矿物掺合料对UHPC性能的影响

硅酸盐通报 ›› 2022, Vol. 41 ›› Issue (9): 3170-3175.

矿物掺合料对UHPC性能的影响

赵雅明¹, 张振², 王畔¹, 张明飞³

1.中铁建设集团有限公司,北京 100040;
2.长安大学公路学院,西安 710064;
3.郑州航空工业管理学院土木建筑学院,郑州 450046

收稿日期:2022-05-13 修回日期:2022-06-23 出版日期:2022-09-15 发布日期:2022-09-27
通讯作者: 张明飞,博士,讲师。E-mail:zhangmingfeiyanjiu@163.com
作者简介:赵雅明(1981—),男,高级工程师。主要从事交通基础设施施工与管理工作。E-mail:ZhaoY198105@163.com
基金资助:
国家自然科学基金(41902266);中铁建设集团有限公司2022年度科技研发计划(22-76D)

Influences of Mineral Admixtures on UHPC Performance

ZHAO Yaming¹, ZHANG Zhen², WANG Pan¹, ZHANG Mingfei³

1. China Railway Construction Group Co., Ltd., Beijing 100040, China;
2. School of Highway, Chang'an University, Xi'an 710064, China;
3. School of Civil Engineering and Architecture, Zhengzhou University of Aeronautics, Zhengzhou 450046, China

Received:2022-05-13 Revised:2022-06-23 Online:2022-09-15 Published:2022-09-27

摘要/Abstract

摘要： 传统超高性能混凝土(UHPC)的硅灰用量一般都比较高,导致其制作成本较高,而且自收缩比较大,对实际工程应用造成了一定的影响。本文用粉煤灰和矿粉部分或全部替代硅灰制备UHPC,并对其工作性能、力学性能、自收缩及孔结构特征进行了试验研究。结果表明:采用粉煤灰或矿粉替代硅灰可以改善UHPC拌合物的流动性,替代率越高,拌合物的流动度越大;当采用粉煤灰或矿粉替代50%(质量分数)硅灰时,在标准养护下,对28 d抗压强度的影响较小,而在高温蒸养下,则会导致28 d抗压强度下降,当替代率达到100%(质量分数)时,无论是标准养护还是高温蒸养,都会显著降低28 d抗压强度;采用粉煤灰或矿粉替代硅灰能降低细孔的占比,增大孔径,减少自收缩,且粉煤灰对于自收缩的抑制效果优于矿粉。

关键词: 超高性能混凝土, 矿物掺合料, 强度, 自收缩, 孔结构

Abstract: For traditional ultra-high performance concrete (UHPC), the dosage of silica fume is generally high, resulting in high production cost and large autogenous shrinkage, which has a certain impact on its practical engineering application. In this paper, UHPC was prepared by partly or completely replacing silica fume with fly ash and mineral powder. The working performance, mechanical properties, autogenous shrinkage and pore structure characteristics of UHPC were studied. The results show that the replacement of silica fume by fly ash or mineral powder improves the fluidity of UHPC mixture. The higher the replacement rate is, the greater the fluidity of the mixture is. When 50% (mass fraction) silica fume is replaced by fly ash or mineral powder, the influence on 28 d compressive strength is small under standard curing, while for high temperature steam curing, the 28 d compressive strength decreases. When the replacement rate reaches 100% (mass fraction), the 28 d compressive strength is significantly reduced under standard curing or high temperature steam curing. Fly ash or mineral powder instead of silica fume reduces the proportion of fine pores, increases pore size and reduces autogenous shrinkage, and the inhibitory effect of fly ash on autogenous shrinkage is better than that of mineral powder.

Key words: ultra-high performance concrete, mineral admixture, strength, autogenous shrinkage, pore structure

中图分类号:

TU528

赵雅明, 张振, 王畔, 张明飞. 矿物掺合料对UHPC性能的影响[J]. 硅酸盐通报, 2022, 41(9): 3170-3175.

ZHAO Yaming, ZHANG Zhen, WANG Pan, ZHANG Mingfei. Influences of Mineral Admixtures on UHPC Performance[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(9): 3170-3175.

参考文献

[1] 陈宝春,韦建刚,苏家战,等.超高性能混凝土应用进展[J].建筑科学与工程学报,2019,36(2):10-20.
CHEN B C, WEI J G, SU J Z, et al. State-of-the-art progress on application of ultra-high performance concrete[J]. Journal of Architecture and Civil Engineering, 2019, 36(2): 10-20 (in Chinese).
[2] 邵旭东,邱明红,晏班夫,等.超高性能混凝土在国内外桥梁工程中的研究与应用进展[J].材料导报,2017,31(23):33-43.
SHAO X D, QIU M H, YAN B F, et al. A review on the research and application of ultra-high performance concrete in bridge engineering around the world[J]. Materials Review, 2017, 31(23): 33-43 (in Chinese).
[3] 王德辉,史才军,吴林妹.超高性能混凝土在中国的研究和应用[J].硅酸盐通报,2016,35(1):141-149.
WANG D H, SHI C J, WU L M. Research and applications of ultra-high performance concrete(UHPC) in China[J]. Bulletin of the Chinese Ceramic Society, 2016, 35(1): 141-149 (in Chinese).
[4] BRÜHWILER E, DENARIÉ E. Rehabilitation and strengthening of concrete structures using ultra-high performance fibre reinforced concrete[J]. Structural Engineering International, 2013, 23(4): 450-457.
[5] RICHARD P, CHEYREZY M. Composition of reactive powder concretes[J]. Cement and Concrete Research, 1995, 25(7): 1501-1511.
[6] HEIKAL M, ALEEM S A E, MORSI W M. Characteristics of blended cements containing nano-silica[J]. HBRC Journal, 2013, 9(3): 243-255.
[7] ABDELAZIZ M A, EL-ALEEM S A, MENSHAWY W M. Effect of fine materials in local quarry dusts of limestone and basalt on the properties of Portland cement pastes and mortars[J]. Int. J. Eng. Res, 2014, 3: 1038-1056.
[8] Ultra high performance concrete(UHPC)[C]//Proceedings of the Second International Symposium on Ultra High Performance Concrete. Kassel, Germany, 2008.
[9] 明阳,陈平,李玲,等.超高性能混凝土的配制及性能研究[J].非金属矿,2021,44(4):26-29.
MING Y, CHEN P, LI L, et al. Research and application of ultra high performance concrete powdery material[J]. Non-Metallic Mines, 2021, 44(4): 26-29 (in Chinese).
[10] LURA P, JENSEN O M, WEISS J. Cracking in cement paste induced by autogenous shrinkage[J]. Materials and Structures, 2009, 42(8): 1089-1099.
[11] MEDDAH M S, TAGNIT-HAMOU A. Pore structure of concrete with mineral admixtures and its effect on self-desiccation shrinkage[J]. ACI Materials Journal, 2009, 106(3): 241-250.
[12] 刘建忠,孙伟,缪昌文,等.矿物掺合料对低水胶比混凝土干缩和自收缩的影响[J].东南大学学报(自然科学版),2009,39(3):580-585.
LIU J Z, SUN W, MIAO C W, et al. Effect of mineral admixtures on drying and autogenous shrinkage of concrete with low water-to-binder ratio[J]. Journal of Southeast University (Natural Science Edition), 2009, 39(3): 580-585 (in Chinese).
[13] 刘宇,黎梦圆,阎培渝.矿物掺合料对胶凝材料浆体流变性能和触变性的影响[J].硅酸盐学报,2019,47(5):594-601.
LIU Y, LI M Y, YAN P Y. Effect of mineral admixtures on rheological properties and thixotropy of binder paste[J]. Journal of the Chinese Ceramic Society, 2019, 47(5): 594-601 (in Chinese).
[14] 于本田,王起才,周立霞,等.矿物掺合料与水胶比对混凝土耐久性的影响研究[J].硅酸盐通报,2012,31(2):391-395+410.
YU B T, WANG Q C, ZHOU L X, et al. Research on effects of mineral admixture and water to binder ratio on durability of concrete[J]. Bulletin of the Chinese Ceramic Society, 2012, 31(2): 391-395+410 (in Chinese).
[15] 陈宝春,李聪,黄伟,等.超高性能混凝土收缩综述[J].交通运输工程学报,2018,18(1):13-28.
CHEN B C, LI C, HUANG W, et al. Review of ultra-high performance concrete shrinkage[J]. Journal of Traffic and Transportation Engineering, 2018, 18(1): 13-28 (in Chinese).
[16] MADANI H, BAGHERI A, PARHIZKAR T. The pozzolanic reactivity of monodispersed nanosilica hydrosols and their influence on the hydration characteristics of Portland cement[J]. Cement and Concrete Research, 2012, 42(12): 1563-1570.
[17] LI Y, BAO J L, GUO Y L. The relationship between autogenous shrinkage and pore structure of cement paste with mineral admixtures[J]. Construction and Building Materials, 2010, 24(10): 1855-1860.