不锈钢渣理化性质分析与应用研究

硅酸盐通报 ›› 2018, Vol. 37 ›› Issue (4): 1225-1230.

不锈钢渣理化性质分析与应用研究

吴春丽;谢红波;陈哲;麦俊明;苏青

广东省建筑材料研究院,广州,510000

出版日期:2018-04-15 发布日期:2021-01-18
基金资助:
广东省省级科技计划项目(2017A070701037)

Analysis on Physicochemical Properties and Research on Application of Stainless Steel Slag

WU Chun-li;XIE Hong-bo;CHEN Zhe;MAI Jun-ming;SU Qing

Online:2018-04-15 Published:2021-01-18

摘要/Abstract

摘要： 借助于XRD、SEM和DSC/TG等测试分析手段进行不锈钢渣理化性质分析与表征.结果表明:不锈钢渣化学成分主要是SiO2和CaO,其次是MgO、Al2O3及Fe2O3;矿物组成包括硅酸三钙(Ca3SiO5)、硅酸二钙(Ca2SiO4)、硅钙石(Ca3Si2O7)、硅酸钙(CaSiO3)及RO相;微观结构由许多尺寸大小不等的颗粒组成,孔隙大、结构疏松;内外照射指数IRa和Iγ均小于1.0,符合GB 6566-2010标准;当不锈钢渣质量百分比掺量为30%时,28 d抗压强度基本达到P· C32.5复合硅酸盐水泥标准,且7 d活性指数显著高于28 d活性指数.并依据研究结果分析不锈钢渣在水泥、混凝土及建筑材料领域资源化利用的可行性.

关键词: 不锈钢渣;理化性质;活性指数;应用分析

Abstract: Analysis and characterization on physicochemical properties of stainless steel slag by XRD, SEM and DSC/TG and so on.The results indicate that the main chemical components of stainless steel slag are SiO2and CaO, the second MgO, Al2O3and Fe2O3.The phase consist of Ca 3SiO5, Ca2SiO4, Ca3Si2O7,CaSiO3and few RO.Microstructure is composed of many particles of unequal size, with the large pore and loose structure.Either of the internal exposure index(IRa)and external exposure index (Iγ)are less than 1.0, which conforms to GB 6566-2010 standard.When the quality percentage of stainless steel slag is 30%,the compressive strength of 28 d reaches the P· C 32.5 standard, and the activity of 7 d is significantly higher than 28 d.And analysis on feasibility of the resource utilization for stainless steel slag in cement,concrete and building materials field based on the research results.

Key words: stainless steel slag;physicochemical property;activity index;application analysis

中图分类号:

TQ174.5

吴春丽;谢红波;陈哲;麦俊明;苏青. 不锈钢渣理化性质分析与应用研究[J]. 硅酸盐通报, 2018, 37(4): 1225-1230.

WU Chun-li;XIE Hong-bo;CHEN Zhe;MAI Jun-ming;SU Qing. Analysis on Physicochemical Properties and Research on Application of Stainless Steel Slag[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2018, 37(4): 1225-1230.

[1]	余冬玲;郑琦;邓立钧;吴南星;陈涛;廖达海. 陶瓷干法造粒搅拌槽结构对粉体混合效果的影响[J]. 硅酸盐通报, 2019, 38(5): 1442-144.
[2]	吴南星;甘振华;赵增怡;余冬玲;江竹亭;廖达海. 挡板对陶瓷干法造粒气-固两相流混合过程的影响[J]. 硅酸盐通报, 2019, 38(1): 239-245.
[3]	吴南星;邓立钧;赵增怡;余冬玲;江竹亭;廖达海. 挡板结构对陶瓷干法造粒室内粉体混合效果的影响[J]. 硅酸盐通报, 2018, 37(12): 3802-3806.
[4]	吴南星;邓立钧;朱祚祥;余冬玲;陈涛;廖达海. 十字形挡板造粒室内干法制粉混料过程数值模拟[J]. 硅酸盐通报, 2018, 37(11): 3545-3550.
[5]	廖达海;朱祚祥;吴南星;江竹亭;陈涛. 基于CFD的陶瓷干法制粉造粒室挡板数目优化[J]. 硅酸盐通报, 2018, 37(5): 1667-1674.
[6]	吴南星;赵增怡;花拥斌;宁翔;徐佳杰;廖达海. 陶瓷墙地砖干法制粉造粒立柱与颗粒均匀度的影响[J]. 硅酸盐通报, 2017, 36(11): 3630-3635.