碱激发偏高岭土基地质聚合物的制备及抗压强度研究

摘要/Abstract

摘要： 为了响应“双碳”政策节能减排的号召,本文采用偏高岭土和高炉矿渣为原材料制备地质聚合物。以抗压强度为指标优化制备条件,探讨确定影响地质聚合物强度的因素。通过正交试验确定偏高岭土基地质聚合物的最佳配比,通过热重和XRD分析不同温度煅烧的偏高岭土组分。研究结果表明,在高岭土煅烧温度为800 ℃时,偏高岭土基地质聚合物的最佳配合比为氢氧化钠与硅酸钠的质量比为6.5∶1,激发剂的质量掺量为14.2%,其28 d抗压强度能达到46.6 MPa。偏高岭土基地质聚合物抗压强度随激发剂的掺量增加而增大,随氢氧化钠与硅酸钠的质量比的增大先增大后减小,随高岭土煅烧温度的升高先增大后减小。

关键词: 地质聚合物, 偏高岭土, 碱激发, 水玻璃模数, 抗压强度, 正交试验

Abstract: In response to the “carbon peak and neutrality” policy of energy saving and emission reduction, in the present paper, geopolymers were prepared with metakaolin and blast furnace slag as raw materials. The compressive strength was used as the index to optimize the preparation conditions and to explore the factors affecting the strength of geopolymer based on metakaolin. The optimum mixing ratio of geopolymer was determined by orthogonal test. The metakaolin fractions calcined at different temperatures were analyzed by thermogravimetry and XRD. The research results show that when the calcining temperature of kaolin is 800 ℃, the optimum mixing ratio of geopolymer based on metakaolin is that the mass ratio of sodium hydroxide to sodium silicate is 6.5∶1 and the mass fraction of activator is 14.2%. Under these conditions, the 28 d compressive strength of the geopolymers reaches 46.6 MPa. The compressive strength of the geopolymer based on metakaolin increases with the addition of the mass fraction of activator, and increases first and then decreases with the increase of the mass ratio of sodium hydroxide to sodium silicate, and increases first and then decreases with the increase of kaolin calcination temperature.

Key words: geopolymer, metakaolin, alkali activated, modulus of sodium silicate, compressive strength, orthogonal test

中图分类号:

TU528.41

杨光, 赵宇, 朱伶俐, 武喜凯. 碱激发偏高岭土基地质聚合物的制备及抗压强度研究[J]. 硅酸盐通报, 2022, 41(3): 894-902.

YANG Guang, ZHAO Yu, ZHU Lingli, WU Xikai. Preparation and Compressive Strength of Geopolymer Based on Alkali Activated Metakaolin[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(3): 894-902.

参考文献

[1] 张大旺,王栋民.地质聚合物混凝土研究现状[J].材料导报,2018,32(9):1519-1527+1540.
ZHANG D W, WANG D M. Research status of geopolymer concrete[J]. Materials Review, 2018, 32(9): 1519-1527+1540 (in Chinese).
[2] 倪文,王恩,周佳.地质聚合物:21世纪的绿色胶凝材料[J].新材料产业,2003(6):24-28.
NI W, WANG E, ZHOU J. Geopolymer: green cementitious material in the 21st century[J]. Advanced Materials Industry, 2003(6): 24-28 (in Chinese).
[3] 吴小缓,张杨,袁鹏,等.地质聚合物的研究进展与应用[J].硅酸盐通报,2016,35(12):4032-4037.
WU X H, ZHANG Y, YUAN P, et al. Research progress and applications of geopolymer[J]. Bulletin of the Chinese Ceramic Society, 2016, 35(12): 4032-4037 (in Chinese).
[4] DAVIDOVITS J. Geopolymers: man-made rock geosynthesis and the resulting development of very early high strength cement[J]. Materials Eduucation, 1994, 16(2/3): 1-25.
[5] 施惠生,袁玲.高岭土应用研究的新进展[J].中国非金属矿工业导刊,2002(6):11-16.
SHI H S, YUAN L. Advanced research and application of kaolin[J]. China Non-Metallic Mining Industry Herald, 2002(6): 11-16 (in Chinese).
[6] 阴江宁,丁建华,陈炳翰,等.中国高岭土矿成矿地质特征与资源潜力评价[J/OL].中国地质:1-20.[2021-11-14].http://kns.cnki.net/kcms/detail/11.1167.p.20210510.0910.002.html.
YIN J N, D J H, CHEN B H, et al. Metallogenic geological characteristics and mineral resources assessment of kaolin in China[J/OL]. Geology in China: 1-20. [2021-11-14]. http://kns.cnki.net/kcms/detail/11.1167.p.20210510.0910.002.html (in Chinese).
[7] 王磊,李金丞,张晓伟,等.地质聚合物激发剂及其激发原理[J/OL].无机盐工业:1-9[2021-08-04].http://kns.cnki.net/kcms/detail/12.1069.TQ.20210524.1354.004.html.
WANG L, LI J C, ZHANG X W, et al. Geopolymer activator and its excitation principle full[J/OL]. Inorganic Chemicals Industry: 1-9[2021-08-04]. http://kns.cnki.net/kcms/detail/12.1069.TQ.20210524.1354.004.html (in Chinese).
[8] 王爱国,王星尧,孙道胜,等.地质聚合物凝结硬化及其调节技术的研究进展[J].材料导报,2021,35(13):5-14.
WANG A G, WANG X Y, SUN D S, et al. Research progress on setting and hardening of geopolymers and their control[J]. Materials Reports, 2021, 35(13): 5-14 (in Chinese).
[9] 杨达,卢明阳,宋迪,等.地质聚合物水泥的研究进展[J].材料导报,2021,35(s1):644-649.
YANG D, LU M Y, SONG D, et al. Research progress of geopolymer cement[J]. Materials Reports, 2021, 35(s1): 644-649 (in Chinese).
[10] 尹明,白洪涛,周吕.粉煤灰地质聚合物混凝土的强度特性[J].硅酸盐通报,2014,33(10):2723-2727.
YIN M, BAI H T, ZHOU L. Strength characteristic of fly ash based geopolymer concrete[J]. Bulletin of the Chinese Ceramic Society, 2014, 33(10): 2723-2727 (in Chinese).
[11] BERNAL S A, BEJARANO J, GARZÓN C, et al. Performance of refractory aluminosilicate particle/fiber-reinforced geopolymer composites[J]. Composites Part B: Engineering, 2012, 43(4): 1919-1928.
[12] SOMNA K, JATURAPITAKKUL C, KAJITVICHYANUKUL P, et al. NaOH-activated ground fly ash geopolymer cured at ambient temperature[J]. Fuel, 2011, 90(6): 2118-2124.
[13] 张锦,贺艳,王艺频,等.地聚物凝胶转换法制备大尺寸方沸石晶体[J].人工晶体学报,2013,42(11):2390-2395.
ZHANG J, HE Y, WANG Y P, et al. Preparation of large size analcime crystals by geopolymer-gel-conversation method[J]. Journal of Synthetic Crystals, 2013, 42(11): 2390-2395 (in Chinese).
[14] GÖRHAN G, KÜRKLÜ G. The influence of the NaOH solution on the properties of the fly ash-based geopolymer mortar cured at different temperatures[J]. Composites Part B: Engineering, 2014, 58: 371-377.
[15] 郑娟荣,刘丽娜.偏高岭土基地质聚合物合成条件的试验研究[J].郑州大学学报(工学版),2008,29(2):44-47.
ZHENG J R, LIU L N. Experimental study on formation conditions of metakaolinite-based geopolymer[J]. Journal of Zhengzhou University (Engineering Science), 2008, 29(2): 44-47 (in Chinese).
[16] SHARIATMADARI N, MOHEBBI H, JAVADI A A. Surface stabilization of soils susceptible to wind erosion using volcanic ash-based geopolymer[J]. Journal of Materials in Civil Engineering, 2021, 33(12): 04021345.
[17] WASIM M, DUC NGO T, LAW D. Durability performance of reinforced waste-based geopolymer foam concrete under exposure to various corrosive environments[J]. Case Studies in Construction Materials, 2021, 15: e00703.
[18] 彭佳,颜子博.地质聚合物的研究进展[J].中国非金属矿工业导刊,2014(1):16-19.
PENG J, YAN Z B. Recent research progress of geopolymer[J]. China Non-Metallic Minerals Industry, 2014(1): 16-19 (in Chinese).
[19] RICKARD W D A, VICKERS L, VAN RIESSEN A. Performance of fibre reinforced, low density metakaolin geopolymers under simulated fire conditions[J]. Applied Clay Science, 2013, 73: 71-77.
[20] 诸华军,姚晓,张祖华.高岭土煅烧活化温度的初选[J].建筑材料学报,2008,11(5):621-625.
ZHU H J, YAO X, ZHANG Z H. Optimization of calcined temperature for kaolin activation[J]. Journal of Building Materials, 2008, 11(5): 621-625 (in Chinese).
[21] 彭晖,崔潮,蔡春声,等.偏高岭土活性的煅烧温度影响及测定方法研究[J].硅酸盐通报,2014,33(8):2078-2084+2094.
PENG H, CUI C, CAI C S, et al. Research on influence of calcination temperature on metakaolin reactivity and its determination[J]. Bulletin of the Chinese Ceramic Society, 2014, 33(8): 2078-2084+2094 (in Chinese).
[22] 赵彦旭,向俊燃,吕擎峰,等.碱激发剂对地聚物固化黄土工程特性的影响[J].北京工业大学学报,2021,47(6):636-643.
ZHAO Y X, XIANG J R, LÜ Q F, et al. Effect of alkali activator on engineering properties of geopolymer-solidified loess[J]. Journal of Beijing University of Technology, 2021, 47(6): 636-643 (in Chinese).
[23] 何卓名,邹家强,刘爱华,等.水玻璃模数对偏高岭土基地聚合物物理力学性能的影响[J].广东公路交通,2017,43(4):6-10+19.
HE Z M, ZOU J Q, LIU A H, et al. Effects of sodium silicate modulus on physical and mechanical properties of metakaolin based geopolymers[J]. Guangdong Highway Communications, 2017, 43(4): 6-10+19 (in Chinese).
[24] 傅博,程臻赟,韩静云,等.碱偏高岭土矿渣地聚合物砂浆强度及新拌性能研究[J].硅酸盐通报,2019,38(12):4013-4020.
FU B, CHENG Z Y, HAN J Y, et al. Strength and fresh properties of alkali activated metakaolin slag geopolymer mortar[J]. Bulletin of the Chinese Ceramic Society, 2019, 38(12): 4013-4020 (in Chinese).
[25] GAO K, LIN K L, WANG D Y, et al. Effects SiO₂/Na₂O molar ratio on mechanical properties and the microstructure of nano-SiO₂ metakaolin-based geopolymers[J]. Construction and Building Materials, 2014, 53: 503-510.
[26] LYU S J, WANG T T, CHENG T W, et al. Main factors affecting mechanical characteristics of geopolymer revealed by experimental design and associated statistical analysis[J]. Construction and Building Materials, 2013, 43: 589-597.
[27] ALONSO S, PALOMO A. Alkaline activation of metakaolin and calcium hydroxide mixtures: influence of temperature, activator concentration and solids ratio[J]. Materials Letters, 2001, 47(1/2): 55-62.
[28] 陈晨,程婷,贡伟亮,等.粉煤灰地聚物反应体系下的反应动力学研究[J].硅酸盐通报,2016,35(9):2717-2723.
CHEN C, CHENG T, GONG W L, et al. Reaction kinetics of fly ash based geopolymer systems[J]. Bulletin of the Chinese Ceramic Society, 2016, 35(9): 2717-2723 (in Chinese).
[29] GAO Y T, FENG Y Z, TONG G Q, et al. Influences of sodium silicate modulus on mechanical properties and microstructure of fly ash geopolymer[J]. IOP Conference Series: Earth and Environmental Science, 2021, 760(1): 012056.
[30] CHI M. Effects of modulus ratio and dosage of alkali-activated solution on the properties and micro-structural characteristics of alkali-activated fly ash mortars[J]. Construction and Building Materials, 2015, 99: 128-136.
[31] 徐小彬,殷素红,杨建军,等.偏高岭土活性快速检验方法的研究[J].硅酸盐通报,2008,27(4):690-694.
XU X B, YIN S H, YANG J J, et al. Study on a fast determination method of metakaoline reactivity[J]. Bulletin of the Chinese Ceramic Society, 2008, 27(4): 690-694 (in Chinese).
[32] 郑娟荣,周同和,陈晓堂.地质聚合物合成中偏高岭土活性的快速检测方法研究[J].硅酸盐通报,2007,26(5):887-891+900.
ZHENG J R, ZHOU T H, CHEN X T. Study on the reactivity and its fast determination method of metakaoline in synthesizing geopolymer[J]. Bulletin of the Chinese Ceramic Society, 2007, 26(5): 887-891+900 (in Chinese).
[33] 马国伟,王德华,钟惟亮,等.粒化高炉矿渣粉替代量对偏高岭土基地质聚合物力学性能及凝结时间影响的研究[J].实验力学,2019,34(5):767-774.
MA G W, WANG D H, ZHONG W L, et al. The effects of GGBS and modulus of water glass on the hardening behavior of metakaolin based geopolymer under normal temperature curing[J]. Journal of Experimental Mechanics, 2019, 34(5): 767-774 (in Chinese).
[34] 罗新春,汪长安.钙含量对偏高岭土/矿渣基地聚合物结构和性能的影响[J].硅酸盐学报,2015,43(12):1800-1805.
LUO X C, WANG C A. Effect of calcia content on structure and properties of metakaolin/blast furnace slag-based geopolymers[J]. Journal of the Chinese Ceramic Society, 2015, 43(12): 1800-1805 (in Chinese).
[35] 刘庆,臧浩宇,王俊祥,等.矿渣基地聚物的制备及其性能研究综述[J].山东科技大学学报(自然科学版),2019,38(3):43-49.
LIU Q, ZANG H Y, WANG J X, et al. An overview of preparation and performance of slag based geopolymer[J]. Journal of Shandong University of Science and Technology (Natural Science), 2019, 38(3): 43-49 (in Chinese).