真空去水压制成型对机制砂混凝土性能的影响

摘要/Abstract

摘要： 为顺应当今建筑工业化和固废资源化趋势,工程界提出了采用真空去水压制成型新工艺,以实现机制砂混凝土的高效预制生产。本文研究了真空去水压制成型时间对不同初始水灰比(W/C)机制砂混凝土性能的影响,结果表明:与天然砂混凝土相比,真空去水压制能更显著提升机制砂混凝土的强度,主要是由于在高密实成型条件下,机制砂充分发挥了嵌锁效应,经真空负压-0.07 MPa及压制15 MPa处理100 s后,机制砂混凝土初始W/C从0.58降低至0.32,抗压强度提升了44.6%,延长处理时间性能提升效果减弱,尤其是对W/C较小的混凝土;压汞测孔(MIP)发现真空去水压制后混凝土硬化体孔隙率大幅降低,尤其是大于50 nm的有害孔,与压制前相比,其比例下降均超过70%,孔径分布得到了改善,且水化程度均提高至0.6以上;扫描电子显微镜(SEM)和X射线衍射(XRD)表明,经真空去水压制处理后,混凝土内硬化浆体变得更密实,定向排列的针状钙矾石及片状Ca(OH)₂含量减少,而界面过渡区(ITZ)黏结性能提高。采用真空去水压制成型机制砂混凝土,符合现代预制混凝土构件生产的绿色、节能、环保发展要求。

关键词: 机制砂混凝土, 预制构件, 真空去水, 压制, 孔结构, 微观组织

Abstract: In order to adapt to the current trend of building industrialization and solid waste recycling, a new technology of vacuum water-removal and compression was proposed in the engineering field to achieve a highly efficient pre-fabrication of machine-made sand concrete. In this study, the effect of the time of vacuum water-removal and compression treatment on the performances of machine-made sand concrete with varied initial water-to-cement ratio (W/C) was investigated. Results show that vacuum water-removal and compression can significantly improve the strength of machine-made sand concrete as compared to natural sand concrete, primarily due to the locking effect of the machine-made sand under the condition of high compaction by the treatment. The initial W/C of machine-made sand concrete decreases from 0.58 to 0.32 and the compressive strength increases by 44.6% after being treated with -0.07 MPa vacuum pressure and 15 MPa compression for 100 s. However, the improvement of performances weakens with prolonged treatment time, especially for concrete with lower W/C. Mercury intrusion porosimetry (MIP) results reveal that the porosity of concrete decreases significantly after vacuum water-removal and compression treatment. In particular, the proportion of capillary pores with pore size larger than 50 nm decreases by more than 70%. Thus, the pore size distribution is improved. The hydration degree also increases to more than 0.6. Scanning electron microscopy (SEM) and X-ray diffraction (XRD) show that the hardened paste in concrete is densified, the amounts of aligned needle-shaped ettringite and plate-shaped Ca(OH)₂ are reduced, and the bonding property of interfacial transition zone (ITZ) is improved by vacuum water-removal and compression. The machine-made sand concrete fabricated by vacuum water-removal and compression is in line with the developing trend of green, energy saving and environmental protection for the production of modern pre-cast concrete members.

Key words: machine-made sand concrete, precast member, vacuum water-removal, compression, pore structure, microstructure

中图分类号:

TU526

周朋, 王有旗, 赵双林, 刘普前, 崔立朕, 孟勇, 徐晶, 詹培敏. 真空去水压制成型对机制砂混凝土性能的影响[J]. 硅酸盐通报, 2023, 42(2): 478-486.

ZHOU Peng, WANG Youqi, ZHAO Shuanglin, LIU Puqian, CUI Lizhen, MENG Yong, XU Jing, ZHAN Peimin. Influence on Performances of Machine-Made Sand Concrete Fabricated by Vacuum Water-Removal and Compression Technique[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2023, 42(2): 478-486.

参考文献

[1] 吴杰, 朱敏涛, 陈兆荣, 等. 新型预制混凝土构件生产技术研究及工艺装备开发[J]. 混凝土世界, 2018(12): 42-51.
WU J, ZHU M T, CHEN Z R, et al. Research on production technology and development of equipment for new precast concrete components[J]. China Concrete, 2018(12): 42-51 (in Chinese).
[2] 夏冬桃, 李向阳, 胡军安. 基于正交试验的透水再生混凝土性能优化试验研究[J]. 硅酸盐通报, 2022, 41(8): 2748-2758.
XIA D T, LI X Y, HU J A. Experimental study on performance optimization of pervious recycled concrete based on orthogonal test[J]. Bulletin of the Chinese Ceramic Society, 2022, 41(8): 2748-2758 (in Chinese).
[3] 黄克宝, 石箭光, 贺阳, 等. 干硬性混凝土制品成型工艺研究综述[J]. 混凝土与水泥制品, 2018(5): 45-47.
HUANG K B, SHI J G, HE Y, et al. Review of preparation technology of dry concrete products[J]. China Concrete and Cement Products, 2018(5): 45-47 (in Chinese).
[4] 程刚, 王乾. 路沿石压制成型新工艺[J]. 科技创新与应用, 2020, 10(24): 29-31.
CHENG G, WANG Q. New technology of pressing and forming along the road[J]. Technology Innovation and Application, 2020, 10(24): 29-31 (in Chinese).
[5] ESKANDARI-NADDAF H, AZIMI-POUR M. Performance evaluation of dry-pressed concrete curbs with variable cement grades by using Taguchi method[J]. Ain Shams Engineering Journal, 2018, 9(4): 1357-1364.
[6] 徐自明, 王乾. 新型仿花岗岩混凝土路缘石成型装置设计与试验研究[J]. 混凝土与水泥制品, 2019(12): 83-86.
XU Z M, WANG Q. Design and experimental study of new imitation granite concrete curb stone forming device[J]. China Concrete and Cement Products, 2019(12): 83-86 (in Chinese).
[7] 欧阳幼玲, 傅勇明, 钱文勋, 等. 真空脱水工艺在港工混凝土中的应用研究[J]. 珠江水运, 2022(2): 85-88.
OUYANG Y L, FU Y M, QIAN W X, et al. Study on the application of vacuum dewatering technology in port concrete[J]. Pearl River Water Transport, 2022(2): 85-88 (in Chinese).
[8] 姚文飞. 道路施工中混凝土真空处理技术的应用研究[J]. 科技与创新, 2017(18): 154-155.
YAO W F. Research on application of vacuum treatment technology of concrete in road construction[J]. Science and Technology & Innovation, 2017(18): 154-155 (in Chinese).
[9] 赵浩. 真空压浆技术在预应力混凝土桥梁施工中的应用[J]. 交通世界, 2021(25): 55-56.
ZHAO H. Application of vacuum grouting technology in prestressed concrete bridge construction[J]. TranspoWorld, 2021(25): 55-56 (in Chinese).
[10] 欧阳幼玲, 傅勇明, 钱文勋, 等. 真空脱水工艺下的混凝土性能[J]. 水利水运工程学报, 2022(3): 66-73.
OUYANG Y L, FU Y M, QIAN W X, et al. Performance of concrete with vacuum dewatering process[J]. Hydro-Science and Engineering, 2022(3): 66-73 (in Chinese).
[11] 杨森, 闫涛, 龚英. 真空脱水工艺对干硬性混凝土性能影响的研究[J]. 水电站设计, 2021, 37(4): 92-94.
YANG S, YAN T, GONG Y. Effect of vacuum dehydration technology on dry concrete property[J]. Design of Hydroelectric Power Station, 2021, 37(4): 92-94 (in Chinese).
[12] 卢自立, 杨振国, 沈卫国, 等. 机制砂混凝土配比设计参数研究[J]. 武汉理工大学学报, 2014, 36(12): 32-36.
LU Z L, YANG Z G, SHEN W G, et al. Proportion design parameter of manufactured sand concrete[J]. Journal of Wuhan University of Technology, 2014, 36(12): 32-36 (in Chinese).
[13] 高志坚. 机制砂特性对混凝土性能的影响研究[J]. 广东建材, 2022, 38(2): 5-7.
GAO Z J. Study on the influence of machine-made sand characteristics on concrete performance[J]. Guangdong Building Materials, 2022, 38(2): 5-7 (in Chinese).
[14] 中华人民共和国住房和城乡建设部. 普通混凝土拌合物性能试验方法标准: GB/T 50080—2016[S]. 北京: 中国建筑工业出版社, 2016.
Ministry of Housing and Urban-Rural Development, PRC. Standard of test method for performance of ordinary concrete mixture: GB/T 50080—2016[S]. Beijing: China Architecture and Building Press, 2016 (in Chinese).
[15] 中华人民共和国住房和城乡建设部, 国家市场监督管理总局. 混凝土物理力学性能试验方法标准: GB/T 50081—2019[S]. 北京: 中国建筑工业出版社, 2019.
Ministry of Housing and Urban-Rural Development, PRC, State Administration for Market Regulation. Test method standard for physical and mechanical properties of concrete: GB/T 50081—2019[S]. Beijing: China Architecture and Building Press, 2019 (in Chinese).
[16] MEHTA P K, MONTEIRO P J M. Concrete: microstructure, properties, and materials[M]. Fourth New Jersey: McGraw-Hill Professional Pub, 2013.
[17] ZHAN P M, XU J, WANG J, et al. Multi-scale study on synergistic effect of cement replacement by metakaolin and typical supplementary cementitious materials on properties of ultra-high performance concrete[J]. Construction and Building Materials, 2021, 307: 125082.
[18] MINDESS S, YOUNG J F, DARWIN D. Concrete[M]. 2nd ed. New York: Prentice Hall, 2002.
[19] 徐晶, 王先志. 纳米二氧化硅对混凝土界面过渡区的改性机制及其多尺度模型[J]. 硅酸盐学报, 2018, 46(8): 1-5.
XU J, WANG X Z. Effect of nano-silica modification on interfacial transition zone in concrete and its multiscale modelling[J]. Journal of the Chinese Ceramic Society, 2018, 46(8): 1-5 (in Chinese).