活性掺合料对环氧树脂修补砂浆综合性能的影响

硅酸盐通报 ›› 2021, Vol. 40 ›› Issue (4): 1137-1146.

活性掺合料对环氧树脂修补砂浆综合性能的影响

龚建清^1,2, 李发磊^1,2, 李柯^1,2, 屈志刚^1,2

1.湖南大学土木工程学院,长沙 410082;
2.湖南大学,绿色先进土木工程材料及应用技术湖南省重点实验室,长沙 410082

收稿日期:2021-01-12 修回日期:2021-02-26 出版日期:2021-04-15 发布日期:2021-05-11
作者简介:龚建清(1963—),男,博士,副教授。主要从事建筑材料的研究和开发,超高性能混凝土和泡沫混凝土性能研究。E-mail:gongjianqing@hnu.edu.cn

Effects of Active Admixtures on Comprehensive Properties of Epoxy Resin Repair Mortar

GONG Jianqing^1,2, LI Falei^1,2, LI Ke^1,2, QU Zhigang^1,2

1. College of Civil Engineering, Hunan University, Changsha 410082, China;
2. Key Laboratory for Green andAdvanced Civil Engineering Materials and Application Technology of Hunan Province, Hunan University, Changsha 410082, China

Received:2021-01-12 Revised:2021-02-26 Online:2021-04-15 Published:2021-05-11

摘要/Abstract

摘要： 为了探究活性掺合料对环氧树脂修补砂浆的改性效果,为修补工程应用提供依据。研究硅灰和粉煤灰对环氧树脂修补砂浆力学性能、粘结强度、尺寸稳定性和抗冻性的影响,并采用扫描电子显微镜(SEM)和压汞法探究和分析影响机理。结果表明:环氧树脂使砂浆抗压强度降低,掺入硅灰可补偿强度损失,掺粉煤灰砂浆的强度随龄期增加而增加,但其中28 d和56 d强度低于对照组;硅灰和低掺量(≤10%,质量分数)粉煤灰可以提高修补砂浆粘结强度;硅灰对修补砂浆尺寸稳定性有不利影响,粉煤灰则相反;砂浆的抗冻性随着硅灰掺量增加先增加后降低,随着粉煤灰掺量增加而降低。

关键词: 环氧树脂修补砂浆, 活性掺合料, 抗压强度, 粘结强度, 尺寸稳定性, 抗冻性

Abstract: In order to explore the modification effect of active admixtures on epoxy resin repair mortar and provide basis for repair engineering application, the effects of silica fume and fly ash on the mechanical properties, bonding strength, dimensional stability and frost resistance of epoxy resin repair mortar were studied. The influence mechanism was explored and analyzed by the scanning electron microscope (SEM) and mercury intrusion method. The results indicate that epoxy resin reduces the compressive strength of mortar. Adding silica fume can make up for strength loss. The strength of mortar mixed with fly ash increases with the increase of age, but the strength of mortar at 28 d and 56 d is lower than that of the control group. Silica fume and low-content fly ash (≤10%, mass fraction) improve the bonding strength of repair mortar. However, silica fume has a negative effect on the dimensional stability of repair mortar, while fly ash has the opposite effect. The frost resistance of mortar increases first and then decreases along with the increase of silica fume content. And the frost resistance decreases with the increase of fly ash content. When epoxy resin emulsion and active admixture are mixed into mortar, the hydration products and the cured epoxy resin film form an interwoven spatial network structure to improve the compactness. And silica fume and fly ash can refine the pore size of slurry. So the improvement effect of silica fume powder is better.

Key words: epoxy resin repair mortar, active admixture, compressive strength, bonding strength, dimensional stability, frost resistance

中图分类号:

TU528.41

龚建清, 李发磊, 李柯, 屈志刚. 活性掺合料对环氧树脂修补砂浆综合性能的影响[J]. 硅酸盐通报, 2021, 40(4): 1137-1146.

GONG Jianqing, LI Falei, LI Ke, QU Zhigang. Effects of Active Admixtures on Comprehensive Properties of Epoxy Resin Repair Mortar[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(4): 1137-1146.

参考文献

[1] AGGARWAL L K, THAPLIYAL P C, KARADE S R. Properties of polymer-modified mortars using epoxy and acrylic emulsions[J]. Construction and Building Materials, 2007, 21(2): 379-383.
[2] 张建生,沈玉龙.环氧乳液水泥砂浆修补材料的性能研究[J].化学建材,2003(2):34-35.
ZHANG J S, SHEN Y L. Study of performance of epoxy emulsion used for cement mortar repair material[J]. Chemical Materials for Construction, 2003(2): 34-35 (in Chinese).
[3] 李志坚,邵亮.环氧胶泥在三峡二期工程导流底孔缺陷修补中的应用[J].水利水电快报,2011,32(12):35-38.
LI Z J, SHAO L. Application of epoxy cement in the defect repair of the diversion bottom hole in the second phase of the Three Gorges Project[J]. Express Water Resources & Hydropower Information, 2011, 32(12): 35-38 (in Chinese).
[4] 黄政宇,田甜.水性环氧树脂乳液改性水泥砂浆性能的研究[J].国外建材科技,2007,28(1):20-23.
HUANG Z Y, TIAN T. Research on properties of waterborne epoxy resin emulsion modified cement mortar[J]. Science and Technology of Overseas Building Materials, 2007, 28(1): 20-23 (in Chinese).
[5] 李国民.耐盐冻水泥基修补材料与旧混凝土粘结性能研究[J].新型建筑材料,2019,46(4):20-23.
LI G M. Study on the bonding properties of salt-resistant cement based patching material with old concrete[J]. New Building Materials, 2019, 46(4): 20-23 (in Chinese).
[6] 孙华东,范维玉,梁明,等.沥青基路面裂缝修补材料粘结性能影响研究[J].新型建筑材料,2014,41(6):92-95.
SUN H D, FAN W Y, LIANG M, et al. The study of cohesive force of asphalt-base crack repairing material[J]. New Building Materials, 2014, 41(6): 92-95 (in Chinese).
[7] 厉伟光,徐玲玲,刘方,等.MMA基混凝土修补材料收缩性能的改善[J].混凝土,2005(11):27-29+45.
LI W G, XU L L, LIU F, et al. Improving shrinkage of the MMA based repair material for concrete[J]. Concrete, 2005(11): 27-29+45 (in Chinese).
[8] 石艳.膨胀剂对水泥基修补材料收缩性能的影响[J].东西南北,2018(23):144-145.
SHI Y. Influence of expander on shrinkage properties of cement-based repair materials[J].East-West, North-Sourth, 2018(23): 144-145 (in Chinese).
[9] 魏涛,苏杰.环氧-聚氨酯互穿聚合物网络水下混凝土修补材料的研究[J].中国建筑防水,2007(11):14-17.
WEI T, SU J. Development of epoxy-polyurethane interpenetrating polymer as mending material for under water concrete[J]. China Building Waterproofing, 2007(11): 14-17 (in Chinese).
[10] 王益国,李国豹,吴友仁,等.混凝土裂缝水下封闭修复技术及其工程应用[J].中国港湾建设,2014,34(5):5-8+13.
WANG Y G, LI G B, WU Y R, et al. Closing patch technology for water concrete cracks and its application[J]. China Harbour Engineering, 2014, 34(5): 5-8+13 (in Chinese).
[11] 雷卧龙,朱涵,刘昂.橡胶颗粒掺量与粒径对环氧树脂混凝土力学与变形性能的影响[J].工业建筑,2017,47(3):137-141+168.
LEI W L, ZHU H, LIU A. Effects of mechanical properties and deformation feature of epoxy resin concrete by dosage and particle size of crumb rubber[J]. Industrial Construction, 2017, 47(3): 137-141+168 (in Chinese).
[12] 肖力光,李海军,焦长军,等.新型环氧树脂乳液改性水泥砂浆性能的研究[J].混凝土,2006(11):46-49.
XIAO L G, LI H J, JIAO C J, et al. Study of cement mortars modified by epoxy emulsion(EEM)[J]. Concrete, 2006(11): 46-49 (in Chinese).
[13] 李显,李飞,陆加越,等.粉煤灰对再生砖砌体骨料混凝土干燥收缩性能的影响[J].混凝土与水泥制品,2018(5):96-100.
LI X, LI F, LU J Y, et al. Influence of fly ash on the drying shrinkage performance of recyled brick masonry aggregate concrete[J]. China Concrete and Cement Products, 2018(5): 96-100 (in Chinese).
[14] 李淑进,赵铁军,吴科如.混凝土渗透性与微观结构关系的研究[J].混凝土与水泥制品,2004(2):6-8.
LI S J, ZHAO T J, WU K R. Relationship between permeability and microstructure of concrete[J]. China Concrete and Cement Products, 2004(2): 6-8 (in Chinese).

[1]	刘永毅, 任尊超, 袁连旺, 栾从起, 王金邦, 周宗辉. 响应曲面法优化高强硅酸盐水泥熟料矿物组成的研究[J]. 硅酸盐通报, 2021, 40(4): 1088-1096.
[2]	陈逸明, 林培桐, 李云龙, 刘锦红, 汪峻峰, 鲁刘磊. 高抗蚀胶凝材料的制备及其抗硫酸盐侵蚀性能研究[J]. 硅酸盐通报, 2021, 40(4): 1116-1127.
[3]	缪汉良, 赵斌, 纪荣健, 杨建明. 早龄期磷酸钾镁水泥砂浆的抗冻性评价[J]. 硅酸盐通报, 2021, 40(4): 1128-1136.
[4]	周茗如, 李宁, 钟琳, 李少飞. 湿陷性黄土地区劈裂注浆桩芯结石体强度试验研究[J]. 硅酸盐通报, 2021, 40(4): 1147-1153.
[5]	黄安, 李北星, 杨建波, 王丽静. 蒸养制度对预制桥面板混凝土强度与抗渗性的影响[J]. 硅酸盐通报, 2021, 40(4): 1170-1177.
[6]	周学军, 咸国栋, 王振, 刘哲, 王兴博, 王卫东. 高强度低导热泡沫混凝土性能研究[J]. 硅酸盐通报, 2021, 40(4): 1186-1192.
[7]	张广泰, 李瑞祥, 刘诗拓, 阿迪力·赛买提, 耿天娇. 冷热循环下纤维混凝土与高强钢筋间粘结强度损伤模型[J]. 硅酸盐通报, 2021, 40(4): 1193-1204.
[8]	管柏伦, 郭荣鑫, 齐荣庆, 付朝书, 张敏, 张文帅. 偏高岭土-粉煤灰基地聚物砂浆力学性能研究[J]. 硅酸盐通报, 2021, 40(4): 1250-1257.
[9]	王旭东, 李伟斌, 赵君, 左楠楠, 史竹青, 王鹏程, 王维维, 高卫杰. 新型赤泥基充填材料的制备与性能研究[J]. 硅酸盐通报, 2021, 40(4): 1280-1285.
[10]	刘蕾, 姚勇, 张玲玲. 改性夯土墙材的强度影响因素相关性研究[J]. 硅酸盐通报, 2021, 40(4): 1286-1295.
[11]	魏达, 朱平华, 王新杰, 刘惠, 刘少峰, 贾学军. 再生粗骨料附着砂浆含量对再生混凝土抗冻耐久性的影响[J]. 硅酸盐通报, 2021, 40(3): 765-774.
[12]	薛文, 王腾, 程文杰, 沈鸿儒, 李乙, 陈江瑛, 朱瑶宏. 低温冻融循环对陶粒混凝土动态力学性能的影响[J]. 硅酸盐通报, 2021, 40(3): 821-828.
[13]	刘广英, 郭向宇, 戴仕炳, 戴仕宝, 满晓磊. 煅烧温度对天然水硬石灰物理力学特性影响研究[J]. 硅酸盐通报, 2021, 40(3): 883-888.
[14]	刘谦, 郭玉森, 仲涛, 黄清云. 高火山灰活性煅烧煤矸石添加量对水泥抗压强度的影响[J]. 硅酸盐通报, 2021, 40(3): 936-942.
[15]	沈燕, 朱航宇, 王培芳, 张伟. 锂盐对硼砂在硫铝酸盐水泥中作用的影响[J]. 硅酸盐通报, 2021, 40(2): 377-383.