煅烧工艺对天然水硬性石灰中硅酸二钙晶相转变的影响

摘要/Abstract

摘要： 天然水硬性石灰(natural hydraulic lime, NHL)是由钙硅质原料煅烧消化所得,主要成分是硅酸二钙(Ca₂SiO₄, C₂S)和氢氧化钙(Ca(OH)₂, CH),与我国古代岩土类建筑物的兼容性较高,是一种优秀的古建筑修复材料。为探究NHL的煅烧工艺,本文使用方解石粉和石英粉作为NHL煅烧原料,设置不同冷却方式(急冷≈500 ℃/min、随炉冷却≈60 ℃/min)、恒温时间(0~180 min)和煅烧温度(1 000~1 200 ℃),通过X射线衍射和游离氧化钙(f-CaO)测试方法评价NHL烧成制度。结果表明:在低于1 150 ℃煅烧C₂S时,改变降温速率不会使C₂S在降温过程中发生晶相转变;同一温度下,随恒温时间的增加NHL煅烧产物中C₂S含量增多,在30~45 min时其含量达到该温度下的最大值,且温度升高能增加该最大值,在恒温过程中C₂S先以β-C₂S存在,随时间延长,逐渐转变为γ-C₂S;煅烧温度1 150 ℃,恒温时间45 min,急速冷却的煅烧制度可用于制备NHL。

关键词: 天然水硬性石灰, 矿相组成, 煅烧工艺, 硅酸二钙, 降温过程, 晶型转变

Abstract: Natural hydraulic lime (NHL) is obtained from calcination and digestion of calcined calc-silicate raw materials. Its main components are dicalcium silicate (Ca₂SiO₄, C₂S) and calcium hydroxide (Ca(OH)₂, CH). It fits ancient lithology buildings well, and the durability is in line with the requirements of people for the restoration of ancient buildings. Using X ray diffraction and free calcium oxide (f-CaO) test methods, this paper evaluated the NHL calcination process by investigating the mineral phase composition and conversion rate of the products obtained under different cooling methods (fast cooling speed which is about 500 ℃/min compared with cooling in the closed furnace for the cooling speed of nearly 60 ℃/min), firing time (0 min to 180 min) and calcination temperatures (1 000 ℃ to 1 200 ℃) and with calcite power and silicate power. The results show that, when the calcination temperature is lower than 1 150 ℃, changing the cooling method will not cause the crystal phase transformation of C₂S during the cooling process. At the same temperature, the content of C₂S in the NHL calcined product increases with the increase of the constant temperature time, and its content reaches the maximum value at this temperature in 30 min to 45 min, and the increase of the calcination temperature increases the maximum value. C₂S first exists in β-lattice, and gradually changes to γ-C₂S over time. With a rapid cooling speed, the calcination temperature of β-C₂S is lower than that of γ-C₂S. To prepare NHL, the calcination process could be firing at 1 150 ℃ for 45 min, and with the rapid cooling system.

Key words: natural hydraulic lime, mineral composition, calcination process, dicalcium silicate, cooling process, transcrystallization

中图分类号:

TU526

薄艾, 张大江, 王璜琪, 王栋民, 王启宝, 刘泽. 煅烧工艺对天然水硬性石灰中硅酸二钙晶相转变的影响[J]. 硅酸盐通报, 2022, 41(4): 1336-1342.

BO Ai, ZHANG Dajiang, WANG Huangqi, WANG Dongmin, WANG Qibao, LIU Ze. Influence of Calcination Process on C₂S Crystal Transformation in Natural Hydraulic Lime[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(4): 1336-1342.

参考文献

[1] 兰明章,聂松,王剑锋,等.古建筑修复用石灰基砂浆的研究进展[J].材料导报,2019,33(9):1512-1516.
LAN M Z, NIE S, WANG J F, et al. A state-of-the-art review on lime-based mortars for restoration of ancient buildings[J]. Materials Reports, 2019, 33(9): 1512-1516 (in Chinese).
[2] 彭反三.天然水硬性石灰[J].石灰,2009,3:44-48.
PENG F S. Natural hydraulic lime[J]. Lime, 2009, 3: 44-48 (in Chinese).
[3] 林宗寿.无机非金属材料工学[M].3版.武汉:武汉理工大学出版社,2008.
LIN Z S. Inorganic nonmetallic materials engineering[M]. 3rd ed. Wuhan: Wuhan University of Technology Press, 2008 (in Chinese).
[4] 张文生,张江涛,叶家元,等.硅酸二钙的结构与活性[J].硅酸盐学报,2019,47(11):1663-1669.
ZHANG W S, ZHANG J T, YE J Y, et al. Structure and activity of dicalcium silicate[J]. Journal of the Chinese Ceramic Society, 2019, 47(11): 1663-1669 (in Chinese).
[5] 冯修吉,闵新民,陶从喜.应用量子化学算法研究硅酸二钙的结构与性能[J].武汉工业大学学报,1994,16(2):1-6+17.
FENG X J, MIN X M, TAO C X. Study on the structure and characteristic of dicalcium silicate with quantum chemistry calculations[J]. Journal of Wuhan University of Technology, 1994, 16(2): 1-6+17 (in Chinese).
[6] WANG Q Q, LI F, SHEN X D, et al. Relation between reactivity and electronic structure for α′L-, β- and γ-dicalcium silicate: a first-principles study[J]. Cement and Concrete Research, 2014, 57: 28-32.
[7] 穆元冬,雪高瑞,赵思雪,等.γ型硅酸二钙的碳化研究进展[J].硅酸盐学报,2017,45(8):1197-1203.
MU Y D, XUE G R, ZHAO S X, et al. Development of carbonation of γ-dicalcium silicate[J]. Journal of the Chinese Ceramic Society, 2017, 45(8): 1197-1203 (in Chinese).
[8] 冯修吉,黄锦扬,陶景扬,等.β-C₂S的稳定性及防止其在普通水泥熟料中粉化的一些因素的探讨[J].硅酸盐学报,1964(2):105-120.
FENG X J, HUANG J Y, TAO J Y, et al. Discussion on the stability of β-C₂S and some factors preventing dusting from Portland cement clinker[J]. Journal of the Chinese Ceramic Society, 1964(2): 105-120 (in Chinese).
[9] 张雄.C₂S转晶反应定量调控[J].硅酸盐学报,1995,23(6):680-684.
ZHANG X. Quantitative control of C₂S transformation[J]. Journal of the Chinese Ceramic Society, 1995, 23(6): 680-684 (in Chinese).
[10] 李黎,赵林毅,李最雄.中国古建筑中几种石灰类材料的物理力学特性研究[J].文物保护与考古科学,2014,26(3):74-84.
LI L, ZHAO L Y, LI Z X. Study on the physical and mechanical properties of several lime materials in ancient Chinese architecture[J]. Sciences of Conservation and Archaeology, 2014, 26(3): 74-84 (in Chinese).
[11] 杨建林,宋文伟,王来贵,等.古建筑用水硬性石灰的合成及力学性能研究[J].硅酸盐通报,2018,37(8):2633-2639.
YANG J L, SONG W W, WANG L G, et al. Research on preparation and mechanical properties of hydraulic lime used for ancient buildings[J]. Bulletin of the Chinese Ceramic Society, 2018, 37(8): 2633-2639 (in Chinese).
[12] 沈雪飞,薛群虎,徐亮,等.利用铅锌尾矿制备天然水硬性石灰可行性研究[J].硅酸盐通报,2013,32(10):1973-1978.
SHEN X F, XUE Q H, XU L, et al. Research of the feasibility to prepare the natural hydraulic limes from the lead and zinc mine tailing[J]. Bulletin of the Chinese Ceramic Society, 2013, 32(10): 1973-1978 (in Chinese).
[13] 赵林毅,李黎,李最雄,等.中国古代建筑中两种传统硅酸盐材料的研究[J].无机材料学报,2011,26(12):1327-1334.
ZHAO L Y, LI L, LI Z X, et al. Research on two traditional silicate materials in China's ancient building[J]. Journal of Inorganic Materials, 2011, 26(12): 1327-1334 (in Chinese).
[14] 刘泽,王琳琳,姜启衎,等.水泥用石灰岩制备天然水硬性石灰NHL2的工艺优化与性能研究[J].硅酸盐通报,2019,38(8):2513-2517.
LIU Z, WANG L L, JIANG Q K, et al. Process optimization and properties research of natural hydraulic lime NHL2 prepared from limestone of cement fabrication[J]. Bulletin of the Chinese Ceramic Society, 2019, 38(8): 2513-2517 (in Chinese).
[15] 罗凯.天然水硬性石灰的设计制备及性能研究[D].绵阳:西南科技大学,2020.
LUO K. Research on the preparation and performance of natural hydraulic lime[D]. Mianyang: Southwest University of Science and Technology, 2020 (in Chinese).
[16] PRITTS I M, DAUGHERTY K E. The effect of stabilizing agents on the hydration rate of β-C₂S[J]. Cement and Concrete Research, 1976, 6(6): 783-795.
[17] KIM Y M, HONG S H. Influence of minor ions on the stability and hydration rates of β-dicalcium silicate[J]. Journal of the American Ceramic Society, 2004, 87(5): 900-905.
[18] ZHAO M. Quantitative control of C₂S crystal transformation[J]. Applied Mechanics and Materials, 2011, 126: 311-315.
[19] HUGHES D C, JAGLIN D, KOZŁOWSKI R, et al. Roman cements—belite cements calcined at low temperature[J]. Cement and Concrete Research, 2009, 39(2): 77-89.
[20] 方永浩,徐玲玲,杨南如.贝利特的活化途径及高贝利特水泥[J].水泥工程,1998(2):26-31+58.
FANG Y H, XU L L, YANG N R. Methods of activation of belite and high belite cement[J]. Cement Engineering, 1998(2): 26-31+58 (in Chinese).
[21] VÁLEK J, VAN HALEM E, VIANI A, et al. Determination of optimal burning temperature ranges for production of natural hydraulic limes[J]. Construction and Building Materials, 2014, 66: 771-780.
[22] 郭汉杰.活性石灰生产理论与工艺[M].北京:化学工业出版社,2014.
GUO H J. Production theory and technology of active lime[M]. Beijing: Chemical Industry Press, 2014 (in Chinese).
[23] ZHANG D J, ZHAO J H, WANG D M, et al. Comparative study on the properties of three hydraulic lime mortar systems: natural hydraulic lime mortar, cement-aerial lime-based mortar and slag-aerial lime-based mortar[J]. Construction and Building Materials, 2018, 186: 42-52.
[24] 钱强.不同方法测定钢渣中游离氧化钙含量的对比分析[J].水泥工程,2019(2):60-63.
QIAN Q. Comparative analysis of determination of free calcium oxide in steel slag by different methods[J]. Cement Engineering, 2019(2): 60-63 (in Chinese).
[25] KASHCHIEV D, BORISSOVA A, HAMMOND R B, et al. Effect of cooling rate on the critical undercooling for crystallization[J]. Journal of Crystal Growth, 2010, 312(5): 698-704.
[26] NA H, WANG Y J, ZHANG X, et al. Hydration activity and carbonation characteristics of dicalcium silicate in steel slag: a review[J]. Metals, 2021, 11(10): 1580.
[27] 杨南如.非传统胶凝材料化学[M].武汉:武汉理工大学出版社,2018.
YANG N R. Chemistry of non-traditional cementitious materials[M]. Wuhan: Wuhan University of Technology Press, 2018 (in Chinese).