有机膦酸对硫氧镁水泥的改性研究

硅酸盐通报 ›› 2022, Vol. 41 ›› Issue (12): 4139-4146.

所属专题：水泥混凝土

有机膦酸对硫氧镁水泥的改性研究

梁慧慧¹, 李阳², 杨红健¹, 刘晓莉¹, 何怡婷¹, 张玉婷¹

1.河北工业大学化工学院,天津 300400;
2.天津市热电设计院有限公司,天津 300204

收稿日期:2022-07-15 修订日期:2022-09-24 出版日期:2022-12-15 发布日期:2023-01-11
通信作者: 杨红健,博士,副教授。E-mail:yanghj@hebut.edu.cn刘晓莉,博士,副教授。E-mail:1993041@hebut.edu.cn
作者简介:梁慧慧(1998—),女,硕士研究生。主要从事镁质胶凝材料的研究。E-mail:15269754497@163.com
基金资助:
天津市科技计划(18YFCZZC00200)

Modification Research of Organic Phosphonic Acid to Magnesium Oxysulfate Cement

LIANG Huihui¹, LI Yang², YANG Hongjian¹, LIU Xiaoli¹, HE Yiting¹, ZHANG Yuting¹

1. School of Chemical Engineering and Technology, Hebei University of Technology, Tianjin 300400, China;
2. Tianjin Thermal Power Designing Institute, Tianjin 300204, China

Received:2022-07-15 Revised:2022-09-24 Online:2022-12-15 Published:2023-01-11

摘要/Abstract

摘要： 本文探究了两种有机膦酸对硫氧镁水泥抗压强度、耐水性能和凝结时间的影响,通过X射线衍射、同步热分析和扫描电子显微镜测试对硫氧镁水泥的物相组成及微观形貌进行表征和分析。结果表明:当氨基三亚甲基膦酸(ATMP)掺量在0.75%(质量分数,下同)时,相较空白组28 d抗压强度增加了113.99%,软化系数增加了101.86%;羟基乙叉二膦酸(HEDP)掺量为0.75%时,硫氧镁水泥表现出最佳机械强度及较高的缓凝效果,且软化系数达到0.93;两种有机膦酸进行复配(总掺量为0.75%),当m(ATMP)∶m(HEDP)为3∶1时,对硫氧镁水泥具有最佳改性效果。有机膦酸能与MgO水化过程中产生的[Mg(OH)(H₂O)_x]⁺形成稳定的螯合物,减缓活性MgO水解为Mg(OH)₂的进程,从而延缓硫氧镁水泥的凝结时间,为硫氧镁水泥在实际工程中的应用提供了可行性。

关键词: 硫氧镁水泥, 有机膦酸, 517晶相, 抗压强度, 耐水性能, 凝结时间

Abstract: The effects of two kinds of organic phosphonic acids on the compressive strength, water resistance, and setting time of magnesium oxysulfate cement were explored. The phase composition and microscopic morphology of magnesium oxysulfate cement were characterized by X-ray diffraction, simultaneous thermal analysis, and scanning electron microscopy. The results show that when the content of amino trimethylene phosphonic acid (ATMP) is 0.75% (mass fraction, the same below), the 28 d compressive strength increases by 113.99%, and the softening coefficient increases by 101.86% compared with the blank group. When the content of 1-hydroxyethylidene-1,1-diphosphonic acid (HEDP) is 0.75%, the magnesium oxysulfate cement shows the best compressive strength and higher retardation effect, and the softening coefficient reaches 0.93. Compounding of two organic phosphonic acids with a total content of 0.75%, when m(ATMP)∶m(HEDP) is 3∶1, it has the best modification effect on magnesium oxysulfate cement. [Mg(OH)(H₂O)_x]⁺ generated during the hydration of MgO and organic phosphonic acid form a stable chelate, which slows down the hydrolysis of active MgO to Mg(OH)₂, thereby delaying the setting time of magnesium oxysulfate cement. The addition of organic phosphonic acid provides feasibility for the application of magnesium oxysulfate cement in practical engineering.

Key words: magnesium oxysulfate cement, organic phosphonic acid, 517 phase, compressive strength, water resistance, setting time

中图分类号:

TQ172

梁慧慧, 李阳, 杨红健, 刘晓莉, 何怡婷, 张玉婷. 有机膦酸对硫氧镁水泥的改性研究[J]. 硅酸盐通报, 2022, 41(12): 4139-4146.

LIANG Huihui, LI Yang, YANG Hongjian, LIU Xiaoli, HE Yiting, ZHANG Yuting. Modification Research of Organic Phosphonic Acid to Magnesium Oxysulfate Cement[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(12): 4139-4146.

参考文献

[1] SOREL S. On a new magnesium cement[J]. Comptes Rendus de l'Académie des Sciences, 1867, 65: 102-104.
[2] 王爱国,楚英杰,徐海燕,等.碱式硫酸镁水泥的研究进展及性能提升技术[J].材料导报,2020,34(13):13091-13099.
WANG A G, CHU Y J, XU H Y, et al. Research progress and performance improvement technology of basic magnesium sulfate cement[J]. Materials Reports, 2020, 34(13): 13091-13099 (in Chinese).
[3] BEAUDOIN J J, RAMACHANDRAN V S. Strength development in magnesium oxysulfate cement[J]. Cement and Concrete Research, 1978, 8(1): 103-112.
[4] WU C Y, ZHANG H F, YU H F. Preparation and properties of modified magnesium oxysulfate cement derived from waste sulfuric acid[J]. Advances in Cement Research, 2016, 28(3): 178-188.
[5] 刘欣伟,冯雅丽,李浩然,等.菱镁矿制备轻烧氧化镁及其水化动力学研究[J].中南大学学报(自然科学版),2011,42(12):3912-3917.
LIU X W, FENG Y L, LI H R, et al. Preparation of light-burned magnesia from magnesite and its hydration kinetics[J]. Journal of Central South University (Science and Technology), 2011, 42(12): 3912-3917 (in Chinese).
[6] DEMEDIUK T, COLE W F. A study of mangesium oxysulphates[J]. Australian Journal of Chemistry, 1957, 10(3): 287.
[7] WANG N, YU H F, BI W L, et al. Effects of sodium citrate and citric acid on the properties of magnesium oxysulfate cement[J]. Construction and Building Materials, 2018, 169: 697-704.
[8] 邓德华.磷酸根离子对氯氧镁水泥水化物稳定性的影响[J].建筑材料学报,2002,5(1):9-12.
DENG D H. Effect of the phosphate anion on the stabilization of hydrate in magnesium oxychloride cement[J]. Journal of Building Materials, 2002, 5(1): 9-12 (in Chinese).
[9] CHEN X Y, ZHANG T T, BI W L, et al. Effect of tartaric acid and phosphoric acid on the water resistance of magnesium oxychloride (MOC) cement[J]. Construction and Building Materials, 2019, 213: 528-536.
[10] 吴成友,余红发,文静,等.改性硫氧镁水泥物相组成及性能研究[J].新型建筑材料,2013,40(5):68-72.
WU C Y, YU H F, WEN J, et al. Study of phase compositions and properties of modified magnesium oxysulphate cement[J]. New Building Materials, 2013, 40(5): 68-72 (in Chinese).
[11] 郑直,詹炳根.柠檬酸对硫氧镁水泥改性作用[J].合肥工业大学学报(自然科学版),2013,36(4):461-464.
ZHENG Z, ZHAN B G. Research on modification effects of citric acid on magnesium oxysulfate cement[J]. Journal of Hefei University of Technology (Natural Science), 2013, 36(4): 461-464 (in Chinese).
[12] RAMACHANDRAN V S, LOWERY M S, WISE T, et al. The role of phosphonates in the hydration of Portland cement[J]. Materials and Structures, 1993, 26(7): 425-432.
[13] 李北星,吕兴栋,魏运权,等.氨基三亚甲基膦酸对水泥水化的影响[J].建筑材料学报,2016,19(3):417-423.
LI B X, LYU X D, WEI Y Q, et al. Effect of amino trimethylene phosphonic acid on hydration of Portland cement[J]. Journal of Building Materials, 2016, 19(3): 417-423 (in Chinese).
[14] 唐芮枫,王子明,兰明章,等.缓凝剂对高贝利特硫铝酸盐水泥水化和性能的影响[J].硅酸盐通报,2020,39(12):3763-3769.
TANG R F, WANG Z M, LAN M Z, et al. Effects of retarders on hydration and properties of high-belite calcium sulphoaluminate cement[J]. Bulletin of the Chinese Ceramic Society, 2020, 39(12): 3763-3769 (in Chinese).
[15] 董金美,余红发,张立明.水合法测定活性MgO含量的试验条件研究[J].盐湖研究,2010,18(1):38-41.
DONG J M, YU H F, ZHANG L M. Study on experimental conditions of hydration methods of determining active magnesium oxide content[J]. Journal of Salt Lake Research, 2010, 18(1): 38-41 (in Chinese).
[16] FELHÖSI I, ÉKES R, BARADLAI P, et al. Coupled radiotracer and voltammetric study of the adsorption of 1-hydroxy-ethane-1, 1-diphosphonic acid on polycrystalline gold[J]. Journal of Electroanalytical Chemistry, 2000, 480(1/2): 199-208.
[17] ZHANG X Y, YANG X W, HAO L, et al. Solid-liquid equilibrium of 1-hydroxyethane-1,1-diphosphonic acid in different solvents[J]. Fluid Phase Equilibria, 2013, 338: 265-268.
[18] WEN R M, DENG S Q, ZHU Z L, et al. Studies on complexation of ATMP, PBTCA, PAA and PMAAA with Ca²⁺ in aqueous solutions[J]. Chemical Research in Chinese Universities, 2004, 20(1): 36-39.
[19] RUNČEVSKI T, WU C Y, YU H F, et al. Structural characterization of a new magnesium oxysulfate hydrate cement phase and its surface reactions with atmospheric carbon dioxide[J]. Journal of the American Ceramic Society, 2013, 96(11): 3609-3616.

有机膦酸对硫氧镁水泥的改性研究

Modification Research of Organic Phosphonic Acid to Magnesium Oxysulfate Cement

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	陈春红, 俞江, 刘荣桂, 王磊, 刘惠, 伍金龙. 干湿循环下再生细骨料混凝土的氯离子渗透性能[J]. 硅酸盐通报, 2023, 42(4): 1217-1225.
[2]	何俊, 管家贤, 吕晓龙, 张驰. 纳米硅粉改良碱渣-矿渣固化淤泥的抗硫酸镁侵蚀性能[J]. 硅酸盐通报, 2023, 42(4): 1344-1352.
[3]	刘扬, 陈湘, 王柏文, 鲁乃唯, 肖欣欣, 罗冬. 碱激发粉煤灰-矿渣-电石渣基地聚物的制备及强度机理[J]. 硅酸盐通报, 2023, 42(4): 1353-1362.
[4]	张先伟, 高永红, 王平, 李江山, 刘世宇, 郎雷, 雷学文. 电解锰渣-生活垃圾焚烧底渣协同制备路面基层材料试验研究[J]. 硅酸盐通报, 2023, 42(4): 1363-1373.
[5]	黄利祥, 刘泽, 原航, 王栋民, 危鹏, 姜宏健. 赤泥-石膏复合激发蒸压加气混凝土的制备与性能研究[J]. 硅酸盐通报, 2023, 42(4): 1393-1399.
[6]	施晓晨, 水中和, 李浩源, 肖勋光, 孙涛, 王雷冲. 紫外预处理对硅酸盐水泥浆体早期碳化性能的影响[J]. 硅酸盐通报, 2023, 42(3): 786-792.
[7]	葛津宇, 韦华, 徐菲, 韩雪松, 朱鹏飞, 肖怀前, 李怀森. CSH-蒙脱石界面能对水泥固化蒙脱土抗压强度的影响[J]. 硅酸盐通报, 2023, 42(3): 827-836.
[8]	陈新明, 张浩文, 焦华喆, 杨柳华, 荣阳阳. HPMC及硼砂对新型防漏高强注浆料性能及微观结构的影响[J]. 硅酸盐通报, 2023, 42(3): 861-870.
[9]	房延凤, 王凇宁, 佟钰, 孙小巍, 丁向群, 苏文. 碳酸化预处理对钢渣-水泥复合胶凝材料体积安定性及水化活性的影响[J]. 硅酸盐通报, 2023, 42(3): 1001-1007.
[10]	王雪芳, 曾天鑫, 周豪杰. 碱激发剂对单组份碱激发镍渣水泥混凝土抗碳化性能的影响[J]. 硅酸盐通报, 2023, 42(3): 1008-1015.
[11]	樊璐洋, 金子豪, 苏英, 崔程嘉, 王斌. 基于响应面法的半水磷石膏复合胶凝材料优化设计及性能研究[J]. 硅酸盐通报, 2023, 42(2): 626-636.
[12]	姜同辉, 杨雄峰, 阳佳丁, 钱枫华, 平乐, 杨腾宇, 王晶, 张营, 冷发光. 石粉种类及含量对C60机制砂混凝土性能的影响[J]. 硅酸盐通报, 2023, 42(1): 92-99.
[13]	关虓, 龙行, 丁莎, 张鹏鑫. 冻融作用下活化煤矸石粉混凝土损伤劣化规律[J]. 硅酸盐通报, 2023, 42(1): 144-150.
[14]	陈邢, 于峰, 曹越, 方圆. 铁尾矿粉-脱硫灰胶凝材料的制备及性能研究[J]. 硅酸盐通报, 2023, 42(1): 180-187.
[15]	张天潇, 廖宜顺, 刘立军, 王海宝, 董淇. 苎麻纤维增强磷建筑石膏复合材料耐水性能和力学性能研究[J]. 硅酸盐通报, 2023, 42(1): 213-221.