碱激发作用下海相软土固化研究

硅酸盐通报 ›› 2021, Vol. 40 ›› Issue (7): 2248-2255.

碱激发作用下海相软土固化研究

王伟齐, 孙红, 葛修润

上海交通大学船舶海洋与建筑工程学院,上海 200240

收稿日期:2021-03-02 修回日期:2021-04-01 出版日期:2021-07-15 发布日期:2021-08-04
通讯作者: 孙红,博士,副教授。E-mail:sunhong@sjtu.edu.cn
作者简介:王伟齐(1995—),男,硕士研究生。主要从事软土固化方面的研究。E-mail:wangzhao568@sjtu.edu.cn
基金资助:
国家自然科学基金(41572255)

Solidification of Marine Soft Soil under Alkali Excitation

WANG Weiqi, SUN Hong, GE Xiurun

School of Naval Architecture, Ocean and Civil Engineering, Shanghai Jiao Tong University, Shanghai 200240, China

Received:2021-03-02 Revised:2021-04-01 Online:2021-07-15 Published:2021-08-04

摘要/Abstract

摘要： 为提高工业废料电石渣、原状灰固化软土的作用效果,选择聚羧酸减水剂,硅酸钠、硫酸钠、三乙醇胺作为外加剂,采用无侧限抗压强度试验、X射线衍射、电镜扫描试验研究各外加剂间的协同作用。结果表明,0.1%质量分数的聚羧酸减水剂分别与3%(质量分数)硅酸钠、0.9%(质量分数)硫酸钠复配时能显著提高固化土强度,并确定硅酸钠与硫酸钠以1:1双掺的复合早强剂。通过正交试验确定出减水剂、复合早强剂与工业废渣复配的最优配比。7 d、28 d龄期时,掺入复合早强剂的工业废渣固化软土比未掺时的强度增幅可达47%、77%。7 d龄期时,减水剂的分散效应在固化土中起主导作用,28 d龄期时,复合早强剂碱激发作用下的火山灰效应则更加明显。

关键词: 海相软土, 无侧限抗压强度, 固化剂, 固化机理

Abstract: In order to improve the effect of industrial waste calcium carbide slag and undisturbed ash on the solidification of soft soil, polycarboxylate superplasticizer, sodium silicate, sodium sulfate, and triethanolamine were selected as additives. The unconfined compressive strength test (UCS), X-ray diffraction (XRD), and scanning electron microscope (SEM) were used to study the synergistic effect of the additives. The results show that 0.1% (mass fraction) polycarboxylate superplasticizer combined with 3% (mass fraction) sodium silicate or 0.9% (mass fraction) sodium sulfate can significantly improve the strength of solidified soil, and the composite early strength agent with 1:1 ratio of sodium silicate and sodium sulfate was determined. The optimum ratio of superplasticizer, composite early strength agent and industrial waste residue were determined by orthogonal test. At the age of 7 d and 28 d, the strength increase of the solidified soft soil with composite early strength agent is 47% and 77% higher than that without composite early strength agent. At the age of 7 d, the dispersion effect of superplasticizer plays a leading role in the solidified soil, while at the age of 28 d, the pozzolanic effect of composite early strength agent under alkali excitation is more obvious.

Key words: marine soft soil, unconfined compressive strength, soil stabilizer, solidification mechanism

中图分类号:

TU447

王伟齐, 孙红, 葛修润. 碱激发作用下海相软土固化研究[J]. 硅酸盐通报, 2021, 40(7): 2248-2255.

WANG Weiqi, SUN Hong, GE Xiurun. Solidification of Marine Soft Soil under Alkali Excitation[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(7): 2248-2255.

参考文献

[1] CHEN L, LIN D F. Stabilization treatment of soft subgrade soil by sewage sludge ash and cement[J]. Journal of Hazardous Materials, 2009, 162(1): 321-327.
[2] ZENTAR R, WANG D X, ABRIAK N E, et al. Utilization of siliceous-aluminous fly ash and cement for solidification of marine sediments[J]. Construction and Building Materials, 2012, 35: 856-863.
[3] ARULRAJAH A, MOHAMMADINIA A, PHUMMIPHAN I, et al. Stabilization of recycled demolition aggregates by geopolymers comprising calcium carbide residue, fly ash and slag precursors[J]. Construction and Building Materials, 2016, 114: 864-873.
[4] KAMPALA A, HORPIBULSUK S. Engineering properties of silty clay stabilized with calcium carbide residue[J]. Journal of Materials in Civil Engineering, 2013, 25(5): 632-644.
[5] HORPIBULSUK S, MUNSRAKEST V, UDOMCHAI A, et al. Strength of sustainable non-bearing masonry units manufactured from calcium carbide residue and fly ash[J]. Construction and Building Materials, 2014, 71: 210-215.
[6] HORPIBULSUK S, PHETCHUAY C, CHINKULKIJNIWAT A, et al. Strength development in silty clay stabilized with calcium carbide residue and fly ash[J]. Soils and Foundations, 2013, 53(4): 477-486.
[7] HORPIBULSUK S, RACHAN R, RAKSACHON Y. Role of fly ash on strength and microstructure development in blended cement stabilized silty clay[J]. Soils and Foundations, 2009, 49(1): 85-98.
[8] MA C, CHEN L Z, CHEN B. Experimental study of effect of fly ash on self-compacting rammed earth construction stabilized with cement-based composites[J]. Journal of Materials in Civil Engineering, 2016, 28(7): 04016022.
[9] 韩天,于佳丽,吴燕开.硫酸钠激发钢渣粉活性改良水泥土试验研究[J].科学技术与工程,2019,19(7):231-238.
HAN T, YU J L, WU Y K. Experimental study on sodium sulfate exciting steel slag power activity and improving cement soil[J]. Science Technology and Engineering, 2019, 19(7): 231-238 (in Chinese).
[10] 郭印,徐日庆,邵允铖.淤泥质土的固化机理研究[J].浙江大学学报(工学版),2008,42(6):1071-1075.
GUO Y, XU R Q, SHAO Y C. Study on mechanism of muddy soil stabilization[J]. Journal of Zhejiang University (Engineering Science), 2008, 42(6): 1071-1075 (in Chinese).
[11] MA C, CHEN L Z, CHEN B. Analysis of strength development in soft clay stabilized with cement-based stabilizer[J]. Construction and Building Materials, 2014, 71: 354-362.
[12] 张豫川,乔子秦,高飞,等.工业废渣复合固化黄土强度特性及影响因素研究[J].长江科学院院报,2019,36(3):103-109.
ZHANG Y C, QIAO Z Q, GAO F, et al. Loess solidified by industrial waste residue composite curing agent: strength performance and influential factors[J]. Journal of Yangtze River Scientific Research Institute, 2019, 36(3): 103-109 (in Chinese).
[13] 俞家人,陈永辉,陈庚,等.地聚物固化软黏土的力学特征及机理分析[J].建筑材料学报,2020,23(2):364-371.
YU J R, CHEN Y H, CHEN G, et al. Mechanical behaviour of geopolymer stabilized clay and its mechanism[J]. Journal of Building Materials, 2020, 23(2): 364-371 (in Chinese).
[14] 都蓉蓉,张雄,顾明东,等.聚羧酸减水剂与增强组分的复合效应及原理[J].材料导报,2019,33(14):2461-2466.
DU R R, ZHANG X, GU M D, et al. The composition effect and mechanism of polycarboxylate superplasticizers and early strength agent[J]. Materials Reports, 2019, 33(14): 2461-2466 (in Chinese).
[15] 吕擎峰,申贝,王生新,等.水玻璃固化硫酸盐渍土强度特性及固化机制研究[J].岩土力学,2016,37(3):687-693+727.
LÜ Q F, SHEN B, WANG S X, et al. Strength characteristics and solidification mechanism of sulphate salty soil solidified with sodium silicate[J]. Rock and Soil Mechanics, 2016, 37(3): 687-693+727 (in Chinese).