城市污泥尾矿陶粒的制备工艺及其性能与应用

硅酸盐通报 ›› 2023, Vol. 42 ›› Issue (4): 1374-1383.

所属专题：资源综合利用

城市污泥尾矿陶粒的制备工艺及其性能与应用

冯玉林¹, 高鸽¹, 柴喜林^2,3, 毛攀³, 董晶亮¹, 徐光前³, 黄柯靓³

1.华东交通大学土木建筑学院,南昌 330013;
2.江西万拓环境检测有限公司,上饶 334000;
3.江西盖亚环保科技有限公司,上饶 334000

收稿日期:2022-12-20 修订日期:2023-02-02 出版日期:2023-04-15 发布日期:2023-04-25
通信作者: 徐光前,工程师。E-mail:xugq@gaiyahb.cn
作者简介:冯玉林(1990—),男,博士,讲师。主要从事工程结构运维安全的研究。E-mail:fengyulin@ecjtu.edu.cn
基金资助:
国家自然科学基金(52268074);江西省自然科学基金(20224BAB214073);中国博士后科学基金面上项目(2022M713544);江西盖亚环保科技有限公司科研项目(HX2022-171,HX2020-086);江西省教育厅科学技术研究项目(GJJ2200646)

Preparation Process of Municipal Sludge Tailing Ceramsite and Its Performance and Application

FENG Yulin¹, GAO Ge¹, CHAI Xilin^2,3, MAO Pan³, DONG Jingliang¹, XU Guangqian³, HUANG Keliang³

1. School of Civil Engineering and Architecture, East China Jiaotong University, Nanchang 330013, China;
2. Jiangxi Wantuo Environmental Testing Co., Ltd., Shangrao 334000, China;
3. Jiangxi Gaia Environmental Protection Technology Co., Ltd., Shangrao 334000, China

Received:2022-12-20 Revised:2023-02-02 Online:2023-04-15 Published:2023-04-25

摘要/Abstract

摘要： 以城市污水处理厂污泥和德兴铜矿尾矿为主要原材料,经高温烧结制备陶粒,通过试验确定原材料配比和烧制工艺参数,分析陶粒的物理性能(堆积密度、表观密度、1 h吸水率、空隙率)、浸出液中重金属含量,以及陶粒对铅离子的吸附性;将陶粒以0%、20%、40%、60%、80%、100%(质量分数)的替代率替代普通混凝土中的碎石,研究混凝土的立方体抗压强度和劈裂抗拉强度变化。结果表明:按照m(污泥)∶m(尾矿)∶m(黏土)=2∶3∶1将原材料混合造粒,烧制工艺为(105±5) ℃干燥3 h,400 ℃预热15 min,1 000 ℃烧结12 min,制得陶粒的堆积密度为528 kg/m³,表观密度为1 004 kg/m³,1 h吸水率为7.64%,空隙率为47.37%;陶粒浸出液中重金属含量均低于国家标准的限值;烧结温度为960 ℃的陶粒在30 ℃恒温水浴锅加热条件下对铅离子的吸附率达到93.57%;掺入陶粒之后,随着陶粒替代率的升高,陶粒混凝土立方体抗压强度和劈裂抗拉强度表现为先增大后减小的变化趋势,当陶粒替代率为60%时,标准养护28 d的立方体试块抗压强度达到最大(35.38 MPa),当陶粒替代率为40%时,劈裂抗拉强度达到最大(5.8 MPa)。

关键词: 城市污泥, 尾矿, 陶粒, 制备工艺, 吸附, 铅离子, 陶粒混凝土

Abstract: In this paper, municipal sewage treatment plant sludge and Dexing copper mine tailings were used as the main raw materials to prepare ceramsite by high temperature sintering. The ratio of raw materials and sintering process parameters were determined by experiments. The physical properties (bulk density, apparent density, 1 h water absorption rate, void ratio) of ceramsite, heavy metal content in leaching solution, and the adsorption of lead ions by ceramsite were analyzed. The ceramsite was used to replace the gravel in ordinary concrete to varying degrees (0%, 20%, 40%, 60%, 80%, 100%, mass fraction), and the changes of cube compressive strength and splitting tensile strength of concrete were studied. The results show that the raw materials are mixed and granulated according to m(sludge)∶m(tailings)∶m(clay)=2∶3∶1, and the sintering process is drying at (105±5) ℃ for 3 h, preheating at 400 ℃ for 15 min, and sintering at 1 000 ℃ for 12 min. Then the bulk density of the prepared ceramsite is 528 kg/m³, the apparent density is 1 004 kg/m³, the 1 h water absorption rate is 7.64%, and the void ratio is 47.37%. The content of heavy metals in ceramsite leaching solution is lower than the limit of national standard. The adsorption rate of lead ions by ceramsite sintered at 960 ℃ reaches 93.57% under the condition of 30 ℃ constant temperature water bath. After adding ceramsite, with the increase of ceramsite replacement rate, the cubic compressive strength and splitting tensile strength of ceramsite concrete increase first and then decrease. When the ceramsite replacement rate is 60%, the compressive strength of the cubic test block cured for 28 d reaches the maximum of 35.38 MPa. When the ceramsite replacement rate is 40%, the splitting tensile strength reaches the maximum of 5.8 MPa.

Key words: municipal sludge, tailing, ceramsite, preparation process, adsorption, Pb²⁺, ceramsite concrete

中图分类号:

X705

冯玉林, 高鸽, 柴喜林, 毛攀, 董晶亮, 徐光前, 黄柯靓. 城市污泥尾矿陶粒的制备工艺及其性能与应用[J]. 硅酸盐通报, 2023, 42(4): 1374-1383.

FENG Yulin, GAO Ge, CHAI Xilin, MAO Pan, DONG Jingliang, XU Guangqian, HUANG Keliang. Preparation Process of Municipal Sludge Tailing Ceramsite and Its Performance and Application[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2023, 42(4): 1374-1383.

参考文献

[1] 解道雷, 孔慈明, 徐龙乾, 等. 城市污泥中重金属存在形态、去除及稳定化研究进展[J]. 化工进展, 2018, 37(1): 330-342.
XIE D L, KONG C M, XU L Q, et al. Developments of the speciation, removal and stabilization of heavy metals in municipal sludge[J]. Chemical Industry and Engineering Progress, 2018, 37(1): 330-342 (in Chinese).
[2] 李哲坤, 张立秋, 杜子文, 等. 城市污泥不同处理处置工艺路线碳排放比较[J]. 环境科学, 2022, 16(7): 1-14.
LI Z K, ZHANG L Q, DU Z W, et al. Comparison of carbon emissions in different treatment and disposal process routes of municipal sludge[J]. Environmental Science, 2022, 16(7): 1-14 (in Chinese).
[3] YANG T, HUANG H J, LAI F Y. Pollution hazards of heavy metals in sewage sludge from four wastewater treatment plants in Nanchang, China[J]. Transactions of Nonferrous Metals Society of China, 2017, 27(10): 2249-2259.
[4] 唐刚, 杨亚东, 刘秀玉, 等. 工业固体废弃物在阻燃材料领域的应用进展[J]. 化工矿物与加工, 2022, 51(11): 13-18.
TANG G, YANG Y D, LIU X Y, et al. Application progress of industrial solid waste in the field of flame retardant materials[J]. Industrial Minerals & Processing, 2022, 51(11): 13-18 (in Chinese).
[5] 顾晓薇, 艾莹莹, 赵昀奇, 等. 铁尾矿资源化利用现状[J/OL]. 中国有色金属学报, 2022: 1-29 (2022-01-13) [2022-12-19]. https://kns.cnki.net/kcms/detail/43.1238.TG.20220112.1844.002.html.
GU X W, AI Y Y, ZHAO Y Q, et al. Status quo of resource utilization of iron ore tailings[J/OL]. The Chinese Journal of Nonferrous Metals, 2022: 1-29 (2022-01-13) [2022-12-19]. https://kns.cnki.net/kcms/detail/43.1238.TG.20220112.1844.002.html (in Chinese).
[6] 王宏洋, 王旭, 陈海燕, 等. 尾矿库环境风险管控相关政策分析及建议[J/OL]. 环境科学研究, 2022, 43(12): 1-13 (2022-11-18) [2022-12-19]. https://doi.org/10.13198/j.issn.1001-6929.2022.11.16.
WANG H Y, WANG X, CHEN H Y, et al. Analysis and suggestions of environmental risk control strategy for tailings ponds[J/OL]. Research of Environmental Sciences, 2022, 43(12): 1-13 (2022-11-18) [2022-12-19]. https://doi.org/10.13198/j.issn.1001-6929.2022.11.16 (in Chinese).
[7] NAKOUZI S, MIELEWSKI D, BALL J C, et al. A novel approach to paint sludge recycling: reclaiming of paint sludge components as ceramic composites and their applications in reinforcement of metals and polymers[J]. Journal of Materials Research, 1998, 13(1): 53-60.
[8] 何必繁, 王里奥, 黄川, 等. 弧叶型旋转窑烧制污泥陶粒实验研究[J]. 环境工程学报, 2011, 5(4): 909-916.
HE B F, WANG L A, HUANG C, et al. Experimental study on producing ceramsite with sewage sludge in arc blade rotary kiln[J]. Chinese Journal of Environmental Engineering, 2011, 5(4): 909-916 (in Chinese).
[9] 徐振华. 污水厂污泥与河道底泥联合高温烧结制备陶粒的技术研究[D]. 北京: 清华大学, 2012: 25-44.
XU Z H. Technology research on sintering of ceramisite with sewage sludge and river sediment[D]. Beijing: Tsinghua University, 2012: 25-44 (in Chinese).
[10] 常成. 城市污泥制陶粒工艺的分析与研究[D]. 西安: 长安大学, 2014: 17-24.
CHANG C. Study and analysis on the city sludge ceramsite treatment process[D]. Xi'an: Chang'an University, 2014: 17-24 (in Chinese).
[11] 闫传霖. 金尾矿焙烧陶粒的制备与性能研究[D]. 济南: 济南大学, 2014: 7-17.
YAN C L. The preparation of gold tailings roasting ceramsite and its performance study[D]. Jinan: University of Jinan, 2014: 7-17 (in Chinese).
[12] FRANUS M, BARNAT-HUNEK D, WDOWIN M. Utilization of sewage sludge in the manufacture of lightweight aggregate[J]. Environmental Monitoring and Assessment, 2016, 188(1): 10.
[13] YANG Y H, WEI Z A, CHEN Y L, et al. Utilizing phosphate mine tailings to produce ceramisite[J]. Construction and Building Materials, 2017, 155: 1081-1090.
[14] 荣辉, 张鸿飞, 张磊, 等. 污泥陶粒焙烧制度优化及其对陶粒性能的影响[J]. 新型建筑材料, 2019, 46(4): 68-72+87.
RONG H, ZHANG H F, ZHANG L, et al. Optimization of sludge ceramsite baking system and its effect on ceramsite performance[J]. New Building Materials, 2019, 46(4): 68-72+87 (in Chinese).
[15] 胡晨光, 邢崇恩, 刘蕾, 等. 铁尾矿与碱渣基核壳高强陶粒的制备与性能研究[J]. 金属矿山, 2019(5): 197-203.
HU C G, XING C E, LIU L, et al. Preparation and performance of high-strength ceramisite with core-shell structure based on iron tailings and alkaline residue[J]. Metal Mine, 2019(5): 197-203 (in Chinese).
[16] 张晓亚, 冯丽娟, 王济, 等. 城市污泥/磷尾矿陶粒的烧结条件及性能研究[J]. 地球环境学报, 2021, 12(4): 447-454.
ZHANG X Y, FENG L J, WANG J, et al. Research on sintering conditions and performance of municipal sludge/phosphate tailings ceramsite[J]. Journal of Earth Environment, 2021, 12(4): 447-454 (in Chinese).
[17] RILEY C M. Relation of chemical properties to the bloating of clays[J]. Journal of the American Ceramic Society, 1951, 34(4): 121-128.
[18] 许开成, 方苇, 陈梦成, 等. 陶瓷再生粗骨料混凝土力学性能研究[J]. 实验力学, 2014, 29(4): 474-480.
XU K C, FANG W, CHEN M C, et al. On the mechanical properties of ceramic recycled coarse aggregate concrete[J]. Journal of Experimental Mechanics, 2014, 29(4): 474-480 (in Chinese).
[19] 黄宏, 曾建涛, 王伊. 取代率对再生陶瓷粗骨料混凝土抗压强度的影响[J]. 华东交通大学学报, 2022, 9(2): 27-34.
HUANG H, ZENG J T, WANG Y. Influence of replacement rate on compressive strength of recycled ceramic coarse aggregate concrete[J]. Journal of East China Jiaotong University, 2022, 39(2): 27-34 (in Chinese).
[20] 李玉平, 王伟, 章鹏, 等. 矿物掺合料对页岩陶粒混凝土抗压强度的影响[J]. 湖南大学学报(自然科学版), 2018, 45(6): 72-77.
LI Y P, WANG W, ZHANG P, et al. Influence of mineral admixture addition on compressive strength of shale ceramsite concrete[J]. Journal of Hunan University (Natural Sciences), 2018, 45(6): 72-77 (in Chinese).

城市污泥尾矿陶粒的制备工艺及其性能与应用

Preparation Process of Municipal Sludge Tailing Ceramsite and Its Performance and Application

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	周丽娜, 蔡颖, 马财龙, 罗玲. 水滑石复合水泥基材料氯离子吸附能力的研究进展[J]. 硅酸盐通报, 2023, 42(4): 1137-1147.
[2]	唐佩, 蒋事成, 邓腾飞, 陈伟. 固废基自发泡烧胀陶粒设计与性能研究[J]. 硅酸盐通报, 2023, 42(4): 1384-1392.
[3]	朱振中, 刘元珍, 王文婧, 王鲜星, 段鹏飞. 玄武岩纤维陶粒混凝土抗裂性能与热工性能试验研究[J]. 硅酸盐通报, 2023, 42(3): 908-916.
[4]	宁旭文, 杨浪, 饶峰, 孙传琳, 方屹, 张凯铭. 铁尾矿在电磁吸波建筑材料中的研究进展[J]. 硅酸盐通报, 2023, 42(3): 925-938.
[5]	潘正华, 蒋亚清, 赵文昊. 发泡浆体流变特性对轻质混凝土匀质性的影响[J]. 硅酸盐通报, 2023, 42(2): 471-477.
[6]	赵珂萍, 李晓玉, 李瑞红, 李浩然, 杨天佐, 犹家进, 彭康. 固废源CaO基CO₂捕集材料的制备与捕集性能研究进展[J]. 硅酸盐通报, 2023, 42(2): 520-530.
[7]	陈辛, 曾祥会, 方伟, 何漩, 杜星, 王大珩, 李薇馨, 赵雷, 陈辉. 二次铝灰制备高强度陶粒及其性能研究[J]. 硅酸盐通报, 2023, 42(2): 618-625.
[8]	申文凯, 元强, 纪友红, 曾荣, 李巍, 李富民, 史才军. 剪切速率和温度对低水胶比水泥浆流变性能的影响[J]. 硅酸盐通报, 2023, 42(1): 48-56.
[9]	陈邢, 于峰, 曹越, 方圆. 铁尾矿粉-脱硫灰胶凝材料的制备及性能研究[J]. 硅酸盐通报, 2023, 42(1): 180-187.
[10]	徐伟, 鲁亚, 刘松柏, 肖民, 陈忠发, 魏琦, 严峻. 碱激发-碳养护对铜尾矿固化砖的作用机理研究[J]. 硅酸盐通报, 2023, 42(1): 188-195.
[11]	赵莉, 席晓晶, 高杰, 李扬, 马晓梦, 张慧盈, 魏敏洁, 陈华军, 田文杰. 新生态MnO₂的制备及其对2,4-二硝基苯酚吸附性能的影响[J]. 硅酸盐通报, 2023, 42(1): 295-301.
[12]	张啸, 王璜琪, 王栋民. 黄金尾矿制备水泥和混凝土的研究进展[J]. 硅酸盐通报, 2022, 41(9): 3121-2128.
[13]	刘名扬, 周彬, 颜峰, 陈龙江, 侯美晴. 铁尾矿-钢渣集料微表处混合料路用性能及耐久性试验研究[J]. 硅酸盐通报, 2022, 41(9): 3176-3189.
[14]	马桂红, 张青, 耿忠, 于海宝. 生物模板法制备离子印迹磁性微马达及污水中Pb²⁺动态去除的研究[J]. 硅酸盐通报, 2022, 41(9): 3324-3334.
[15]	殷玉兰, 陈俊宏, 谢燕, 敖先权. F^-在方解石表面的吸附及其对方解石表面性质的影响[J]. 硅酸盐通报, 2022, 41(8): 2785-2791.