红砂岩集料对水稳基层强度与抗软化性能的影响

硅酸盐通报 ›› 2022, Vol. 41 ›› Issue (9): 3138-3147.

红砂岩集料对水稳基层强度与抗软化性能的影响

陈福玲¹, 温郁斌², 单俊鸿¹, 魏杰², 周明凯³, 高鹏⁴

1.河北工程大学土木工程学院,邯郸 056000;
2.山西昔榆高速公路有限公司,晋中 030600;
3.武汉理工大学材料科学与工程学院,武汉 430070;
4.长治市武理工工程技术研究院,长治 046000

收稿日期:2022-05-15 修回日期:2022-06-18 出版日期:2022-09-15 发布日期:2022-09-27
通讯作者: 单俊鸿,博士,教授。E-mail:hopeshan@163.com
作者简介:陈福玲(1998—),女,硕士研究生。主要从事道路固废材料的研究。E-mail:1903653994@qq.com

Influence of Red Sandstone Aggregate on Strength and Softening Resistance Performance of Cement Stabilized Base

CHEN Fuling¹, WEN Yubin², SHAN Junhong¹, WEI Jie², ZHOU Mingkai³, GAO Peng⁴

1. College of Civil Engineering, Hebei University of Engineering, Handan 056000, China;
2. Shanxi Xiyu Expressway Co., Ltd., Jinzhong 030600, China;
3. School of Materials Science and Engineering, Wuhan University of Technology, Wuhan 430070, China;
4. Institute of Wuhan University of Technology in Changzhi, Changzhi 046000, China

Received:2022-05-15 Revised:2022-06-18 Online:2022-09-15 Published:2022-09-27

摘要/Abstract

摘要： 红砂岩具有遇水软化的特性,通过与石灰岩集料对比,研究了红砂岩粗、细集料硬度与抗软化性能及其对水泥稳定基层(水稳基层)强度与抗软化性能的影响规律,并通过界限含水率、XRD与SEM测试,对比了红砂岩、石灰岩集料浸水前后的矿物成分与微观形貌。结果表明,红砂岩集料浸水后质量减少,硬度降低,抗软化性变差,制备的红砂岩水稳基层强度、软化系数低于石灰岩水稳基层,但红砂岩粗集料制备的水稳基层强度、软化系数降低幅度小于红砂岩细集料制备的水稳基层。红砂岩集料中的黏土矿物遇水崩解剥落、膨胀疏松化是红砂岩水稳基层强度、软化系数降低的主要原因。本研究可以为红砂岩在路面基层材料中的组成设计与工程应用提供理论参考。

关键词: 红砂岩集料, 路面基层, 强度, 抗软化性能, 黏土矿物, 软化崩解

Abstract: Red sandstone has the characteristic of water softening. By comparing with limestone aggregate, the hardness and softening resistance performance of coarse and fine aggregate of red sandstone were studied. Then the influence law of red sandstone aggregate on the strength and softening resistance performance ofcement stabilized base were studied. The mineral composition and microstructure of red sandstone and limestone aggregate before and after immersion were compared by boundary moisture content measurement, XRD and SEM examination. The results show that the weight and hardness of red sandstone aggregate decrease after immersion, and the softening resistance performance becomes worse. The strength and softening coefficient of cement stabilized red sandstone base are lower than those ofcement stabilized limestone base, but the decreasing degree of strength and softening coefficient of cement stabilized red sandstone coarse aggregate base is less than those of cement stabilized red sandstone fine aggregate base. The main reason for the decrease of strength and softening coefficient of cement stabilized red sandstone base is that clay minerals in red sandstone aggregate are disintegrated and expanded in water. This study provides theoretical reference for the composition design and application of red sandstone in pavement base.

Key words: red sandstone aggregate, pavement base, strength, softening resistance performance, clay mineral, softening and disintegration

中图分类号:

U414

陈福玲, 温郁斌, 单俊鸿, 魏杰, 周明凯, 高鹏. 红砂岩集料对水稳基层强度与抗软化性能的影响[J]. 硅酸盐通报, 2022, 41(9): 3138-3147.

CHEN Fuling, WEN Yubin, SHAN Junhong, WEI Jie, ZHOU Mingkai, GAO Peng. Influence of Red Sandstone Aggregate on Strength and Softening Resistance Performance of Cement Stabilized Base[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(9): 3138-3147.

参考文献

[1] 沈卫国,郑小平,王庆,等.柔性半柔性路面基层的服役情况调研[J].武汉理工大学学报,2021,43(12):1-6.
SHEN W G, ZHENG X P, WANG Q, et al. Service investigation of flexible and semi-flexible road base[J]. Journal of Wuhan University of Technology, 2021, 43(12): 1-6 (in Chinese).
[2] 沈卫国,胡金强,李瑞林,等.大掺量粉煤灰路面基层专用水泥性能研究[J].武汉理工大学学报,2009,31(12):15-19.
SHEN W G, HU J Q, LI R L, et al. Properties of the high volume fly-ash special purpose cement for road base stabilization[J]. Journal of Wuhan University of Technology, 2009, 31(12): 15-19 (in Chinese).
[3] 刘晓明,熊力,罗卫华.通平高速公路红砂岩崩解的微观特性[J].公路交通科技,2011,28(10):7-11.
LIU X M, XIONG L, LUO W H. Micro characteristics of disintegration of red sandstone of Tongcheng-Pingjiang expressway[J]. Journal of Highway and Transportation Research and Development, 2011, 28(10): 7-11 (in Chinese).
[4] 林志红,王俊杰.红砂岩遇水崩解软化机理的试验研究[J].路基工程,2019(3):94-98.
LIN Z H, WANG J J. Experimental research on water disintegration and softening mechanism of red sandstone[J]. Subgrade Engineering, 2019(3): 94-98 (in Chinese).
[5] 吴道祥,刘宏杰,王国强.红层软岩崩解性室内试验研究[J].岩石力学与工程学报,2010,29(s2):4173-4179.
WU D X, LIU H J, WANG G Q. Laboratory experimental study of slaking characteristics of red-bed soft rock[J]. Chinese Journal of Rock Mechanics and Engineering, 2010, 29(s2): 4173-4179 (in Chinese).
[6] 周勇.水泥稳定砂岩碎石混合料的力学性能研究[D].重庆:重庆交通大学,2018.
ZHOU Y. Study on mechanical properties of cement stabilized sandstone crushed stone mixture[D]. Chongqing: Chongqing Jiaotong University, 2018 (in Chinese).
[7] 周哲,陈善雄,戴张俊,等.基于点荷载试验的新生代红砂岩强度软化规律研究[J].岩土力学,2021,42(11):2997-3007.
ZHOU Z, CHEN S X, DAI Z J, et al. Study on strength softening law of Cenozoic red sandstone based on point load test[J]. Rock and Soil Mechanics, 2021, 42(11): 2997-3007 (in Chinese).
[8] 范祥,林杭,熊威,等.吸水率和吸水时间对红砂岩施密特硬度的影响[J].中国矿业大学学报,2015,44(2):233-240.
FAN X, LIN H, XIONG W, et al. Influence of water absorption rate and time on the Schmidt hardness of red sandstone[J]. Journal of China University of Mining & Technology, 2015, 44(2): 233-240 (in Chinese).
[9] 陈勇,秦邦民,张莉萍,等.红山窑红砂岩膨胀变形和软化特性试验研究[J].水文地质工程地质,2004,31(5):77-79+87.
CHEN Y, QIN B M, ZHANG L P, et al. Test study on expansive and softtening characteristic of red sandstone in Hongshanyao[J]. Hydrogeology and Engineering Geology, 2004, 31(5): 77-79+87 (in Chinese).
[10] 周翠英,黄思宇,刘镇,等.红层软岩软化的界面过程及其动力学模型[J].岩土力学,2019,40(8):3189-3196+3206.
ZHOU C Y, HUANG S Y, LIU Z, et al. The interface process and its dynamic model of red-bed soft rock softening[J]. Rock and Soil Mechanics, 2019, 40(8): 3189-3196+3206 (in Chinese).
[11] 吴恩江,韩宝平,王桂梁.红层中水-岩作用微观信息特征及对孔隙演化的影响:以兖州矿区为例[J].中国矿业大学学报,2005,34(1):123-128.
WU E J, HAN B P, WANG G L. Micro-information of water-rock interaction and its influence on pore evolution of red-bed in Yanzhou mining area[J]. Journal of China University of Mining & Technology, 2005, 34(1): 123-128 (in Chinese).
[12] 俞明.水泥稳定砂岩碎石混合料力学性能与抗冻性能试验研究[D].西安:长安大学,2019.
YU M. Experimental study on mechanical properties and frost resistance of cement stabilized sandstone gravel mixture[D]. Xi'an: Chang'an University, 2019 (in Chinese).
[13] 生海航.水泥稳定砂岩碎石路面基层的性能研究[D].重庆:重庆交通大学,2019.
SHENG H H. Study on the performance of cement stabilized sandstone macadam pavement base[D]. Chongqing: Chongqing Jiaotong University, 2019 (in Chinese).
[14] 成浩,王佳,张家生,等.粒状土与结构接触面强度特性粒径效应影响研究[J].公路,2022,67(4):299-305.
CHENG H, WANG J, ZHANG J S, et al. Study of the particle size effect on shear mechanism of interface between granular soil and structure[J]. Highway, 2022, 67(4): 299-305 (in Chinese).
[15] 缪澄宇,杨柳,许永震,等.基于核磁共振监测的砂岩强度软化实验及微观机制研究[J].岩石力学与工程学报,2021,40(11):2189-2198.
MIAO C Y, YANG L, XU Y Z, et al. Experimental study on strength softening behaviors and micro-mechanisms of sandstone based on nuclear magnetic resonance[J]. Chinese Journal of Rock Mechanics and Engineering, 2021, 40(11): 2189-2198 (in Chinese).
[16] 蒋丽君,薛金顺,曹帆.水泥稳定碎石强嵌挤型骨架密实级配研究[J].公路交通科技(应用技术版),2013,9(5):112-115.
JIANG L J, XUE J S, CAO F. Study on dense gradation of cement-stabilized macadam with strong extruding framework[J]. Highway Traffic Technology (Applied Technology Edition), 2013, 9(5): 112-115 (in Chinese).
[17] 蒋银萍.道路基层建设水泥粉煤灰稳定碎石材料应用[J].公路与汽运,2010(4):111-113+140.
JIANG Y P. Application of cement fly ash stabilized macadam material in road base construction[J]. Highways & Automotive Applications, 2010(4): 111-113+140 (in Chinese).
[18] 刘婉姝.不同塑性指数粘性土冻融循环损伤特性研究[J].江西建材,2022(4):22-24+27.
LIU W S. Study on freeze-thaw cycle damage characteristics of clay soils with different plasticity indexes[J]. Jiangxi Building Materials, 2022(4): 22-24+27 (in Chinese).
[19] 仓向辉,王锦.某矿区粘土矿物的物相分析及改性处理[J].理化检验(物理分册),2016,52(11):763-767.
CANG X H, WANG J. Phase analysis and modification treatment on clay minerals of one mining area[J]. Physical Testing and Chemical Analysis (Part A: Physical Testing), 2016, 52(11): 763-767 (in Chinese).
[20] 胡圆圆,胡再元.扫描电镜在碎屑岩储层粘土矿物研究中的应用[J].四川地质学报,2012,32(1):25-28.
HU Y Y, HU Z Y. The application of SEM to the study of clay minerals from clastic rock reservoir[J]. Acta Geologica Sichuan, 2012, 32(1): 25-28 (in Chinese).
[21] 从金瑶,杨恒,涂博,等.磷石膏-铜尾矿砂混合料的土工性能及微观机理研究[J].硅酸盐通报,2022,41(2):685-692.
CONG J Y, YANG H, TU B, et al. Geotechnical performance and micro-mechanism of phosphogypsum-copper tailings sand mixture[J]. Bulletin of the Chinese Ceramic Society, 2022, 41(2): 685-692 (in Chinese).