新型水泥基电池的制备与电化学性能研究

硅酸盐通报 ›› 2024, Vol. 43 ›› Issue (7): 2685-2696.

所属专题：新型功能材料

新型水泥基电池的制备与电化学性能研究

夏冬林¹, 王亚杰², 蒋洋^2,3

1.武汉理工大学硅酸盐建筑材料国家重点实验室,武汉 430070;
2.武汉理工大学材料科学与工程学院,武汉 430070;
3.中能建绿色建材有限公司,武汉 430015

收稿日期:2023-12-15 修订日期:2024-02-05 出版日期:2024-07-15 发布日期:2024-07-24
通信作者: 蒋洋,博士,教授级高级工程师。E-mail:13501138929@139.com
作者简介:夏冬林(1964—),男,博士,副研究员。主要从事新能源材料的研究。E-mail:donglinxia@126.com
基金资助:
江西省重点研发计划(20214BBG74002)

Preparation and Electrochemical Properties of Novel Cement-Based Batteries

XIA Donglin¹, WANG Yajie², JIANG Yang^2,3

1. State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology, Wuhan 430070, China;
2. School of Materials Science and Engineering, Wuhan University of Technology, Wuhan 430070, China;
3. China Energy Green Building Material Co., Ltd., Wuhan 430015, China

Received:2023-12-15 Revised:2024-02-05 Online:2024-07-15 Published:2024-07-24

摘要/Abstract

摘要： 新型水泥基电池作为一种建筑储能装置,具有成本低、环境友好和可充电性等优点而受到国内外科研工作者的广泛关注。本文将不同导电填料与正、负极活性物质混合研磨,然后经真空干燥处理制成新型水泥基可充电电池的电极,研究了不同导电填料和用量对可充电水泥基电池电化学性能的影响。结果表明:在正、负极活性物质中掺入质量分数为25%的炭黑导电填料的水泥基电池的容量达到12.5 mAh,能量密度为1.575 Wh/m²,放电寿命超过了3.3 h,其电化学性能优于相同质量分数的石墨和石墨烯导电填料水泥基电池。

关键词: 水泥基电池, 可充电性, 建筑储能, 导电填料, 电化学性能

Abstract: As a kind of building energy storage device, the novel cement-based battery has the advantages of low cost, environmental friendliness and rechargeability, and has been widely concerned by researchers at home and abroad. In this study, the electrode of a new cement-based rechargeable battery was made by mixing different conductive fillers with positive and negative active substances and grinding, and then drying by vacuum. And the effects of the kinds and content of the conductive fillers on the electrochemical property of the rechargeable cement-based batteries were investigated. The results show the cement-based battery with the mass fraction of 25% carbon black possesses a battery capacity of 12.5 mAh, an energy density of 1.575 Wh/m², and the discharge lifespan exceeds 3.3 h, its electrochemical properties are better than that of graphite cement-based batteries and graphene cement-based batteries with the same mass fraction.

Key words: cement-based battery, rechargeability, building energy storage, conductive filler, electrochemical property

中图分类号:

TU528

夏冬林, 王亚杰, 蒋洋. 新型水泥基电池的制备与电化学性能研究[J]. 硅酸盐通报, 2024, 43(7): 2685-2696.

XIA Donglin, WANG Yajie, JIANG Yang. Preparation and Electrochemical Properties of Novel Cement-Based Batteries[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2024, 43(7): 2685-2696.

参考文献

[1] SALAMI B A, OYEHAN T A, TANIMU A, et al. Cement-based batteries design and performance: a review[J]. Environmental Chemistry Letters, 2022, 20(3): 1671-1694.
[2] MENG Q L, CHUNG D D L. Battery in the form of a cement-matrix composite[J]. Cement and Concrete Composites, 2010, 32(10): 829-839.
[3] HOLMES N, BYRNE A, NORTON B. First steps in developing cement-based batteries to power cathodic protection of embedded steel in concrete[J]. Journal of Sustainable Design and Research (SDAR), 2015, 3(1): 3-9.
[4] BYRNE A, BARRY S, HOLMES N, et al. Optimising the performance of cement-based batteries[J]. Advances in Materials Science and Engineering, 2017, 2017: 4724302.
[5] BURSTEIN G T, SPECKERT E I. Developing a battery using concrete as an electrolyte[J]. ECS Transactions, 2006, 3(42): 13-20.
[6] MA W Y, ZHANG D. Multifunctional structural supercapacitor based on graphene and magnesium phosphate cement[J]. Journal of Composite Materials, 2019, 53(6): 719-730.
[7] XU C, ZHANG D. Multifunctional structural supercapacitor based on cement/PVA-KOH composite and graphene[J]. Journal of Composite Materials, 2020, 55(10): 1359-1369.
[8] FANG C Q, ZHANG D. A large areal capacitance structural supercapacitor with a 3D rGO@MnO₂ foam electrode and polyacrylic acid-Portland cement-KOH electrolyte[J]. Journal of Materials Chemistry A, 2020, 8(25): 12586-12593.
[9] ZHANG J J, XU J M, ZHANG D. A structural supercapacitor based on graphene and hardened cement paste[J]. Journal of the Electrochemical Society, 2015, 163(3): E83-E87.
[10] ZHANG E Q, TANG L P. Rechargeable concrete battery[J]. Buildings, 2021, 11(3): 103.
[11] HOLMES N, BYRNE A, NORTON B. An overview of the development of cement-based batteries for the cathodic protection of embedded steel in concrete[J]. Civil Engineering Research in Ireland, 2016, 1(1): 593-597.
[12] JOSEPH R J. Development of cement-based batteries for self-powering cathodic protection systems[D]. Edinburgh:Heriot-Watt University, 2018.
[13] BYRNE A, HOLMES N, NORTON B. Cement based batteries and their potential for use in low power operations[J]. IOP Conference Series: Materials Science and Engineering, 2015, 96: 012073.
[14] 袁学锋, 王花. 硅酸盐水泥基复合电解质的制备及其在建筑储能器件中的应用[J]. 硅酸盐通报, 2021, 40(12): 3938-3944+3955.
YUAN X F, WANG H. Preparation of Portland cement based composite electrolyte and its application in building energy storage devices[J]. Bulletin of the Chinese Ceramic Society, 2021, 40(12): 3938-3944+3955 (in Chinese).

[1]	陈志强, 崔磊, 董晶, 李海霞, 夏炜炜. 钛网上CdS纳米微球的制备及可见光下产氢性能研究[J]. 硅酸盐通报, 2024, 43(2): 727-733.
[2]	袁仲纯, 李佳, 姚梦琴, 刘飞, 马俊, 耿硕. 多晶型MnO₂改善富锂锰基正极材料的电化学性能[J]. 硅酸盐通报, 2023, 42(9): 3387-3394.
[3]	李琦旺, 张卫珂, 王佳玮, 高博文, 陈柳玲. Si-C-N-Al的表面限域合成及其电化学性能研究[J]. 硅酸盐通报, 2023, 42(8): 2895-2903.
[4]	刘欣楠, 肖彦之, 黄美琪, 蒋菡, 孔江榕, 周涛. Ni、Cu共浸渍的LSCM-GDC复合阴极性能研究[J]. 硅酸盐通报, 2022, 41(7): 2458-2466.
[5]	黄晋萍, 陈庆, 李建保, 骆丽杰, 陈拥军. Ga掺杂FeNb₁₁O₂₉材料的制备及其电化学性能[J]. 硅酸盐通报, 2021, 40(8): 2740-2747.
[6]	查成, 张天宇, 季雨辰, 刘树和. 锂硫电池正极材料的研究进展[J]. 硅酸盐通报, 2021, 40(4): 1352-1360.
[7]	黄均艳;王小丽;黄美英;夏明星. 乙酸锌活化制备柚子皮衍生活性碳及其电化学和吸附性能研究[J]. 硅酸盐通报, 2020, 39(7): 2335-2342.
[8]	王春源;黄杜斌;宋波涛;程宏飞. 硅藻土涂层改性锌负极及其在锌离子电池中的应用[J]. 硅酸盐通报, 2020, 39(6): 1909-1915.
[9]	王万玺;王凤英;王刚;李海宾. 富锂锰基正极材料的形貌与结构调控及电化学性能研究[J]. 硅酸盐通报, 2020, 39(3): 885-889.
[10]	李晓俊;张金华;郑刚;汪伟;倪江秀;王金龙. 石墨烯复合碳纳米管添加量对锂离子电池性能的影响[J]. 硅酸盐通报, 2020, 39(3): 896-900.
[11]	张丽娜;张平;张山;袁明珞. TiO2/In2S3复合薄膜的制备及光电化学性能研究[J]. 硅酸盐通报, 2019, 38(8): 2403-240.
[12]	李瑞锋;王文娟;刘诚;黄康;李纯;鲁自鼎. LaBaCoFeO5+δ-Ce0.8Sm0.2O1.9复合阴极的电化学性能研究[J]. 硅酸盐通报, 2019, 38(4): 1012-101.
[13]	季鸣童;王晓爽. 多孔氮掺杂石墨烯/MnO2的制备及其电化学性能[J]. 硅酸盐通报, 2019, 38(12): 3814-382.
[14]	王晓亮;闫慧妍;张佳齐;杨绍斌;程焱;孟令强;刘忆. SAS对镍铝水滑石材料超级电容性能的影响[J]. 硅酸盐通报, 2018, 37(10): 3108-3112.
[15]	张瑛洁;赵丽文;楚华;袁龙飞. 溶胶凝胶法制备Si/TiO2复合锂离子电池负极材料的研究进展[J]. 硅酸盐通报, 2016, 35(8): 2454-2459.

新型水泥基电池的制备与电化学性能研究

Preparation and Electrochemical Properties of Novel Cement-Based Batteries

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价