玄武岩纤维编织网增强混凝土高温后力学性能及损伤机理

硅酸盐通报 ›› 2021, Vol. 40 ›› Issue (12): 3976-3984.

玄武岩纤维编织网增强混凝土高温后力学性能及损伤机理

侯振国^1,2, 何海英^1,2, 徐平³, 孙维东^1,2, 代峻峰^1,2, 胡广钦^1,2

1.中国建筑第七工程局有限公司,郑州 450004;
2.中建七局总承包有限公司,郑州 450004;
3.河南理工大学土木工程学院,焦作 454003

出版日期:2021-12-15 发布日期:2022-01-07
通讯作者: 徐平,博士,副教授。E-mail:hpuxuping@126.com
作者简介:侯振国(1985—),男,高工。主要从事工程结构及施工技术研究。E-mail:houzhenguo@cscec.com
基金资助:
河南省科技攻关项目(202102310253);河南省交通运输厅科技项目(2019J-2-13)

Mechanical Properties and Damage Mechanism of Basalt Textile Reinforced Concrete after High Temperature

HOU Zhenguo^1,2, HE Haiying^1,2, XU Ping³, SUN Weidong^1,2, DAI Junfeng^1,2, HU Guangqin^1,2

1. China Construction Seventh Engineering Division Corp. Ltd, Zhengzhou 450004, China;
2. China Construction Seventh Engineering Division Corp. , Ltd General Contracting Company, Zhengzhou 450004, China;
3. School of Civil Engineering, Hennan Polytechnic University, Jiaozuo 454003, China

Online:2021-12-15 Published:2022-01-07

摘要/Abstract

摘要： 通过制备普通及高铝水泥玄武岩纤维编织网增强混凝土(TRC)薄板,采用四点弯曲试验、XRD衍射和扫描电镜微观分析,探究玄武岩TRC在高温作用后的力学性能和损伤机理。研究结果表明:玄武岩纤维织物能有效减小TRC薄板在高温下的变形,抑制裂纹的扩张,且高铝水泥玄武岩TRC高温后的变形及质量损失均小于普通水泥TRC;玄武岩TRC的抗弯承载力随着温度的升高近似呈线性降低,降低的主要原因是高温下混凝土基体损伤、纤维编织网高温劣化及纤维与基体的黏结劣化三者的共同作用;扫描电镜分析可知,高铝酸盐水泥基TRC比普通硅酸盐水泥基TRC更致密,对高温有更强的抵抗作用。本研究可为TRC在高温环境中的设计和应用提供借鉴。

关键词: 玄武岩纤维编织网增强混凝土, 高铝酸盐水泥, 四点弯曲试验, 高温, 微观结构, 损伤机理

Abstract: Basalt textile reinforced concrete (TRC) was prepared with Portland and high aluminate cement respectively. The damage mechanism of TRC after high temperature was investigated by four-point bending test, XRD diffraction and SEM. The results show that basalt fiber textile can effectively reduce the deformation of TRC sheets and inhibit the expansion of cracks at high temperature. The deformation and mass loss of high aluminate cement-based TRC are smaller than those of Portland cement-based TRC after high temperature. The flexural bearing capacity of basalt TRC decreases approximately linearly with the increase of temperature, and the decrease is mainly due to the combined effect of three factors: the damage of concrete matrix at high temperature, the high temperature deterioration of fiber woven fabric, the deterioration of bond between fiber and TRC matrix. SEM analysis shows that high aluminate cement-based TRC is denser and more resistant to high temperature than Portland cement-based TRC. This study provides a reference for the design and application of TRC in high temperature environment.

Key words: basalt textile reinforced concrete, high aluminate cement, four-point bending test, high temperature, microstructure, damage mechanism

中图分类号:

TU528.58

侯振国, 何海英, 徐平, 孙维东, 代峻峰, 胡广钦. 玄武岩纤维编织网增强混凝土高温后力学性能及损伤机理[J]. 硅酸盐通报, 2021, 40(12): 3976-3984.

HOU Zhenguo, HE Haiying, XU Ping, SUN Weidong, DAI Junfeng, HU Guangqin. Mechanical Properties and Damage Mechanism of Basalt Textile Reinforced Concrete after High Temperature[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(12): 3976-3984.

参考文献

[1] LI T, DENG M K, JIN M N, et al. Performance of axially loaded masonry columns confined using textile reinforced concrete (TRC) added with short fibers[J]. Construction and Building Materials, 2021, 279: 122413.
[2] HOMORO O, VU X H, FERRIER E. Experimental and analytical study of the thermo-mechanical behaviour of textile-reinforced concrete (TRC) at elevated temperatures: role of discontinuous short glass fibres[J]. Construction and Building Materials, 2018, 190: 645-663.
[3] 荆磊,尹世平,徐世烺.纤维编织网增强水泥基材料加固砌体结构研究进展[J].土木工程学报,2020,53(6):79-89.
JING L, YIN S P, XU S L. State-of-the-art review on strengthening masonry structures with fabric-reinforced cementitious matrix[J]. China Civil Engineering Journal, 2020, 53(6): 79-89 (in Chinese).
[4] 陈雷,马芹永.碳纤维网增强混凝土巷道抗弯与抗裂性能研究[J].地下空间与工程学报,2020,16(S2):610-617+633.
CHEN L, MA Q Y. Study on bending and cracking resistance of carbon fiber mesh reinforced concrete roadway[J]. Chinese Journal of Underground Space and Engineering, 2020, 16(S2): 610-617+633 (in Chinese).
[5] 尹世平,成帅安,荆磊.FRP和TRC加固砌体墙受剪性能试验研究[J].建筑结构学报,2020,41(S1):315-322.
YIN S P, CHENG S A, JING L, Experimental research on shear performance of masonry wall strengthened with FRP and TRC[J]. Journal of Building Structures, 2020, 41(S1): 315-322 (in Chinese).
[6] NGUYEN K T Q, NAVARATNAM S, MENDIS P, et al. Fire safety of composites in prefabricated buildings: from fibre reinforced polymer to textile reinforced concrete[J]. Composites Part B: Engineering, 2020, 187: 107815.
[7] 尹世平,徐世.纤维编织网增强混凝土的拉伸力学模型[J].复合材料学报,2012,29(5):222-229.
YIN S P, XU S. Tensile mechanical model of textile reinforced concrete[J]. Acta Materiae Compositae Sinica, 2012, 29(5): 222-229 (in Chinese).
[8] 尹世平,徐世烺,王菲.纤维编织网在细粒混凝土中的黏结和搭接性能[J].建筑材料学报,2012,15(1):34-41.
YIN S P, XU S L, WANG F. Investigation on bonding and overlapping performance of textile in fine grained concrete[J]. Journal of Building Materials, 2012, 15(1): 34-41 (in Chinese).
[9] 田稳苓,刘晓铮,赵晓艳,等.玻璃纤维编织网增强混凝土薄板力学性能研究[J].河北工业大学学报,2013,42(6):83-87+99.
TIAN W L, LIU X Z, ZHAO X Y, et al. Mechanical property for thin sheet of glass textile reinforced concrete[J]. Journal of Hebei University of Technology, 2013, 42(6): 83-87+99 (in Chinese).
[10] 王欣,王激扬,沈玲华,等.纤维编织网增强混凝土薄板耐高温力学性能的试验与有限元分析[J].低温建筑技术,2021,43(6):24-27+31.
WANG X, WANG J Y, SHEN L H, et al. Experimental study and fem analysis on high temperature mechanical properties of textile reinforced concrete thin-plates[J]. Low Temperature Architecture Technology, 2021, 43(6): 24-27+31 (in Chinese).
[11] FRST R, VLACH T, POKORNY＇ M, et al. Study of behavior of textile-reinforced concrete with epoxy resin matrix in fire[J]. Fire Technology, 2021: 1-22.
[12] 王激扬,沈玲华,徐世烺.钢纤维TRC薄板的常温及高温后弯曲力学性能[J].工程力学,2016,33(s1):6-10+17.
WANG J Y, SHEN L H, XU S L. Bending behavior of trc thin-plates with short steel fibers at room temperature and after high temperature[J]. Engineering Mechanics, 2016, 33(s1): 6-10+17 (in Chinese).
[13] TRUONG G T, PARK S H, CHOI K K. Tensile behaviors of lap-spliced carbon fiber-textile reinforced mortar composites exposed to high temperature[J]. Materials, 2019, 12(9): 1512.
[14] 杜运兴,张蒙蒙,周芬.玄武岩纤维TRC板拉伸性能试验研究[J].湖南大学学报(自然科学版),2018,45(1):61-67.
DU Y X, ZHANG M M, ZHOU F. Experimental study on tensile performance of basalt TRC plate[J]. Journal of Hunan University (Natural Sciences), 2018, 45(1): 61-67 (in Chinese).

[1]	徐翔波, 于泳, 金祖权, 朱崇爱. 养护制度对超高性能混凝土微观结构和力学性能影响的研究综述[J]. 硅酸盐通报, 2021, 40(9): 2856-2870.
[2]	邵化建, 李宗利, 肖帅鹏, 姚希望, 张宁. 干湿循环作用下混凝土力学性能及微观结构研究[J]. 硅酸盐通报, 2021, 40(9): 2948-2955.
[3]	杨达, 庞来学, 宋迪, 卢明阳, 王佳斌, 管泽斌. 粉煤灰对碱激发矿渣/粉煤灰体系的作用机理研究[J]. 硅酸盐通报, 2021, 40(9): 3005-3011.
[4]	齐秋霖, 周健, 葛仲熙, 李辉, 徐名凤, 陈智丰, 张振秋, 崔素萍. 硫铝酸盐水泥抗酸侵蚀性能与机理研究[J]. 硅酸盐通报, 2021, 40(8): 2508-2514.
[5]	王悦, 王琴, 郑海宇, 詹达富. 分散剂对石墨烯水泥基复合材料压敏性能的影响研究[J]. 硅酸盐通报, 2021, 40(8): 2515-2526.
[6]	郑昊, 梁咏宁, 詹建伟, 季韬. MgO和CaO对碱矿渣混凝土抗碳化性能的影响[J]. 硅酸盐通报, 2021, 40(8): 2564-2573.
[7]	樊祺, 杜红秀, 赵壮. 辅助胶凝材料对预应力高强混凝土管桩强度及工艺的影响[J]. 硅酸盐通报, 2021, 40(8): 2591-2599.
[8]	杨凡凡, 张瑜, 张涛, 王健, 赵伟, 李晋宇, 王坤, 刘玉浩, 郝桓民, 范丽君, 黄小萧, 温广武. SiC/C纤维热力学生长机理研究[J]. 硅酸盐通报, 2021, 40(8): 2702-2712.
[9]	姚苏琴, 查文华, 刘新权, 季圣星, 何昌春, 余跃. 萍乡废弃煤矸石理化特性及热活化性能研究[J]. 硅酸盐通报, 2021, 40(7): 2280-2287.
[10]	阿拉腾沙嘎, 陈冠宏, 陈星. 磁场作用下冷冻铸造法制备仿生材料研究进展[J]. 硅酸盐通报, 2021, 40(7): 2348-2359.
[11]	李克, 杨章富, 李新柱, 朱朝东, 肖美慧, 张俊杰, 卜国秀. γ-AlON陶瓷粉体合成的研究进展[J]. 硅酸盐通报, 2021, 40(7): 2360-2367.
[12]	冯振刚, 马锦元, 刘昌, 王伟, 邓新龙, 林淞山. 热管对沥青混合料降温特性及高温稳定性的影响[J]. 硅酸盐通报, 2021, 40(7): 2437-2443.
[13]	崔聪聪, 李珊, 李伟, 包建勋, 张舸, 王功. 立体光固化3D打印成型碳化硅陶瓷的烧结特性[J]. 硅酸盐通报, 2021, 40(6): 1937-1942.
[14]	陈俊松, 王伟, 乔敏, 赵爽, 曾鲁平. 高岩温对喷射混凝土性能影响研究进展[J]. 硅酸盐通报, 2021, 40(5): 1441-1452.
[15]	朱德, 韩阳, 段君峰, 沈雷, 姚秀鹏, 曹茂森. 高温后钢纤维加强混凝土有效导热系数计算方法[J]. 硅酸盐通报, 2021, 40(5): 1510-1519.