严寒环境下磷酸镁水泥砂浆与混凝土的粘结强度及影响因素研究

硅酸盐通报 ›› 2024, Vol. 43 ›› Issue (6): 2064-2072.

严寒环境下磷酸镁水泥砂浆与混凝土的粘结强度及影响因素研究

侯铁军¹, 李想¹, 张晨琛¹, 贾兴文², 侯鹏坤³

1.青海交通职业技术学院,西宁 810003;
2.重庆大学材料科学与工程学院,重庆 400045;
3.济南大学材料科学与工程学院,济南 250022

收稿日期:2023-11-14 修订日期:2024-01-16 出版日期:2024-06-15 发布日期:2024-06-18
通信作者: 贾兴文,博士,教授。E-mail:jiaxingwen@126.com
作者简介:侯铁军(1977—),男,博士,教授。主要从事道路修复技术的研究。E-mail:howard2030@qq.com
基金资助:
青海省科技计划项目(2021-ZJ-733);西宁市科技计划项目(2023-Y-19)

Bond Strength and Influencing Factors of Magnesium Phosphate Cement Mortar and Concrete in Severe Cold Environment

HOU Tiejun¹, LI Xiang¹, ZHANG Chenchen¹, JIA Xingwen², HOU Pengkun³

1. Qinghai Communications Technical College, Xining 810003, China;
2. College of Materials Science and Engineering, Chongqing University, Chongqing 400045, China;
3. College of Materials Science and Engineering, University of Jinan, Jinan 250022, China

Received:2023-11-14 Revised:2024-01-16 Online:2024-06-15 Published:2024-06-18

摘要/Abstract

摘要： 在严寒环境下实施混凝土路面的快速修复,要求修复材料具有早期强度高且与混凝土粘结强度好的特点。磷酸镁水泥(MPC)早期强度高,采用MPC制备快速修复材料时有利于在无养护条件下实现冬季混凝土路面的快速修复。本文研究了在严寒环境下,镁磷质量比(M/P)、硼镁质量比(B/M)和水胶比(W/C)对MPC砂浆与普通混凝土的粘结强度的影响,分析了MPC砂浆与混凝土的界面粘结强度发展规律与粘结机制。结果表明,在严寒环境下,当M/P为4~5、B/M为0.02~0.03、W/C为0.12~0.14时更有利于提高MPC砂浆与普通混凝土的粘结强度,3 h粘结强度可达2.5 MPa,能满足严寒环境下混凝土路面的快速修复要求。

关键词: 磷酸镁水泥, 粘结强度, 严寒环境, 抗弯强度, 界面特征, 快速修复

Abstract: The rapid repair of concrete pavement under severe cold environment requires the repair materials to have high early strength and high bond strength with concrete. Using magnesium phosphate cement (MPC) with high early strength to prepare rapid repair materials is beneficial for achieving rapid repair of concrete pavement under non curing conditions in the winter. The effects of magnesium phosphorus ratio (M/P), boron magnesium ratio (B/M), and water cement ratio (W/C) on bond strength between MPC mortar and ordinary Portland cement concrete (OPC) in severe cold environment were studied, and the interface bonding mechanism were analyzed. The results show that M/P 4~5, B/M 0.02~0.03, and W/C 0.12~0.14 are more conducive to improve bond strength between MPC mortar and OPC in severe cold environment. The 3 h bond strength between MPC mortar and OPC can exceed 2.5 MPa, meeting the requirements for rapid repair of concrete pavement in severe cold environment.

Key words: magnesium phosphate cement, bond strength, severe cold environment, flexural strength, interface characteristic, rapid repair

中图分类号:

TU526

侯铁军, 李想, 张晨琛, 贾兴文, 侯鹏坤. 严寒环境下磷酸镁水泥砂浆与混凝土的粘结强度及影响因素研究[J]. 硅酸盐通报, 2024, 43(6): 2064-2072.

HOU Tiejun, LI Xiang, ZHANG Chenchen, JIA Xingwen, HOU Pengkun. Bond Strength and Influencing Factors of Magnesium Phosphate Cement Mortar and Concrete in Severe Cold Environment[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2024, 43(6): 2064-2072.

参考文献

[1] SEEHRA S S, GUPTA S, KUMAR S. Rapid setting magnesium phosphate cement for quick repair of concrete pavements: characterisation and durability aspects[J]. Cement and Concrete Research, 1993, 23(2): 254-266.
[2] YANG Q B, ZHU B R, ZHANG S Q, et al. Properties and applications of magnesia-phosphate cement mortar for rapid repair of concrete[J]. Cement and Concrete Research, 2000, 30(11): 1807-1813.
[3] HAQUE M A, CHEN B. Research progresses on magnesium phosphate cement: a review[J]. Construction and Building Materials, 2019, 211: 885-898.
[4] FENG H, SHAUKAT A J, RIN D, et al. Mechanical properties of high-ductility magnesium phosphate cement composite cured at low temperatures[J]. Journal of Building Engineering, 2021, 44: 103275.
[5] YUAN J, HUANG X, CHEN X, et al. Early-age mechanical properties and hydration degrees of magnesium phosphate cement paste in freezing winter of cold regions[J]. Construction and Building Materials, 2022, 345: 128337.
[6] LI Y, CHEN B. Factors that affect the properties of magnesium phosphate cement[J]. Construction and Building Materials, 2013, 47: 977-983.
[7] CHEN B, ODERJI S Y, CHANDAN S, et al. Feasibility of magnesium phosphate cement (MPC) as a repair material for ballastless track slab[J]. Construction and Building Materials, 2017, 154: 270-274.
[8] YANG Q B, ZHANG S Q, WU X L. Deicer-scaling resistance of phosphate cement-based binder for rapid repair of concrete[J]. Cement and Concrete Research, 2002, 32(1): 165-168.
[9] QIAO F, CHAU C K, LI Z J. Property evaluation of magnesium phosphate cement mortar as patch repair material[J]. Construction and Building Materials, 2010, 24(5): 695-700.
[10] YANG Q B, WU X L. Factors influencing properties of phosphate cement-based binder for rapid repair of concrete[J]. Cement and Concrete Research, 1999, 29(3): 389-396.
[11] LI Y, ZHANG G S, HOU D S, et al. Nanoscale insight on the initial hydration mechanism of magnesium phosphate cement[J]. Construction and Building Materials, 2021, 276: 122213.
[12] LI Y, SUN J, CHEN B. Experimental study of magnesia and M/P ratio influencing properties of magnesium phosphate cement[J]. Construction and Building Materials, 2014, 65: 177-183.
[13] YOU C, QIAN J S, QIN J H, et al. Effect of early hydration temperature on hydration product and strength development of magnesium phosphate cement (MPC)[J]. Cement and Concrete Research, 2015, 78: 179-189.
[14] SOUDÉE E, PÉRA J. Mechanism of setting reaction in magnesia-phosphate cements[J]. Cement and Concrete Research, 2000, 30(2): 315-321.
[15] JIA X W, LUO J Y, ZHANG W X, et al. Reaction characteristics and compressive strength of magnesia-phosphate cement at negative temperatures[J]. Construction and Building Materials, 2021, 305: 124819.
[16] 范英儒, 秦继辉, 汪宏涛, 等. 磷酸盐对磷酸镁水泥粘结性能的影响[J]. 硅酸盐学报, 2016, 44(2): 218-225.
FAN Y R, QIN J H, WANG H T, et al. Effect of phosphates on bond performance of magnesium phosphate cement[J]. Journal of the Chinese Ceramic Society, 2016, 44(2): 218-225 (in Chinese).
[17] LIU F, PAN B F, CAO P, et al. Multi-scale characterization on behaviors of the interface between magnesium phosphate cement and Portland cement[J]. Construction and Building Materials, 2021, 275: 122139.
[18] QIN J H, QIAN J S, YOU C, et al. Bond behavior and interfacial micro-characteristics of magnesium phosphate cement onto old concrete substrate[J]. Construction and Building Materials, 2018, 167: 166-176.
[19] 肖炳斐, 陈玥, 房琦, 等. 磷酸镁水泥复合材料的研究进展[J]. 功能材料, 2020, 51(8): 7-13.
XIAO B F, CHEN Y, FANG Q, et al. Research progresses on magnesium phosphate cement-based composites: a review[J]. Journal of Functional Materials, 2020, 51(8): 7-13 (in Chinese).
[20] WAGH A S. Chemically bonded phosphate ceramic coatings[M]. 2nd ed. Netherlands: Elsevier, 2016.