高流动性磷酸铵镁水泥硬化浆体耐盐腐蚀性能试验研究

硅酸盐通报 ›› 2021, Vol. 40 ›› Issue (3): 750-757.

高流动性磷酸铵镁水泥硬化浆体耐盐腐蚀性能试验研究

李涛¹, 张继文², 姜海楼², 杨建明³

1.三江学院土木工程学院,南京 210012;
2.东南大学土木工程学院,南京 210096;
3.盐城工学院土木工程学院,盐城 224051

收稿日期:2020-10-21 修回日期:2021-01-01 出版日期:2021-03-15 发布日期:2021-04-13
通讯作者: 张继文,教授。E-mail:Jwzhang@vip.163.com
作者简介:李涛(1990—),男,讲师。主要从事新型材料耐久性的研究。E-mail:yglitaotao@163.com
基金资助:
中国铁路总公司科研项目(P2018G005);国家自然科学基金面上项目(51578475)

Salt Corrosion Resistance of Hardened Slurry of Magnesium Ammonium Phosphate Cement with High Fluidity

LI Tao¹, ZHANG Jiwen², JIANG Hailou², YANG Jianming³

1. School of Civil Engineering, San Jiang University, Nanjing 210012, China;
2. School of Civil Engineering, Southeast University, Nanjing 210096, China;
3. School of Civil Engineering, Yancheng Institute of Technology, Yancheng 224051, China

Received:2020-10-21 Revised:2021-01-01 Online:2021-03-15 Published:2021-04-13

摘要/Abstract

摘要： 为研究高流动性磷酸铵镁水泥(MAPC)硬化浆体耐盐腐蚀性能,通过测试高流动性MAPC的抗压强度、抗折强度、变形、吸水率、流动性、水化温度曲线以及微观形貌,对比研究了空白组M0和单掺水玻璃M1的MAPC硬化浆体长期浸泡在清水、氯化钠和硫酸钠溶液中的相关性能。试验结果表明:单掺水玻璃提高了MAPC硬化浆体的早期水化反应速率以及流动性;单掺水玻璃提高了MAPC硬化浆体的强度,改善了变形,降低了吸水率。此外,单掺水玻璃的M1浆体试块无论在何种溶液下进行浸泡,其性能均优于空白组M0,其中在硫酸盐溶液下性能最佳。

关键词: 磷酸铵镁水泥(MAPC), 高流动性, 硬化浆体, 腐蚀, 水玻璃, 强度

Abstract: In order to study the salt corrosion resistance of hardened slurry of magnesium ammonium phosphate cement with high fluidity. The compressive strength, flexural strength, deformation, water absorption, fluidity, hydration temperature curve and microstructure of MAPC cement with high fluidity were tested. The properties of MAPC hardened slurry of the blank group M0 and single mixing water glass M1 immersed in water, sodium chloride and sodium sulfate solutions for a long time were studied. The experimental results show that the early hydration reaction rate and fluidity of MAPC hardened slurry are improved by single mixing water glass. The strength, deformation and water absorption of MAPC hardened slurry are improved by single mixing water glass. In addition, no matter under any solution, the performance of M1 slurry sample of single mixing water glass is better than that of the blank group M0, and the performance is the best under sulfate solution.

Key words: magnesium ammonium phosphate cement (MAPC), high fluidity, hardened slurry, corrosion, water glass, strength

中图分类号:

TQ172

李涛, 张继文, 姜海楼, 杨建明. 高流动性磷酸铵镁水泥硬化浆体耐盐腐蚀性能试验研究[J]. 硅酸盐通报, 2021, 40(3): 750-757.

LI Tao, ZHANG Jiwen, JIANG Hailou, YANG Jianming. Salt Corrosion Resistance of Hardened Slurry of Magnesium Ammonium Phosphate Cement with High Fluidity[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(3): 750-757.

参考文献

[1] 杜采颐.新型化学结合磷酸盐胶凝材料性能的研究[D].绵阳:西南科技大学,2008:7-8.
DU C Y. Study on properties of new chemically bonded phosphate cementitious materials[D]. Mianyang: Southwest University of Science and Technology, 2008: 7-8 (in Chinese).
[2] SEEHRA S S, GUPTA S, KUMAR S. Rapid setting magnesium phosphate cement for quick repair of concrete pavements-characterisation and durability aspects[J]. Cement and Concrete Research, 1993, 23(2): 254-266.
[3] 姜自超,张时豪,房汉鸣,等.磷酸铵镁水泥修补材料修补性能研究[J].硅酸盐通报,2017,36(1):391-395.
JIANG Z C, ZHANG S H, FANG H M, et al. Repair performance of magnesium ammonium phosphate cement (MAPC) mending materials[J]. Bulletin of the Chinese Ceramic Society, 2017, 36(1): 391-395 (in Chinese).
[4] 姜洪义,梁波,张联盟.MPB超早强混凝土修补材料的研究[J].建筑材料学报,2001,4(2):196-198.
JIANG H Y, LIANG B, ZHANG L M. Investigation of MPB with super early strength for repair of concrete[J]. Journal of Building Materials, 2001, 4(2): 196-198 (in Chinese).
[5] YANG Q B, ZHANG S Q, WU X L. Deicer-scaling resistance of phosphate cement-based binder for rapid repair of concrete[J]. Cement and Concrete Research, 2002, 32(1): 165-168.
[6] YANG Q B, WU X L. Factors influencing properties of phosphate cement-based binder for rapid repair of concrete[J]. Cement and Concrete Research, 1999, 29(3): 389-396.
[7] WAGH A S, GEORGE W, DROZD V, et al. Inorganic phosphate compositions and methods: US8858702[P]. 2014-10-14.
[8] WAGH A S, SINGH D, JEONG S Y. Chemically bonded phosphate ceramics for stabilization and solidification of mixed waste[M]//Hazardous and Radioactive Waste Treatment Technologies Handbook. Boca Raton: CRC Press, 2001: 545-562.
[9] 李东旭,李鹏晓,冯春花.磷酸镁水泥耐水性的研究[J].建筑材料学报,2009,12(5):505-510.
LI D X, LI P X, FENG C H. Research on water resistance of magnesium phosphate cement[J]. Journal of Building Materials, 2009, 12(5): 505-510 (in Chinese).
[10] SARKAR A K. Phosphate cement-based fast-setting binders[J]. American Ceramic Society Bulletin, 1990, 69(2): 234-238.
[11] SUGAMA T, KUKACKA L E. Magnesium monophosphate cements derived from diammonium phosphate solutions[J]. Cement and Concrete Research, 1983, 13(3): 407-416.
[12] 汪宏涛.高性能磷酸镁水泥基材料研究[D].重庆:重庆大学,2006:81-98.
WANG H T. Study on the high performance magnesia-phosphate cement based composites[D]. Chongqing: Chongqing University, 2006: 81-98 (in Chinese).
[13] 杨建明,钱春香,周启兆,等.水玻璃对磷酸钾镁水泥性能的影响[J].建筑材料学报,2011,14(2):227-233.
YANG J M, QIAN C X, ZHOU Q Z, et al. Effect of waterglass on the performance of potassium and magnesium phosphate cement paste[J]. Journal of Building Materials, 2011, 14(2): 227-233 (in Chinese).
[14] CHONG L L, YANG J M, XU Z Z, et al. Freezing and thawing resistance of MKPC paste under different corrosion solutions[J]. Construction and Building Materials, 2019, 212: 663-674.
[15] 顾华健,杨建明,吴庆,等.水玻璃对大流动度磷酸钾镁水泥浆体性能的影响[J].新型建筑材料,2019,46(11):127-130+139.
GU H J, YANG J M, WU Q, et al. Effect of sodium silicate on the performance of high fluidity potassium and magnesium phosphate cement paste[J]. New Building Materials, 2019, 46(11): 127-130+139 (in Chinese).
[16] 纪荣健,杨建明,吴庆,等.水玻璃对大流动度的磷酸铵镁水泥浆体性能的影响[J].硅酸盐通报,2020,39(1):28-33.
JI R J, YANG J M, WU Q, et al. Effect of water glass on properties of high flowing magnesium ammonium phosphate cement paste[J]. Bulletin of the Chinese Ceramic Society, 2020, 39(1): 28-33 (in Chinese).
[17] 杨全兵.混凝土盐冻破坏机理(Ⅱ):冻融饱水度和结冰压[J].建筑材料学报,2012,15(6):741-746.
YANG Q B. One of mechanisms on the deicer-frost scaling of concrete(Ⅱ): degree of saturation and ice-formation pressure during freezing-thawing cycles[J]. Journal of Building Materials, 2012, 15(6): 741-746 (in Chinese).
[18] SHI C J, YANG J M, YANG N, et al. Effect of waterglass on water stability of potassium magnesium phosphate cement paste[J]. Cement and Concrete Composites, 2014, 53: 83-87.