连续碳纤维增强热固性酚醛树脂复合材料的3D打印工艺及性能研究

摘要/Abstract

摘要： 针对连续碳纤维增强热固性酚醛树脂复合材料3D打印成型工艺的技术难题,本文提出了浸渍-原位预固化-后固化的3D打印成型方案,实现了连续碳纤维增强热固性酚醛树脂复合材料的3D打印成型,并研究浸渍温度对酚醛树脂接触角与表面张力,以及打印工艺对样件形貌和力学性能的影响规律。结果表明:当浸渍温度为40 ℃,预固化温度为180 ℃时,纤维-树脂界面结合效果最佳,原料具备成型条件;当打印间距为0.5 mm时,样件的弯曲强度及模量达到最大值,分别为660.00 MPa和57.99 GPa,层间剪切强度达到20.14 MPa。此连续碳纤维增强热固性酚醛树脂复合材料一体化制备工艺解决了3D打印热固性树脂原位成型难的问题,为制备具有复杂结构的连续纤维增强热固性树脂复合材料提供了参考。

关键词: 3D打印, 连续碳纤维, 热固性酚醛树脂, 复合材料, 打印参数, 力学性能

Abstract: In view of the technical difficulties in the 3D printing and molding process of continuous carbon fiber reinforced thermosetting phenolic resin (CCF-TSPR) composites, this paper proposes a 3D printing and molding scheme of impregnation, in-situ pre-curing and post-curing to realize 3D printing of continuous carbon fiber reinforced thermosetting phenolic resin composites. The influence of the immersion temperature on the contact angle and surface tension of the phenolic resin, as well as the printing process on the morphology and mechanical properties of the sample were studied. The results show that when the dipping temperature is 40 ℃ and the pre-curing temperature is 180 ℃, the raw material is available for molding with optimal fiber-resin interface bonding. When the printing spacing is 0.5 mm, the bending strength and modulus of the sample reach the maximum values of 660.00 MPa and 57.99 GPa respectively, and the interlaminar shear strength reaches 20.14 MPa. This integrated preparation process of CCF-TSPR composites solves the difficulty of in-situ molding of 3D printing thermosetting resins, and provides a reference for the preparation of continuous fiber reinforced thermosetting resin composites with complex structures.

Key words: 3D printing, continuous carbon fiber, thermosetting phenolic resin, composite material, printing parameter, mechanical property

中图分类号:

TB334

刘陶欣, 鲍崇高, 董文彩, 马海强, 鲁文奇. 连续碳纤维增强热固性酚醛树脂复合材料的3D打印工艺及性能研究[J]. 硅酸盐通报, 2022, 41(7): 2494-2501.

LIU Taoxin, BAO Chonggao, DONG Wencai, MA Haiqiang, LU Wenqi. 3D Printing Process and Properties of Continuous Carbon Fiber Reinforced Thermasetting Phenolic Resin Composites[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(7): 2494-2501.

参考文献

[1] 李奇辉,刘向阳,房晓斌.碳纤维复合材料的应用现状及我国碳纤维工业的发展方向[J].价值工程,2016,35(17):113-115.
LI Q H, LIU X Y, FANG X B. Application status of carbon fiber composites and the development trend of carbon fiber industry in China[J]. Value Engineering, 2016, 35(17): 113-115 (in Chinese).
[2] HIRANO Y, YAMANE T, TODOROKI A. Through-thickness electric conductivity of toughened carbon-fibre-reinforced polymer laminates with resin-rich layers[J]. Composites Science and Technology, 2016, 122: 67-72.
[3] 高迪.酚醛树脂浸渍碳纤维三维编织体的成型与烧蚀行为研究[D].哈尔滨:哈尔滨工业大学,2011.
GAO D. Reserch on fabrication and ablation behavior of phenolic impregnated three-dimention carbon fiber braid composites[D]. Harbin: Harbin Institute of Technology, 2011 (in Chinese).
[4] 王烽屹.耐烧蚀酚醛树脂基复合材料的制备及其性能研究[D].武汉:武汉理工大学,2017.
WANG F Y. Investigation of preparation and performance of ablation resistant phenolic resin composites[D]. Wuhan: Wuhan University of Technology, 2017 (in Chinese).
[5] 于海宁,高长星,王艳华.碳纤维增强树脂基复合材料的应用及展望[J].合成纤维工业,2020,43(1):55-59.
YU H N, GAO C X, WANG Y H. Application and prospect of carbon fiber reinforced resin-based composites[J]. China Synthetic Fiber Industry, 2020, 43(1): 55-59 (in Chinese).
[6] 肖光明,赵安安,郭俊刚,等.热固性树脂基复合材料固化变形控制及其应用[J].材料科学与工程学报,2018,36(6):883-887.
XIAO G M, ZHAO A N, GUO J G, et al. Curing deformation control of thermoset resin matrix composite and its application[J]. Journal of Materials Science and Engineering, 2018, 36(6): 883-887 (in Chinese).
[7] 宋学智,李长德,魏化震.固体火箭发动机喷管用烧蚀隔热材料研究进展[J].弹箭技术,1998(4):11-21.
SONG X Z, LI C D, WEI H Z. Advance of researching of ablative and thermal insulating materials used in the solid rockef motor nozzle[J]. Rocket Technology, 1998(4): 11-21 (in Chinese).
[8] 谢久明,周学均,武晋,等.碳纤维增强复合材料模压成型质量预测综述[J].机械设计,2020,37(S1):112-114.
XIE J M, ZHOU X J, WU J, et al. Review on the quality prediction of carbon fiber reinforced composite molding[J]. Journal of Machine Design, 2020, 37(S1): 112-114 (in Chinese).
[9] 邓杰,艾涛.树脂传递模塑工艺成型三维编织复合材料树脂体系研究[J].粘接,2006,27(4):7-9.
DENG J, AI T. Study of resin system for RTM processes of three dimention braided composite[J]. Adhesion in China, 2006, 27(4): 7-9 (in Chinese).
[10] 许丽丹,王澜.碳纤维增强树脂基复合材料的应用研究[J].塑料制造,2007(s1):81-85.
XU L D, WANG L. Study of resin matrix composites reinforced by carbon fiber[J]. Plastics Manufacture, 2007(s1): 81-85 (in Chinese).
[11] 刘甲秋,伊翠云,彭德功,等.连续纤维复合材料增材制造的发展研究[J].纤维复合材料,2020,37(3):91-94.
LIU J Q, YI C Y, PENG D G, et al. Research on the additive manufacturing of continuous fiber reinforced composites[J]. Fiber Composites, 2020, 37(3): 91-94 (in Chinese).
[12] 田小永,刘腾飞,杨春成,等.高性能纤维增强树脂基复合材料3D打印及其应用探索[J].航空制造技术,2016,59(15):26-31.
TIAN X Y, LIU T F, YANG C C, et al. 3D printing for high performance fiber reinforced polymer composites and exploration on its applications[J]. Aeronautical Manufacturing Technology, 2016, 59(15): 26-31 (in Chinese).
[13] 陈向明,姚辽军,果立成,等.3D打印连续纤维增强复合材料研究现状综述[J].航空学报,2021,42(10):524787.
CHEN X M, YAO L J, GUO L C, et al. 3D printed continuous fiber-reinforced composites: state of the art and perspectives[J]. Acta Aeronautica et Astronautica Sinica, 2021, 42(10): 524787 (in Chinese).
[14] 明越科,王奔,周晋,等.基于3D打印的连续纤维增强热固性复合材料性能及其应用探索[J].航空制造技术,2021,64(15):58-65.
MING Y K, WANG B, ZHOU J, et al. Performance and applications of 3D printed continuous fiber-reinforced thermosetting composites[J]. Aeronautical Manufacturing Technology, 2021, 64(15): 58-65 (in Chinese).
[15] HAO W F, LIU Y, ZHOU H, et al. Preparation and characterization of 3D printed continuous carbon fiber reinforced thermosetting composites[J]. Polymer Testing, 2018, 65: 29-34.
[16] 王智,于宁,黎静.熔融沉积纤维增强复合材料的研究进展[J].材料导报,2021,35(15):15197-15204.
WANG Z, YU N, LI J. Research progress in fused deposition modeling of fiber-reinforced composites[J]. Materials Reports, 2021, 35(15): 15197-15204 (in Chinese).
[17] 韩玉凤.热固性树脂固化过程的监测研究:交流阻抗谱技术的应用[D].天津:天津大学,2019.
HAN Y F. Monitor the curing process of thermosetting resins: application of AC impedance spectroscopy[D]. Tianjin: Tianjin University, 2019 (in Chinese).
[18] SHI B H, SHANG Y Y, ZHANG P, et al. Dynamic capillary-driven additive manufacturing of continuous carbon fiber composite[J]. SSRN Electronic Journal, 2019: 51.
[19] 王晓静,李寅,梁欢,等.基于原位红外光谱的热固性酚醛树脂固化过程研究[J].宇航材料工艺,2018,48(6):72-77.
WANG X J, LI Y, LIANG H, et al. Study on curing process of thermosetting phenolic resin based on in situ infrared spectroscopy[J]. Aerospace Materials & Technology, 2018, 48(6): 72-77 (in Chinese).
[20] 汤旭,李征,孙程阳.先进复合材料在航空航天领域的应用[J].中国高新技术企业,2016(13):39-42.
TANG X, LI Z, SUN C Y. Application of advanced composite materials in aerospace[J]. China High-Tech Enterprises, 2016(13): 39-42 (in Chinese).