煅烧温度对水泥熟料矿物相含量及形貌影响的Rietveld法研究

硅酸盐通报 ›› 2021, Vol. 40 ›› Issue (9): 2871-2876.

煅烧温度对水泥熟料矿物相含量及形貌影响的Rietveld法研究

杨欢¹, 齐砚勇¹, 高宇蕾², 邓磊³, 李诗颖⁴

1.西南科技大学材料科学与工程学院,绵阳 621010;
2.绵阳职业技术学院材料与建造学院,绵阳 621000;
3.四川峨胜水泥集团股份有限公司,乐山 614222;
4.四川利森建材集团有限公司,德阳 618400

收稿日期:2021-03-26 修回日期:2021-04-13 出版日期:2021-09-15 发布日期:2021-10-08
通讯作者: 齐砚勇,博士,副教授。E-mail:274217698@qq.com
作者简介:杨欢(1995—),女,硕士研究生。主要从事水泥工艺的研究。E-mail:1196875298@qq.com

Influence of Calcination Temperature on Mineral Phase Content and Morphology of Cement Clinker by Rietveld Method

YANG Huan¹, QI Yanyong¹, GAO Yulei², DENG Lei³, LI Shiying⁴

1. School of Materials Science and Engineering, Southwest University of Science and Technology, Mianyang 621010, China;
2. School of Materials and Construction, Mianyang Polytechnic, Mianyang 621000, China;
3. Sichuan Esheng Cement Group Co., Ltd., Leshan 614222, China;
4. Sichuan Lisen Building Materials Group Co., Ltd., Deyang 618400, China

Received:2021-03-26 Revised:2021-04-13 Online:2021-09-15 Published:2021-10-08

摘要/Abstract

摘要： 为了探究煅烧温度对水泥熟料矿物相的影响,采用XRD分析法、Rietveld法以及岩相法,对不同煅烧温度下得到的熟料矿物相进行定性、定量以及形貌分析。研究结果表明:采用Rietveld法可快速、准确测得熟料中各矿物相的相对含量;通过Rietveld法计算得到的矿物相含量可明显看出,煅烧温度对熟料中各矿物相的含量有直接影响,其中对C₃S和C₂S含量的影响最为明显;Rietveld法与鲍格算法得到的矿物相含量结果接近,但拟合得到的C₃A含量会偏低,这是由于熟料的急冷使得C₃A以玻璃相形式存在;煅烧温度升高,晶体成核和发育更加完善,熟料能呈现更好的形貌。

关键词: Rietveld法, 岩相, 煅烧温度, 硅酸盐水泥熟料, 矿物相含量

Abstract: In order to explore the influence of calcination temperature on the mineral phase of cement clinker, the clinker was analyzed qualitatively, quantitatively and morphologically by XRD, Rietveld and lithofacies method. The results show that Rietveld method can be used to measure the relative content of each mineral phase in the clinker quickly and accurately. According to the content of mineral phase calculated by Rietveld method, it can be seen that calcination temperature has a direct effect on the content of mineral phase in the clinker, especialy C₃S and C₂S. The results of mineral phase content obtained by Rietveld method are close to those obtained by Bague algorithm, but the content of C₃A obtained by fitting is lower. This is due to the rapid cooling of clinker which makes C₃A exist as glass phase. With the increase of calcination temperature, the crystal nucleation and development are more perfect, and the clinker shows better morphology.

Key words: Rietveld method, lithofacies, calcination temperature, Portland cement clinker, mineral phase content

中图分类号:

TQ172

杨欢, 齐砚勇, 高宇蕾, 邓磊, 李诗颖. 煅烧温度对水泥熟料矿物相含量及形貌影响的Rietveld法研究[J]. 硅酸盐通报, 2021, 40(9): 2871-2876.

YANG Huan, QI Yanyong, GAO Yulei, DENG Lei, LI Shiying. Influence of Calcination Temperature on Mineral Phase Content and Morphology of Cement Clinker by Rietveld Method[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(9): 2871-2876.

[1]	刘倩, 邓磊, 高宇蕾, 齐砚勇. 冷却方式对熟料矿物及C₃S晶型的影响[J]. 硅酸盐通报, 2021, 40(9): 2877-2883.
[2]	刘永毅, 任尊超, 袁连旺, 栾从起, 王金邦, 周宗辉. 响应曲面法优化高强硅酸盐水泥熟料矿物组成的研究[J]. 硅酸盐通报, 2021, 40(4): 1088-1096.
[3]	严峻, 聂松, 刘松柏, 邱廷省. 利用铜尾矿作硅质原料制备硅酸盐水泥熟料的研究[J]. 硅酸盐通报, 2021, 40(4): 1273-1279.
[4]	刘广英, 郭向宇, 戴仕炳, 戴仕宝, 满晓磊. 煅烧温度对天然水硬石灰物理力学特性影响研究[J]. 硅酸盐通报, 2021, 40(3): 883-888.
[5]	王菲, 刘泽, 韩乐, 谢福助. 活化煤矸石地质聚合物的制备与性能研究[J]. 硅酸盐通报, 2021, 40(3): 914-920.
[6]	刘振正, 谢春磊, 王学营, 郭亮, 武悦悦, 陈琴, 段平. 稻壳灰的制备及其对地聚物力学性能的影响[J]. 硅酸盐通报, 2020, 39(12): 3881-3888.
[7]	郑培毓;张玲;张超;张欢. 纳米η-Al2O3粉体固相反应制备Na-β"-Al2O3粉体[J]. 硅酸盐通报, 2019, 38(5): 1556-156.
[8]	贺贤举;管俊芳;陈志强;段树桐;张凌燕. 河北邢台地区脉石英矿的包裹体研究[J]. 硅酸盐通报, 2017, 36(9): 3070-3074.
[9]	莫宗云;马腾飞;王大光. 偏高岭土活性研究进展[J]. 硅酸盐通报, 2017, 36(1): 110-115.
[10]	高云琴;张由子;马爱琼. Sol-Gel法合成锌铝尖晶石的影响因素研究[J]. 硅酸盐通报, 2016, 35(12): 4149-4153.
[11]	葛大顺;马素花;李伟峰;于锦;沈晓冬;汤国芳;蔡建. 硫铝酸钙改性硅酸盐水泥熟料研究进展[J]. 硅酸盐通报, 2015, 34(7): 1878-1884.
[12]	陈本稳;考宏涛;张千程;刘府. 不同碱含量生料生产熟料的岩相分析[J]. 硅酸盐通报, 2015, 34(12): 3622-3625.
[13]	彭晖;崔潮;蔡春声;李树霖;张雄飞. 偏高岭土活性的煅烧温度影响及测定方法研究[J]. 硅酸盐通报, 2014, 33(8): 2078-2084.
[14]	嵇鹰;周静;杨康;徐德龙;李霞;陈冠君. 高镁硅酸盐水泥熟料矿物形成及性能研究[J]. 硅酸盐通报, 2014, 33(10): 2445-2450.
[15]	张晶晶;齐砚勇;温馨. 煅烧温度对水泥熟料主要矿物形成的影响[J]. 硅酸盐通报, 2013, 32(9): 1756-1762.