基于ESPI技术的混凝土单轴拉伸断裂特性研究

摘要/Abstract

摘要： 为了研究混凝土的拉伸断裂特性,对带有预制切口的C80高强混凝土棱柱体进行单轴拉伸试验,采用电子散斑干涉(ESPI)技术测量棱柱体表面的场位移等信息,分析加载过程得到混凝土的断裂参数以及断裂特性等。为进行对比分析,本次试验还采用线性位移计和夹式位移计测量试件的变形程度。对比结果表明ESPI技术的测量结果与夹式位移计结果吻合较好,证实了ESPI技术用于测量混凝土表面位移场的精确性和可行性。分析得到:初裂点应力约为峰值应力的82%;峰值下裂缝口张开位移(CMOD)为11 μm,结合公式得到混凝土在单轴拉伸下的断裂韧度约为0.41 MPa·m^1/2,断裂能约为24.71 N/m;利用两种拟合公式对试验应力-应变关系进行拟合,得到了较好的拟合结果。最后,通过不同加载步骤下ESPI技术测得的位移云图分析裂缝口张开位移随试件宽度的变化规律,得到了单轴拉伸下的裂纹扩展规律。

关键词: 高强混凝土, ESPI, 单轴拉伸试验, 断裂特性, 裂缝口张开位移, 裂缝长度

Abstract: In order to study the tensile fracture characteristics of concrete, the uniaxial tensile test of C80 high-strength concrete prism with precast cuts was carried out, the field displacement of the prism surface was measured by electronic speckle pattern interferometry (ESPI) technology, and the fracture parameters and fracture characteristics of concrete were analyzed during the loading process. For comparative analysis, the deformation of specimen was also measured using a linear displacement meter and a clip-on displacement meter. The comparison results show that the ESPI technology measurement results are in good agreement with the clip-on displacement meter results, which confirms the accuracy and feasibility of ESPI technology to measure the displacement field of concrete surface. The analysis shows that the initial crack point stress is about 82% of the peak stress. The crack mouth opening displacement (CMOD) of the peak load is 11 μm, and the fracture toughness of concrete under uniaxial tension is obtained by combining the formula to obtain a fracture toughness of about 0.41 MPa·m^1/2, and the fracture energy is about 24.71 N/m. The experimental stress-strain relationship is fitted by using two fitting formulas, and the fitting results are good. Finally, the crack propagation law under uniaxial tension was obtained by analyzing the crack mouth opening displacement varied with the width of specimen in the displacement cloud map measured by ESPI technology at different loading steps.

Key words: high-strength concrete, ESPI, uniaxial tensile test, fracture characteristic, crack mouth opening displacement, crack length

中图分类号:

TU528

龙津润, 赵炳震, 陈红鸟, 许应杰. 基于ESPI技术的混凝土单轴拉伸断裂特性研究[J]. 硅酸盐通报, 2022, 41(12): 4263-4272.

LONG Jinrun, ZHAO Bingzhen, CHEN Hongniao, XU Yingjie. Uniaxial Tensile Fracture Characteristics of Concrete Based on ESPI Technology[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(12): 4263-4272.

参考文献

[1] 徐世烺,赵艳华.混凝土裂缝扩展的断裂过程准则与解析[J].工程力学,2008,25(s2):20-33.
XU S L, ZHAO Y H. Analysis and criterion of fracture process for crack propagation in concrete[J]. Engineering Mechanics, 2008, 25(s2): 20-33 (in Chinese).
[2] 赵艳华,徐世烺,吴智敏.混凝土结构裂缝扩展的双G准则[J].土木工程学报,2004,37(10):13-18+51.
ZHAO Y H, XU S L, WU Z M. A dual-G criterion for crack propagation in concrete structures[J]. China Civil Engineering Journal, 2004, 37(10): 13-18+51 (in Chinese).
[3] 徐世烺,赵国藩.混凝土结构裂缝扩展的双K断裂准则[J].土木工程学报,1992,25(2):32-38.
XU S L, ZHAO G F. A double-K fracture criterion for the crack propagatiom in goncrete structures[J]. China Civil Engineering Journal, 1992, 25(2): 32-38 (in Chinese).
[4] 唐宇翔.准脆性材料断裂过程区特性的试验和数值模拟研究[D].贵阳:贵州大学,2020.
TANG Y X. Experimental and numerical simulation study on characteristics of fracture process zone of quasi-brittle materials[D]. Guiyang: Guizhou University, 2020 (in Chinese).
[5] 吴智敏,董伟,许青.混凝土Ⅰ~Ⅱ复合型裂缝扩展准则及扩展全过程的数值模拟[J].水利学报,2009,40(2):180-187.
WU Z M, DONG W, XU Q. Propagation criterion for mixed mode Ⅰ~Ⅱ crack propagation and numerical simulation of the whole propagation process[J]. Journal of Hydraulic Engineering, 2009, 40(2): 180-187 (in Chinese).
[6] 赵艳华.混凝土断裂过程中的能量分析研究[D].大连:大连理工大学,2002.
ZHAO Y H. The analytical study on the energy in the fracture process of concrete[D]. Dalian: Dalian University of Technology, 2002 (in Chinese).
[7] 王德强.往复荷载下混凝土梁的断裂性能研究[D].贵阳:贵州大学,2020.
WANG D Q. Study on fracture performance of concrete beams under cyclic loading[D]. Guiyang: Guizhou University, 2020 (in Chinese).
[8] 富立志.冻融环境下混凝土单轴受拉性能的试验研究[D].扬州:扬州大学,2010.
FU L Z. Experimental study on the strength of concrete under uniaxial tensile load after freeze-thaw cycles[D]. Yangzhou: Yangzhou University, 2010 (in Chinese).
[9] 孙启林,王利民.钢纤维混凝土单轴拉伸实验方法[J].山西建筑,2009,35(25):1-3.
SUN Q L, WANG L M. Uniaxial tensile test method for steel fiber concrete[J]. Shanxi Architecture, 2009, 35(25): 1-3 (in Chinese).
[10] 徐荣耀.箍筋约束超高性能混凝土的单轴特性及本构模型试验研究[D].成都:西南交通大学,2019.
XU R Y. Experimental reaserch of uniaxial behavior and constitutive model of stirrup confined ultra-high performance concrete[D]. Chengdu: Southwest Jiaotong University, 2019 (in Chinese).
[11] 时文涛.混凝土单轴压缩及单轴拉伸破坏过程的细观数值试验及CT验证[D].西安:长安大学,2017.
SHI W T. Mesoscopic numerical simulation and CT verification of failure process of concrete under uniaxial compression and uniaxial tension[D]. Xi'an: Chang'an University, 2017 (in Chinese).
[12] 彭勃,郑伟.混凝土单轴直接拉伸强度试验方法的研究[J].湖南大学学报(自然科学版),2004,31(2):79-83.
PENG B, ZHENG W. Study on the test method of concrete strength in uniaxial direct tension[J]. Journal of Hunan University (Natural Science), 2004, 31(2): 79-83 (in Chinese).
[13] 邓宗才,李建辉,傅智,等.聚丙烯纤维混凝土直接拉伸性能的试验研究[J].公路交通科技,2005,22(7):45-48.
DENG Z C, LI J H, FU Z, et al. The uniaxial tension test of polypropylene fiber reinforced concrete[J]. Journal of Highway and Transportation Research and Development, 2005, 22(7): 45-48 (in Chinese).
[14] 何吉,章嘉伟,徐小雪,等.全级配混凝土抗拉性能的随机特性及数值分析[J].三峡大学学报(自然科学版),2019,41(5):6-11.
HE J, ZHANG J W, XU X X, et al. Study of stochastic behavior of tensile properties of full-grade concrete by numerical analysis[J]. Journal of China Three Gorges University (Natural Sciences), 2019, 41(5): 6-11 (in Chinese).
[15] 田梦云,张恩,曹瑞东,等.基于细观尺度的混凝土单轴力学性能仿真计算分析[J].应用力学学报,2020,37(3):975-981+1384.
TIAN M Y, ZHANG E, CAO R D, et al. Meso-scale simulation analysis of uniaxial mechanical behavior of concrete[J]. Chinese Journal of Applied Mechanics, 2020, 37(3): 975-981+1384 (in Chinese).
[16] 纪恩武.单轴循环荷载下UHTCC力学性能研究[D].大连:大连理工大学,2021.
JI E W. Study on mechanical properties of UHTCC subjected to uniaxial cyclic loading[D]. Dalian: Dalian University of Technology, 2021 (in Chinese).
[17] 赵一鹤,孙振平,穆帆远,等.钢纤维对UHPC拉伸性能及其拔出行为的影响[J].建筑材料学报,2021,24(2):276-282.
ZHAO Y H, SUN Z P, MU F Y, et al. Effect of steel fibers on tensile properties of ultra-high performance concrete and its pullout behavior[J]. Journal of Building Materials, 2021, 24(2): 276-282 (in Chinese).
[18] 徐世烺,赵国藩.混凝土裂缝的稳定扩展过程与临界裂缝尖端张开位移[J].水利学报,1989,20(4):33-44.
XU S L, ZHAO G F. The stable propagation of crack in concrete and the determination of critical crack tip opening displacement[J]. Journal of Hydraulic Engineering, 1989, 20(4): 33-44 (in Chinese).
[19] 孙平,王海峰,张熹,等.三维电子散斑干涉技术及其应用研究[J].光学学报,2003,23(7):840-844.
SUN P, WANG H F, ZHANG X, et al. Study on three-dimensional ESPI and its application[J]. Acta Optica Sinica, 2003, 23(7): 840-844 (in Chinese).
[20] 潘建伍,曹双寅,何小元,等.散斑干涉在纤维与混凝土粘结面位移场测量中的应用[J].东南大学学报(自然科学版),2003,33(3):347-350.
PAN J W, CAO S Y, HE X Y, et al. Application of ESPI in displacement measurement of bond area between FRP and concrete[J]. Journal of Southeast University (Natural Science Edition), 2003, 33(3): 347-350 (in Chinese).
[21] 王青原,陈红鸟,袁波,等.基于电子散斑干涉技术的混凝土裂纹扩展特性研究[J].水力发电学报,2018,37(4):26-35.
WANG Q Y, CHEN H N, YUAN B, et al. Behaviors of crack propagation in concrete using electronic speckle pattern interferometry[J]. Journal of Hydroelectric Engineering, 2018, 37(4): 26-35 (in Chinese).
[22] 吴锋.混凝土单轴抗拉应力-应变全曲线的试验研究[D].长沙:湖南大学,2006.
WU F. Experimental study on whole stress-strain curves of concrete under axial tension[D]. Changsha: Hunan University, 2006 (in Chinese).
[23] 张俊,陈红鸟,王德强.基于DIC技术的混凝土往复荷载下断裂力学特性研究[J].应用力学学报,2021,38(4):1636-1643.
ZHANG J, CHEN H N, WANG D Q. Study on fracture properties of concrete under cyclic loading by using DIC technique[J]. Chinese Journal of Applied Mechanics, 2021, 38(4): 1636-1643 (in Chinese).
[24] TADA H, PARIS P C, IRWIN G R. The stress analysis of cracks handbook[M]. New York: ASME Press, 2000: 667.
[25] YANKELEVSKY D Z, REINHARDT H W. Response of plain concrete to cyclic tension[J]. Materials Journal, 1987, 84(5): 53-55.
[26] 中华人民共和国住房和城乡建设部.混凝土结构设计规范:GB 50010—2010[S].北京:中国建筑工业出版社,2011.
Ministry of Housing and Urban Rural Development of the People's Republic of China. Code for design of concrete structures: GB 50010—2010[S]. Beijing: China Architecture Press, 2011 (in Chinese).