再生混凝土单轴受压下多重界面过渡区的破坏机理研究

摘要/Abstract

摘要： 为研究再生粗骨料混凝土在单轴受压荷载下的破坏特性,使用数字图像相关技术记录混凝土立方体在破坏过程中的应变变化规律,并结合显微硬度测试、背散射电子成像技术等观测手段对界面过渡区的宽度和孔隙率进行定量表征。试验结果表明,分别经骨料强化和砂浆强化后,再生混凝土的抗压强度较未处理试样提升了17.86%和35.55%,说明砂浆强化更有利于提升再生混凝土的抗压强度。骨料强化可以提升老砂浆显微硬度值,降低老骨料-老砂浆界面过渡区孔隙率;砂浆强化可以提升新砂浆显微硬度值,降低老骨料-新砂浆界面过渡区以及新-老砂浆界面过渡区的孔隙率。经强化处理后的特定界面产生贯通裂缝的概率降低。

关键词: 再生粗骨料混凝土, 破坏机理, 界面过渡区, 骨料强化, 砂浆强化, 显微硬度, 孔隙率

Abstract: To study the failure characteristics of recycled coarse aggregate concrete under uniaxial compression, the strain change law of concrete cube in the failure process was recorded by digital image correlation technology, and the width and porosity of interfacial transition zones were characterized by microhardness test and backscattered electron imaging. The experimental results show that the compressive strength of recycled concrete increases by 17.86% and 35.55% compared with untreated samples after aggregate reinforcement and mortar reinforcement, respectively. It indicates that mortar reinforcement is more helpful for improving the compressive strength of recycled concrete. The microhardness of the old mortar increases, and the porosity of the interface transition zone between old aggregate and old mortar is reduced by aggregate reinforcement. The microhardness of new mortar increases, and the porosity of the interface transition zone between old aggregate and new mortar and between old mortar and new mortar is reduced by mortar reinforcement. The probability of passing penetrating cracks decreases for reinforcement interfaces.

Key words: recycled coarse aggregate concrete, failure mechanism, interfacial transition zone, aggregate reinforcement, mortar reinforcement, microhardness, porosity

中图分类号:

TU528

郭嘉, 高嵩, 班顺莉, 宫尧尧, 孟书灵. 再生混凝土单轴受压下多重界面过渡区的破坏机理研究[J]. 硅酸盐通报, 2022, 41(10): 3445-3457.

GUO Jia, GAO Song, BAN Shunli, GONG Yaoyao, MENG Shuling. Failure Mechanism of Multi-Interfacial Transition Zones of Recycled Concrete under Uniaxial Compression[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2022, 41(10): 3445-3457.

参考文献

[1] 陈明星,隋昱文,郭莎莎.中国新型城镇化在“十九大”后发展的新态势[J].地理研究,2019,38(1):181-192.
CHEN M X, SUI Y W, GUO S S. Perspective of China's new urbanization after 19th CPC national congress[J]. Geographical Research, 2019, 38(1): 181-192 (in Chinese).
[2] 常洪雷,陈繁育,金祖权,等.再生骨料混凝土在护岸工程应用的可行性[J].材料导报,2020,34(s2):1206-1211.
CHANG H L, CHEN F Y, JIN Z Q, et al. Feasibility of utilizing recycled aggregate concrete for revetment engineering[J]. Materials Reports, 2020, 34(s2): 1206-1211 (in Chinese).
[3] 陈守开,常承艳,郭磊,等.再生骨料掺量对透水混凝土性能的影响[J].应用基础与工程科学学报,2018,26(1):98-108.
CHEN S K, CHANG C Y, GUO L, et al. Influence of recycled aggregates content on the performance of pervious concrete[J]. Journal of Basic Science and Engineering, 2018, 26(1): 98-108 (in Chinese).
[4] GAO S, GONG Y Y, LI N, et al. A comparative study of the properties of recycled concrete prepared with nano-SiO₂ and CO₂ cured recycled coarse aggregates subjected to aggressive ions environment[J]. Materials (Basel, Switzerland), 2021, 14(17): 4960.
[5] ZENG W L, ZHAO Y X, ZHENG H B, et al. Improvement in corrosion resistance of recycled aggregate concrete by nano silica suspension modification on recycled aggregates[J]. Cement and Concrete Composites, 2020, 106: 103476.
[6] 李秋义,李云霞,朱崇绩.颗粒整形对再生粗骨料性能的影响[J].材料科学与工艺,2005,13(6):579-581+585.
LI Q Y, LI Y X, ZHU C J. The influence of a particle shape correcting technique in properties of recycled coarse aggregate[J]. Materials Science and Technology, 2005, 13(6): 579-581+585 (in Chinese).
[7] CHEN R M, MO K H, LING T C. Offsetting strength loss in concrete via ITZ enhancement: from the perspective of utilizing new alternative aggregate[J]. Cement and Concrete Composites, 2022, 127: 104385.
[8] HOSAN A, SHAIKH F U A, SARKER P, et al. Nano- and micro-scale characterisation of interfacial transition zone (ITZ) of high volume slag and slag-fly ash blended concretes containing nano SiO₂ and nano CaCO₃[J]. Construction and Building Materials, 2021, 269: 121311.
[9] GUO L X, GUO Y H, ZHONG L. Research on the back analysis and failure mechanism of recycled concrete aggregate meso-parameters based on Box-Behnken Design response surface model[J]. Journal of Building Engineering, 2022, 51: 104317.
[10] 韩燕华,谢作为,刘方,等.基于CT图像的再生混凝土内部微变形演化分析[J].华南理工大学学报(自然科学版),2019,47(5):73-80.
HAN Y H, XIE Z W, LIU F, et al. Internal micro-deformation analysis of recycled aggregate concrete based on CT images[J]. Journal of South China University of Technology (Natural Science Edition), 2019, 47(5): 73-80 (in Chinese).
[11] 毛灵涛,孙倩文,袁则循,等.基于CT图像的混凝土单轴压缩裂隙与应变场分析[J].建筑材料学报,2016,19(3):449-455.
MAO L T, SUN Q W, YUAN Z X, et al. Crack and strain field analysis in concrete under uniaxial compression based on CT images[J]. Journal of Building Materials, 2016, 19(3): 449-455 (in Chinese).
[12] 高嵩,宫尧尧,班顺莉.硫酸盐侵蚀对纳米SiO₂改性再生混凝土性能的影响[J].沈阳建筑大学学报(自然科学版),2021,37(5):907-914.
GAO S, GONG Y Y, BAN S L. Effect of sulfate attack on properties of recycled concrete modified by nano-SiO₂[J]. Journal of Shenyang Jianzhu University (Natural Science), 2021, 37(5): 907-914 (in Chinese).
[13] 魏康,员方,董志强,等.基于标志点的多相机数字图像相关方法精度分析及土木工程中的应用[J].东南大学学报(自然科学版),2021,51(2):219-226.
WEI K, YUAN F, DONG Z Q, et al. Precision analysis and civil application of multi-camera digital image correlation method based on encoded targets[J]. Journal of Southeast University (Natural Science Edition), 2021, 51(2): 219-226 (in Chinese).
[14] 吴恺云,罗素蓉,郑建岚.基于非接触式观测技术的再生骨料混凝土断裂性能分析[J].工程力学,2022,39(3):147-157.
WU K Y, LUO S R, ZHENG J L. Fracture propertie analysis of recycled aggregate concrete based on digital image correlation technique[J]. Engineering Mechanics, 2022, 39(3): 147-157 (in Chinese).
[15] 国家质量监督检验检疫总局,中国国家标准化管理委员会.混凝土用再生粗骨料:GB/T 25177—2010[S].北京:中国标准出版社,2011.
General Administration of Quality Supervision, Inspection and Quarantine, Standardization Administration of China. Recycled coarse aggregate for concrete: GB/T 25177—2010[S]. Beijing: Standards Press of China, 2011 (in Chinese).
[16] 中华人民共和国住房和城乡建设部,国家市场监督管理总局.混凝土物理力学性能试验方法标准:GB/T 50081—2019[S].北京:中国建筑工业出版社,2019.
Ministry of Housing and Urban-Rural Development, PRC, State Administration for Market Regulation. Concrete physical and mechanical properties test method standard: GB/T 50081—2019[S]. Beijing: China Architecture and Building Press, 2019 (in Chinese).
[17] 白鹏翔,朱飞鹏,雷冬.基于数字图像相关技术的混凝土裂纹探测[J].混凝土,2020(12):138-141+146.
BAI P X, ZHU F P, LEI D. Concrete micro crack detection based on digital image correlation[J]. Concrete, 2020(12): 138-141+146 (in Chinese).
[18] MENG T, WEI H D, DAI D W, et al. Effect of brick aggregate on failure process of mixed recycled aggregate concrete via X-CT[J]. Construction and Building Materials, 2022, 327: 126934.
[19] 黄燕,胡翔,史才军,等.混凝土中水泥浆体与骨料界面过渡区的形成与改进综述[J/OL].材料导报,2023(1):1-22[2022-07-14].http://kns.cnki.net/kcms/detail/50.1078.TB.20211201.2349.002.html.
HUANG Y, HU X, SHI C J, et al. Summary of formation and improvement of interface transition zone between cement paste and aggregate in concrete[J/OL]. Material Report, 2023(1): 1-22 [2022-07-14]. http://kns.cnki.net/kcms/detail/50.1078.TB.20211201.2349.002.htm (in Chinese).
[20] 吴子豪,王武祥,刘晓通,等.硅灰对超轻水泥基复合保温材料性能的影响[J].硅酸盐通报,2021,40(12):4030-4036.
WU Z H, WANG W X, LIU X T, et al. Effect of silica fume on properties of ultra-light cement-based composite thermal insulation materials[J]. Bulletin of the Chinese Ceramic Society, 2021, 40(12): 4030-4036 (in Chinese).
[21] 徐晶,王先志.纳米二氧化硅对混凝土界面过渡区的改性机制及其多尺度模型[J].硅酸盐学报,2018,46(8):1053-1058.
XU J, WANG X Z. Effect of nano-silica modification on interfacial transition zone in concrete and its multiscale modelling[J]. Journal of the Chinese Ceramic Society, 2018, 46(8): 1053-1058 (in Chinese).
[22] 张雄,张恒,张晓乐,等.硅灰调控混凝土力学性能的关键界面参数研究[J].建筑材料学报,2019,22(4):626-631.
ZHANG X, ZHANG H, ZHANG X L, et al. Key interface parameters for the control of silica fume on mechanical properties of concrete[J]. Journal of Building Materials, 2019, 22(4): 626-631 (in Chinese).
[23] ZHENG Y X, ZHUO J B, ZHANG P. A review on durability of nano-SiO₂ and basalt fiber modified recycled aggregate concrete[J]. Construction and Building Materials, 2021, 304: 124659.
[24] WONG H S, BUENFELD N R. Patch microstructure in cement-based materials: fact or artefact?[J]. Cement and Concrete Research, 2006, 36(5): 990-997.
[25] BEUSHAUSEN H, HÖHLIG B, TALOTTI M. The influence of substrate moisture preparation on bond strength of concrete overlays and the microstructure of the OTZ[J]. Cement and Concrete Research, 2017, 92: 84-91.
[26] 王德辉,史才军.水泥-硅灰-矿粉-粉煤灰四组分水泥基超高强混凝土的硬化过程[J].硅酸盐通报,2018,37(12):3951-3956+3962.
WANG D H, SHI C J. Hardening process of ultra-high strength concrete with cement-silica fume-slag-fly ash four binders[J]. Bulletin of the Chinese Ceramic Society, 2018, 37(12): 3951-3956+3962 (in Chinese).
[27] HEJAZI F, KARIM H, KAZEMI H, et al. Fracture mechanics modeling of reinforced concrete joints strengthened by CFRP sheets[J]. Case Studies in Construction Materials, 2022, 17: e01273.