39(2): 359-366.
[10]	潘慧敏;王树伟;付建航. 扰动对混凝土性能影响的尺寸效应试验研究[J]. 硅酸盐通报, 2019, 38(8): 2414-241.
[11]	易双秦;刘开志;邱晶;余睿;水中和;赵旭东;刘轩睿. 吸水珊瑚砂作为超高性能混凝土(UHPC)内养护介质的研究[J]. 硅酸盐通报, 2019, 38(8): 2506-251.
[12]	李亮. 利用低温氯化渣制备发泡多孔陶瓷材料研究[J]. 硅酸盐通报, 2019, 38(6): 1759-176.
[13]	孙凯利;王彩辉;孙国文;谷峪;张广田;郭子良. 海泡石对砂浆抗氯离子和碳化侵蚀性能的影响[J]. 硅酸盐通报, 2019, 38(10): 3111-312.
[14]	康春阳;李博;田健. 聚合氯化铝提升矿渣硅酸盐水泥性能及微观机理研究[J]. 硅酸盐通报, 2018, 37(9): 2693-2698.
[15]	夏明钢. 煅烧硅藻土对轻集料保温混凝土性能的影响[J]. 硅酸盐通报, 2018, 37(9): 3012-3016.