偏高岭土对高流动性钢纤维混凝土早期力学性能和细观结构的影响

硅酸盐通报 ›› 2021, Vol. 40 ›› Issue (9): 2911-2920.

偏高岭土对高流动性钢纤维混凝土早期力学性能和细观结构的影响

于子豪^1,2, 张彤炜^1,2, 崔科旺^1,2

1.兰州大学西部灾害与环境力学教育部重点实验室,兰州 730000;
2.兰州大学土木工程与力学学院,兰州 730000

收稿日期:2021-03-26 修回日期:2021-04-09 出版日期:2021-09-15 发布日期:2021-10-08
通讯作者: 张彤炜,博士,副教授。E-mail:ztw@lzu.edu.cn
作者简介:于子豪(1996—),男,硕士研究生。主要从事混凝土和地聚合物的研究。E-mail:yuzh19@lzu.edu.cn
基金资助:
国家重点研发计划(2018YFC1504700,2019YFC1806004);中国博士后科学基金面上项目(2019M653791);甘肃省自然科学基金面上项目(20JR5RA259);中央高校基本科研业务费专项资金自由探索项目(lzujbky-2020-pd08)

Effect of Metakaolin on Early Mechanical Property and Microstructure of High Fluidity Steel Fiber Reinforced Concrete

YU Zihao^1,2, ZHANG Tongwei^1,2, CUI Kewang^1,2

1. Key Laboratory of Mechanics on Disaster and Environment in Western China, The Ministry of Education of China, Lanzhou University, Lanzhou 730000, China;
2. College of Civil Engineering and Mechanics, Lanzhou University, Lanzhou 730000, China

Received:2021-03-26 Revised:2021-04-09 Online:2021-09-15 Published:2021-10-08

摘要/Abstract

摘要： 为了提高泵送混凝土流动性及早期力学性能,降低水泥用量,本文研究了高流动性偏高岭土和钢纤维复合混凝土的流动性、抗压和抗拉强度、弹性模量、破坏形态和微观结构,并在此基础上评价了偏高岭土和钢纤维对混凝土性能的影响。结果表明,随着钢纤维和偏高岭土含量的增加,浆体的流动性降低,偏高岭土影响更加显著。偏高岭土提高了钢纤维混凝土养护7 d后的抗压强度、抗拉强度和弹性模量,钢纤维对残余拉伸强度和裂纹扩展有明显的影响。通过扫描电镜(SEM)观察与X射线衍射(XRD)分析,偏高岭土的添加使试样内部产生了更稳定的水化硅酸钙(CSH)凝胶、单硫型水化硫铝酸钙(AFm)和高硫型水化硫铝酸钙(AFt)等物质。这些产物减少了孔隙和缺陷的产生,增强了界面过渡区的粘结力。由于偏高岭土和钢纤维对和易性的影响机制分别为增加黏度和提升浆体的抗剪切能力,本质上都为阻碍各组分的相对运动,所以二者在降低混凝土流动性方面具有耦合作用。偏高岭土与钢纤维影响混凝土力学性能的阶段不同,前者在未开裂阶段,后者在开裂阶段。

关键词: 偏高岭土, 钢纤维, 高流动性混凝土, 力学性能, 微观机制

Abstract: To improve the workability of the pumped concretes at early curing stage, which are normally used in driven cast-in-place piles, this paper investigated thefluidity, compressive and tensile strength, elastic modulus, destruction morphology and microstructure of high fluidity metakaolin (MK) and steel fiber (SF) concrete. Then, the effects of metakaolin and steel fiber on concrete properties were evaluated. The results show that the fluidity of the paste decreases with the increase of steel fiber or metakaolin respectively. As metakaolin contents increased, the increment of metakaolin dominates the fluidity of concrete, and the effect of steel fiber is not evident. The compressive strength, tensile strength and elastic modulus after 7 d curing increase with SF or metakaolin respectively, and metakaolin is the key factor effecting the strength of high fluidity MK-SF concretes. Whist the residual tensile strength and crack development are significantly dominates by steel fiber. From the scanning electronic microscope (SEM) images and X-ray diffraction (XRD) spectrogram, more stable hydrated calcium silicate (CSH) gel, monosulfide calcium sulphoaluminate hydrate (AFm) and polysulfide calcium sulphoaluminate hydrate (AFt) are produced by metakaolin addition. These products reduce the porosity and defects, and strengthen the bonding in interfacial transition zone. The metakaolin and steel fiber increase the viscosity of paste and the shear resistance of interfaces, which is essentially to hinder the relative movement of each component. Then, they have a coupling effect on reducing the fluidity of concrete. The mechanisms of metakaolin and steel fiber influencing the mechanical behavior of concretes are different. Generally, the steel fiber effects the cracking stage and the metakaolin influences the non-cracking stage in strain-stress curves.

Key words: metakaolin, steel fiber, high fluidity concrete, mechanical property, micromechanism

中图分类号:

TU528

于子豪, 张彤炜, 崔科旺. 偏高岭土对高流动性钢纤维混凝土早期力学性能和细观结构的影响[J]. 硅酸盐通报, 2021, 40(9): 2911-2920.

YU Zihao, ZHANG Tongwei, CUI Kewang. Effect of Metakaolin on Early Mechanical Property and Microstructure of High Fluidity Steel Fiber Reinforced Concrete[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(9): 2911-2920.

参考文献

[1] RASHAD A M. Metakaolin as cementitious material: history, scours, production and composition: a comprehensive overview[J]. Construction and Building Materials, 2013, 41: 303-318.
[2] SIDDIQUE R, KLAUS J. Influence of metakaolin on the properties of mortar and concrete: a review[J]. Applied Clay Science, 2009, 43(3/4): 392-400.
[3] AKCAY B, TASDEMIR M A. Performance evaluation of silica fume and metakaolin with identical finenesses in self compacting and fiber reinforced concretes[J]. Construction and Building Materials, 2018, 185: 436-444.
[4] ANTONI M, ROSSEN J, MARTIRENA F, et al. Cement substitution by a combination of metakaolin and limestone[J]. Cement and Concrete Research, 2012, 42(12): 1579-1589.
[5] GÜNEYISI E, GESOĞLU M, KARAOĞLU S, et al. Strength, permeability and shrinkage cracking of silica fume and metakaolin concretes[J]. Construction and Building Materials, 2012, 34: 120-130.
[6] 赵人达,赵成功,原元,等.超高性能混凝土中钢纤维的应用研究进展[J/OL].中国公路学报:1-27[2021-04-09].http://kns.cnki.net/kcms/detail/61.1313.U.20210104.1605.015.html.
ZHAO R D, ZHAO C G, YUAN Y, et al. Research progress on application of steel fiber in ultra-high performance concrete[J]. China Journal of Highway and Transport: 1-27 [2021-04-09]. http://kns.cnki.net/kcms/detail/61.1313.U.20210104.1605.015.html (in Chinese).
[7] DUAN P, SHUI Z H, CHEN W, et al. Effects of metakaolin, silica fume and slag on pore structure, interfacial transition zone and compressive strength of concrete[J]. Construction and Building Materials, 2013, 44: 1-6.
[8] 邓永锋,吴子龙,刘松玉,等.地聚合物对水泥固化土强度的影响及其机理分析[J].岩土工程学报,2016,38(3):446-453.
DENG Y F, WU Z L, LIU S Y, et al. Influence of geopolymer on strength of cement-stabilized soils and its mechanism[J]. Chinese Journal of Geotechnical Engineering, 2016, 38(3): 446-453 (in Chinese).
[9] RAMEZANIANPOUR A A, BAHRAMI JOVEIN H. Influence of metakaolin as supplementary cementing material on strength and durability of concretes[J]. Construction and Building Materials, 2012, 30: 470-479.
[10] MELO K A, CARNEIRO A M P. Effect of MetakaoliŃs finesses and content in self-consolidating concrete[J]. Construction and Building Materials, 2010, 24(8): 1529-1535.
[11] 莫宗云,高小建.偏高岭土混合水泥水化研究进展[J].混凝土,2017(6):80-84.
MO Z Y, GAO X J. Research progess on the hydration of metakaolin blended cement[J]. Concrete, 2017(6): 80-84 (in Chinese).
[12] 吴子龙,朱向阳,邓永锋,等.掺入钢渣与偏高岭土水泥改性土的性能与微观机制[J].中国公路学报,2017,30(9):18-26.
WU Z L, ZHU X Y, DENG Y F, et al. Behavior and micro-mechanism of cement-based modified compaction soil composed of steel slag and metakaolin[J]. China Journal of Highway and Transport, 2017, 30(9): 18-26 (in Chinese).
[13] MADANDOUST R, MOUSAVI S Y. Fresh and hardened properties of self-compacting concrete containing metakaolin[J]. Construction and Building Materials, 2012, 35: 752-760.
[14] POON C S, KOU S C, LAM L. Compressive strength, chloride diffusivity and pore structure of high performance metakaolin and silica fume concrete[J]. Construction and Building Materials, 2006, 20(10): 858-865.
[15] POON C S, SHUI Z H, LAM L. Compressive behavior of fiber reinforced high-performance concrete subjected to elevated temperatures[J]. Cement and Concrete Research, 2004, 34(12): 2215-2222.
[16] HOLSCHEMACHER K, MUELLER T, RIBAKOV Y. Effect of steel fibres on mechanical properties of high-strength concrete[J]. Materials & Design (1980—2015), 2010, 31(5): 2604-2615.
[17] MOHAMMADI Y, SINGH S P, KAUSHIK S K. Properties of steel fibrous concrete containing mixed fibres in fresh and hardened state[J]. Construction and Building Materials, 2008, 22(5): 956-965.
[18] SONG P S, HWANG S. Mechanical properties of high-strength steel fiber-reinforced concrete[J]. Construction and Building Materials, 2004, 18(9): 669-673.
[19] YAZICI Š, DE İNAN G, TABAK V. Effect of aspect ratio and volume fraction of steel fiber on the mechanical properties of SFRC[J]. Construction and Building Materials, 2007, 21(6): 1250-1253.
[20] 吴浩,王振地,王玲,等.钢纤维类型和掺量对高强混凝土流动性的影响[J].低温建筑技术,2017,39(9):1-3+13.
WU H, WANG Z D, WANG L, et al. Influence of steel fiber forms and dosage on fluidity of high strength concrete[J]. Low Temperature Architecture Technology, 2017, 39(9): 1-3+13 (in Chinese).
[21] BERNAL S A, MEJÍA DE GUTIÉRREZ R, PROVIS J L. Engineering and durability properties of concretes based on alkali-activated granulated blast furnace slag/metakaolin blends[J]. Construction and Building Materials, 2012, 33: 99-108.
[22] GÜNEYISI E, GESOĞLU M, AKOI A O M, et al. Combined effect of steel fiber and metakaolin incorporation on mechanical properties of concrete[J]. Composites Part B: Engineering, 2014, 56: 83-91.
[23] HAN J L, SHUI Z H, WANG G M, et al. Performance evaluation of steam cured HPC pipe piles produced with metakaolin based mineral additives[J]. Construction and Building Materials, 2018, 189: 719-727.
[24] ANTONI M, ROSSEN J, MARTIRENA F, et al. Cement substitution by a combination of metakaolin and limestone[J]. Cement and Concrete Research, 2012, 42(12): 1579-1589.
[25] ZHANG T W, YUE X B, DENG Y F, et al. Mechanical behaviour and micro-structure of cement-stabilised marine clay with a metakaolin agent[J]. Construction and Building Materials, 2014, 73: 51-57.