B4 C／Al-Mg 复合材料的制备及性能研究

硅酸盐通报 ›› 2016, Vol. 35 ›› Issue (9): 2816-2820.

B4 C／Al-Mg 复合材料的制备及性能研究

王涛

西安科技大学材料学院,西安,710054

出版日期:2016-09-15 发布日期:2021-01-18

Preparation and Properties of B4 C/Al-Mg Composite Material

WANG Tao

Online:2016-09-15 Published:2021-01-18

摘要/Abstract

摘要： 用模压成型法制备了B4 C／Al-Mg复合材料。采用水静力天平、抗折强度测定仪、X射线衍射仪和SEM对其物理性能、力学性能和晶体结构和微观形貌进行了分析，研究了原料配方及烧结温度对B4 C／Al-Mg复合材料的晶型转变、微观形貌、体积密度、力学性能等的影响。结果表明，当Al、Mg的配比为37．0％和3．0％，烧结温度为1150℃时复合材料的综合性能最佳，体积密度为2．40 g／cm3，抗折强度为303．67 MPa，硬度为79．4 HRC。

关键词: B4 C/Al-Mg复合材料;模压成型法;力学性能

Abstract: The B4 C/Al-Mg composites were prepared by compression molding method , the crystal phases and micrographs were analyzed by XRD and SEM .The effect of Mg content and the sinter temperature on the volume density and mechanical properties of composite were studied .The results show:when Al and Mg contents are 37%and 3%, the sintering temperature is 1150 ℃,the mechanical properties of B 4 C/Al-Mg composites are best .The bending strength is 303.67 MPa, hardness is 79.4 HRC and volume density is 2 .40 g/cm3 .

Key words: B4 C/Al-Mg composite material;molding processing method;mechanical property

中图分类号:

TQ163

王涛. B4 C／Al-Mg 复合材料的制备及性能研究[J]. 硅酸盐通报, 2016, 35(9): 2816-2820.

WANG Tao. Preparation and Properties of B4 C/Al-Mg Composite Material[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2016, 35(9): 2816-2820.

[1]	徐保海;王晓刚;李阳;吴泽民;任小雷;段晓波. 热源并联式全透气碳化硅合成炉的模拟分析[J]. 硅酸盐通报, 2017, 36(4): 1401-1405.
[2]	王福;曹文斌;孙加林;何荣亮. 碳热还原法制备球形SiC微粉[J]. 硅酸盐通报, 2007, 26(6): 1049-1052.