CFB灰渣抹灰砂浆的组成设计与性能研究

硅酸盐通报 ›› 2022, Vol. 41 ›› Issue (2): 425-432.

CFB灰渣抹灰砂浆的组成设计与性能研究

周明凯^1,2, 叶青², 陈潇^1,2, 张嘉琛², 陈立顺², 王怀德¹

1.武汉理工大学,硅酸盐建筑材料国家重点实验室,武汉 430070;
2.武汉理工大学,材料科学与工程学院,武汉 430070

收稿日期:2021-11-02 修回日期:2021-12-21 出版日期:2022-02-15 发布日期:2022-03-01
通讯作者: 陈潇,博士,副研究员。E-mail:1172934546@qq.com
作者简介:周明凯(1964—),男,教授。主要从事固体废弃物综合利用的研究。E-mail:zhoumingkai@163.com
基金资助:
国家重点研发计划(2020YFC1909903)

Composition Design and Performance of CFB Fly Ash and CFB Slag Plastering Mortar

ZHOU Mingkai^1,2, YE Qing², CHEN Xiao^1,2, ZHANG Jiachen², CHEN Lishun², WANG Huaide¹

1. State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology, Wuhan 430070, China;
2. School of Materials Science and Engineering, Wuhan University of Technology, Wuhan 430070, China

Received:2021-11-02 Revised:2021-12-21 Online:2022-02-15 Published:2022-03-01

摘要/Abstract

摘要： 为了提高抹灰砂浆的强度和体积稳定性,研究了水泥用量和灰渣比(循环硫化床(CFB)飞灰和CFB炉渣的质量比)对CFB灰渣抹灰砂浆2 h稠度损失率、抗压强度和体积稳定性的影响,并采用扫描电子显微镜、X射线能谱仪和X射线衍射仪对砂浆的微观形貌、元素分布和物相组成进行测试表征。结果表明,当水泥用量为5%、8%、12%(质量分数)时,CFB灰渣抹灰砂浆分别达到抹灰砂浆M10、M15、M20的强度等级。当胶凝材料用量一定时,随着水泥用量增大,砂浆2 h稠度损失率减小;当水泥用量一定时,随着灰渣比增大,砂浆2 h稠度损失率增大,膨胀效应减弱。CFB灰渣抹灰砂浆中生成的膨胀性钙矾石有效填充了颗粒之间的孔隙,从而提高砂浆的强度和体积稳定性。

关键词: CFB飞灰, CFB炉渣, 抹灰砂浆, 灰渣比, 抗压强度, 体积稳定性, 微观结构

Abstract: In order to improve the strength and volume stability of plastering mortar, the effects of cement content and ash-slag ratio (mass ratio of CFB fly ash to CFB slag) on 2 h consistency loss rate, compressive strength and volume stability of CFB fly ash and CFB slag plastering mortar were studied. The micro morphology, element distribution and phase composition of mortar were characterized by scanning electron microscope, X-ray energy spectrometer and X-ray diffractometer. The results show that when the cement content is 5%, 8% and 12% (mass fraction), the strength grade of CFB fly ash and CFB slag plastering mortar reaches M10, M15 and M20, respectively. When the content of cementitious material is constant, the 2 h consistency loss rate of mortar decreases with the increase of cement content. And when the content of cement is constant, the 2 h consistency loss rate of mortar increases and the expansion effect decreases with the increase of ash-slag ratio. Expansive ettringite generated in the CFB fly ash and slag plastering mortar fills the pores between the particles effectively, so as to improve the strength and volume stability of mortar.

Key words: CFB fly ash, CFB slag, plastering mortar, ash-slag ratio, compressive strength, volume stability, microstructure

中图分类号:

TU525

周明凯, 叶青, 陈潇, 张嘉琛, 陈立顺, 王怀德. CFB灰渣抹灰砂浆的组成设计与性能研究[J]. 硅酸盐通报, 2022, 41(2): 425-432.

ZHOU Mingkai, YE Qing, CHEN Xiao, ZHANG Jiachen, CHEN Lishun, WANG Huaide. Composition Design and Performance of CFB Fly Ash and CFB Slag Plastering Mortar[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(2): 425-432.

参考文献

[1] 袁亮.我国煤矿安全发展战略研究[J].中国煤炭,2021,47(6):1-6.
YUAN L. Study on the development strategy of coal mine safety in China[J]. China Coal, 2021, 47(6): 1-6 (in Chinese).
[2] KOUKOUZAS N, KETIKIDIS C, ITSKOS G, et al. Synthesis of CFB-coal fly ash clay bricks and their characterisation[J]. Waste and Biomass Valorization, 2011, 2(1): 87-94.
[3] SHON C S, MUKHOPADHYAY A K, SAYLAK D, et al. Potential use of stockpiled circulating fluidized bed combustion ashes in controlled low strength material (CLSM) mixture[J]. Construction and Building Materials, 2010, 24(5): 839-847.
[4] 芋艳梅,刘永明.固硫灰渣和粉煤灰的特性对比分析[J].水泥工程,2021(4):8-11.
YU Y M, LIU Y M. Properties analysis of sulfur-fixing ash and fly ash[J]. Cement Engineering, 2021(4): 8-11 (in Chinese).
[5] CHEN X M, YAN Y, LIU Y Z, et al. Utilization of circulating fluidized bed fly ash for the preparation of foam concrete[J]. Construction and Building Materials, 2014, 54: 137-146.
[6] LI X G, CHEN Q B, MA B G, et al. Utilization of modified CFBC desulfurization ash as an admixture in blended cements: physico-mechanical and hydration characteristics[J]. Fuel, 2012, 102: 674-680.
[7] SHENG G H, LI Q, ZHAI J P. Investigation on the hydration of CFBC fly ash[J]. Fuel, 2012, 98: 61-66.
[8] 宁美,王智,钱觉时,等.固硫灰渣的特性及其与现行标准的适应性[J].硅酸盐通报,2019,38(3):688-693+701.
NING M, WANG Z, QIAN J S, et al. Characteristics of fluidized bed coal combustion fly ash and slag and its adaptability with current standards[J]. Bulletin of the Chinese Ceramic Society, 2019, 38(3): 688-693+701 (in Chinese).
[9] 郑娟荣,谷迪.石灰石粉对机制砂干混抹灰砂浆性能影响的试验研究[J].混凝土,2015(5):122-123+127.
ZHENG J R, GU D. Experimental study on the effect of limestone powder on the properties of dry-mixed plastering mortar with machine-made sand[J]. Concrete, 2015(5): 122-123+127 (in Chinese).
[10] 孔哲,李秋义,韩帅,等.机制砂制备干混砌筑砂浆的试验研究[J].混凝土,2016(5):102-105.
KONG Z, LI Q Y, HAN S, et al. Experimental research on manufactured sand preparing dry-mixed masonry mortar[J]. Concrete, 2016(5): 102-105 (in Chinese).
[11] 章银祥,夏旺,王国强,等.机制砂在干混砂浆中的应用[J].新型建筑材料,2015,42(3):14-17.
ZHANG Y X, XIA W, WANG G Q, et al. Application of manufactured sand in the dry-mixed mortar[J]. New Building Materials, 2015, 42(3): 14-17 (in Chinese).
[12] 潘小平,吴漫天,徐建华,等.机制砂特点与干混砂浆的生产及施工[J].建设机械技术与管理,2019,32(2):52-56.
PAN X P, WU M T, XU J H, et al. Crushed sands specialty & dry mixed mortar production and application[J]. Construction Machinery Technology & Management, 2019, 32(2): 52-56 (in Chinese).
[13] 宋远明,钱觉时,王智,等.固硫灰渣的微观结构与火山灰反应特性[J].硅酸盐学报,2006,34(12):1542-1546.
SONG Y M, QIAN J S, WANG Z, et al. Microstructure and pozzolanic reactivity of fluidized bed combustion ashes[J]. Journal of the Chinese Ceramic Society, 2006, 34(12): 1542-1546 (in Chinese).
[14] 刘宏,刘红宇.固硫灰渣用于预拌砌筑砂浆的试验研究[J].科学技术与工程,2015,15(21):195-198+204.
LIU H, LIU H Y. Research on desulfurized coal ash/slag used in ready mixed mortar[J]. Science Technology and Engineering, 2015, 15(21): 195-198+204 (in Chinese).
[15] 宋远明,钱觉时,王智,等.固硫灰渣对水泥胶砂耐久性影响研究[J].建筑材料学报,2010,13(1):66-69.
SONG Y M, QIAN J S, WANG Z, et al. Effect of fluidized bed combustion (FBC) ashes on durability of cement mortar[J]. Journal of Building Materials, 2010, 13(1): 66-69 (in Chinese).
[16] 唐明浩,姜志炜,张士萍,等.矿渣活性研究现状及发展[J].建材发展导向,2020,18(4):4-7.
TANG M H, JIANG Z W, ZHANG S P, et al. Research status and development of slag activity[J]. Development Guide to Building Materials, 2020, 18(4): 4-7 (in Chinese).
[17] 李佳,倪文,张思奇,等.矿渣水泥的综合应用[J].黄金,2018,39(9):74-77.
LI J, NI W, ZHANG S Q, et al. Comprehensive application of slag cement[J]. Gold, 2018, 39(9): 74-77 (in Chinese).
[18] 宋远明.流化床燃煤固硫灰渣水化研究[D].重庆:重庆大学,2007.
SONG Y M. Study on hydration of fluidized bed combustion ashes[D]. Chongqing: Chongqing University, 2007 (in Chinese).
[19] 彭金生,胡明玉,丁成平,等.脱硫灰特性及其干粉砂浆试验研究[J].新型建筑材料,2010,37(9):19-21.
PENG J S, HU M Y, DING C P, et al. Experimental study on desulfurization ash characteristics and dry-mixed mortar[J]. New Building Materials, 2010, 37(9): 19-21 (in Chinese).
[20] SIDDIQUE S, KIM H, JANG J G. Properties of high-volume slag cement mortar incorporating circulating fluidized bed combustion fly ash and bottom ash[J]. Construction and Building Materials, 2021, 289: 123150.
[21] LEKLOU N, NGUYEN V H, MOUNANGA P. The effect of the partial cement substitution with fly ash on delayed ettringite formation in heat-cured mortars[J]. KSCE Journal of Civil Engineering, 2017, 21(4): 1359-1366.
[22] LEE H K, JEON S M, LEE B Y, et al. Use of circulating fluidized bed combustion bottom ash as a secondary activator in high-volume slag cement[J]. Construction and Building Materials, 2020, 234: 117240.
[23] 纪宪坤,周永祥,冷发光.流化床(FBC)燃煤固硫灰渣研究综述[J].粉煤灰,2009,21(6):41-45.
JI X K, ZHOU Y X, LENG F G. An overview of study of fluidized bed combustion(FBC) ash residue[J]. Coal Ash, 2009, 21(6): 41-45 (in Chinese).[24] 刘虎林,王昭,伍媛婷,等.固硫灰渣的基本特性及其作水泥混合材的关键问题研究进展[J].硅酸盐通报,2021,40(6):2052-2061+2069.
LIU H L, WANG Z, WU Y T, et al. Review on characteristics of fluidized bed combustion ashes and key issues in their application as cement admixtures[J]. Bulletin of the Chinese Ceramic Society, 2021, 40(6): 2052-2061+2069 (in Chinese).
[25] TAYLOR H F W, FAMY C, SCRIVENER K L. Delayed ettringite formation[J]. Cement and Concrete Research, 2001, 31(5): 683-693.
[26] 芮雅峰,王栋民,李端乐,等.固硫灰中含钙矿物对其水化特性影响的研究进展[J].硅酸盐通报,2019,38(2):386-391.
RUI Y F, WANG D M, LI D L, et al. Review on the effect of calcium-containing minerals on hydration in circulating fluidized bed combustion fly ash[J]. Bulletin of the Chinese Ceramic Society, 2019, 38(2): 386-391 (in Chinese).