钢纤维喷射砂浆力学性能与流动度多因素正交试验分析

硅酸盐通报 ›› 2024, Vol. 43 ›› Issue (2): 466-477.

所属专题：水泥混凝土

钢纤维喷射砂浆力学性能与流动度多因素正交试验分析

潘慧敏, 张昊, 李梦谊, 谢少康, 赵庆新

燕山大学,城市固废无害化协同处置及利用河北省工程研究中心,秦皇岛 066004

收稿日期:2023-07-31 修订日期:2023-10-26 出版日期:2024-02-15 发布日期:2024-02-05
通信作者: 张昊,硕士研究生。E-mail:zh13315364941@163.com
作者简介:潘慧敏(1978—),女,博士,教授。主要从事高性能混凝土材料的研究。E-mail:hmpan2005@163.com
基金资助:
国家自然科学基金(51608469,52078450)

Multi-Factor Orthogonal Test Analysis of Mechanical Properties and Fluidity of Steel Fiber Sprayed Mortar

PAN Huimin, ZHANG Hao, LI Mengyi, XIE Shaokang, ZHAO Qingxin

Hebei Province Engineering Research Center for Harmless Synergistic Treatment and Recycling of Municipal Solid Waste, Yanshan University, Qinhuangdao 066004, China

Received:2023-07-31 Revised:2023-10-26 Online:2024-02-15 Published:2024-02-05

摘要/Abstract

摘要： 为探究基体因素对钢纤维喷射砂浆力学性能和流动度的影响,基于正交试验方法对砂浆试件进行了力学性能和流动度测试。结果表明:砂胶比(A)对劈裂抗拉强度的影响较大,对7 d抗压强度有一定的影响,对后期抗折强度影响特别显著;钢纤维掺量(B)对劈裂抗拉强度、前期抗折强度和前中期抗压强度的影响分别为特别显著、显著和不显著;速凝剂掺量(C)对7 d前抗压强度、中后期劈裂抗拉强度影响显著;粉煤灰掺量(D)仅对后期抗压强度的影响显著;前述四种因素掺量对流动度的影响均不显著。由层次分析法得到对抗压强度、抗折强度、劈裂抗拉强度和流动度改善效果最佳的配合比分别为A₁B₃C₃D₁、A₃B₃C₁D₂、A₃B₃C₃D₁、A₂B₁C₁D₃,由功效系数法得到综合最佳配合比为A₂B₃C₁D₂。钢纤维在基体中起桥接与锚固加强的作用,速凝剂在水化过程中消耗大量的Ca(OH)₂并生成钙矾石,促使喷射砂浆早期强度迅速提升。

关键词: 喷射砂浆, 钢纤维, 正交试验, 功效系数法, 微观分析

Abstract: In order to explore the influence of matrix factors on the mechanical properties and fluidity of steel fiber sprayed mortar, the mechanical properties and fluidity of mortar specimens were tested based on orthogonal test method. The results show that the ratio of sand to cement (A) has a great influence on the splitting tensile strength, and has a certain influence on 7 d compressive strength, and has a particularly significant effect on later flexural strength. The influence of steel fiber content (B) on splitting tensile strength, early flexural strength and early and middle compressive strength is particularly significant, significant and insignificant, respectively. The content of accelerator (C) has a significant effect on compressive strength before 7 d and the splitting tensile strength in middle and late stages. The content of fly ash (D) has significant influence on compressive strength in late stage. The four factors have no significant influence on fluidity. The optimal mix ratio of compressive strength, flexural strength, splitting tensile strength and fluidity are obtained by analytic hierarchy process as A₁B₃C₃D₁, A₃B₃C₁D₂, A₃B₃C₃D₁, A₂B₁C₁D₃, and the optimal mix ratio is obtained by efficiency coefficient method as A₂B₃C₁D₂. The steel fiber plays a bridging and anchoring strengthening role in matrix. During the hydration process, the accelerator consumes a large amount of Ca(OH)₂ and generates ettringite, which is the main reason for the rapid increase in early strength of sprayed mortar.

Key words: sprayed mortar, steel fiber, orthogonal test, efficiency coefficient method, microanalysis

中图分类号:

TU528.58

潘慧敏, 张昊, 李梦谊, 谢少康, 赵庆新. 钢纤维喷射砂浆力学性能与流动度多因素正交试验分析[J]. 硅酸盐通报, 2024, 43(2): 466-477.

PAN Huimin, ZHANG Hao, LI Mengyi, XIE Shaokang, ZHAO Qingxin. Multi-Factor Orthogonal Test Analysis of Mechanical Properties and Fluidity of Steel Fiber Sprayed Mortar[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2024, 43(2): 466-477.

参考文献

[1] 赵楠, 卿龙邦, 杨卓凡, 等. 不同龄期钢纤维增强水泥砂浆纤维拉拔试验与模拟研究[J]. 硅酸盐通报, 2021, 40(7): 2165-2173.
ZHAO N, QING L B, YANG Z F, et al. Experimental and numerical studies on fiber pull-out of steel fiber reinforced cement mortar at different ages[J]. Bulletin of the Chinese Ceramic Society, 2021, 40(7): 2165-2173 (in Chinese).
[2] 李建强. 高韧性纤维增强水泥基复合材料试验研究[D]. 西安: 长安大学, 2017.
LI J Q. Experimental study on high toughness fiber reinforced cement-based composites[D]. Xi'an: Chang'an University, 2017 (in Chinese).
[3] 杨晓, 赵蔚, 贾清秀, 等. 水泥基纤维复合材料研究进展[J]. 高分子通报, 2013(12): 21-30.
YANG X, ZHAO W, JIA Q X, et al. The research status of engineered cementitious composite[J]. Chinese Polymer Bulletin, 2013(12): 21-30 (in Chinese).
[4] 陈相宇. 纤维混凝土抗冲击性能的试验研究[D]. 大连: 大连理工大学, 2012.
CHEN X Y. Experimental study on impact resistance of fiber reinforced concrete[D]. Dalian: Dalian University of Technology, 2012 (in Chinese).
[5] 邓云飞, 金凌志, 何来, 等. 钢纤维聚合物水泥砂浆力学性能试验研究[J]. 井冈山大学学报(自然科学版), 2016, 37(6): 65-70.
DENG Y F, JIN L Z, HE L, et al. Experimental study of mechanical properties effects on polymer cement mortar and steel fibers[J]. Journal of Jinggangshan University (Natural Sciences Edition), 2016, 37(6): 65-70 (in Chinese).
[6] 陈慧敏. 钢-聚丙烯混杂纤维水泥基材料的性能研究[D]. 重庆: 西南大学, 2016.
CHEN H M. Study on properties of steel-polypropylene hybrid fiber cement-based materials[D]. Chongqing: Southwest University, 2016 (in Chinese).
[7] 白敏, 牛荻涛, 姜磊, 等. 钢纤维改善混凝土力学性能和微观结构的研究[J]. 硅酸盐通报, 2013, 32(10): 2084-2089.
BAI M, NIU D T, JIANG L, et al. Research on improving the mechanical properties and microstructure of concrete with steel fiber[J]. Bulletin of the Chinese Ceramic Society, 2013, 32(10): 2084-2089 (in Chinese).
[8] 张金龙, 马伟斌, 郭小雄, 等. 钢纤维喷射混凝土的弯曲韧性及工程应用[J]. 铁道建筑, 2022, 62(4): 98-101.
ZHANG J L, MA W B, GUO X X, et al. Bending toughness and engineering application of steel fiber shotcrete[J]. Railway Construction, 2022, 62(4): 98-101 (in Chinese).
[9] DÜZGÜN O A, GÜL R, AYDIN A C. Effect of steel fibers on the mechanical properties of natural lightweight aggregate concrete[J]. Materials Letters, 2005, 59(27): 3357-3363.
[10] PAJK M, PONIKIEWSKI T. Flexural behavior of self-compacting concrete reinforced with different types of steel fibers[J]. Construction and Building Materials, 2013, 47: 397-408.
[11] 何为, 薛卫东, 唐斌. 优化试验设计方法及数据分析[M]. 北京: 化学工业出版社, 2012.
HE W, XUE W D, TANG B, et al. Optimization experiment design method and data analysis[M]. Beijing: Chemical Industry Press, 2012 (in Chinese).
[12] 中华人民共和国住房和城乡建设部. 砌筑砂浆配合比设计规程: JGJ/T 98—2010[S]. 北京: 中国建筑工业出版社, 2011.
Ministry of Housing and Urban-Rural Development, PRC. Design specification for mixing ratio of masonry mortar: JGJ/T 98—2010[S]. Beijing: China Architecture and Building Press, 2010 (in Chinese).
[13] 国家市场监督管理总局, 国家标准化管理委员会. 水泥胶砂强度检验方法(ISO法): GB/T 17671—2021[S]. 北京: 中国标准出版社, 2021.
State Administration of Morket Supervision and Administration, National Standardization Management Committee. Test method for strength of cement mortar (ISO method): GB/T 17671—2021[S]. Beijing: Standards Press of China, 2021 (in Chinese).
[14] 王军, 高飞, 邱树恒, 等. 无碱液态高效水泥速凝剂的研制与速凝机理研究[J]. 混凝土与水泥制品, 2013(4): 14-17.
WANG J, GAO F, QIU S H, et al. Development of alkali-free liquid high-efficiency cement accelerator and study on its rapid setting mechanism[J]. China Concrete and Cement Products, 2013(4): 14-17 (in Chinese).
[15] 李悦, 蔡博群, 吴玉生, 等. 喷射混凝土用速凝剂的研究进展[J]. 混凝土, 2020(9): 121-125.
LI Y, CAI B Q, WU Y S, et al. Research progress of flash setting admixtures for shotcrete[J]. Concrete, 2020(9): 121-125 (in Chinese).
[16] 曾玻. 粉煤灰物理特性对水泥浆体力学性能及微观结构的影响[D]. 绵阳: 西南科技大学, 2016.
ZENG B. Effect of physical properties of fly ash on mechanical properties and microstructure of cement paste[D]. Mianyang: Southwest University of Science and Technology, 2016 (in Chinese).
[17] 李辉, 张志明, 陈裕佳, 等. 不同细度超细粉煤灰对砂浆及混凝土性能影响的研究[J]. 硅酸盐通报, 2016, 35(9): 2821-2825+2831.
LI H, ZHANG Z M, CHEN Y J, et al. Property comparision of ultra-fine fly ash with different fineness[J]. Bulletin of the Chinese Ceramic Society, 2016, 35(9): 2821-2825+2831 (in Chinese).
[18] 张学兵, 匡成钢, 方志, 等. 钢纤维粉煤灰再生混凝土强度正交试验研究[J]. 建筑材料学报, 2014, 17(4): 677-684+694.
ZHANG X B, KUANG C G, FANG Z, et al. Orthogonal experimental study on strength of steel fiber reinforced fly ash recycled concrete[J]. Journal of Building Materials, 2014, 17(4): 677-684+694 (in Chinese).
[19] 孟凡奇, 李广杰, 王庆兵, 等. 基于功效系数法的泥石流灾害预警研究[J]. 岩土力学, 2012, 33(3): 835-840.
MENG F Q, LI G J, WANG Q B, et al. Research on early warning of debris flow based on efficacy coefficient method[J]. Rock and Soil Mechanics, 2012, 33(3): 835-840 (in Chinese).

钢纤维喷射砂浆力学性能与流动度多因素正交试验分析

Multi-Factor Orthogonal Test Analysis of Mechanical Properties and Fluidity of Steel Fiber Sprayed Mortar

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	洪侨亨, 贺雄飞, 张明朗, 唐刚, 黄伟. 固废基盾构惰性同步注浆材料力学性能及抗水分散性研究[J]. 硅酸盐通报, 2024, 43(2): 617-626.
[2]	杨鑫, 于奎, 吉冯春, 聂堂哲, 李科, 白天. SiO₂/KH560改性玄武岩纤维混凝土力学性能研究[J]. 硅酸盐通报, 2024, 43(1): 102-112.
[3]	周文娟, 胡牛涛, 钮浩翔, 谢谦. 全固废再生流态混合料制备及性能研究[J]. 硅酸盐通报, 2024, 43(1): 257-267.
[4]	彭蔓, 高涌涛, 韩杨, 陈秀丽, 寇雄俊. 废旧钢纤维增强橡胶混凝土力学性能试验研究[J]. 硅酸盐通报, 2023, 42(9): 3286-3294.
[5]	王二成, 李格格, 柴颖珂, 张红春, 李彦苍, 王燕杰. 钢-剑麻混杂纤维再生混凝土断裂性能研究[J]. 硅酸盐通报, 2023, 42(8): 2754-2763.
[6]	龚明子, 潘阿馨, 张子龙, 王涛, 饶先鹏, 陈晨, 黄伟. 超高性能纤维增强混凝土中钢纤维拔出行为研究[J]. 硅酸盐通报, 2023, 42(8): 2764-2772.
[7]	李海礁, 王加军, 韩希平, 陶琦, 张仕龙. 大掺量矿物掺合料纤维增强轻骨料混凝土的抗疲劳性能[J]. 硅酸盐通报, 2023, 42(8): 2856-2864.
[8]	孙庭超, 曾德明, 曹明莉. 硅烷偶联剂改性钢纤维水泥基复合材料弯曲性能研究[J]. 硅酸盐通报, 2023, 42(7): 2326-2335.
[9]	王青, 高舒畅, 高嘉呈, 文长城, 徐港. 掺陶砂超高性能轻质混凝土的性能及其影响因素[J]. 硅酸盐通报, 2023, 42(6): 1996-2006.
[10]	曹锋, 乔宏霞, 张颖, 李双营, 赵紫岩. 新型生物质硅掺合料的活性及影响因素研究[J]. 硅酸盐通报, 2023, 42(6): 2140-2149.
[11]	吴礼程, 陈湘生, 雷江松, 郑爱元, 王雪涛, 邓一三. 基于三点开口梁弯曲试验分析3D端钩钢纤维混凝土抗弯性能[J]. 硅酸盐通报, 2023, 42(5): 1661-1671.
[12]	曹军平, 朱健, 高镇. 基于正交试验的EPS轻型混凝土配合比设计及性能研究[J]. 硅酸盐通报, 2023, 42(4): 1270-1281.
[13]	赵竞一, 王闻之, 王其琛, 符有杰, 段佳岐, 李铭涵, 姜宏. 自增韧锌尖晶石-透辉石微晶玻璃力学性能的研究[J]. 硅酸盐通报, 2023, 42(4): 1458-1465.
[14]	唐咸远, 马杰灵, 罗杰, 何滨冰, 陆澄剑. 钢渣微粉生态型超高性能混凝土力学性能影响因素分析[J]. 硅酸盐通报, 2023, 42(2): 607-617.
[15]	刘子仪, 宋少民. 基于响应面法的混杂纤维-复合胶凝材料体系优化设计[J]. 硅酸盐通报, 2023, 42(12): 4197-4207.