LDHs-NO2对水泥砂浆性能及钢筋锈蚀的影响

doi:10.16552/j.cnki.issn1001-1625.2024.1003

硅酸盐通报 ›› 2025, Vol. 44 ›› Issue (1): 1-10.DOI: 10.16552/j.cnki.issn1001-1625.2024.1003

• 水泥混凝土 • 下一篇

LDHs-NO₂对水泥砂浆性能及钢筋锈蚀的影响

张轶¹, 张彪¹, 邓翔文², 何宏杰³

1.枣庄学院城市与建筑工程学院,枣庄 277100;
2.枣庄学院美术与艺术设计学院,枣庄 277100;
3.同济大学土木工程学院,上海 200092

收稿日期:2024-08-29 修订日期:2024-10-27 出版日期:2025-01-15 发布日期:2025-01-23
通信作者: 张彪,博士,讲师。E-mail:zhangbiao0610@126.com
作者简介:张轶(1985—),男,高级实验师。主要从事钢筋混凝土腐蚀防护方面的研究。E-mail:zhy180212@163.com
基金资助:
国家自然科学基金(52008234)

Effect of LDHs-NO₂ on Properties of Cement Mortar and Corrosion of Steel Bar

ZHANG Yi¹, ZHANG Biao¹, DENG Xiangwen², HE Hongjie³

1. School of City and Architecture Engineering, Zaozhuang University, Zaozhuang 277100, China;
2. College of Art and Design, Zaozhuang University, Zaozhuang 277100, China;
3. College of Civil Engineering, Tongji University, Shanghai 200092, China

Received:2024-08-29 Revised:2024-10-27 Published:2025-01-15 Online:2025-01-23

摘要/Abstract

摘要： 本文采用水热法将NO^-₂插层到Zn-Al-LDHs(LDHs为层状双金属氢氧化物)层间制备了改性水滑石(LDHs-NO₂),并对LDHs-NO₂进行表征,探究了不同掺量LDHs-NO₂对水泥砂浆流动性、力学性能、氯离子扩散系数、孔隙结构、氯离子吸附量和钢筋阻锈性能的影响。试验结果表明,在水泥砂浆中掺入不同掺量LDHs-NO₂,水泥砂浆的抗压、抗折强度提高,同时氯离子扩散系数和孔隙率降低。与基准组相比,掺加2%(质量分数)LDHs-NO₂的水泥砂浆性能提升最为显著,之后随着LDHs-NO₂掺量(4%、6%)继续增加,水泥砂浆的流动性、力学性能降低,但仍高于基准组;孔隙率有所增大,但仍低于基准组。LDHs-NO₂通过层间离子交换实现对Cl^-的吸附,在吸附Cl^-过程中伴随着层间NO^-₂的释放。LDHs-NO₂能够有效延缓水泥砂浆中的钢筋锈蚀,且在一定范围内LDHs-NO₂掺量越多,水泥砂浆中钢筋的耐腐蚀性能越好。

关键词: 水泥砂浆, 改性水滑石, 氯离子吸附, 钢筋锈蚀, 阻锈机理

Abstract: In this paper, NO^-₂ was intercalated into the interlayer of Zn-Al-LDHs (layered double hydroxides, LDHs) by hydrothermal method to prepare modified hydrotalcite (LDHs-NO₂), and LDHs-NO₂ was characterized. The effect of different LDHs-NO₂ content on the fluidity, mechanical properties, chloride ion diffusion coefficient, pore structure, chloride ion adsorption of cement mortar and corrosion resistance of steel bar was investigated. The test results show that the compressive strength and flexural strength of cement mortar are improved, and the chloride ion diffusion coefficient and porosity are decreased by adding different content of LDHs-NO₂ into cement mortar. Compared with the reference group, the performance of cement mortar with 2% (mass fraction) LDHs-NO₂ is the most significant. Then, with the continuous increase of LDHs-NO₂ content (4%, 6%), the fluidity and mechanical properties of mortar decrease, but still higher than the reference group. The porosity of cement mortar has increased, but it is still lower than the reference group. LDHs-NO₂ achieves the adsorption of Cl^- through interlayer ion exchange, which is accompanied by the release of interlayer NO^-₂ during the adsorption of Cl^-. LDHs-NO₂ can effectively delay the corrosion of steel bars in cement mortar, and the more LDHs-NO₂ content in a certain range, the better the corrosion resistance of steel bars.

Key words: cement mortar, modified hydrotalcite, chloride ion adsorption, corrosion of steel bar, rust inhibition mechanism

中图分类号:

TU528

张轶, 张彪, 邓翔文, 何宏杰. LDHs-NO₂对水泥砂浆性能及钢筋锈蚀的影响[J]. 硅酸盐通报, 2025, 44(1): 1-10.

ZHANG Yi, ZHANG Biao, DENG Xiangwen, HE Hongjie. Effect of LDHs-NO₂ on Properties of Cement Mortar and Corrosion of Steel Bar[J]. BULLETIN OF THE CHINESE CERAMIC SOCIETY, 2025, 44(1): 1-10.

参考文献

[1] 郭群, 李晓珍, 宋屹林, 等. 钢筋阻锈剂在碳化钢筋混凝土中的阻锈作用[J]. 建筑材料学报, 2023, 26(1): 21-28.
GUO Q, LI X Z, SONG Y L, et al. Effect of steel bar corrosion inhibitors in carbonated reinforced concrete[J]. Journal of Building Materials, 2023, 26(1): 21-28 (in Chinese).
[2] LI C Z, JIANG L H, LI S S. Effect of limestone powder addition on threshold chloride concentration for steel corrosion in reinforced concrete[J]. Cement and Concrete Research, 2020, 131: 106018.
[3] ZUO J D, WU B, DONG B Q, et al. Effects of nitrite ion intercalated CaAl and MgAl layered double hydroxides on the properties of concrete mortar[J]. Cement and Concrete Composites, 2024, 145: 105306.
[4] ZHANG Y G, SUN C T, ZHANG P, et al. Chloride binding of monosulfate hydrate (AFm) and its effect on steel corrosion in simulated concrete pore solution[J]. Journal of Building Engineering, 2023, 67: 105945.
[5] 梁文杰, 谭洪波, 吕周岭. 混凝土内源氯离子固化的研究进展[J]. 硅酸盐通报, 2023, 42(8): 2667-2682.
LIANG W J, TAN H B, LYU Z L. Research progress on endogenous chloride ion binding of concrete[J]. Bulletin of the Chinese Ceramic Society, 2023, 42(8): 2667-2682 (in Chinese).
[6] HU X, POON C S. Chloride-related steel corrosion initiation in cement paste prepared with the incorporation of blast-furnace slag[J]. Cement and Concrete Composites, 2022, 126: 104349.
[7] 冯跃, 耿健, 李东. 焙烧水滑石对砂浆中氯离子渗透的影响[J]. 硅酸盐通报, 2018, 37(4): 1195-1199.
FENG Y, GENG J, LI D. Influence of calcined hydrotalcite on chloride penetration in mortar[J]. Bulletin of the Chinese Ceramic Society, 2018, 37(4): 1195-1199 (in Chinese).
[8] 李珂珂, 薛江伟, 王露威, 等. 镁铝水滑石对高铁低钙硅酸盐水泥性能的影响[J]. 无机盐工业, 2024, 56(4): 57-63.
LI K K, XUE J W, WANG L W, et al. Effect of MgAl-layered double hydroxides on properties of high-iron low-calcium Portland cement[J]. Inorganic Chemicals Industry, 2024, 56(4): 57-63 (in Chinese).
[9] CHEN Y X, SHUI Z H, CHEN W, et al. Chloride binding of synthetic Ca-Al-NO₃ LDHs in hardened cement paste[J]. Construction and Building Materials, 2015, 93: 1051-1058.
[10] YANG Z X, FISCHER H, POLDER R. Synthesis and characterization of modified hydrotalcites and their ion exchange characteristics in chloride-rich simulated concrete pore solution[J]. Cement and Concrete Composites, 2014, 47: 87-93.
[11] CAO Y H, ZHENG D J, LUO J S, et al. Insight into the fabrication of ZnAl layered double hydroxides intercalated with organic anions and their corrosion protection of steel reinforced concrete[J]. Journal of the Electrochemical Society, 2019, 166(16): 617-623.
[12] TIAN Y W, DONG C F, WANG G, et al. Zn-Al-NO₂ layered double hydroxide as a controlled-release corrosion inhibitor for steel reinforcements[J]. Materials Letters, 2019, 236: 517-520.
[13] CHEN M Z, WU F, YU L W, et al. Chloride binding capacity of LDHs with various divalent cations and divalent to trivalent cation ratios in different solutions[J]. CrystEngComm, 2019, 21(44): 6790-6800.
[14] SU Y, QIU S H, YANG D P, et al. Active anti-corrosion of epoxy coating by nitrite ions intercalated MgAl LDH[J]. Journal of Hazardous Materials, 2020, 391: 122215.
[15] WANG Y, ZHANG D. Synthesis, characterization, and controlled release anticorrosion behavior of benzoate intercalated Zn-Al layered double hydroxides[J]. Materials Research Bulletin, 2011, 46(11): 1963-1968.
[16] ALIBAKHSHI E, GHASEMI E, MAHDAVIAN M, et al. Corrosion inhibitor release from Zn-Al-[PO^3-₄]-[CO^2-₃] layered double hydroxide nanoparticles[J]. Progress in Color, Colorants and Coatings, 2016, 9: 233-248.
[17] HE Q Q, ZHOU M J, HU J M. Electrodeposited Zn-Al layered double hydroxide films for corrosion protection of aluminum alloys[J]. Electrochimica Acta, 2020, 355: 136796.
[18] SUBASRI R, SOMA RAJU K R C, REDDY D S, et al. Environmentally friendly Zn-Al layered double hydroxide (LDH)-based sol-gel corrosion protection coatings on AA 2024-T3[J]. Journal of Coatings Technology and Research, 2019, 16(5): 1447-1463.
[19] CHEN M Z, WEI Y N, ZHENG H B, et al. Ca-LDH-modified cementitious coating to enhance corrosion resistance of steel bars[J]. Journal of Building Engineering, 2022, 51: 104301.
[20] 张曼, 赵云良, 吴飞达. 焙烧态Ca-Mg-Al类水滑石的制备及其吸附As(Ⅴ)的研究[J]. 硅酸盐通报, 2018, 37(4): 1344-1349+1354.
ZHANG M, ZHAO Y L, WU F D. Preparing calcined Ca-Mg-Al hydrotalcite-like compound for adsorption of As(Ⅴ) in water[J]. Bulletin of the Chinese Ceramic Society, 2018, 37(4): 1344-1349+1354 (in Chinese).
[21] TANG Y M, ZHANG F, HU S X, et al. Novel benzimidazole derivatives as corrosion inhibitors of mild steel in the acidic media. part I: gravimetric, electrochemical, SEM and XPS studies[J]. Corrosion Science, 2013, 74: 271-282.
[22] POZNYAK S K, TEDIM J, RODRIGUES L M, et al. Novel inorganic host layered double hydroxides intercalated with guest organic inhibitors for anticorrosion applications[J]. ACS Applied Materials & Interfaces, 2009, 1(10): 2353-2362.
[23] CAO Y H, DONG S G, ZHENG D J, et al. Multifunctional inhibition based on layered double hydroxides to comprehensively control corrosion of carbon steel in concrete[J]. Corrosion Science, 2017, 126: 166-179.
[24] YANG Z X, FISCHER H, POLDER R. Laboratory investigation of the influence of two types of modified hydrotalcites on chloride ingress into cement mortar[J]. Cement and Concrete Composites, 2015, 58: 105-113.
[25] SHARMILA P, DHINAKARAN G. Compressive strength, porosity and sorptivity of ultra fine slag based high strength concrete[J]. Construction and Building Materials, 2016, 120: 48-53.
[26] DUAN P, CHEN W, MA J T, et al. Influence of layered double hydroxides on microstructure and carbonation resistance of sulphoaluminate cement concrete[J]. Construction and Building Materials, 2013, 48: 601-609.
[27] SHI J J, MING J, SUN W. Electrochemical behaviour of a novel alloy steel in alkali-activated slag mortars[J]. Cement and Concrete Composites, 2018, 92: 110-124.
[28] CUI L, HANG M Y, HUANG H H, et al. Experimental study on multi-component corrosion inhibitor for steel bar in chloride environment[J]. Construction and Building Materials, 2021, 313: 125533.
[29] BELLAL Y, BENGHANEM F, KERAGHEL S. A new corrosion inhibitor for steel rebar in concrete: synthesis, electrochemical and theoretical studies[J]. Journal of Molecular Structure, 2021, 1225: 129257.

LDHs-NO₂对水泥砂浆性能及钢筋锈蚀的影响

Effect of LDHs-NO₂ on Properties of Cement Mortar and Corrosion of Steel Bar

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	沈斐, 乔敏, 单广程, 吴庆勇. 负载不同引气剂的SiO₂复合材料的制备及其在水泥基材料中的应用[J]. 硅酸盐通报, 2024, 43(9): 3157-3163.
[2]	崔莹莹, 何健辉, 吕民望, 杨露, 刘云鹏. 可完全循环水泥砂浆配料制备贝利特水泥熟料的性能研究[J]. 硅酸盐通报, 2024, 43(9): 3348-3358.
[3]	黄煌煌, 陈铁锋, 高小建. CO₂矿化改性高钙粉煤灰对水泥砂浆力学性能和微结构的影响[J]. 硅酸盐通报, 2024, 43(5): 1889-1896.
[4]	张路曼, 侯风. 相变调温墙板热工性能试验和数值模拟研究[J]. 硅酸盐通报, 2024, 43(3): 866-877.
[5]	张逸舟, 苏俊儒, 郑城, 王迎豪, 蒲云东, 张惠一, 袁小亚. 石墨烯与羟基化石墨烯复掺对水泥砂浆性能的影响[J]. 硅酸盐通报, 2024, 43(11): 3968-3975.
[6]	李祥翔, 金祖权, 逄博. 杂散电流与复合离子作用下埋地碱激发矿渣混凝土中钢筋锈蚀研究[J]. 硅酸盐通报, 2024, 43(10): 3595-3606.
[7]	万小梅, 王博世, 孙忠涛, 张东方. 碱激发矿渣液相环境中钢筋钝化膜形成及破坏规律[J]. 硅酸盐通报, 2024, 43(10): 3607-3614.
[8]	张娜, 孙倩, 张鹏宇, 王冬梅, 王琴. 聚合物对砂浆热老化后防水及力学性能的影响[J]. 硅酸盐通报, 2023, 42(8): 2703-2711.
[9]	何娅兰, 宁麟, 李炀, 钟秀杰. 基于核磁共振技术对水泥砂浆高温后孔隙结构及水分迁移特征的研究[J]. 硅酸盐通报, 2023, 42(7): 2336-2343.
[10]	周丽娜, 蔡颖, 马财龙, 罗玲. 水滑石复合水泥基材料氯离子吸附能力的研究进展[J]. 硅酸盐通报, 2023, 42(4): 1137-1147.
[11]	余海燕, 徐晴, 王英翔, 董德宇. 不同环境下碳铝酸钙的稳定性研究[J]. 硅酸盐通报, 2023, 42(3): 845-853.
[12]	陈文瑶, 张卓翔, 孟二从, 黎强. 膨润土和玄武岩纤维改性水泥砂浆的防渗抗裂性能[J]. 硅酸盐通报, 2023, 42(2): 439-447.
[13]	李贤, 宁麟, 陈亮亮, 李炀, 邓小江. 基于核磁共振技术分析骨料粒径对水泥砂浆微观结构的影响[J]. 硅酸盐通报, 2023, 42(12): 4216-4223.
[14]	李帅, 梅军鹏, 李海南, 戴俊杰, 谢安合. 聚甲醛-玄武岩混杂纤维增强砂浆力学性能[J]. 硅酸盐通报, 2023, 42(10): 3454-3461.
[15]	郝明月, 李静, 蔡基伟, 许鸽龙, 田青. 磁铁尾矿砂在水泥基材料中的化学稳定性研究[J]. 硅酸盐通报, 2023, 42(10): 3688-3694.