锰渣与再生砖骨料制备免烧砖的性能及应用

硅酸盐通报 ›› 2022, Vol. 41 ›› Issue (10): 3533-3541.

锰渣与再生砖骨料制备免烧砖的性能及应用

白敏¹, 龙广成¹, 谢友均¹, 王凡¹, 石莹莹¹, 周天阳²

1.中南大学土木工程学院,长沙 410075;
2.湘潭建工集团有限公司,湘潭 411100

收稿日期:2022-05-13 修回日期:2022-07-13 出版日期:2022-10-15 发布日期:2022-10-26
通讯作者: 龙广成,博士,教授。E-mail:longguangcheng@csu.edu.cn
作者简介:白敏(1996—),男,硕士研究生。主要从事固废资源化利用的研究。E-mail:minbai2021@163.com
基金资助:
湖南省重点领域研发计划(2020WK2005)

Properties and Application of Non-Fired Bricks Prepared from Manganese Slag and Recycled Brick Aggregates

BAI Min¹, LONG Guangcheng¹, XIE Youjun¹, WANG Fan¹, SHI Yingying¹, ZHOU Tianyang²

1. School of Civil Engineering, Central South University, Changsha 410075, China;
2. Xiangtan Construction Engineering Group Co., Ltd., Xiangtan 411100, China

Received:2022-05-13 Revised:2022-07-13 Online:2022-10-15 Published:2022-10-26

摘要/Abstract

摘要： 锰渣与再生砖骨料均属于大宗固废,提升大宗固废利用率具有重要的环境效益和经济效益。本文利用锰渣、再生砖骨料等制备了免烧砖,探究了锰渣掺量对免烧砖各项性能的影响,且对其微观结构及有害物质浸出行为进行了分析。结果表明:制备的免烧砖外观质量优良,色泽均一,尺寸标准;结合强度要求和抗冻性要求,锰渣掺量不超过10%(质量分数)时,可制备出强度、耐水性和耐久性优异的MU20免烧砖,锰渣掺量不超过15%时,可制备出性能优异的MU15免烧砖;掺适量锰渣的免烧砖中形成了较多的钙矾石相,有利于强度发展。锰渣和再生砖骨料制备的免烧砖可以应用于人行道等市政工程,应用效果良好。研究结果可为锰渣低碳资源化利用以及生态砖制品的生产和应用提供技术支持。

关键词: 锰渣, 再生砖骨料, 免烧砖, 强度, 耐水性, 耐久性, 工程应用

Abstract: Manganese slag and recycled brick aggregates both belong to bulk solid waste. Improvingthe utilization rate of bulk solid waste has important environmental and economic benefits. In this paper, non-fired bricks were prepared using manganese slag and recycled brick aggregates, the effect of manganese slag content on various properties of non-fired bricks were investigated, and the microstructure and harmful substance leaching behavior were analyzed. The results show that the non-fired bricks have good appearance quality, uniform color and standard size. Combining strength requirements and frost resistance requirements, MU20 non-fired bricks with excellent strength, water resistance and durability are prepared when manganese slag content is less than 10% (mass fraction). MU15 non-fired bricks with excellent properties are prepared when manganese slag content is less than 15%. More ettringite hydrate phase is formed in the non-fired bricks, which is beneficial to strength development. The non-fired bricks made from manganese slag and recycled brick aggregates have good application effect in sidewalks and other municipal projects. The research results provide technical support for the low carbon resource utilization of manganese slag and production and application of ecological brick products.

Key words: manganese slag, recycled brick aggregate, non-fired brick, strength, water resistance, durability, engineering application

中图分类号:

TU522

白敏, 龙广成, 谢友均, 王凡, 石莹莹, 周天阳. 锰渣与再生砖骨料制备免烧砖的性能及应用[J]. 硅酸盐通报, 2022, 41(10): 3533-3541.

BAI Min, LONG Guangcheng, XIE Youjun, WANG Fan, SHI Yingying, ZHOU Tianyang. Properties and Application of Non-Fired Bricks Prepared from Manganese Slag and Recycled Brick Aggregates[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(10): 3533-3541.

参考文献

[1] 江权.锰的存在及应用[J].中国锰业,2001,3:37-39.
JIANG Q. Manganese's exicfance and applyment[J]. China Manganese Industry, 2021, 3: 37-39 (in Chinese).
[2] WANG F, LONG G C, BAI M, et al. Application of electrolytic manganese residues in cement products through pozzolanic activity motivation and calcination[J]. Journal of Cleaner Production, 2022, 338: 130629.
[3] 聂紫萌,杨点,熊玉路,等.电解锰渣浆液烟气脱硫性能及机制[J].化工进展,2022,41(2):1063-1072.
NIE Z M, YANG D, XIONG Y L, et al. Performance and mechanism of electrolytic manganese slag slurry for flue gas desulfurization[J]. Chemical Industry and Engineering Progress, 2022, 41(2): 1063-1072 (in Chinese).
[4] 孙俊,饶帅,王东兴,等.硫酸-方铅矿体系高效浸出电解锰渣[J].中南大学学报(自然科学版),2021,52(11):3800-3812.
SUN J, RAO S, WANG D X, et al. High-efficiency leaching of electrolytic manganese residues in sulfuric acid-galena system[J]. Journal of Central South University (Science and Technology), 2021, 52(11): 3800-3812 (in Chinese).
[5] 刘士朋,张欢欢,程金科.电解锰渣中氨氮的草酸浸取工艺及机理研究[J].硅酸盐通报,2022,41(2):715-724.
LIU S P, ZHANG H H, CHENG J K. Technology and mechanism of leaching ammonia nitrogen from electrolyticmanganese residue with oxalic acid[J]. Bulletin of the Chinese Ceramic Society, 2022, 41(2): 715-724 (in Chinese).
[6] LI B, SHU J C, WU Y H, et al. Enhanced removal of Mn²⁺ and $\text{NH}^{+}_{4}$ in electrolytic manganese residue leachate by electrochemical and modified phosphate ore flotation tailings[J]. Separation and Purification Technology, 2022, 291.
[7] WANG Y G, GAO S, LIU X M, et al. Preparation of non-sintered permeable bricks using electrolytic manganese residue: environmental and NH₃-N recovery benefits[J]. Journal of Hazardous Materials, 2019, 378: 120768.
[8] 吴霜.电解锰渣制备免烧砖的实验研究[D].贵阳:贵州大学,2016:14-16.
WU S. Experimental study on preparation of non-burnt brick by electrolytic manganese residue[D]. Guiyang: Guizhou University, 2016: 14-16 (in Chinese).
[9] QIN J T, WANG J W, WANG H F, et al. Effect of aggregate addition on the properties of unburned brick of electrolytic manganese slag[J]. IOP Conference Series: Earth and Environmental Science, 2017, 94: 012173.
[10] 郭盼盼,张云升,范建平,等.免烧锰渣砖的配合比设计、制备与性能研究[J].硅酸盐通报,2013,32(5):786-793.
GUO P P, ZHANG Y S, FAN J P, et al. Mixture ratio design, preparation and performance of non-burnt manganese slag brick[J]. Bulletin of the Chinese Ceramic Society, 2013, 32(5): 786-793 (in Chinese).
[11] LAN J R, ZHANG S S, MEI T, et al. Mechanochemical modification of electrolytic manganese residue: ammonium nitrogen recycling, heavy metal solidification, and baking-free brick preparation[J]. Journal of Cleaner Production, 2021, 329: 129727.
[12] 尤晓宇,王家伟,王海峰,等.混料含水率对电解锰渣免烧砖性能的影响[J].硅酸盐通报,2020,39(10):3311-3315.
YOU X Y, WANG J W, WANG H F, et al. Influence of water content of mixture on properties of unburned brick with electrolytic manganese slag[J]. Bulletin of the Chinese Ceramic Society, 2020, 39(10): 3311-3315 (in Chinese).
[13] LI C X, ZHANG Q W. Preparation and property of unfired brick using electrolytic manganese residue[J]. Journal of Physics: Conference Series, 2020, 1681(1): 012009.
[14] ZHOU C B, DU B, WANG N F, et al. Preparation and strength property of autoclaved bricks from electrolytic manganese residue[J]. Journal of Cleaner Production, 2014, 84: 707-714.
[15] 秦吉涛,王家伟,王海峰,等.水泥添加量对电解锰渣免烧砖性能的影响[J].硅酸盐通报,2017,36(10):3511-3515.
QIN J T, WANG J W, WANG H F, et al. Effect of cement addition on the properties of unburned brick of electrolytic manganese slag[J]. Bulletin of the Chinese Ceramic Society, 2017, 36(10): 3511-3515 (in Chinese).
[16] 赵敏,彭家惠,张明涛,等.硅酸盐水泥增强陶瓷模具石膏机理研究[J].湖南大学学报(自然科学版),2014,41(12):46-52.
ZHAO M, PENG J H, ZHANG M T, et al. Mechanisms for the enhanced ceramics gypsum model with ordinary Portland cement[J]. Journal of Hunan University (Natural Sciences), 2014, 41(12): 46-52 (in Chinese).
[17] 付建.硅酸盐水泥对建筑石膏强度和耐水性的影响[J].非金属矿,2019,42(5):39-41.
FU J. Effect of Portland cement on strength and water resistance of building gypsum[J]. Non-Metallic Mines, 2019, 42(5): 39-41 (in Chinese).
[18] BALASUBRAMANIAM T, KARTHIK P, SURESHKUMAR S, et al. Effectiveness of industrial waste materials used as ingredients in fly ash brick manufacturing[J]. Materials Today: Proceedings, 2021, 45: 7850-7858.
[19] XU Y T, LIU X M, ZHANG Y L, et al. Investigation on sulfate activation of electrolytic manganese residue on early activity of blast furnace slag in cement-based cementitious material[J]. Construction and Building Materials, 2019, 229: 116831.
[20] WANG Y G, ZHANG N, REN Y Y, et al. Effect of electrolytic manganese residue in fly ash-based cementitious material: hydration behavior and microstructure[J]. Materials (Basel, Switzerland), 2021, 14(22): 7047.
[21] WANG F, LONG G C, BAI M, et al. Cleaner and safer disposal of electrolytic manganese residues in cement-based materials using direct electric curing[J]. Journal of Cleaner Production, 2022, 356: 131842.