铋及钴掺杂TiO2陶瓷负载膜的制备及光催化性能

摘要/Abstract

摘要： 以钛酸四丁酯为钛源,Bi(NO₃)₃·5H₂O为铋源,Co(NO₃)₂·6H₂O为钴源,采用溶胶-凝胶法在陶瓷基片上分别制备了应用于固定式光催化反应器的Bi-TiO₂复合膜及Co-TiO₂复合膜。研究了涂膜方式及煅烧升温速率对膜表面形态的影响,并以甲基橙溶液为目标降解物,对比了旋涂法及浸渍提拉法制备的薄膜在不同升温速率下的光催化活性。通过热分析仪(TG-DSC)、X射线衍射仪(XRD)和扫描电镜(SEM)等测试手段分析了掺杂薄膜的结构。结果表明,采用旋涂法制备的薄膜与陶瓷基体结合较为紧密,而浸渍提拉法制备的薄膜催化活性较高。当煅烧温度为500 ℃,升温速率为10 ℃/min时,其对甲基橙的降解率较高。当摩尔比为0.010时Bi-TiO₂复合膜的催化活性较佳,100 min光降解甲基橙比率达到8.10%。钴或铋掺杂TiO₂均可提高TiO₂催化剂的光催化活性,Bi-TiO₂膜的催化活性优于Co-TiO₂膜。

关键词: 光催化反应器, 溶胶-凝胶法, Bi-TiO₂复合膜, Co-TiO₂复合膜, 离子掺杂改性, 甲基橙

Abstract: Bi-TiO₂ and Co-TiO₂ composite films applied on the fixed photocatalytic reactor were prepared on ceramic substrate by sol-gel method, with the titanium source of tetrabutyl titanate, the Bi source of Bi(NO₃)₃·5H₂O and the Co source of Co(NO₃)₂·6H₂O. The effects of coating processes and heating rates of calcination on the surface morphology of the films were studied.The photocatalytic activity of the films prepared by spin-coating method and dip-coating method at different heating rates was compared with methyl orange solution. The structures of the films were conducted by TG-DSC, XRD and SEM tests. The results show that Bi or Co ion doping are beneficial to the phase transformation of amorphous TiO₂ to anatase TiO₂.The results show that the films prepared by spin-coating method are closely bonded to the ceramic substrate, while the films prepared by dip-coating method have higher catalytic activity. When the calcination temperature is 500 ℃ and the heating rate is 10 ℃/min, the degradation rate of methyl orange is higher. When the atom mole ratio is 0.010, the photodegradation of methyl orange catalyzed by the Bi-TiO₂ films is up to 8.10% after 100 min reactions. Co or Bi ion-doped process are able to improve the photocatalytic activity of the TiO₂ catalyst and the catalytic activity of Bi-TiO₂ films is better than that of Co-TiO₂ films.

Key words: photocatalytic reactor, sol-gel method, Bi-TiO₂ composite film, Co-TiO₂ composite film, ion doping modification, methyl orange

中图分类号:

TB34

田清泉, 李沛莹, 曹攀婷, 余强霞. 铋及钴掺杂TiO₂陶瓷负载膜的制备及光催化性能[J]. 硅酸盐通报, 2021, 40(11): 3750-3755.

TIAN Qingquan, LI Peiying, CAO Panting, YU Qiangxia. Preparation and Photocatalytic Performance of Bi and Co Doped TiO₂ Ceramic Films[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2021, 40(11): 3750-3755.

参考文献

[1] 石双欣,卫静.光催化技术处理染料废水研究进展[J].绿色科技,2021,23(2):63-65.
SHI S X, WEI J. Research progress in the treatment of dye wastewater by photocatalytic technology[J]. Journal of Green Science and Technology, 2021, 23(2): 63-65 (in Chinese).
[2] 赖苗.Ag、Bi修饰TiO₂光催化降解甲苯的性能及机理研究[D].西安:陕西科技大学,2019.
LAI M. Research on performance and mechanism of photocatalytic toluene degradation by Ag and/or Bi modified TiO₂[D]. Xi'an: Shaanxi University of Science & Technology, 2019 (in Chinese).
[3] 陈艺兰,肖良建,陈文玉,等.花生壳改性TiO₂可见光催化降解甲基橙研究[J].化工新型材料,2020,48(9):231-234+239.
CHEN Y L, XIAO L J, CHEN W Y, et al. Photocatalytic degradation of methyl organge with peanut shell modified TiO₂[J]. New Chemical Materials, 2020, 48(9): 231-234+239 (in Chinese).
[4] 张静玉,苑蕾.偶氮染料甲基橙的降解研究综述[J].山东化工,2017,46(6):157-158.
ZHANG J Y, YUAN L. Research on the degradation of azo dye methyl orange[J]. Shandong Chemical Industry, 2017, 46(6): 157-158 (in Chinese).
[5] 张青青,曾婷,张磊,等.光催化膜反应器应用于废水处理的研究进展[J].环境化学,2020,39(5):1297-1306.
ZHANG Q Q, ZENG T, ZHANG L, et al. Review of photocatalytic membrane reactors in water treatment[J]. Environmental Chemistry, 2020, 39(5): 1297-1306 (in Chinese).
[6] SAMY M, IBRAHIM M G, FUJII M, et al. CNTs/MOF-808 painted plates for extended treatment of pharmaceutical and agrochemical wastewaters in a novel photocatalytic reactor[J]. Chemical Engineering Journal, 2021, 406: 127152.
[7] 徐春华,邹晓娜,张梦薇,等.光催化反应器的设计与应用研究进展[J].化工技术与开发,2021,50(4):29-32.
XU C H, ZOU X N, ZHANG M W, et al. Research progress on design and application of photocatalytic reactor[J]. Technology & Development of Chemical Industry, 2021, 50(4): 29-32 (in Chinese).
[8] 刘恒.固定化光催化剂涂层的制备及其对有机污染物降解性能的研究[D].南昌:南昌大学,2020.
LIU H. Preparation of immobilized photocatalyst coatings and study on the performance for the degradation of organic pollutants[D]. Nanchang: Nanchang University, 2020 (in Chinese).
[9] 方书起,曹奇,常春,等.以TiO₂为光催化剂的反应器结构研究进展[J].现代化工,2019,39(3):45-50.
FANG S Q, CAO Q, CHANG C, et al. Research advances in structure of reactor with TiO₂ as photocatalyst[J]. Modern Chemical Industry, 2019, 39(3): 45-50 (in Chinese).
[10] 杨瑾.Bi-TiO₂系光催化剂的制备及活性炭/Bi-TiO₂在水性涂料中应用初探[D].西安:西北大学,2018.
YANG J. Preparation of Bi-TiO₂ photocatalyst and application of activated carbon/Bi-TiO₂ in waterborne coatings[D]. Xi'an: Northwest University, 2018 (in Chinese).
[11] 芦琼,翟莉慧,肖寒,等.TiO₂掺杂改性提高光催化剂有机物降解能力技术研究进展[J].广东化工,2021,48(1):37-39+59.
LU Q, ZHAI L H, XIAO H, et al. Research progress of doping modification of TiO₂ to improve photocatalyst organic degradation[J]. Guangdong Chemical Industry, 2021, 48(1): 37-39+59 (in Chinese).
[12] 崔丹凤,李渊凯,范燕云,等.Co₃O₄/TiO₂纳米材料的制备及其光催化性能[J].微纳电子技术,2020,57(10):776-781.
CUI D F, LI Y K, FAN Y Y, et al. Fabrication and photocatalytic performance of Co₃O₄/TiO₂ nanomaterials[J]. Micronanoelectronic Technology, 2020, 57(10): 776-781 (in Chinese).
[13] 王红月.负载型g-C₃N₄光催化剂的制备及降解罗丹明B性能的研究[D].沈阳:辽宁大学,2020.
WANG H Y. Preparation of supported g-C₃N₄ photocatalyst and study on degradation of Rhodamine B[D]. Shenyang: Liaoning University, 2020 (in Chinese).
[14] 秦海洋,郑永杰,田景芝,等.Bi₂O₃-TiO₂/污泥活性炭复合催化剂的制备及其可见光催化性能研究[J].现代化工,2021,41(3):154-158.
QIN H Y, ZHENG Y J, TIAN J Z, et al. Preparation of Bi₂O₃-TiO₂/sludge activated carbon composite catalyst and study on its photocatalytic performance[J]. Modern Chemical Industry, 2021, 41(3): 154-158 (in Chinese).
[15] WANG N, LI X, YANG Y L, et al. Two-stage calcination composite of Bi₂O₃-TiO₂ supported on powdered activated carbon for enhanced degradation of sulfamethazine under solar irradiation[J]. Journal of Water Process Engineering, 2020, 35: 101220.
[16] 吴国浩,郑树凯,吕霄.Bi掺杂锐钛矿相TiO₂第一性原理计算[J].无机化学学报,2013,29(1):9-14.
WU G H, ZHENG S K, LÜ X. First-principles calculation of Bi-doped anatase TiO₂[J]. Chinese Journal of Inorganic Chemistry, 2013, 29(1): 9-14 (in Chinese).
[17] 邹浩,宋绵新,刘攀,等.Bi₂O₃/TiO₂复合光催化剂对甲基橙的光催化作用[J].武汉理工大学学报,2014,36(9):12-16.
ZOU H, SONG M X, LIU P, et al. Photocatalytic research of Bi₂O₃/TiO₂ composite catalysts on methyl orange[J]. Journal of Wuhan University of Technology, 2014, 36(9): 12-16 (in Chinese).

铋及钴掺杂TiO₂陶瓷负载膜的制备及光催化性能

Preparation and Photocatalytic Performance of Bi and Co Doped TiO₂ Ceramic Films

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	段宁, 张湘泰, 陆成龙, 张银凤, 李崇瑞. 硝酸对溶胶-凝胶法制备AlOOH胶粒粒度的影响[J]. 硅酸盐通报, 2021, 40(9): 3105-3113.
[2]	刘帅, 谢银德, 闫硕, 侯保森, 刘瑞杰. 复合催化剂ZnFe₂O₄/FeVO₄的制备及光催化性能[J]. 硅酸盐通报, 2021, 40(5): 1707-1713.
[3]	吴洪, 陈前林, 李翠芹. 多孔竹炭负载SnO₂的制备及其电化学性能研究[J]. 硅酸盐通报, 2021, 40(11): 3740-3749.
[4]	马生花;马芙莲;解玉龙. BiOI/ZIF-8复合材料的制备及光催化性能[J]. 硅酸盐通报, 2020, 39(9): 2993-3000.
[5]	邵凌波;田长安;梁升;王亚君;陈捷;阳杰. 固体氧化物燃料电池电解质材料 Ce0.8Sm0.2-xCuxO1.9-δ的制备与性能研究[J]. 硅酸盐通报, 2020, 39(5): 1608-1613.
[6]	陈七;何峰;张树岩;张博文;张鸣奇;刘锡宇;施江. 不同ATO掺量对SiO2/ATO-SiO2疏水型抗静电增透膜性能的影响[J]. 硅酸盐通报, 2019, 38(8): 2391-239.
[7]	张小婷;汪潇;杨浩远;李东林;赵建礼. pH值对纤维增强SiO2气凝胶隔热材料性能的影响[J]. 硅酸盐通报, 2019, 38(8): 2668-267.
[8]	高奕红;王珊;邓玲娟. 壳聚糖/SiO2复合材料的制备及对甲基橙的吸附性能[J]. 硅酸盐通报, 2019, 38(5): 1579-158.
[9]	焦静涛;姜芸;杨松;张敬敏;邓朝勇;王旭. 锆钛酸钡钙的结构与铁电光学性能研究[J]. 硅酸盐通报, 2019, 38(11): 3524-352.
[10]	陆文涛;赵青南;王晓宏;常潇;董玉红;赵杰. 可见光照射下Fe3+掺杂量对玻璃基TiO2薄膜亲水性能的影响[J]. 硅酸盐通报, 2019, 38(10): 3293-330.
[11]	刘展晴. 钛酸铜镧粉末及陶瓷的制备、结构及介电性能研究[J]. 硅酸盐通报, 2018, 37(4): 1332-1337.
[12]	孙美丽;钱海燕;陈京. 二氧化钛薄膜的制备及光催化性能研究[J]. 硅酸盐通报, 2017, 36(8): 2595-2599.
[13]	刘展晴. 溶胶-凝胶法制备Na1/2La1/2Cu3Ti4O12粉体及陶瓷的结构与巨介电性研究[J]. 硅酸盐通报, 2017, 36(3): 816-821.
[14]	林茵茵;谢襄漓;李存军;王昕;张兵;王林江. LDO负载纳米二氧化钛复合物的制备及其光催化性能研究[J]. 硅酸盐通报, 2017, 36(11): 3829-3834.
[15]	邢宏伟;谷少鹏;刘志刚;杨立荣. 高炉渣纤维负载TiO2光催化材料的制备及其光催化性能[J]. 硅酸盐通报, 2016, 35(8): 2329-2334.